CN101869538B - Tourmaline toothpaste - Google Patents

Abstract

The invention relates to a tourmaline toothpaste, which comprises the following components: tourmaline powder, calcium carbonate, hydrated silica, sorbic alcohol, deionized water, sodium lauryl sulfate, sodium benzoate, sodium carboxymethylcellulose, xanthan gum, sodium pyrophosphate, saccharin, peppermint essence and the like. The tourmaline toothpaste can effectively clean teeth, remove mildew stains and dental stains, diminish inflammation, stop bleeding, prevent dental ulcer, inhibit oral bacteria, and remove bad breath; and rich trace elements can inhibit the intrusion of pathogenes such as bacteria and the like.

Description

A kind of tourmaline toothpaste

Technical field

The invention belongs to the bath accessory technical field, particularly a kind of tourmaline toothpaste.

Background technology

The toothpaste of domestic production is at present mainly processed by raw materials such as abrasivus, foaming agent, heat preserving agent, thickening agent, sweeting agent, oxidant, essence, and significant feature is cleaning teeth, remove tooth stain, mildew etc.These toothpaste rely on the abrasivus that contains in toothpaste and the mildew generation physical property of dental surface to rub, and reach the removal purpose, but DeGrain, and tooth is had certain damage.And oral ulcer also is one of recurrent oral problem at present, is a kind of common oral disease, due to virus or antibacterial, is generally caused by streptococcus, staphylococcus aureus, escherichia coli.Some toothpaste adds Chinese herbal medicine in raw material at present, like Radix Zanthoxyli, Flos Lonicerae, Radix Notoginseng etc.Purpose is to eliminate pathogenic bacteria.Prevent gingival hemorrhage, oral ulcer, remove halitosis etc., but some user reaction, taste is difficult for accepting, and can't satisfy consumers in general.

Summary of the invention

The purpose of this invention is to provide a kind of tourmaline toothpaste; This toothpaste not only has the effect of ordinary toothpaste cleaning and tooth-whitening; And have and remove halitosis, antiinflammatory, stop blooding, prevent many effects such as oral ulcer, and taste is pure and fresh, is easy to people and accepts.

Purpose of the present invention provides a kind of tourmaline toothpaste.

Another object of the present invention provides the method for preparing of said tourmaline toothpaste.

The objective of the invention is to realize through following technical scheme.

A kind of tourmaline toothpaste, it is formed by the feedstock production that comprises following parts by weight;

Preferably, a kind of tourmaline toothpaste, it is formed by the feedstock production that comprises following parts by weight;

The method for preparing of a kind of tourmaline toothpaste of the present invention, it may further comprise the steps;

1) at first the tourmaline mineral aggregate is joined and carry out fragmentation in the disintegrating machine; After washing, drying, get in the twin-roll machine and grind to form the fine sand shape; Remove ferrum wherein through magnetic separation, get in the high-speed eddy mill through closed conduit again and pulverize, and the entering grader separates; Obtaining fine grained is Φ≤1250 order powder body, gets in the supersonic airstream mill and further is ground into the micro/nano level tourmaline powder body that granularity is 3-5 μ m;

2) take by weighing each raw material by formula ratio, using deionized water to be configured to concentration sorbitol is 70% solution for standby; Again sodium carboxymethyl cellulose, xanthan gum, tetrasodium pyrophosphate, sodium benzoate and glucide are joined in the remaining deionized water, high-speed stirred, 6000 rev/mins, time 30-50 minute, it was subsequent use to process transparent colloidal solution;

3) with after sorbitol solution and the transparent colloidal solution mixing, add calcium carbonate, tourmaline powder, sodium lauryl sulfate and hydration Silicon stone again, under greater than the 0.096Mpa vacuum; High-speed stirred 1-2 hour; Add Herba Menthae essence again, under greater than the 0.096Mpa vacuum, high-speed stirred 10-20 minute; Process mastic, packing is promptly accomplished.

Tourmaline powder in the toothpaste of the present invention is a micro/nano level, discharges a large amount of anion being heated, rubbing or can produce electric charge during other energy excitations, and can be emitting far-infrared, has special electromagnetic protection function, if.

Tourmaline toothpaste of the present invention through a large amount of experimental studies of inventor, is selected specific raw material and weight proportion; Solved the deficiency of prior art; It can not only the effective cleaning tooth, removes mildew, tooth stain, and can antiinflammatory, stop blooding, prevent oral ulcer; And can restrain oral cavity bacterium and remove halitosis, abundant trace element can be restrained the intrusion of pathogen such as antibacterial.

The specific embodiment

Below through specific embodiment the present invention is described further.

