CN101654600A - Adhesive tape and use thereof - Google Patents
Adhesive tape and use thereof Download PDFInfo
- Publication number
- CN101654600A CN101654600A CN200810191190A CN200810191190A CN101654600A CN 101654600 A CN101654600 A CN 101654600A CN 200810191190 A CN200810191190 A CN 200810191190A CN 200810191190 A CN200810191190 A CN 200810191190A CN 101654600 A CN101654600 A CN 101654600A
- Authority
- CN
- China
- Prior art keywords
- adhesive tape
- described adhesive
- aforesaid right
- film
- cable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an adhesive tape with a strap-shaped substrate material, which is used for wrapping a longitudinally extending object, particularly a conductor bundle or cable bunch. At least one side of the substrate material is spread with a special pressure-sensitive adhesive. The tape is characterized in that: the substrate material is formed by embossed PVC thin films; and the embosseddepth is 0.01 to 8mum, preferably 0.1 to 3mum.
Description
Technical field
The present invention relates to adhesive tape, especially be used for insulating and wrap up the adhesive tape of lead or cable, it has single or double gummed base material; And relate to this adhesive tape and bring the application of twining wrapping and harness (especially in motor vehicle such as the automobile) lead and cable as insulating tape or wrapping.
Background technology
Insulating tape and cable wrap are made of the plasticized PVC film of single spreading usually.This class also is used for electrical lead is wrapped up into bunch of cables in automobile based on the adhesive tape of PVC flexible film.If originally to original adhesive tape of developing as insulating tape, it is very important to improve electrical insulation capability, so this adhesive tape just must be realized other function now, for example some unit cables are tied up and are permanently fixed more stable bunch of cables, prevent that perhaps cable from suffering the environmental influence of machinery, heat and chemical aspects.
Even in today, most these type of bunchs of cables still wrap up with manual mode.And when manual when cutting off common flexible film adhesive tape, cause the carrier thin film overstretching easily, form the waviness that is difficult to reliably cling and tear the edge.
Retraction after the overstretching may cause bonding end to peel off (professional is alice (Flagging)).For alice, be generally understood as the tendency of the terminal perk of bandage of parcel.Reason is the comprehensive action of bonding force, carrier rigidity and the bunch of cables diameter of tackiness agent.
Not only just the perk phenomenon can occur, and the design of special cable bundle also can cause this phenomenon because of the improper use of film adhesive tape.Especially peel off tendency in the terminal existence of the adhesive tape that is directly adjacent to bunch of cables vary in diameter part.Bunch of cables manufacturers avoids this problem in various mode.For example common practice is to finish parcel on each bigger parts of diameter.In addition, also attempt additional high elastic force pressure and make good especially fixing of adhesive tape end.But all these solutions all need additional overhead when the parcel bunch of cables, and this should be avoided as far as possible.
Therefore, on the back side of adhesive tape, higher clinging power to be arranged usually, to avoid occurring alice.And higher clinging power usually means that tackiness agent is very soft, and this can cause tackiness agent to overflow from the rubber roll side again.The professional is called strike-through with the sticking viscosity of this side.
In order to satisfy the environmental requirement of upgrading, had since the several years trend of avoiding in the adhesive tape production process, using solvent.Especially can not volatilize solvent (professional being VOC, i.e. volatile organic compounds) at the employed product of auto industry field strong request.
Relatively difficulty and expense are bigger owing to give PVC flexible film coating hot-melt adhesive, so manufacturers all uses water accack to address this problem.
Yet, to compare with solvent-based systems, these moisture tackiness agent and PVC flexible film bonded clinging power are less.For some adhesive system,,, in the time the alice phenomenon can not occurring, also can use the less tackiness agent of clinging power for the consideration of cost aspect although can evade this shortcoming by proper formula.
DE 102 02 038 A1 disclose a kind of adhesive tape that is used to insulate and wraps up lead or cable, has single or double gummed base material, and base material is thick in 40 μ m, preferred banded between 20～40 μ m and preferably be subjected to tensile PVC film and constitute by thickness, and is substantially free of softening agent.
Can embossing on this PVC film, and the embossing degree of depth is preferably 10～30 μ m, and/or embossing is made of a kind of style with vertical or horizontal, continuous or discontinuous lines.
