CN101844151A - The production equipment of stainless steel strip and discontinuous production method thereof - Google Patents
The production equipment of stainless steel strip and discontinuous production method thereof Download PDFInfo
- Publication number
- CN101844151A CN101844151A CN201010155460A CN201010155460A CN101844151A CN 101844151 A CN101844151 A CN 101844151A CN 201010155460 A CN201010155460 A CN 201010155460A CN 201010155460 A CN201010155460 A CN 201010155460A CN 101844151 A CN101844151 A CN 101844151A
- Authority
- CN
- China
- Prior art keywords
- band
- equipment
- rolling
- main line
- annealing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to by before being coated with the oxidation cortex through hot rolling, the hot rolled strip of rolling is produced the equipment of corrosion resistant plate metal tape, comprise at least one main line that is called, rotation direction along band comprises at least: uncoiler (5), annealing furnace under the oxidation atmosphere (6), mechanical descaling's device (7,8), be used for fragmentation and destroy oxidation cortex on the band, band is carried out the device (9) of chemical pickling, irreversible apparatus for cold rolling (10), comprise at least three frames, at least one band up-coiler (11), wherein said equipment is especially open, except improving the quality of the band of producing, also have the possibility that increases production capacity, can not cause when improving usefulness and ask the initial input of described main line.
Description
Technical field
The present invention relates to by the method for before coming discontinuous production stainless steel band through the steel band of hot rolling.
The invention still further relates to by the equipment that before came discontinuous production corrosion resistant plate metal tape through the steel band of hot rolling.
Background technology
In the stainless steel field, known three kinds by the device cluster (plant family) that before came discontinuous production stainless steel band through the steel band of hot rolling.
At first, first kind of device cluster is so-called " independent equipment ", and annealing that it is preliminary and preliminary pickling line are to separate with preliminary cold rolling line.Therefore, the steel band that hot-working is produced is the first step annealing of process and preliminary acid pickling step on first production line at first, in addition rewinding around, be transported to second production line then to carry out preliminary cold-rolling process always.
In the downstream of preliminary rolling mill practice, to steel band carry out rewinding around, must carry out transportation processing so that during another passage or rolling number of times (pass), carry out final pickling annealing to the roll coil of strip (coil) then.Under the situation of " skin-pass (skin pass) " type surface rolling mill practice that links up, such equipment can be produced the corrosion resistant plate metal tape of 2D or 2B surface quality.Yet such equipment exists not enough, promptly will carry out too many time steel coil strip carrying operation between different production lines.
" half is integrated " device cluster is also known, wherein in mechanical descaling or (scale the cleaning) (tension straingtening that descales, sandblast then) and before the chemical pickling scale removal, preliminary cold-rolling process and preliminary annealing steps are associated on same production line.
In present operation and known equipment, preliminary cold rolling step carries out in the first upstream of step annealing on hot rolled strip.Such equipment thereby can be on described production line produce the low steel band of surface quality, i.e. 2E with single step or maximum three steps.
In order to obtain the steel of fine quality, i.e. 2D or 2B surface quality, the production of sheet metal is discontinuous, needs reel steel sheet metal, to carry the roll coil of strip, the processing of should reeling thus before carrying out the cold-rolling process second time; During second passage, carry out the cold-rolling process second time, be secondary annealing and acid pickling step afterwards, thereby can obtain the stainless steel of 2D surface quality, perhaps under the situation of carrying out " skin-pass " type surface rolling mill practice consistently, still obtain the steel band of 2B quality.
Yet there is defective in the equipment of this " half integrated " type on first production line, and this first production line includes a kind of irreversible apparatus for cold rolling that is positioned at the production line original position, particularly is mechanical descaling and a kind of descaling bath subsequently.Yet point out that as the inventor because preliminary rolling mill practice, two equipments after leaning on are all long especially, this has just increased the speed of service of milling train downstream part band.
At last, the 3rd device cluster of generally mentioning is so-called " integral body " equipment, and wherein the band of being produced by hot-working is realized the production of stainless steel metal plate on a continuous production line.Such equipment especially can be produced the band of 2B quality.Same tinuous production thereby comprise mechanical descaling's device (oxide carbon dust and sanding machine), acid dip pickle such as chemical bath, it is irreversible preliminary apparatus for cold rolling thereafter, final annealing device, and final acid dip pickle and final " skin-pass " type surface rolling device.
