CN101671793A - 一种铁铬铝纤维丝 - Google Patents
一种铁铬铝纤维丝 Download PDFInfo
- Publication number
- CN101671793A CN101671793A CN200810196089A CN200810196089A CN101671793A CN 101671793 A CN101671793 A CN 101671793A CN 200810196089 A CN200810196089 A CN 200810196089A CN 200810196089 A CN200810196089 A CN 200810196089A CN 101671793 A CN101671793 A CN 101671793A
- Authority
- CN
- China
- Prior art keywords
- percent
- iron
- chromium
- aluminum filament
- filament
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种铁铬铝纤维丝,其组成及质量百分比为:C:0.06-0.08%,Mn:0.20-0.46%,Si:0.40-0.63%,RE:0.02-0.10%,Al:4.8-5.9%,Cr:15-26%,Cu:1-2%,Fe:余量。由于本发明采用以上技术方案,使得铁铬铝纤维丝适宜拉拔加工,单丝直径可达6um,强度>16CN(牛顿/平方毫米),延伸率1.40%,大大提高了铁铬铝纤维丝成品的综合性能,完全克服了拉不细、脆而易断的缺点。
Description
技术领域
本发明涉及一种金属产品,具体地说是一种铁铬铝纤维丝,属冶金技术领域。
背景技术
目前,市场上用的不锈钢纤维,如:名称为“不锈钢纤维材料及加工工艺和不锈钢纤维***器芯”,申请号为99120164.7,它的主要特点采用1Cr17Mo,由如下成分和配比组成:化学成分为:C:0.06-0.08,Si:0.4-0.6,Mn:0.4-0.6,P:<0.03,S:<0.021,Cr:6.5-18,Mo:0.75-1.2,Ni:<0.2,Fe:余量;还有,名称为“成束拉拔的不锈钢纤维”,申请号为02814697.2,其不锈钢纤维的组成包含铁以及下述组分(以wt.%表示):C≤0.05%,Mn≤5%,Si≤2%,8%≤Ni≤12%,15%≤Cr≤20%,Mo≤3%,Cu≤4%,N≤0.05%,S≤0.03%,以及P≤0.05%。它们一般不能拉得很细,或者虽然拉得很细,但在拉到一定程度后,纤维丝综合性能不高,脆而易断。
另外,不锈钢纤维通常采用的生产工艺为:钢丝检验----装管-----拉拔-----退火---清洗-----成品包装等工艺加工而成。经此工艺加工而成的纤维丝综合性能不高,脆而易断。
发明内容
本发明的目的是,针对上述存在问题,提供一种铁铬铝纤维丝产品及其加工工艺,使金属纤维丝综合性能大大提高,适宜拉拔,且拉拔后纤维丝的强度和延伸率等性能良好。
为了达到以上目的,本发明提供一种铁铬铝纤维丝,其组成及质量百分比为:C:0.06-0.08%,Mn:0.20-0.46%,Si:0.40-0.63%,RE:0.02-0.10%,Al:4.8-5.9%,Cr:15-26%,Cu:1-2%,Fe:余量。
由于本发明采用以上技术方案,使得铁铬铝纤维丝适宜拉拔加工,单丝直径可达6um,强度>16CN(牛顿/平方毫米),延伸率1.40%,大大提高了铁铬铝纤维丝成品的综合性能,完全克服了拉不细、脆而易断的缺点。
具体实施方式
下面结合实施例对本发明作进一步说明
实施例一
一种铁铬铝纤维丝,各组份的质量百分比为:C:0.06%,Mn:0.36%,Si:0.55%,Ce:0,02%,Al:4.8%,Cr:26%,Cu:1%,Fe:余量。
其加工工艺为:包铜----装管-----拉拔-----退火------酸丝-----清洗-----成品包装
具体描述如下:
1、包铜:检查钢丝表面,配制清洗主镀、预镀等溶液后都进行预镀和主镀;
2、装管:先把所需规格的铜管擦干净,再把镀好的钢丝装入铜管中;
3、拉拔:配好所需规格拉拔模具,后进行拉拔操作;
4、退火:管道炉退火,退火温度750-890℃;
5、酸洗:把清洗干净的金属丝放入配好酸液的酸丝池中(一般浓度为96%的硝酸加水1份),酸丝池温度保持在56-75℃范围内;
6、清洗、烘干。烘箱温度控制在120-180℃;
7、成品包装、入库。
实施例二
同实施例一的一种铁铬铝纤维丝,其不同之处在于,各组份的质量百分比为:C:0.07%,Mn:0.20%,Si:0.40%,RE:0.06%,Al:5.3%,Cr:15%,Cu:1.5%,Fe:余量。
实施例三
同实施例一的一种铁铬铝纤维丝,其不同之处在于,各组份的质量百分比为:C:0.08%,Mn:0.46%,Si:0.63%,RE:0.10%,Al:5.9%,Cr:20%,Cu:2.0%,Fe:余量。
除上述实施例外,本发明还可以有其他实施方式。凡采用等同替换或等效变换形成的技术方案,均落在本发明要求的保护范围内。
Claims (1)
1、一种铁铬铝纤维丝,其组成及质量百分比为:C:0.06-0.08%,Mn:0.20-0.46%,Si:0.40-0.63%,RE:0.02 0.10%,Al:4.8 5.9%,Cr:15-26%,Cu:1-2%,Fe:余量。