CN101654357A - Light building material and preparation method thereof - Google Patents
Light building material and preparation method thereof Download PDFInfo
- Publication number
- CN101654357A CN101654357A CN200810012893A CN200810012893A CN101654357A CN 101654357 A CN101654357 A CN 101654357A CN 200810012893 A CN200810012893 A CN 200810012893A CN 200810012893 A CN200810012893 A CN 200810012893A CN 101654357 A CN101654357 A CN 101654357A
- Authority
- CN
- China
- Prior art keywords
- dash board
- glasscloth
- roll
- building material
- light building
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of building materials and relates to a light building material and a preparation method thereof. The light building material is characterized by comprisingthe raw materials of magnesium oxide, plant powder, fly ash and an assistant in a mixing ratio of 1:0.5:1:0.002:1, wherein the assistant is mixed solution of magnesium chloride for solution and magnesium sulfate. Plates made from the light building material have the characteristics of desirable overall performance, prefabricated installation, high construction efficiency, the realization of production industrialization, product standardization, construction prefabrication, excellent surface decoration performance, low overall cost, quick construction, short period and the like and reduce construction cost by 30 percent compared with clay bricks and cavity blocks.
Description
Technical field
The invention belongs to building materials technology field, relate to a kind of light building material and preparation method thereof.
Background technology
At present, domestic needs according to novel housing structure system development, promote the use of light steel frame system and supporting assembled sheet material thereof, the novel large bay bearing structural system of research and development on the large bay load larrying member basis of summing up and carrying out, especially Lightweight Steel Construction heat preservation energy-saving light-weight aseismatic wallboard urgently becomes people's needs, the needs of social progress development, it will become the main flow of new walling.The Light trabs of making in technique known at present and using has many kinds, and hole, garden GRC batten is arranged, square hole GRC batten, but main raw is a sand-cement slurry, still can not effectively lower unit weight, incubation and thermal insulation function is not obvious, moisture-sensitive, dry with after strain.
Summary of the invention
The present invention has overcome the defective of above-mentioned existence, and purpose provides a kind of light building material and preparation method thereof.
Light building material of the present invention and preparation method thereof content Description:
Light building material of the present invention and preparation method thereof is characterized in that:
The light building material raw material is: magnesium oxide, vegetation powder, flyash, auxiliary agent are solution magnesium chloride, sal epsom mixing solutions;
Proportion of raw materials is:
Magnesium oxide: vegetation powder: flyash: auxiliary agent: solution magnesium chloride, sal epsom mixing solutions=1: 0.5: 1: 0.002: 1;
Producing the light building material plate finishes by following processing step:
1, template is carried on the input grillage of laminator, manufacture the end during dash board at roll front, first road shop fixtures dash board bottom glasscloth, glasscloth must be balanced rolling the rod surface;
2, the upper strata glasscloth of end dash board is taped against second and balances to the front of roll, with under the Lv Yang Magnesium cement material that stirs for No. between the first road roll and second roll; The glasscloth of shop fixtures dash board before the second road roll, cloth be layered on material above, and will stir Lv Yang Magnesium cement material and be pushed into second below roll;
3, end dash board cuts off the glasscloth of end dash board to proceeding to five meters, and above the end dash board that the polystyrene foam central layer (EPS) that combines is placed on, makes;
4, spread dash board bottom glasscloth in the front of the 3rd road roll, the Lv Yang Magnesium cement material that stirs is pushed into below the 3rd road roll, (irritate flat in the EPS) De Sew crack polystyrene foam plate that combines;
5, spread dash board upper strata glasscloth and non-woven fabrics in the front of the 4th road roll, and the Lv Yang Magnesium cement material that stirs is pushed into below the 4th road roll;
6, with the glasscloth on dash board upper strata on the light building material plate of making, cloth is disconnected with lancinating, and runs to download to lift on the board bracket, plate is transported in the curing area be cured, and the reaction of light building material plate finishes after 15 hours, just can the demoulding.
The light building material sheet material good integrity that the present invention makes, can install by assembled, the operating efficiency height, can accomplish manufactureization, the standardization of products, construction assemblingization, decorative surface is good, comprehensive cost is low, construction is quick, characteristics such as the cycle is short reduce construction costs 30% relatively than clay brick, holllow building block.