Summary of the invention
The objective of the invention is to, a kind of adhesive tape that has based on the base material of PVC is provided, this adhesive tape can be used to tie up cable fast, simply, and the unlikely shortcoming that prior art occurs especially refers to alice and strike-through.
The application relates to following invention:
1. adhesive tape, especially be used for wrapping up the longitudinal extension article especially as bundle conductor or bunch of cables, this adhesive tape has the band-shaped substrate material that single face at least is coated with pressure-sensitive adhesive, described adhesive tape is characterised in that, its base material is made of embossing PVC film, the embossing degree of depth is 0.01 μ m～8 μ m, is preferably 0.1 μ m～3 μ m.
2. 1 a described adhesive tape is characterized in that the thickness of PVC film is 40 μ m～350 μ m, is preferably 70 μ m～150 μ m.
3. 1 or 2 a described adhesive tape is characterized in that, is added with softening agent, stablizer, filler, pigment, anti-impact modifier, lubricant and/or processing subsidiary material in the PVC film.
4. at least one described adhesive tape in the item 1～3 is characterized in that tackiness agent is based on the self-adhesive of water polyacrylic acid, polyisoprene or polyisobutene.
5. above-mentioned at least one described adhesive tape is characterized in that, tackiness agent is with at 10～50g/m
2In the scope, especially at 15～30g/m
2Apply in the scope.
6. above-mentioned at least one described adhesive tape is characterized in that, vertically with the strips adhesive coating, and the width of band is less than the adhesive tape substrate film along adhesive tape.
7. above-mentioned at least one described adhesive tape is characterized in that adhesive tape has coarse cut edge.
8. above-mentioned at least one described adhesive tape is characterized in that, adhesive tape can self-gravitation, is through painted and/or be black.
9. above-mentioned at least one described adhesive tape is characterized in that the clinging power of tackiness agent on adhesive tape self back side is 0.2～3N/cm scope, is preferably 0.5～1.5N/cm scope.
10. above-mentioned at least one described adhesive tape is characterized in that between PVC film and tackiness agent coating being arranged.
11. the purposes of above-mentioned at least one described adhesive tape is used for insulation, parcel lead or cable.
12. the purposes of above-mentioned at least one described adhesive tape is used for wrapping up the longitudinal extension article, especially as the bunch of cables in the automobile.
13. the purposes of above-mentioned at least one described adhesive tape wherein makes adhesive tape along spiral-line around the longitudinal extension article.
14. the purposes of above-mentioned at least one described adhesive tape wherein makes adhesive tape coat the longitudinal extension article vertically.
15. the purposes of above-mentioned at least one described adhesive tape, wherein when according to LV 312 (in January, 2006 version, article 5.5), under the temperature condition more than 100 ℃, the complex body of bunch of cables and adhesive tape composition was deposited until 3000 hours, and then when the bent spindle cable, be bonded in the cable that has the PVC coating layer and the adhesive tape that has on the cable of polyolefine coating layer can not destroy cable.
Embodiment
According to this, the present invention relates to be used for especially wrapping up the adhesive tape of longitudinal extension article such as bundle conductor or bunch of cables, this adhesive tape has the band-shaped substrate material, described base material single face at least scribbles pressure-sensitive adhesive, and base material is made of embossing PVC film, the embossing degree of depth is 0.01 μ m～8 μ m, is preferably 0.1 μ m～3 μ m.
The embossing degree of depth is poor (following also will explain in detail measuring the required detection method of the embossing degree of depth) of thickness of calculating according to weight per unit area and the thickness that utilizes the detecting thickness instrument to measure, between 0.01 μ m and 8 μ m, the style of embossing is unimportant in principle.The embossed film that preferably has vertical or horizontal, continuous or discontinuous lines.
The shape of embossing and the degree of depth play favourable influence to the kindliness of film when the wrapping cable.The film embossing also helps stretching, because at first can extrude the air that is contained between film and the cementing agent under tension force.In addition, so also can realize less uncoiling power, thereby help handling adhesive tape with hand.
The professional is unexpected to be found: the key factor of avoiding alice is not to be clinging power (below will explain in detail measuring the required detection method of alice) on tackiness agent self back side, but exists between the embossing degree of depth and alice characteristic and direct relation that clinging power has nothing to do.
In addition, unexpected discovery also has: with regard to different film formulation and all thinkable adhesive formulations, all can prove to have this effect.