Embodiment 1 (kg)

Its preparation method is following

1) at first the tourmaline mineral aggregate is joined and carry out fragmentation in the disintegrating machine; After washing, drying, get in the twin-roll machine and grind to form the fine sand shape; Remove ferrum wherein through magnetic separation, get in the high-speed eddy mill through closed conduit again and pulverize, and the entering grader separates; Obtaining fine grained is Φ≤1250 order powder body, gets in the supersonic airstream mill and further is ground into the micro/nano level tourmaline powder body that granularity is 5 μ m;

2) take by weighing each raw material by formula ratio, using deionized water to be configured to concentration sorbitol is 70% solution for standby; Again sodium carboxymethyl cellulose, xanthan gum, tetrasodium pyrophosphate, sodium benzoate and glucide are joined in the remaining deionized water, high-speed stirred, 6000 rev/mins, 50 minutes time, it is subsequent use to process transparent colloidal solution;

3) with after sorbitol solution and the transparent colloidal solution mixing, add calcium carbonate, tourmaline powder, sodium lauryl sulfate and hydration Silicon stone again, under greater than the 0.096Mpa vacuum; High-speed stirred 2 hours; Add Herba Menthae essence again, under greater than the 0.096Mpa vacuum, high-speed stirred 20 minutes; Process mastic, packing is promptly accomplished.

Embodiment 2 (kg)

Its preparation method is following

1) preparation of tourmaline powder is with embodiment 1;

2) take by weighing each raw material by formula ratio, using deionized water to be configured to concentration sorbitol is 70% solution for standby; Again sodium carboxymethyl cellulose, xanthan gum, tetrasodium pyrophosphate, sodium benzoate and glucide are joined in the remaining deionized water, high-speed stirred, 6000 rev/mins, 45 minutes time, it is subsequent use to process transparent colloidal solution;

3) with after sorbitol solution and the transparent colloidal solution mixing, add calcium carbonate, tourmaline powder, sodium lauryl sulfate and hydration Silicon stone again, under greater than the 0.096Mpa vacuum; High-speed stirred 1.5 hours; Add Herba Menthae essence again, under greater than the 0.096Mpa vacuum, high-speed stirred 15 minutes; Process mastic, packing is promptly accomplished.

It below is the tourmaline toothpaste comparative test of the embodiment of the invention 1

Select the patient of 16 halitosiss of all suffering from different symptoms, gingival hemorrhage, tooth mildew, be divided into 2 groups, every group 8 people;

Matched group: every day, early, middle and late each the 3 times commercially available Radix Zanthoxyli medicated toothpaste of use were brushed teeth, and each consumption is 2/3 length of head toothbrushes;

Experimental group: every day, early, middle and late each 3 times use tourmaline toothpastes of the present invention were brushed teeth, and each consumption is 2/3 length of head toothbrushes;

Above-mentioned patient is used for the toothbrush of " Colgate-Palmolive " same model, and brushing time was controlled at each 2 minutes.

The result is following:

Matched group 8 people use the above-mentioned various symptoms in a week back that alleviation is in various degree arranged, and wherein have 3 halitosiss and gingival hemorrhage to fully recover, have the dirt degree of 4 tooth mildews to reduce by 30%.

Experimental group 8 people use the above-mentioned various symptoms in a week back that alleviation is in various degree also arranged, and wherein have 5 halitosiss and gingival hemorrhage to fully recover, have the dirt degree of 4 tooth mildews to reduce by 50%.

Above-mentioned 2 groups were used after one month, and 1, matched group suffers from existing 5 recoveries from illness of halitosis and gingival hemorrhage symptom, remaining 2 sxs; And 8 tooth stain degree of suffering from tooth mildew symptom all have decline; Wherein there is the dirt degree of 4 tooth mildews to reduce by 40%,, 4 potential drops low 30%.2, experimental group suffers from existing 7 recoveries from illness of halitosis and gingival hemorrhage symptom, and remaining 1 symptom obviously alleviates, and 8 tooth stain degree of suffering from tooth mildew symptom all have much decline very much, wherein has the dirt degree of 5 tooth mildews to reduce by 70%., 3 potential drops low 50%.

Each raw material weight proportioning that the above contrast test explanation embodiment of the invention 1 tourmaline toothpaste adopts obviously is superior to the medicated toothpaste of matched group on effect.

Claims (1)

1. tourmaline toothpaste, its feedstock production by following parts by weight forms;

Its preparation method is following

1) at first the tourmaline mineral aggregate is joined and carry out fragmentation in the disintegrating machine; After washing, drying, get in the twin-roll machine and grind to form the fine sand shape; Remove ferrum wherein through magnetic separation, get in the high-speed eddy mill through closed conduit again and pulverize, and the entering grader separates; Obtaining fine grained is Φ≤1250 order powder body, gets in the supersonic airstream mill and further is ground into the micro/nano level tourmaline powder body that granularity is 5 μ m;

2) take by weighing each raw material by formula ratio, using deionized water to be configured to concentration sorbitol is 70% solution for standby; Again sodium carboxymethyl cellulose, xanthan gum, tetrasodium pyrophosphate, sodium benzoate and glucide are joined in the remaining deionized water, high-speed stirred, 6000 rev/mins, 50 minutes time, it is subsequent use to process transparent colloidal solution;

3) with after sorbitol solution and the transparent colloidal solution mixing, add calcium carbonate, tourmaline powder, sodium lauryl sulfate and hydration Silicon stone again, under greater than the 0.096Mpa vacuum; High-speed stirred 2 hours; Add Herba Menthae essence again, under greater than the 0.096Mpa vacuum, high-speed stirred 20 minutes; Process mastic, packing is promptly accomplished.