Such production line discloses in document EP-0 769 333.In case arbitrary equipment item breaks down yet the shortcoming of this tinuous production is it, equipment integral body will be worked.
In addition, first section of above-mentioned production line, especially comprise preliminary pickling and preliminary rolling mill practice, its production capacity is subjected to realizing the restriction of the second downstream production line portion section of final pickling, and wherein portion's section of back can not have first band running speed that section is equally high as described.Such continuous device thereby production capacity are limited.
Summary of the invention
The purpose of this invention is to provide a kind of method that is used for discontinuous production stainless steel band of correcting aforementioned disadvantages.
More specifically, the method that the purpose of this invention is to provide a kind of discontinuous production stainless steel band, and the equipment that is used for discontinuous production stainless steel band, can be according to the viewpoint of production capacity or band quality to be produced, carry out in the mode of open or expansible type (open-ended), it especially can improve quality by investment progressively, and can not bring problem to initial capitalization.
Another object of the present invention provides a kind of method and the equipment that can realize the production corrosion resistant plate metal tape of high productive capacity.
Another object of the present invention provides a kind of equipment with the length space requirement that reduces to some extent.
Other purposes of the present invention and advantage will provide in the following description, and it is the purpose of explaining rather than is construed as limiting.
At first the present invention relates to the technology of discontinuous production stainless steel band at least one production line.
According to the present invention, before mainly passed through following steps in order through hot rolled strip hot rolling, that be coated with oxidation cortex, wound into coiled stock:
-in the phase I, on described at least one so-called main line, carry out first passage:
-the roll coil of strip is untied coiling,
-band is carried out step annealing just,
-band is carried out mechanical descaling, so as broken and destroy the oxidation cortex,
-band is carried out preliminary chemical pickling, removing remaining oxide skin,
-band is carried out tentatively cold rolling, producing cold rolling or cold-hammer hits (cold hammered) band,
-cold-strip reeled makes it be roll coil of strip form,
-and at least one second stage, during carrying out second passage on described same the so-called main line, band is along identical rotation direction, or on different, so-called second production line, carry out:
-cold-strip is untied coiling,
-cold-strip is annealed under oxidizing atmosphere, produces oxide skin on the band,
-band after the annealing is carried out chemical pickling with scale removal or scale removal,
-according to circumstances, the band after the annealing carries out the surface rolling of " skin-pass " type,
-the corrosion resistant plate metal tape is reeled.
The invention still further relates to by the equipment that before brought discontinuous production corrosion resistant plate metal tape, comprise at least one so-called main line, comprise at least along the rotation direction of band through the hot-rolled steel that is coated with oxidation cortex, wound into coiled stock of hot rolling:
-uncoiler,
Annealing furnace under the-oxidation atmosphere,
-mechanical descaling device is used for fragmentation and destroys oxidation cortex on the band,
-band is carried out the device of chemical pickling,
-irreversible apparatus for cold rolling comprises at least three frames,
-at least one band up-coiler.
Method during this device especially can be carried out according to the present invention.
Therefore, preferably, the method in according to the present invention can be by comprising single tinuous production, be that the equipment of described main line is carried out, and this just makes the initial investment can be controlled.
In this case, then can be in each step of the second stage of during second passage, carrying out the method according to this invention on the same main line, only the described mechanical descaling device of main line is closed, and the frame of apparatus for cold rolling is opened.
When the production capacity of essential increase equipment, can be during second time investment stage provide one or two second production lines might be provided at the output of main line.
In this case, each step of the phase I of described method is carried out on described main line, and each step of the second stage of described method is carried out on described second production line.
Because the output of main line is greater than second production line, can be according to circumstances provide two so-called second production lines in output place of described main line, wherein each step of second stage can alternately be carried out on arbitrary in two described second production lines.Consequently obtain equipment with high productive capacity.
Advantageously, in first passage of described method on described main line, the downstream at preliminary cold rolling step can comprise the step of deoiling.According to equipment of the present invention thereby can be equipped with degreasing machine on described main line, it is positioned at the downstream of irreversible apparatus for cold rolling, and in the upstream of described at least one band up-coiler.