According to first kind of useful embodiment of the present invention, base material by thickness be 40 μ m～350 μ m, the PVC film that is preferably 70 μ m～150 μ m constitutes.
Adhesive tape of the present invention can be made with the film that contains the conventional monomeric plasticizer in 5～60phr scope, this monomeric plasticizer for example is dioctyl phthalate (DOP) (DOP, two (2-ethylhexyl) phthalic ester), diisononyl phthalate (DINP), Di Iso Decyl Phthalate (DIDP), three (2-ethylhexyl) trimellitate (TOTM); And the same available film that contains the typical polymers softening agent in 10～70phr scope is made, this polymeric plasticizer for example is that hexanodioic acid, sebacic acid, nonane diacid, phthalic acid and dibasic alcohol are as 1,3-butyleneglycol, 1,2-propylene glycol, 1,4-butyleneglycol, 1, the polyester (M of 6-hexylene glycol and other glycol
rBe about 1800～13000) make.Also can produce film, described phosphate plasticizer such as di(2-ethylhexyl)phosphate benzene toluene ester (DPCF), diphenyl octyl phosphate (DPOF, (2-ethylhexyl) diphenyl phosphoester) or three (2-ethylhexyl) phosphoric acid ester (TOF) with typical phosphate plasticizer.
Can use the mixture that contains one or more the above-mentioned type softening agent equally.
The K value of PVC powder can change in broad range equally.So use range does not have much influences at the PVC of 40～90K emulsion powder or suspension powder to the improvement of alice characteristic.
But the PVC that the K value is bigger is because thermostability is higher and preferred, and for example the K value is 78 PVC emulsion.For example at Hand book of PVC formulating (editor E.J.Wickson, J.Wiley﹠amp; Sons, 1993) in or at PVC:Production, Properties and Uses has put down in writing this class material and working method thereof in (G.Mattews, The Institute of Materials, 1996).Therefore, the K value of film especially should be between 75～80 preferably between 60～90.
Also can be with all other additives of PVC film (as stablizer, for example at " the Plastics Additives Handbook " of Hanser press (the 5th edition) or John Wiley ﹠amp; The stablizer of being put down in writing in " the Handbook of PVC Formulating " of Sons press) adds among the adhesive tape of the present invention, and can not have any impact the alice characteristic.
For avoiding the PVC film to suffer pyrolytic damage (for example embrittlement) in the process that adds man-hour or use as adhesive tape, it is desirable adding stablizer such as diphenyl thiourea material.According to a kind of preferred implementation of the present invention, film contains stablizer.Be applicable to the especially tin compound class stablizer of adhesive tape of the present invention, preferably those allowances are used for the tin compound stablizer of food packaging film, for example dibutyl tin-two-(2-ethylhexyl mercaptoacetate).Equally also can use the stablizer of leaded or cadmium, but these stablizers are for the reason of toxicity and environment aspect, less use.The content of stablizer is between 0.3～10 weight part (in 100 weight part PVC polymkeric substance) for example, in order to reach higher thermostability, are at least 0.7phr, preferably are at least 1phr (in the shared weight part of 100 weight part PVC).
Common other additive such as filler, pigment, impact modifier, lubricant and/or processing subsidiary material (Verarbeitungshilfsmittel) in the PVC film (Paraloid K 120 ND for example, Rohm﹠amp; Haas) also can be used for making the carrier thin film of adhesive tape of the present invention.In " Kunststoff-Handbuch-Polyvinylchlorid 2/1 " (the 2nd edition, Hanser Verlag.) the 6th chapter, put down in writing common additives.Use the montanic acid ester type waxes
As preferred lubricant, its consumption is favourable with 100 weight part PVC polymkeric substance timing with 2～5 weight parts.
Preferably on rolling press, prepare carrier thin film, carry out drawing-off especially again with high temperature or low temperature process.Be higher than in temperature under 95 ℃ the condition, go up with the film drawing-off repeatedly, make that thickness is corresponding to be reduced by the roller speed that increases gradually at roll-type drafting machine (Rollenstrecke).Film can also be widened (KOBRA slightly
Technology).Luvitherm
Technology is particularly suitable for adhesive tape of the present invention, because also can handle higher K value without a doubt.For example at Kunststoff-Handbuch (Carl-Hanser Verlag.), just put down in writing Luvitherm on 240～243 pages in chapter 2 polyvinyl chloride the 1st chapter
Technology.This technology is made up of two processing steps, with lower temperature calendering polyvinyl chloride, promptly by roller it is pressed into film in the fs, carries out the short period of time with comparatively high temps and handle in subordinate phase, will have the film sintered of widget intensity very.Also can hard PVC be processed into film, but this technology only is suitable for lower K value with blow molding process.
