CN101845256A - Elastic rubber paint with high wear resistance - Google Patents
Elastic rubber paint with high wear resistance Download PDFInfo
- Publication number
- CN101845256A CN101845256A CN 201010190317 CN201010190317A CN101845256A CN 101845256 A CN101845256 A CN 101845256A CN 201010190317 CN201010190317 CN 201010190317 CN 201010190317 A CN201010190317 A CN 201010190317A CN 101845256 A CN101845256 A CN 101845256A
- Authority
- CN
- China
- Prior art keywords
- powder
- weight
- elasticity
- high abrasion
- varnish according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a rubber paint with high wear resistance, which comprises film-forming material, solvent, auxiliary agent and pigment, wherein the pigment comprises matte powder, wax powder and elastic powder; and the elastic rubber paint has the components by weight percent: film-forming material: solvent: auxiliary agent: pigment= (36%-40%): (38%-45%): (0.5%-1.5%): (17.4%-19.4%). The elastic rubber paint with high wear resistance can maintain the attractive appearance of a product, and prolongs the service life of the product.
Description
Technical field
The present invention relates to rubber paint, relate in particular to a kind of abrasive rubber lacquer.
Background technology
Paint also can be described as coating, coating is a kind of easy construction, cheap, effect is obvious, value added is high Chemicals, it not only has makes the surface of buildings, boats and ships, machinery etc. prevent corrosion, the effect of prolongs life, also have decorative environment, give the beautiful enjoyment or the function of eye-catching mark, along with the continuous development of science and technology, coating progressively becomes the strong fine chemistry product of a kind of specificity.
Especially along with people constantly increase the demand of electronic product, competition between each electronics producer not only is confined to built-in function, require also more and more higher to the aesthetic measure of the appearance of electronic product and the anti-damage of surfacing, therefore, each electronics firm also transfers to the focus of paying close attention on the surface-coated.At this moment, paint just seems particularly important.
Often need the product that touches at some, mouse for example, to the paint of its surface-coated just need high abrasion and flexible be best.Beautiful outward appearance in the time of can making product appearance keep dispatching from the factory for a long time can be because of being seemed ugly by the mill flower.More existing in the market wearproof paints, its abrasion resistance can reach 200 times, but this is far from being enough, and therefore the main task of having painted us of a high abrasion is provided.
Summary of the invention
Purpose of the present invention will overcome above-mentioned shortcoming of the prior art exactly, and a kind of elastic rubber paint with high wear resistance is provided, and makes often to be touched to such an extent that product can keep beautiful appearance for a long time.
Technical scheme of the present invention is: a kind of high abrasion rubber elastic rubber paint is provided, comprise filmogen, solvent, auxiliary agent and pigment, wherein, described pigment bag make mute powder, wax powder and elasticity powder, the weight percent of described elastic rubber paint composition is as follows: filmogen: solvent: auxiliary agent: pigment=(36%～40%): (38%～45%): (0.5%～1.5%): (17.4%～19.4%).
Further, described solvent comprises vinyl acetic monomer, N-BUTYL ACETATE and ethylene glycol ether acetate, and its weight proportion of composing is 15: 19: 8.
Further again, described auxiliary agent comprises siccative, and the weight of described T-12 siccative is 0.5%～1.5%, and preferred 1%.
Further again, described filmogen is an acrylic resin.
Further again, the weight percent of the mute powder of described OK520 is 6%～6.6%, preferred 6.3%.
Further again, the part by weight of described 1778 wax powder is 3%～5%.
Further, the part by weight of described 1778 wax powder is 3.8～4.5%, and preferred 4.3%.
Further again, the part by weight of described 5070D elasticity powder is 7%～9%.
Further, the part by weight of described 5070D elasticity powder is 7.6%～8.3%, and preferred 7.8%.
Beneficial effect of the present invention is: the first, elastic rubber paint with high wear resistance provided by the invention can keep the beautiful outward appearance of product.
The second, elastic rubber paint with high wear resistance provided by the invention can prolong work-ing life of product.
Specific embodiment
The scientific research personnel of company is through a large amount of experiment confirms, when the starting material of selecting for use are acrylic resin, vinyl acetic monomer, N-BUTYL ACETATE, ethylene glycol ether acetate, T-12 siccative (supplier's DOW Chemical), the mute powder (supplier U.S. Gray Si) of 0K520,1778 wax powder (supplier U.S. Lu Borun) and 5070D elasticity powder (the Japanese Asahi Chemical Industry of supplier), the rub proofness of the rubber paint of producing is the highest, equally on experiment basis, adopting above starting material, is best according to the preparation of the weight percent in disclosure of the Invention content effect.