Advantageously, such layout can be deoiled to cold-strip before each step of second stage carrying out.Thereby preferably on described second production line, do not provide degreasing machine, guaranteeing in that as above to carry out device extension such, under having the situation of two second parallel production lines, can exempt described equipment that promptly the degreasing machine device being set.
Advantageously, embodiment according to the inventive method, annealing steps during the second stage can be a final annealing, and the acid pickling step during the second stage can be final pickling, thereby under the situation when described band and then through the surface rolling step of " skin-pass " type the time, can produce the steel sheet metal band of 2D surface quality, perhaps even the band of 2B quality.
According to another embodiment of the present invention, the annealing steps during the second stage can be an intermediate annealing process, and wherein the acid pickling step during the second stage is final acid cleaning process, and wherein:
Band after the-pickling also carries out reversible cold rolling step during the phase III on independent production line, and
-on another independent production line, during the quadravalence section, carry out the bright annealing step through reversible band after cold rolling, thereafter followed by be the surface rolling of " skin-pass " type, thereby can produce the steel sheet metal band of BA surface quality.
So can have following optional feature according to equipment of the present invention:
-described equipment can be that described main line is formed by the wall scroll production line,
-alternatively, its equipment is except main line, can also comprise second production line, it at least mainly is shown as: the rotation direction along band is provided with uncoiler, annealing furnace under the oxidation atmosphere, the acid dip pickle of use chemical reagent, optionally the surface rolling device of " skin-pass " type, and band up-coiler
-obtain high output in order to make equipment, two parallel what is called second production lines can be arranged at the output of described main line,
-in order to produce the steel band of BA surface quality, except the described main line and described second production line that may exist, described equipment can have reversible cold rolling independent production line on the one hand, it comprises: a kind of first roll coil of strip up-coiler/uncoiler, a kind of particularly such as the such reversible rolling device of Sendzimir (Sendzimir) type, and a kind of second roll coil of strip up-coiler/uncoiler, on the other hand, equipment has independent bright anneling production line, and it comprises: the rotation direction along band is provided with uncoiler, annealing device with the heating furnace under the reducing atmosphere, the optional apparatus for cold rolling of " skin-pass " type, and up-coiler.
Description of drawings
The present invention can understand in below in conjunction with the description of the drawings better.
-Fig. 1 is the sketch of the method according to this invention, and it can be carried out by single so-called main line and be used to carry out the stainless production of 2D or 2B surface quality,
-Fig. 2 is a sketch according to a second embodiment of the method according to the invention, it carries out the phase I of described method and the step of second stage by main line, equipment has wherein had independently reversible rolling line in addition, independently bright annealing line and subsequent " skin-pass ", thereby can produce the stainless steel band of BA modified surface quality
-Fig. 3 is the schematic diagram according to the 3rd embodiment of the inventive method, this method is by a kind of equipment realization that has the main line that can implement the phase I step and can implement second production line of second stage step, it can be used for producing the steel band of 2D or 2B quality
-Fig. 4 is the schematic diagram according to the 4th embodiment of the inventive method, the realization of this method is by feat of the independent production line of the described main line that realizes each step of phase I, described second production line of realizing each step of second stage and reversible rolling and independently bright annealing production line and subsequent " skin-pass ", thereby can produce the steel sheet metal band of BA surface quality.
Fig. 5 is the schematic diagram according to the 5th embodiment of the inventive method.
The Reference numeral translation:
The HRC-hot rolled strip
HAPRL-thermal annealing pickling rolling line
The cold annealing and pickling production line of CAPL-
The CRC-cold-strip
The SPM-skin milll
The ZR-Sendzimir
BAL-bright annealing production line
The specific embodiment
Therefore, the present invention relates to be used for by the equipment that before brought discontinuous production corrosion resistant plate metal tape through the hot-rolled steel that is coated with oxidation cortex, wound into coiled stock of hot rolling, it comprises at least one so-called main line 1.
Described main line comprises at least along the rotation direction of band:
-uncoiler 5,
Annealing furnace 6 under the-oxidation atmosphere,
-be used for fragmentation and destroy mechanical descaling's device 7,8 of the oxidation cortex on the band,
-make band stand the device 9 of chemical pickling, removing residual oxide skin,
-irreversible apparatus for cold rolling 10 comprises at least three frames, particularly three, four or five,
-at least one strip uncoiler 11.
