CN101759433A - Doped modified barium titanate-based high-pressure porcelain capacitor material - Google Patents
Doped modified barium titanate-based high-pressure porcelain capacitor material Download PDFInfo
- Publication number
- CN101759433A CN101759433A CN200910264550A CN200910264550A CN101759433A CN 101759433 A CN101759433 A CN 101759433A CN 200910264550 A CN200910264550 A CN 200910264550A CN 200910264550 A CN200910264550 A CN 200910264550A CN 101759433 A CN101759433 A CN 101759433A
- Authority
- CN
- China
- Prior art keywords
- titanate
- capacitor material
- barium titanate
- barium
- based high
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a doped modified barium titanate-based high-pressure porcelain capacitor material which is prepared from barium titanate, bismuth titanate, strontium titanate, calcium titanate, zinc oxide, zirconium oxide and niobium oxide. The materials are mixed, and then polyvinyl alcohol is added for pressing and forming and then is sintered at approximate 1240 degrees to obtain a high-dielectricity low-loss porcelain capacitor material resisting high pressure. The capacitor material sintered by adopting a porcelain material preparation formula improves the compressive strength by 9.4kv/mm, the dielectric constant delta r to be 3469 and the dielectric loss tan delta to be 0.0004 under an alternating working current of 1MHz.
Description
Technical field
The present invention relates to the high voltage bearing high-permitivity ceramics capacitor material behind a kind of doping vario-property.
Background technology
The specific inductivity of the high-pressure porcelain capacitor material of widespread production use at present is less, can not satisfy electronic circuit and miniaturization of devices demand thereof; Dielectric loss is big, is unfavorable for the job stability and the energy utilization rate of device.
And the withstand voltage of the lead-free ceramic capacitance modulator material of general prescription is not high enough simultaneously.
Summary of the invention
The invention provides a kind of high voltage bearing high low-loss ceramic capacitor material that is situated between.
Technical scheme is as follows: a kind of barium titanate-based high-pressure porcelain capacitor material of doping vario-property is characterized in that being made up of barium titanate, bismuth titanates, strontium titanate, calcium titanate, zinc oxide, zirconium white and niobium oxides.Above-mentioned materials is mixed the back add polyvinyl alcohol compression moulding, obtain high voltage bearing high low-loss ceramic capacitance material that is situated between at 1240 ℃ of left and right sides sintering then.
Adopt this porcelain prescription agglomerating capacitor material, its compressive strength value is brought up to 9.4kv/mm, DIELECTRIC CONSTANT
r=3469, under the working alternating current of 1MHz, dielectric loss tan δ=0.0004.
Embodiment
During actual fabrication, respectively with barium carbonate BaCO
3, bismuth oxide Bi
2O
3, Strontium carbonate powder, lime carbonate and titanium dioxide TiO
2According to certain proportioning weighing, oven dry makes barium titanate BaTiO under 800 to 1200 degrees centigrade after ball milling mixes
3, bismuth titanates Bi
2O
33TiO
2, strontium titanate SrTiO
3And calcium titanate CaTiO
3
According to mole proportioning 66~70% barium titanates, 2~4% bismuth titanates, 18~20% strontium titanate and 9~10% calcium titanates make the matrix porcelain, the mass percent of mixing is 0.2~0.4% zinc oxide ZnO, 0.5~2% zirconium white ZrO then
2With 1~4% niobium oxides Nb
2O
5Mix by ball milling after the prescription weighing, drying, the polyvinyl alcohol that adds 8wt% carries out granulation, 1240 degrees centigrade of following sintering get final product the unleaded high-voltage capacitance modulator material of this porcelain prescription.
Claims (3)
1. the barium titanate-based high-pressure porcelain capacitor material of a doping vario-property is characterized in that being made up of barium titanate, bismuth titanates, strontium titanate, calcium titanate, zinc oxide, zirconium white and niobium oxides.Above-mentioned materials is mixed the back add polyvinyl alcohol compression moulding, obtain high voltage bearing high low-loss ceramic capacitance material that is situated between at 1240 ℃ of left and right sides sintering then.
2. the barium titanate-based high-pressure porcelain capacitor material of doping vario-property according to claim 1 is characterized in that barium carbonate BaCO
3, bismuth oxide Bi
2O
3, Strontium carbonate powder, lime carbonate and titanium dioxide TiO
2According to certain proportioning weighing, after the ball milling oven dry, under 800 to 1200 degrees centigrade, make barium titanate BaTiO
3, bismuth titanates Bi
2O
33TiO
2, strontium titanate SrTiO
3With calcium titanate CaTiO
3
3. the barium titanate-based high-pressure porcelain capacitor material of doping vario-property according to claim 1, the titanate that it is characterized in that making, according to mole proportioning 65~70% barium titanates, 0~5% bismuth titanates, 12~20% strontium titanate and 4~10% calcium titanates make the matrix porcelain, the mass percent of mixing is 0~1% zinc oxide ZnO, 0~4% zirconium white ZrO then
2With 0~6% niobium oxides Nb
2O
5By ball milling after the prescription weighing, the polyvinyl alcohol that dry back adds 7~12wt% carries out granulation, at 1200~1250 degrees centigrade of following sintering.