The PVC base material is single spreading at least.Can use the tackiness agent of all common types, for example with tackiness agent based on aqueous polyacrylic ester, polyisoprene and/or polyisobutene, General Purpose Rubber or acrylate.This type of rubber for example can be the homopolymer or the multipolymer of iso-butylene, 1-butylene, vinyl acetate, acrylate, divinyl or isoprene, and the main prescription that uses based on acrylate, divinyl or isoprene.
Typically the cementing agent based on acrylate can be polymerized with alkyl acrylate that contains 4～17 carbon atoms and/or methacrylic ester.Can add the suitable comonomer that has functional group's (as carboxyl or hydroxyl) by polymerization, improve mechanical characteristics and adhesiveness targetedly.
Can use solution, be coated with the tackiness agent of all these types with dispersion or hot melts form.The selection of coating method is to the not significantly influence of alice characteristic.But should preferably use the water accack system.
Can be at 10～50g/m
2, especially at 15～30g/m
2The suitable tackiness agent of coating in the amount ranges.
Clinging power on the back side can be at 0.2～3N/cm, preferably can change in 0.5～1.5N/cm scope, can not influence the alice characteristic.
For optimization characteristics, one or more additives can be added, as tackifier (resin), softening agent, filler, pigment, UV light absorber, photostabilizer, fire retardant, antiaging agent, light trigger, linking agent or crosslinking reaction promotor in used Autoadhesive.For example, tackifier can be that hydrocarbon resin is (for example based on unsaturated C
5-or C
9-polymer of monomers); The terpene phenolic resin; Polyterpene resin based on raw material such as α-Pai Xi or beta-pinene; Aromatic resin, as coumarone-indene resin, the perhaps resin of styrene-based or alpha-methyl styrene, as rosin and secondary species thereof, for example nilox resin, dimerization colophonium or esterified rosin, for example with the reaction product of ethylene glycol, glycerol or tetramethylolmethane, or the like.Preferred use does not contain the resin of two keys of easy oxidation, as terpene phenolic resin, aromatic resin, especially preferred resin, for example hydrogenated aromatic resin, hydrogenation polycyclopentadiene resin, staybelite derivative or hydrogenation polyterpene resin by the hydrogenation reaction preparation.
The filler and the pigment that are suitable for for example have carbon black, titanium dioxide, lime carbonate, zinc carbonate, zinc oxide, silicate or silicic acid.The suitable softening agent that can mix for example has aliphatics mineral oil, alicyclic mineral oil and aromatic series mineral oil; The diester of phthalic acid, trimellitic acid or hexanodioic acid or polyester; Liquid rubber (for example paracril or polyisoprene rubber); The liquid polymerization product of butylene and/or iso-butylene; Acrylate; Polyvingl ether; With tackifying resin, wool wax and other wax or liquid silicone resin is the liquid resin or the soft resin of base-material.
Linking agent for example can be isocyanic ester, resol or halogenated phenols urea formaldehyde, melamine resin and formaldehyde resin.The crosslinking reaction promotor that is suitable for for example has maleimide, allyl ester such as triallyl cyanurate, the polyfunctional group ester of acrylic or methacrylic acid.
Antiaging agent for example can be a sterically hindered phenol, and the sterically hindered phenol of known commodity Irganox by name is wherein arranged.
It is favourable forming crosslinked, holds sticking (holding power) because can improve, and can reduce the distortion tendency (flexible or formation cavity be also referred to as space) of coiled material in depositing process.Also can reduce tackiness agent excessive (strike-through), promptly at the no glue side of coiled material and be spirally wound on adhesive tape around the cable and do not have in the glue limit and overflow.Hold the sticking plasticizer loading that also depends on adhesive component and film, be preferably greater than 150 minutes.
Tackiness agent can vertically be painted ribbon along adhesive tape, and strip width is less than adhesive band base.Decide on applicable cases, also can on base material, apply a plurality of parallel tackiness agent bands.