In addition, as shown in Figure 5, this production line can also have: cutter 16 between up-coiler 5 and accumulator 13 and welding unit 17, and another accumulator 14 between acid dip pickle 9 and irreversible rolling device, and another accumulator 15 (being thereafter cutter 18) that is positioned at up-coiler 11 upstreams.
Advantageously, according to preferred embodiment, in the downstream of the irreversible cold-rolling equipment 10 of what is called and the upstream of described at least one band up-coiler 11, described main line preferably is shown has degreasing machine 12.
When the institute of phase I all carried out in steps, this main line was called HAPRL in the accompanying drawings for short, with expression " thermal annealing pickling and rolling line ".
Described equipment alternatively by an independent production line, be that described main line is formed, particularly the method shown in 1 with reference to the accompanying drawings makes it can produce the steel band of 2D or 2B quality.
Replacedly, except main line, described equipment can also comprise second production line 2, and especially as shown in Figure 5, along the rotation direction of band, it at least mainly comprises:
-uncoiler 19,
Annealing furnace 20 under the-oxidation atmosphere,
The acid dip pickle 21 of-use chemical reagent,
The surface rolling device 23 of-optional " skin-pass " type,
-band up-coiler 22.
In addition, as shown in Figure 5, second production line has: be positioned at the cutter 28 and the welding unit 29 in uncoiler 19 downstreams, be positioned at the band accumulator 25 of annealing furnace 20 upstreams, and be positioned at the acid dip pickle 21 of use chemical reagent and another accumulator 26 between " skin-pass " device 23.
Another accumulator can be positioned between the surface rolling device 23 and up-coiler 22 of " skin-pass " type.On described main line and described second production line, using the acid dip pickle 9 and 21 of chemical reagent can be chemical tank well known to those skilled in the art.
As for being used for fragmentation and destroying mechanical descaling's device 7,8 of the oxidation cortex on the band, it can be the form of the oxide carbon dust utmost point under the effect of tractive force 7 so that broken oxidation cortex, thereafter followed by be sand-blasting machine 8.
As described in accompanying drawing 5, the present invention can be the equipment of high yield, and it is shown as two parallel what is called second production lines that have at the main line output.It should be noted that these second production lines do not have degreaser, the step of wherein deoiling is subsequently by using degreasing machine 12 to realize on main line.
At last, according to the embodiment that does not specify, except the described main line 1 and described second production line 2 that may exist, described equipment can also have reversible cold rolling independent production line 3 on the one hand, and it comprises the reversible rolling device and the second roll coil of strip up-coiler/uncoiler of first roll coil of strip up-coiler/uncoiler, Sendzimir type well known to those skilled in the art.
On the other hand, described equipment can also have independent bright anneling production line 4, and its rotation direction along band comprises uncoiler, has the bright annealing device of the heating furnace reducing atmosphere under, the apparatus for cold rolling and the up-coiler of optional " skin-pass " type.
Described bright annealing device is different with form well known to those skilled in the art, but is expanded simply thereon.It forms with the form of the heating furnace under non-oxide (reduction) atmosphere, generally follows hard on the cooling end section thereafter, and this cooling has non-oxidized gas to blow on the tropocal wood equally.
This annealing device can be annealed to band, and can not damage the surface appearance of the band that is obtained by the reversible rolling step on the milling train of Sendzimir type.
Can carry out the method according to this invention in particular according to equipment of the present invention.
The present invention thereby relate at least one stainless steel band production line, through the technology that the hot rolled strip HRC oxidation cortex, that be wound into the roll coil of strip (being used for hot-rolled coil) carries out discontinuous production that is coated with of hot rolling, it mainly experienced following steps in order by before:
-during the phase I, in described at least one first passage that is called on the main line 1:
-uncoiling,
-band is carried out step annealing just,
-band is carried out mechanical descaling, with fragmentation and destroy the oxidation cortex,
-band is carried out preliminary chemical pickling, removing remaining oxidation cortex,
-band is carried out tentatively cold rolling, producing cold-strip CRC (being used for the cold rolling roll coil of strip),
-cold-strip reeled makes its form that is the roll coil of strip,
-and during at least one second stage, during carrying out second passage on the described same so-called main line, band is along identical rotation direction, or carry out in different being called on second production line 2:
The uncoiling of-cold-strip,
-cold-strip is annealed under oxidizing atmosphere, produces the oxidation cortex on the strip surface,
-band after the annealing is carried out chemical pickling removing dirt,
-alternatively, the band after the annealing carries out the surface rolling of " skin-pass " type,
-the corrosion resistant plate metal tape is reeled.