Embodiment
Light building material of the present invention and preparation method thereof is achieved in that adopting magnesium oxide, vegetation powder, flyash, auxiliary agent is that solution is raw material with magnesium chloride, sal epsom mixing solutions, and proportion of raw materials is:
Magnesium oxide: vegetation powder: flyash: auxiliary agent: solution magnesium chloride, sal epsom mixing solutions=1: 0.5: 1: 0.002: 1;
Producing the light building material plate finishes by following processing step:
1, template is carried on the input grillage of laminator, manufacture the end during dash board at roll front, first road shop fixtures dash board bottom glasscloth, glasscloth must be balanced rolling the rod surface;
2, the upper strata glasscloth of end dash board is taped against second and balances to the front of roll, with under the Lv Yang Magnesium cement material that stirs for No. between the first road roll and second roll; The glasscloth of shop fixtures dash board before the second road roll, cloth be layered on material above, and will stir Lv Yang Magnesium cement material and be pushed into second below roll;
3, end dash board cuts off the glasscloth of end dash board to proceeding to five meters, and above the end dash board that the polystyrene foam central layer (EPS) that combines is placed on, makes;
4, spread dash board bottom glasscloth in the front of the 3rd road roll, the Lv Yang Magnesium cement material that stirs is pushed into below the 3rd road roll, (irritate flat in the EPS) De Sew crack polystyrene foam plate that combines;
5, spread dash board upper strata glasscloth and non-woven fabrics in the front of the 4th road roll, and the Lv Yang Magnesium cement material that stirs is pushed into below the 4th road roll;
6, with the glasscloth on dash board upper strata on the light building material plate of making, cloth is disconnected with lancinating, and runs to download to lift on the board bracket, plate is transported in the curing area be cured, and the reaction of light building material plate finishes after 15 hours, just can the demoulding.
This light building material plate: light-weight aseismatic, Light trabs is compared with clay solid brick, more than light ten times, more than the light 100kg of holllow building block, solve the problem of crossbeam, huge pillar, deep foundation, being connected of plate and cylinder has good seismic resistance, is not only applicable to low-rise building, also be applicable to Highrise buildings, buildings such as hag matter and sandy beach, seabeach.
Claims (2)
1, a kind of light building material and preparation method thereof is characterized in that:
The light building material raw material is: magnesium oxide, vegetation powder, flyash, auxiliary agent are solution magnesium chloride, sal epsom mixing solutions;
Proportion of raw materials is:
Magnesium oxide: vegetation powder: flyash: auxiliary agent: solution magnesium chloride, sal epsom mixing solutions=1: 0.5: 1: 0.002: 1.
2, light building material according to claim 1 is characterized in that: produce the light building material plate and finish by following processing step:
(1), template is carried on the input grillage of laminator, manufacture the end during dash board at roll front, first road shop fixtures dash board bottom glasscloth, glasscloth must be balanced rolling the rod surface;
(2), the upper strata glasscloth of end dash board be taped against second balance to the front of roll, with under the Lv Yang Magnesium cement material that stirs for No. between the first road roll and second roll; The glasscloth of shop fixtures dash board before the second road roll, cloth be layered on material above, and will stir Lv Yang Magnesium cement material and be pushed into second below roll;
(3), end dash board cuts off the glasscloth of end dash board to proceeding to five meters, and above the end dash board that the polystyrene foam central layer (EPS) that combines is placed on, makes;
(4), spread dash board bottom glasscloth in the front of the 3rd road roll, the Lv Yang Magnesium cement material that stirs is pushed into below the 3rd road roll, (irritate flat in the EPS) De Sew crack polystyrene foam plate that combines;
(5), spread dash board upper strata glasscloth and non-woven fabrics, and with the Lv Yang Magnesium cement material that stirs be pushed into below the 4th road roll in the front of the 4th road roll;
(6), with the glasscloth on dash board upper strata on the light building material plate of making, cloth is disconnected with lancinating, and runs to download to lift on the board bracket, plate is transported in the curing area be cured, the reaction of light building material plate finishes after 15 hours, just can the demoulding.