Below by embodiment the present invention is described in further details;
Drawing what the wear resisting property of rubber paint is had the greatest impact for technology of the present invention through a large amount of experiments is the part by weight of starting material wax powder and elasticity powder, because of change on the performance can not take place to the wear resistance of rubber paint in filmogen when making subtle change, therefore, following examples adopt other amounts constant, and the situation of having only the weight percent of filmogen and wax powder and elasticity powder to change describes;
Implement sharp one:
The weight percentages of components of elastic rubber paint with high wear resistance under situation as shown in table 1, the fastness to rubbing of testing rubber lacquer.
Table 1
Under the situation of rubber paint component ratio such as table 1, the product that is coated with rubber paint is tested its result such as table 2
Table 2
| Test event | Testing tool | The loading parameter | Testing method | Test result (material exceeds to see the bottom) |
| Paper tape is wear-resisting | The RCA abrasion tester | 175g power | The product of paper tape friction coating rubber lacquer | 458 times |
In wax powder value ratio is 3.8%, and elasticity powder value ratio is 7.3% o'clock, and the abrasion resistance of coating rubber lacquer product is 458 times.
Embodiment two:
The weight percentages of components of elastic rubber paint with high wear resistance under situation as shown in table 3, the fastness to rubbing of testing rubber lacquer.
Table 3
Under rubber paint component ratio such as table 3 situation, the product that is coated with rubber paint is tested its result such as table 4
Table 4
| Test event | Testing tool | The loading parameter | Testing method | Test result (material exceeds to see the bottom) |
| Paper tape is wear-resisting | The RCA abrasion tester | 175g power | The product of paper tape friction coating rubber lacquer | 507 times |
In wax powder value ratio is 4.3%, and elasticity powder value ratio is 7.8% o'clock, and the abrasion resistance of coating rubber lacquer product is 507 times.
Embodiment three:
The weight percentages of components of elastic rubber paint with high wear resistance under situation as shown in table 5, the fastness to rubbing of testing rubber lacquer.
Table 5
Under rubber paint component ratio such as table 5 situation, the product that is coated with rubber paint is tested its result such as table 6
Table 6
| Test event | Testing tool | The loading parameter | Testing method | Test result (material exceeds to see the bottom) |
| Paper tape is wear-resisting | The RCA abrasion tester | 175g power | The product of paper tape friction coating rubber lacquer | 469 times |
In wax powder value ratio is 4.5%, and elasticity powder value ratio is 7.6% o'clock, and the abrasion resistance of coating rubber lacquer product is 469 times.
As can be seen in raw-material weight per-cent such as embodiment two disclosed situations, effect is best from the contrast of above three embodiment.
Though preferred embodiment of the present invention is disclosed with the purpose as illustration, it will be appreciated by those skilled in the art that various modifications, interpolation and replacement are possible, as long as it does not break away from the spirit and scope of the present invention that describe in detail in the claims.
Claims (9)
1. a high abrasion rubber elastic rubber paint comprises filmogen, solvent, auxiliary agent and pigment, it is characterized in that: described pigment bag make mute powder, wax powder and elasticity powder, and the weight percent of described elastic rubber paint composition is as follows:
Filmogen: 36%～40%
Solvent: 38%～45%
Auxiliary agent: 0.5%～1.5%
Pigment: 17.4%～19.4%.
2. high abrasion rubber elasticity shellac varnish according to claim 1, it is characterized in that: described solvent comprises vinyl acetic monomer, N-BUTYL ACETATE and ethylene glycol ether acetate, its weight proportion of composing is 15: 19: 8.
3. high abrasion rubber elasticity shellac varnish according to claim 1, it is characterized in that: described auxiliary agent comprises siccative, and the model of described siccative is T-12, and the weight of described T-12 siccative is 0.5%～1.5%.
4. high abrasion rubber elasticity shellac varnish according to claim 1, it is characterized in that: described filmogen is an acrylic resin.
5. high abrasion rubber elasticity shellac varnish according to claim 1 is characterized in that: described mute powder model is OK520, and the part by weight of the mute powder of described OK520 is 6%～6.6%.
6. high abrasion rubber elasticity shellac varnish according to claim 1, it is characterized in that: the model of described wax powder is 1778, and the part by weight of described 1778 wax powder is 3%～5%.
7. high abrasion rubber elasticity shellac varnish according to claim 6, it is characterized in that: the part by weight of described 1778 wax powder is 3.8～4.5%.
8. high abrasion rubber elasticity shellac varnish according to claim 1, it is characterized in that: the model of described elasticity powder is 5070D, the part by weight of described 5070D elasticity powder is 7%～9%.
9. high abrasion rubber elasticity shellac varnish according to claim 8, it is characterized in that: the part by weight of described 5070D elasticity powder is 7.6%～8.3%.