In addition, especially as shown in Figure 5, described method can comprise the step of deoiling in first passage on described main line, and it is in the downstream of preliminary cold rolling step.
Advantageously, each step of second stage can be carried out on described main line 1, and especially the method shown in the accompanying drawing 1 according to the present invention perhaps remains the method shown in the accompanying drawing 2 according to the present invention.
The method of Fig. 1 example is that the annealing steps during a kind of wherein second stage is the method for final annealing technology, and the acid pickling step during the second stage of described method is final pickling operation, thereby the time when described band and then through the surface rolling step of " skin-pass " type, can produce the steel sheet metal band of 2D surface quality, perhaps or even the band of 2B quality.
" skin-pass " device can be provided in the end of described main line, or still with erect-position that described main line links up mutually on.
Equally, mainly the method for being carried out by described main line has realized " thermal annealing pickling rolling line " in the step of the phase I shown on accompanying drawing 1 during first passage, that abbreviate HAPRL as, and at " cold annealing and pickling production line " in the accompanying drawing step of 1 described phase I, that abbreviate CAPL as during second passage.For with its realization, during second passage, only mechanical descaling's device 7,8 has been closed, and the frame of reversible cold-rolling equipment 10 is opened.
" skin-pass " type surface cold rolling step abbreviates SPM as, with expression " skin milll ".
What the example of accompanying drawing 2 and accompanying drawing 1 were different is the steel band that its method can be produced the excellent surface quality of BA.
Except main line 1, described equipment comprises independent reversible rolling production line, and it is called ZR with expression " Sendzimir ", and the bright annealing production line, and it abbreviates BAL as with expression " bright annealing line ".Next be that " skin-pass " abbreviates SPM as, with expression " skin milll ".
2 example with reference to the accompanying drawings, main line 1 can realize each step according to phase I of the present invention and second stage, as described in the example of before accompanying drawing 1.End in each step of second stage has produced the steel band of 2D quality, it is reeled to carry then up to reversible rolling line 3 handle.
In the production line of back, band carries out several reversible cold rolling steps consistently along rotation direction, thereby can obtain good surface appearance.Reeled then band and with its carrying until bright annealing line 4 independently, so that band is carried out bright annealing.
At last, the band after the annealing carries out the surface rolling step, to obtain the stainless steel band of BA quality.
According to another embodiment of the present invention, shown in Fig. 3 and 4, each step of second stage can be carried out on second production line 2 especially, and as previously mentioned, second production line and main line distinguish, this method thereby have higher productivity.Therefore we will introduce the example of Fig. 3, and it at first handled hot rolled strip HRC on described main line 1 before each step of the phase I of carrying out described method, and this abbreviates HAPRL as.
The cold-reduced sheet metal tape is handled upside down then and enters second production line 2 and handled, and to carry out each step of second stage, abbreviates CAPL as.Can be in the end of second production line or still on the erect-position that links up, carry out under the situation of " skin-pass ", consequently second production line output 2D or even the steel band of 2B quality.
Advantageously, the embodiment shown in 5 with reference to the accompanying drawings, its method can be implemented on the equipment with two second parallel production lines, thereby handles the cold-reduced sheet metal tape to another then since the phase I on of two production lines alternatively.
The difference of the example of accompanying drawing 4 and accompanying drawing 3 is: except the main line 1 and second production line 2, its equipment also has independently reversible cold rolling line 3, abbreviate ZR as with expression Sendzimir, have independently bright annealing line thereafter, abbreviate BAL as with expression " bright annealing line ".In this case, the steel band of described method second stage end can be reeled and carry out reversible rolling then on reversible rolling line 3, and then reels and be moved to independent bright annealed wire and handle." skin-pass " can carry out in the end of bright annealing line, perhaps on the erect-position that links up, thereby can produce the steel band of BA surface quality.
Certainly, can expect other embodiment, and need not to depart from the framework of determining by following claim of the present invention.