The position of band on base material can be selected arbitrarily, preferably is arranged on certain one side of base material.Preferably with adhesive coated on whole of base material.
Can have at least one to hide bar on the adhesive coating of base material, this hides bar or these hide bar along the adhesive tape longitudinal extension, and the rubber cover adhesive coating layer 20～90%.
According to a kind of preferred implementation of the present invention, just in time be one and hide bar on adhesive coating.
The position of band on adhesive coating can be selected arbitrarily, preferably is set directly on a certain vertical limit of base material.Obtain by this way along the adhesive tape longitudinal extension and with the isolated gluing band in another vertical limit of base material.
If adhesive tape is used for coating bunch of cables, its mode is to make adhesive tape center on the bunch of cables spiral motion, then can wrap up bunch of cables like this: make tackiness agent on the adhesive tape only adhere to adhesive tape from one's body, and article do not contact with tackiness agent.
Because any tackiness agent of shortage is fixing to cable, Bao Zha bunch of cables has very high snappiness like this.Therefore, also be like this even can obviously improve its bending property one when mounted at narrow path or sharp bend position.
If with adhesive tape to be fixed on to a certain degree on the article, then can coat like this, make a gluing band part adhere to adhesive tape from one's body, another part then adheres on the article.
According to the favourable embodiment of another kind, band is placed on the adhesive coating centre, thereby forms two gluing bands on vertical limit of base material along the adhesive tape longitudinal extension.
For adhesive tape being wrapped in around the bunch of cables reliably, economically in above-mentioned spiral motion mode, and prevent that formed sheath from sliding, these two the gluing bands that are each positioned on the vertical limit of adhesive tape are favourable, especially when wherein narrower than second a band usually band is used as sealing as second band of assisting fixture and broad.By this way adhesive tape suitably is adhesive on the cable, thereby prevents that bunch of cables from sliding, and still keep snappiness.
In addition, also have some that one or more cover strip is placed embodiment on the adhesive coating.As long as when it comes to a cover strip, the professional will associate so, and many cover strips also necessarily can while rubber cover adhesive layer.
The scope of this cover strip rubber cover adhesive coating layer is preferably altogether between 50～80%.Diameter according to applicable cases and bunch of cables is selected level of coverage.
Described percentage value is the cover strip width and the ratio of base material width.
Especially preferably leave the tackiness agent band that one or two total width is total up to 20～50% base material width.
Can be used as film that especially is usually used in the cable cladding applications (for example polypropylene film of polyethylene film, polypropylene film, uniaxial orientation or diaxial orientation, polyester film, PA film and other film) or PVC that cover material is used based on polyolefins, preferred plasticizer content 20 and 60phr between film.
Advantageously between carrier thin film and tackiness agent, use undercoat to improve the clinging power of tackiness agent on film, thereby avoid in the uncoiling process, tackiness agent being relayed on the film back side.About the illustrative examples of the tackiness agent commonly used of adhesive tape and barrier coat and undercoat as consulting " Handbook ofPressure Sensitive Technology (pressure sensitive adhesive technical manual) ", D.Satas (the 3rd edition).
Can be used as known dispersant system that undercoat uses and solvent system for example has rubber based on isoprene or divinyl, thermoprene, and paracril especially.Isocyanic ester as additive can improve clinging power, and in the slip resistance that after internal diffusion, can improve tackiness agent.
Can apply one deck coating at the base material back side in case of necessity and adjust uncoiling power.
The coating (can mix other polymkeric substance in case of necessity) that can apply known release agent realizes breaking away from effect.For example can use stearyl compound (for example urea that constitutes of the stearyl compound of polyvinyl stearyl carbamate, transition metal such as Cr or Zr, polymine and stearyl isocyanic ester, polysiloxane (for example as contain the multipolymer of urethane or as polyolefin-based graft copolymer), thermoplastic fluoropolymer.Stearyl refers to carbonatoms and is at least 10 all straight chains or branched-chain alkyl or thiazolinyl, for example octadecyl.
In order to obtain the tearable fragility of good craft (Handeinrei β barkeit), when making roll of tape, generation can be examined under a microscope the coarse cutting edge of crackle, and these crackles promote to tear.This especially can use blunt or certain zigzag rotary cutter to squeeze and cut, and perhaps uses fixed blunt edges to carry out rewinding and cuts (Abstechschnitt) and realize this effect.Because thickness is little and flexible tendency is little, thus 33～100m coiled material continuity length can be obtained without a doubt, and traditional product has the smaller length of 10～33m usually.
