CN101829701A - New method for producing copper (aluminum) rows and rods and small-cross section profiles - Google Patents
New method for producing copper (aluminum) rows and rods and small-cross section profiles Download PDFInfo
- Publication number
- CN101829701A CN101829701A CN200910218766A CN200910218766A CN101829701A CN 101829701 A CN101829701 A CN 101829701A CN 200910218766 A CN200910218766 A CN 200910218766A CN 200910218766 A CN200910218766 A CN 200910218766A CN 101829701 A CN101829701 A CN 101829701A
- Authority
- CN
- China
- Prior art keywords
- continuous
- continuously extruded
- hydraulic
- continuous drawing
- goods
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a new method for producing copper (aluminum) rows and rods and small-cross section profiles, which belongs to a non-ferrous metal processing technology. After continuous extrusion, a hydraulic continuous drawing machine is provided to carry out drawing processing in a continuous drawing way, and then a new continuous extruding and hydraulic continuous drawing processing method is formed. The technology comprises a continuous extruding and on-line hydraulic continuous drawing method and a continuous extruding and off-line hydraulic continuous drawing method. The continuous drawing method has the characteristic that the product is clamped and drawn from the outside surface of the product by clamping pliers, holding pliers or clamping blocks in the normal drawing process. The product has no damage in the clamping process, and continuously moves in the drawing process, and the products with any length can be drawn in a full-automatic way. The invention can realize high-efficiency, high-finished rate and high-quality drawing, reduce occupation area of equipment, enhance the automation degree, and improve the working environments.
Description
Technical field
The present invention's " a kind of method of new production of copper (aluminium) row, bar and small-cross section profiles " is a kind of non-ferrous metal process technology, belongs to the non-ferrous metal manufacture field.
This technology is used for the processing of elongated article such as the flat row of copper (aluminium), bar and profiled-cross-section section bar, is different from the technology of the continuously extruded+flat row of single interruption Hubbing method production of copper (aluminium), bar and the profile shapes that generally use at present.This technology can overcome that single is interrupted the shortcoming of Hubbing method after the continuously extruded operation, thereby enhances productivity, improves lumber recovery, reduce cost, and reduces floor space, improves automaticity and improve work situation.
The term that this paper is involved in the following description:
Goods: all refer to copper (aluminium) row, copper (aluminium) bar, and small bore copper (aluminium) section bar.
Processing method: all refer to copper (aluminium) row, copper (aluminium) bar, and the processing method of small bore copper (aluminium) section bar.
Background technology
1. three sport technique segments of copper bar processing
Present copper bar processing haply must be through following link.
1.1. up-drawing method casting base link
Adopt up-drawing method to cast out sufficiently long copper bar or aluminium bar, it is gathered into the blank of coil shape.The texture of these blank inside of this moment is rendered as cast sturcture thick in the metallography fully.
1.2. continuously extruding and molding link
The continuously extruded grain structure that forms cross sectional shape, surface quality and the hope of arts demand afterwards of blank process with up casting.These intermediates of this moment are organized the tiny orderly forging tissue that is rendered as fully in the metallography through the crystal inside of its material after the violent distortion, and are the hot-working softening forms after the tempering again.
1.3. the drawing link is strengthened and the typing link
The intermediate of coming out pressurizeing is continuously carried out drawing processing, make it through necessary cold conditions stretcher strain, thereby improve intensity and toughness index and other physical performance index of these goods, and further improved goods geometric accuracy and surface quality, made it reach good comprehensive quality index.The product of this moment is through the more tiny cold-work strengthening state of grain size after the cold stretch distortion.
2. correlation technique
2.1. up-drawing method casting copper (aluminium) bar
Irrelevant with this patent, so repeat no more.
2.2. it is continuously extruded
Continuously extruded, claim Kang Feng extruding (Conform Extrusion) again, a large amount of in recent years extruding bases that is used for copper (aluminium) row, bar and part profiled-cross-section section bar has almost completely replaced the billet production method of traditional copper (aluminium) row, copper bar and part sections with small cross-section.It is continuously extruded that this technology is that copper (aluminium) bar of coil shape that the up casting method is produced carries out, and forms preliminary flat row, bar and profile shapes, and these all are intermediate products; This method is the most effectively blank-making method of generally acknowledging at present.
These continuously extruded intermediate products that come out also need could form final products through follow-up drawing processing.
2.3. the drawing mode that traditional single is interrupted
At present, after continuously extruded, be used for copper (aluminium) row, copper (aluminium) bar, and the special-shaped small bore copper of part (aluminium) section bar drawing processing all is the chain drawbench that falls behind, the hydraulic drawbench of the perhaps relatively backward long stroke of single cylinder carries out drawing.The drawing mode that these singles are interrupted is a kind of traditional old drawing mode, and the feature of this Hubbing method and shortcoming are:
1) stretching interruption is carried out.All the original very long material cut-out of coiling to be become short sectional vertical bar material before each drawing, just can drawing.
2) in the whole process of drawing, the head that draw carriage can only the clamping goods carries out drawing; Because clamp has tooth, in the drawing process of every section goods, all can crush the head of goods, thereby make that the section of being held becomes waste material;
3) drawing length depends on the drawing haul distance with drawbench, is the drawing of finite length, and efficient is low;
4) each section goods all will be made head before drawing, and lumber recovery is low, and efficient is low;
5) carry out fixed ruler cutting again after drawing is over;
6) drawbench takies very big floor area, operation is disperseed, and the workshop is arranged in disorder;
7) workshop is in disorder, automaticity is low, work situation and operating condition are poor.