Claims (13)
1. the discontinuous production method of a stainless steel band that at least one production line of equipment, carries out, it is characterized in that, by before through hot rolling, surface coverage has the hot rolled strip oxidation cortex, wound into coiled stock (HRC), mainly carries out following steps in order:
-in the phase I, first passage on described at least one main line (1);
-uncoiling,
-band is carried out step annealing just,
-band is carried out mechanical descaling, with fragmentation and destroy the oxidation cortex,
-band is carried out preliminary chemical pickling, removing remaining oxide skin,
-band is carried out tentatively cold rolling, producing cold-strip (CRC),
-cold-strip is reeled so that it is the form of the roll coil of strip,
-and, on same described main line (1), carrying out second passage at least one second stage, band is along identical rotation direction, or carries out in different being called on second production line (2);
The uncoiling of-cold-strip,
-cold-strip is annealed under oxidizing atmosphere, produces oxide skin on the band,
-band after the annealing is carried out chemical pickling with scale removal,
-according to circumstances, the band after the annealing carries out the surface rolling of " skin-pass " type,
-the corrosion resistant plate metal tape is reeled.
2. according to the method for claim 1, in first passage of described main line, also has the step of deoiling in addition in the downstream of preliminary cold rolling step.
3. according to the method for claim 2, wherein each step of second stage is carried out on described main line (1).
4. according to the method for claim 1 or 2, wherein each step of second stage is carried out on described second production line (2).
5. according to the method for claim 4, wherein two second production lines (2) are arranged on the output of main line (1), and wherein each step of second stage is carried out on arbitrary in described two second production lines (2) alternatively.
6. according to arbitrary method in the claim 1 to 5, wherein the annealing steps of second stage is a final annealing technology, and the acid pickling step of described second stage is final acid cleaning process, thereby under the situation when described band and then through the surface rolling step of " skin-pass " type the time, can produce the steel sheet metal band of 2D surface quality, perhaps even the band of 2B quality.
7. according to arbitrary method in the claim 1 to 5, wherein the annealing steps of second stage is an intermediate annealing process, and the acid pickling step of described second stage is final acid cleaning process, and wherein:
Band after the-pickling is also gone up at independent production line (3) and is carried out reversible cold rolling step in the phase III, and
-go up at another independent production line (4) through reversible band after cold rolling and to carry out the bright annealing step in the quadravalence section, thereafter followed by be the surface rolling of " skin-pass " type, thereby can produce the steel sheet metal band of BA surface quality.
8. be used for comprising at least one main line that is called (1) through equipment hot rolling, that be coated with the discontinuous production corrosion resistant plate of the hot rolled strip oxidation cortex, wound into coiled stock metal tape, comprise at least along the rotation direction of being with by previous:
-uncoiler (5),
Annealing furnace under the-oxidation atmosphere (6),
-mechanical descaling device (7,8) is used for fragmentation and destroys oxidation cortex on the band,
-band is carried out the device (9) of chemical pickling,
-irreversible apparatus for cold rolling (10) comprises at least three frames,
-at least one band up-coiler (11).
9. equipment according to Claim 8, wherein said main line (1) is equipped with degreasing machine, and it is positioned at the downstream of described irreversible apparatus for cold rolling (10), and is positioned at the upstream of described at least one band up-coiler (11).
10. according to Claim 8 or 9 equipment, it is that described main line (1) is formed by single production line.
11. according to Claim 8 or 9 equipment, it also comprises second production line (2) except main line (1), at least mainly comprises along the rotation direction of band:
-uncoiler (19),
Annealing furnace under the-oxidation atmosphere (20),
The acid dip pickle (21) of-use chemical reagent,
The surface rolling device (23) of-optional " skin-pass " type,
-band up-coiler (22).
12. according to the equipment of claim 11, the output in described main line (1) has two parallel second production lines (2) that are called.
13. arbitrary equipment in 12 according to Claim 8, except the described main line (1) and described second production line (2) that may exist, on the one hand, described equipment can have reversible cold rolling independent production line (3), and it comprises first up-coiler/uncoiler, for example particularly the reversible rolling equipment of Sendzimir type and second up-coiler/uncoiler; On the other hand, described equipment can also have independent bright anneling production line (4), comprise uncoiler, bright annealing equipment, the optionally apparatus for cold rolling and the coiling machine of " skin-pass " type along the rotation direction of band, described bright return of goods equipment comprises the stove under the reducing atmosphere.