Adhesive tape of the present invention preferably has color, especially is black.Color is managed to make do in film, adhesive layer and/or the undercoat, perhaps before adhesive coating, afterwards or in the coating procedure color is imprinted on the film.
The basement membrane of adhesive tape and base material are said on the whole and can be contained fire retardant.Can use not halogen-containing material, these materials for example are the carbonate or the oxyhydroxide of aluminium, calcium or magnesium, for example borate, for example filler of stannate and so on for this reason; The nitrogen based flameproofing of melamine cyanurate, Dyhard RU 100, red phosphorus, organic or inorganic phosphoric acid salt such as polyphosphate or bulky amine such as HA (L) S level bulky amine and so on for example.Require to use bromated fire retardant when very high, as hexabromocyclododecane, poly-Dowspray 9 or preferably use two (penta-bromophenyl) ethane.The decabrominated dipheny base oxide can be used, antimonous oxide (Sb can be used in addition
2O
3).
Owing to have an above-mentioned advantageous feature, this adhesive tape can be used for insulation, parcel lead or cable very with flying colors.Advantageously be suitable for wrapping up the bunch of cables in longitudinal extension article, the especially automobile in addition, adhesive tape can be extended along spiral-line around the longitudinal extension article at this moment, perhaps axially wrapping up the longitudinal extension article with adhesive tape.If according to the regulation of LV 312 (in January, 2006 version, article 5.5), under temperature more than 100 ℃, the complex body that cable and adhesive tape constituted was deposited to 3000 hours, then around the bent spindle cable, then when being bonded in the cable that has the PVC coating layer and have on the cable of polyolefine coating layer, adhesive tape also can not destroy these cables especially.
The cross section of bunch of cables shown in Fig. 1, bunch of cables is made of the unit cable that is bundled together (7), and is surrounded by adhesive tape of the present invention.Make adhesive tape center on the bunch of cables spiral motion.
Shown in look out two circle adhesive tape I and II on the bunch of cables cross section.Other circle extends in the past left, does not draw here.
On adhesive coating (4), there is one to hide bar (5), thereby produces a strip of adhesive (6) along the adhesive tape longitudinal extension.The non-gluing segment of adhesive tape (11,21,23) alternately occurs with gluing segment (12,22,24).(sections 22,24 is opposite with exposed adhesive 12, can't see from the outside, and, therefore with darker shadow representation).Coat bunch of cables like this, gluing band (6) is glued fully be posted on the adhesive tape.Not bonding with cable (7).
" adhesive tape " of the present invention this general term comprises all planar products, as the film of two-dimensional development or film fragment, length direction launches and width is limited band, strap section, die-cut, label etc.
Detection method
In temperature is that 23 ± 1 ℃ and relative air humidity are to measure under 50 ± 5% the detection atmosphere.
All put down in writing the common methods of laboratory scale mensuration alice characteristic in the technical specifications of different automobile manufacturing companies.At this moment, standard is to make a sample that is made of 5～25 unit cables with same diameter or different diameter.Covering material of cable is abideed by the temperature grade of adhesive tape to be tested.Use adhesive tape to be tested to wrap up these cables then, make and respectively enclose overlapping 50%.The sample that will obtain like this places under the different temperature and envrionment conditions then, and then the axle around a diameter 80mm makes its bending.And then assessment alice situation.This alice test is very inresponsive, and many adhesive tapes that do not show defective in this test process alice can occur in actual application.
Therefore researched and developed a kind of novel test method that when making bunch of cables, can adjust situation.Give 13 general grade 0.85mm of commerce that are about 2 meters for this reason
2Unit cable mix 10 long 10cm, diameter is the barrel of 10mm.Use adhesive tape to be tested that it is twined then, make and respectively enclose overlapping 50%.About 5cm place finishes to twine after the barrel end, and tears adhesive tape by hand, makes it respectively have half to be bonded on the adhesive tape back side and the bunch of cables.The axle spiral that the sample that will obtain like this is long 1.5 meters around one then, diameter is 80cm twines, fixes.At room temperature leave standstill after 24 hours and remove sample, and the alice characteristic of assessment adhesive tape end.If more than the terminal perk 1mm of adhesive tape, then be assessed as alice.