2.4. the hydraulic continuous drawing of invention indication
Here said hydraulic continuous drawing is for the single that alternate manner is realized is interrupted drawing mode.Hydraulic continuous drawing is meant in the process of normal drawing, with clamp or embrace pincers or method that grip block carries out drawing from the lateral surface clamping goods of goods.
Before this, continuous drawing technique mainly is to adopt mechanical continuous drawing machine and the cooling red copper coil of pipes of technology processing, and some steel pipe's production.
The characteristics of this Hubbing method and advantage are as follows:
1) two dollies are by hydraulic-driven, and alternately back and forth movement carries out drawing;
2) clamp or armful pincers or grip block clamping goods lateral surface are not only to add the head of holding goods;
3) this clamping is to not damage of product surface;
4) goods are advancing continuously in the drawing process;
5) goods length that can drawing and clamp, it doesn't matter to embrace the stroke of pincers, grip block;
6) can draw the goods of random length;
7) the production efficiency height, become a useful person high, quality of item is good;
8) it is few to take floor area, and neat appearance is arranged in the workshop, has high automaticity;
9) has good work operating environment.
3. the present processing method of using
The method of using is at present:
Continuously extruded+single is interrupted Hubbing method.
Goal of the invention
The object of the invention is to overcome continuously extruded+single and is interrupted the shortcoming that single is interrupted drawing in the flat row of hubbing production of copper (aluminium), bar and the section bar, solves at continuously extruded single afterwards to be interrupted low, the problems such as lumber recovery is low, section quality is not high, occupation area of equipment is big, automaticity is low, working condition difference of the existing production efficiency of drawing; Utilize the present invention can realize high efficiency, high yield, high-quality drawing, save occupation area of equipment simultaneously, improve automation Chengdu, improve work situation.
Summary of the invention
Content of the present invention is:
At continuously extruded (Conform Extrusion, claim again Kang Feng extruding) afterwards, utilize the hydraulic continuous drawing machine to carry out drawing (stretchings) and process, thereby replace continuously extruded+single interruption drawing (stretching) process in the mode of continuous drawing (stretchings).
Comprising two kinds of methods
The 1st kind is continuously extruded+on-line hydraulic continuous drawing method
The 2nd kind is continuously extruded+off-line hydraulic continuous drawing method
The specific embodiment
Embodiments of the present invention can have two kinds of methods.
1. continuously extruded+the on-line hydraulic continuous drawing method
After continuous extruder, dispose the hydraulic continuous drawing machine.Directly enter the hydraulic continuous drawing machine through the continuously extruded goods that come out and carry out drawing; In continuously extruded process of carrying out, the speed of continuous drawing automatically adjusts according to continuously extruded discharging speed, realizes online continuous drawing processing.Continuous extruder and the hydraulic continuous drawing machine of this moment work online simultaneously.
2. continuously extruded+the off-line hydraulic continuous drawing method
After continuous extruder, dispose online winder, continuously extruded goods are collected to become coil material, then this is coiled material and after continuous extruder, remove, carry out continuous drawing again before transporting the hydraulic continuous drawing machine to.Continuous extruder and the hydraulic continuous drawing machine of this moment are worked respectively, and the two work is independent of each other.
3. continuously extruded device therefor
Hydraulic continuous drawing machine (hydraulic combined drawbench, double end hydraulic drawbench).
Claims (6)
1. the present invention is a kind of new production of copper (aluminium) row, the method that bar reaches small-cross section profiles.It is to utilize existing continuously extruded technology and hydraulic continuous drawing technology to organically combine a kind of new processing method that forms.Being used in this method carries out hydraulic continuous drawing with continuously extruded intermediate of coming out and produces qualified copper (aluminium) row, bar and and small-cross section profiles.
2. according to the described invention of claim 1, it is characterized in that: adopt the mode of hydraulic continuous drawing to carry out drawing processing through continuously extruded intermediate of coming out.
3. according to the described invention of claim 1, one of its feature is: the lateral surface of continuously extruded intermediate of the coming out random length position that the drawbench jaw can the clamping goods when carrying out drawing is not only the head of clamping goods.
4. according to the described invention of claim 1, one of its feature is: the goods that continuously extruded intermediate of coming out can the drawing random length when carrying out drawing are not only a length relevant with the drawbench stroke.
5. according to the described invention of claim 1, one of its feature is: dispose the hydraulic continuous drawing machine after continuous extruder.Enter the hydraulic continuous drawing machine through the continuously extruded goods that come out and carry out drawing, continuous extruder and the hydraulic continuous drawing machine of this moment work online simultaneously, form continuously extruded and the production method on-line continuous drawing.
6. according to the described invention of claim 1, one of it is characterized in that being: after continuous extruder, continuously extruded goods are collected to become coil material, then this is coiled material and after continuous extruder, remove, transport on the station of hydraulic continuous drawing machine and carry out continuous drawing again.Continuous extruder and the hydraulic continuous drawing machine of this moment are worked respectively, and the two work is independent of each other, and form continuously extruded and continuous drawing method off-line.