CN101643363B - 粘土低铁浇钢砖及其制备方法 - Google Patents

粘土低铁浇钢砖及其制备方法 Download PDF

Info

Publication number
CN101643363B
CN101643363B CN2009101700077A CN200910170007A CN101643363B CN 101643363 B CN101643363 B CN 101643363B CN 2009101700077 A CN2009101700077 A CN 2009101700077A CN 200910170007 A CN200910170007 A CN 200910170007A CN 101643363 B CN101643363 B CN 101643363B
Authority
CN
China
Prior art keywords
clay
iron
brick
mix
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2009101700077A
Other languages
English (en)
Other versions
CN101643363A (zh
Inventor
赵海军
梁成福
刘利明
赵有贵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2009101700077A priority Critical patent/CN101643363B/zh
Publication of CN101643363A publication Critical patent/CN101643363A/zh
Application granted granted Critical
Publication of CN101643363B publication Critical patent/CN101643363B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种粘土低铁浇钢砖，它的组分和重量含量如下：1-3mm的三、四混级矾土熟料含量为30-40％，0-1mm的三、四混级矾土熟料含量为10-20％，0.074mm的三、四混级矾土熟料含量为15-25％，0.20mm的结合粘土20-40％。所述粘土低铁浇钢砖的制备方法，步骤如下：a、原料拣选分级；b、原料粉碎加工；c、加工的颗粒三、四混级钒土熟料与结合粘土混配；d、砖坯成型；e、砖坯干燥；f、干燥的砖坯入隧道窑烧结，烧结温度计1320～1350℃；g、出窑后成品检验入库。本发明降低了粘土低铁浇钢砖的烧结温度，从而节约了能源，降低了它的制作成本。

Description

粘土低铁浇钢砖及其制备方法
技术领域
本发明属于一种耐火材料，具体涉及一种粘土低铁浇钢砖及其制备方法。
背景技术
粘土低铁浇钢砖现在广泛应用在浇钢中，但由于Al2O3含量的要求不一样，所以选用的三、四混级钒土熟料的含量都不一样，尤其是隧道窑烧结时温度一般为1420℃以上，由于需要的烧结温度高，所以浪费能源，制成的粘土低铁浇钢砖的成本高。
发明内容
本发明所要解决的技术问题是提供一种粘土低铁浇钢砖及其制备方法，它在隧道窑中烧结温度低，温度在1320～1350℃之间，可降低砖的成本，节约能源。
本发明的技术方案：一种粘土低铁浇钢砖，它的组分和重量含量如下：
1-3mm的三、四混级矾土熟料含量为30-40％，
0-1mm的三、四混级矾土熟料含量为10-20％，
0.074mm的三、四混级矾土熟料含量为15-25％，
0.20mm的结合粘土20-40％。
上述粘土低铁浇钢砖的制备方法，其步骤如下：a、原料拣选分级；b、原料粉碎加工；c、加工的颗粒三、四混级钒土熟料与结合粘土混配；d、砖坯成型；e、砖坯干燥；f、干燥的砖坯入隧道窑烧结，烧结温度计1320～1350℃；g、出窑后成品检验入库。
本发明与现有技术相比具有以下有益效果：本发明选用当地的三、四混级钒土熟料，成本低；其原料组分少，含量独特，尤其在隧道窑中烧结温度由常规的1420℃降低到1320～1350℃，从而节约了能源，降低了粘土低铁浇钢砖的成本，给企业带来了更大的利润。
具体实施方式
实施例1
一种粘土低铁浇钢砖，它的组分和重量含量如下：
1-3mm的三、四混级矾土熟料含量为40％，
0-1mm的三、四混级矾土熟料含量为10％，
0.074mm的三、四混级矾土熟料含量为15％，
0.20mm的结合粘土20％。
实施例2
一种粘土低铁浇钢砖，它的组分和重量含量如下：
1-3mm的三、四混级矾土熟料含量为30％，
0-1mm的三、四混级矾土熟料含量为20％，
0.074mm的三、四混级矾土熟料含量为25％，
0.20mm的结合粘土40％。
实施例3
一种粘土低铁浇钢砖，它的组分和重量含量如下：
1-3mm的三、四混级矾土熟料含量为35％，
0-1mm的三、四混级矾土熟料含量为15％，
0.074mm的三、四混级矾土熟料含量为20％，
0.20mm的结合粘土30％。
上述三种粘土低铁浇钢砖的制备方法，其步骤如下a、原料拣选分级；b、原料粉碎加工；c、加工的颗粒三、四混级钒土熟料与结合粘土混配；d、砖坯成型；e、砖坯干燥；f、干燥的砖坯入隧道窑烧结，烧结温度计1320～1350℃；g、出窑后成品检验入库。

Claims (2)

1.一种粘土低铁浇钢砖，其特征是它的组分和重量含量如下：
1-3mm的三、四混级矾土熟料含量为30-40％，
0-1mm的三、四混级矾土熟料含量为10-20％，
0.074mm的三、四混级矾土熟料含量为15-25％，
0.20mm的结合粘土20-40％。
2.一种权利要求1所述的粘土低铁浇钢砖的制备方法，其特征是其步骤如下：a、原料拣选分级；b、原料粉碎加工；c、加工的颗粒三、四混级钒土熟料与结合粘土混配；d、砖坯成型；e、砖坯干燥；f、干燥的砖坯入隧道窑烧结，烧结温度计1320～1350℃；g、出窑后成品检验入库。
CN2009101700077A 2009-09-01 2009-09-01 粘土低铁浇钢砖及其制备方法 Expired - Fee Related CN101643363B (zh)