The embossing degree of depth is by calculating with thickness difference afterwards before the embossing operation.Under the style situation of having pressed, this can be estimated as follows: at first by weight per unit area (recording by DIN 53352) and proportion (PVC=1.37g/m
3) calculate theoretic throat.Then this theoretic throat is deducted the actual (real) thickness of measuring with flat probe (planen Taster) by DIN 53370 regulations.The result roughly is equivalent to the embossing degree of depth.
The K value of PVC is measured by DIN 53726/ISO 1628-2.
Utilize gel permeation chromatography (GPC) determining molecular weight Mr.Use contains the THF (tetrahydrofuran (THF)) of 0.1% (volume) trifluoroacetic acid as eluent.Under 25 ℃ of temperature condition, measure.Use PSS-SDV, 5 μ,
ID 8.0mm * 50mm is as the pre-separation post
Use each tool ID 8.0mm * 300mm, 5 μ, 10
3And 10
5With 10
6The PSS-SDV post separate.Sample solution concentration is 4g/l, and the per minute flow is 1.0ml.Measuring each PMMA standard of certificate carries out.
To explain that below the present invention is not limited to these embodiment according to a plurality of embodiment in detail to the present invention.
Embodiment
Embodiment 1
Adhesive tape based on acrylic ester adhesive
Adhesive tape 1:
Has following composition (pressing the 100phr polymkeric substance calculates)
The 50phr polymeric plasticizer
10phr filler (chalk)
The 1phr carbon black
The 1phr stablizer
Weight per unit area is 100g/m
2, the embossing degree of depth is to be coated with 25g/m on the PVC flexible film of 15 μ m
2Acrylate-based aqueous adhesive (the water soluble acrylic acid ester dispersion of Rohm and Haas company, (solid contents is 53% (weight) to trade(brand)name Primal PS83D; Ammonia content＜0.2% (weight); The pH value is 9.1～9.8)).
Adhesive tape 2:
To weight per unit area is 100g/m
2, the embossing degree of depth is that the above-mentioned PVC flexible film of 1 μ m is coated with 25g/m
2Apply acrylate-based aqueous adhesive.
Adhesive tape 3:
To weight per unit area is 100g/m
2, the embossing degree of depth is that the above-mentioned PVC flexible film of 1 μ m is coated with 15g/m
2Acrylate-based aqueous adhesive.
| Feature | Method | Unit | Adhesive tape 1 | Adhesive tape 2 | Adhesive tape 3 |
| The steel clinging power | ??ASTM?D1000 | ??N/cm | ??1.4 | ??1.4 | ??1.0 |
| Back side clinging power | ??ASTM?D1000 | ??N/cm | ??0.8 | ??0.9 | ??0.5 |
| Breaking tenacity | ??ASTM?D1000 | ??N/cm | ??21.4 | ??20.7 | ??20.4 |
| Elongation at break | ??ASTM?D1000 | ??％ | ??189 | ??214 | ??205 |
| The embossing degree of depth | ??μm | ??15 | ??1 | ??1 | |
| The alice characteristic | ??％ | ??20 | ??0 | ??0 |
PVC flexible film prescription in the present embodiment is constant, has only changed the embossing degree of depth.The identical tackiness agent based on acrylate dispersoid is used for adhesive tape 1～3.
For the professional, be unexpectedly:, also do not have the alice phenomenon although the clinging power on adhesive tape 3 back sides is significantly less than adhesive tape 1.This characteristic can be clearly owing to having used the embossing degree of depth of the present invention.
Embodiment 2
Adhesive tape based on rubber dispersion:
Adhesive tape 4:
To weight per unit area is 140g/m
2, the embossing degree of depth is that the above-mentioned PVC flexible film of 15 μ m is coated with 25g/m
2Rubber-based aqueous adhesive with following composition:
80% (weight) (doing) natural rubber
45% (weight) (doing) resin (C
5-resin)
1% (weight) (doing) antiaging agent
4% (weight) (doing) softening agent
Adhesive tape 5:
To weight per unit area is 140g/m
2, the embossing degree of depth is that the above-mentioned PVC flexible film of 1 μ m is coated with 25g/m
2The rubber-based aqueous adhesive.
Adhesive tape 6:
To weight per unit area is 140g/m
2, the embossing degree of depth is that the above-mentioned PVC flexible film of 1 μ m is coated with 15g/m
2The rubber-based aqueous adhesive.
| Feature | Method | Unit | Adhesive tape 4 | |
|
| The steel clinging power | ??ASTM?D1000 | ??N/cm | ??2.1 | ??2.1 | ??1.7 |
| Back side clinging power | ??ASTM?D1000 | ??N/cm | ??1.5 | ??1.4 | ??0.8 |
| Breaking tenacity | ??ASTM?D1000 | ??N/cm | ??26.1 | ??27.8 | ??26.9 |
| Elongation at break | ??ASTM?D1000 | ??％ | ??213 | ??222 | ??231 |
| The embossing degree of depth | ??μm | ??15 | ??1 | ??1 | |
| The alice characteristic | ??％ | ??30 | ??0 | ??0 |
In each film of present embodiment, PVC flexible film prescription is still constant, only changes the embossing degree of depth.The identical tackiness agent based on rubber dispersion is used for adhesive tape 4～6.Find unexpected result once more:, alice do not occur although the clinging power on adhesive tape 6 self back side is significantly less than adhesive tape 4.The obvious cause of this characteristic just has been to use the embossing degree of depth of the present invention.
If the result of adhesive tape 3 (clinging power on the adhesive tape back side only 0.5N/cm and alice do not occur) and the result of adhesive tape 4 are compared, then can clearly reach a conclusion: the high clinging power on adhesive tape self back side is for alice phenomenon unrooted Ben Yiyi not occurring again.
Claims (15)
1. adhesive tape, especially be used for wrapping up the longitudinal extension article especially as bundle conductor or bunch of cables, this adhesive tape has the band-shaped substrate material that single face at least is coated with pressure-sensitive adhesive, described adhesive tape is characterised in that, its base material is made of embossing PVC film, the embossing degree of depth is 0.01 μ m～8 μ m, is preferably 0.1 μ m～3 μ m.
2. the described adhesive tape of claim 1 is characterized in that, the thickness of PVC film is 40 μ m～350 μ m, is preferably 70 μ m～150 μ m.
3. claim 1 or 2 described adhesive tapes is characterized in that, are added with softening agent, stablizer, filler, pigment, anti-impact modifier, lubricant and/or processing subsidiary material in the PVC film.
4. at least one described adhesive tape in the claim 1～3 is characterized in that tackiness agent is based on the self-adhesive of water polyacrylic acid, polyisoprene or polyisobutene.
5. at least one described adhesive tape is characterized in that during aforesaid right required, and tackiness agent is with at 10～50g/m
2In the scope, especially at 15～30g/m
2Apply in the scope.
6. at least one described adhesive tape is characterized in that during aforesaid right required, and vertically with the strips adhesive coating, and the width of band is less than the adhesive tape substrate film along adhesive tape.
7. at least one described adhesive tape is characterized in that adhesive tape has coarse cut edge during aforesaid right required.
8. at least one described adhesive tape is characterized in that during aforesaid right required, and adhesive tape can self-gravitation, was through painted and/or be black.
9. at least one described adhesive tape is characterized in that the clinging power of tackiness agent on adhesive tape self back side is 0.2～3N/cm scope, is preferably 0.5～1.5N/cm scope during aforesaid right required.
10. at least one described adhesive tape is characterized in that between PVC film and tackiness agent coating being arranged during aforesaid right required.
11. the purposes of at least one described adhesive tape during aforesaid right requires is used for insulation, parcel lead or cable.
12. the purposes of at least one described adhesive tape was used for wrapping up the longitudinal extension article, especially as the bunch of cables in the automobile during aforesaid right required.
13. the purposes of at least one described adhesive tape during aforesaid right requires wherein makes adhesive tape along spiral-line around the longitudinal extension article.
14. the purposes of at least one described adhesive tape wherein made adhesive tape coat the longitudinal extension article vertically during aforesaid right required.
The purposes of at least one described adhesive tape during 15. aforesaid right requires, wherein when according to LV 312 (in January, 2006 version, article 5.5), under the temperature condition more than 100 ℃, the complex body of bunch of cables and adhesive tape composition was deposited until 3000 hours, and then when the bent spindle cable, be bonded in the cable that has the PVC coating layer and the adhesive tape that has on the cable of polyolefine coating layer can not destroy cable.