CN101624487A - 一种弹性漆 - Google Patents
一种弹性漆 Download PDFInfo
- Publication number
- CN101624487A CN101624487A CN200910181994A CN200910181994A CN101624487A CN 101624487 A CN101624487 A CN 101624487A CN 200910181994 A CN200910181994 A CN 200910181994A CN 200910181994 A CN200910181994 A CN 200910181994A CN 101624487 A CN101624487 A CN 101624487A
- Authority
- CN
- China
- Prior art keywords
- paint
- emulsion
- ippon
- agent
- elastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种弹性漆,涉及乳胶漆的生产工艺技术领域,特别是室内、外乳胶漆生产工艺。主要由丙二醇、多功能助剂、分散剂、消泡剂、润湿剂、钛白粉、硅酸铝、碳酸钙、高岭土、硅灰石、成膜剂、立邦乳液22-1、立邦乳液860、增稠剂、防腐剂、防霉剂和水组成。将本发明产品涂抹在试验板上,耐洗刷可达200次以上,断裂伸长率可达236,拉伸强度可达1.03MPa。将本发明产品涂抹于室内、外墙面上,不易出现墙面裂纹、剥落现象,使用寿命长于现有乳胶漆。
Description
技术领域
本发明涉及乳胶漆的生产工艺技术领域,特别是室内、外乳胶漆生产工艺。
背景技术
随着建筑行业和建筑装潢的需要,乳胶漆被大量地应用于墙体表面,有的为外墙体,有的为内墙体。由于温湿度的变化,特别是室外建筑物需面临风吹雨淋日照,大多乳胶漆的使用寿命不长,易出现墙体漆裂纹,甚至剥落,极大地影响了建筑物的外表美观,直接影响了外墙乳胶漆的大量使用。
发明内容
本发明目的在于提供一种可适应温湿度变化的使用寿命长的弹性漆。
本发明包括丙二醇、多功能助剂、分散剂、消泡剂、润湿剂、钛白粉、硅酸铝、碳酸钙、高岭土、硅灰石、成膜剂、立邦乳液22-1、立邦乳液860、增稠剂、防腐剂、防霉剂和水。
本发明每1000kg乳胶漆中含纳米TiO2、纤维素、多功能助剂、分散剂、丙二醇、消泡剂、钛白粉、岭土、滑石粉、碳酸钙、乳液868、成膜剂、防霉剂、增稠剂、防腐剂分别为10~30kg、2.4kg、1.0kg、10kg、10kg、2.0kg、50kg、50kg、100kg、150kg、150kg、8.0kg、2.0kg、2.0kg、1.5kg。
所述每1000kg乳胶漆中含丙二醇、多功能助剂、分散剂、消泡剂、润湿剂、钛白粉、硅酸铝、碳酸钙、高岭土、硅灰石、成膜剂、立邦乳液22-1、立邦乳液860、增稠剂、防腐剂、防霉剂分别为16kg、1.0kg、10kg、2.0kg、1.0kg、150kg、25kg、175kg、75kg、75kg、15kg、300kg、100kg、3.0kg、2.5kg、1.8kg。
上述多功能助剂的型号为AMP-95。
将本发明产品涂抹在试验板上,耐洗刷可达200次以上,断裂伸长率可达236,拉伸强度可达1.03Mpa。将本发明产品涂抹于室内、外墙体上,不易出现墙面裂纹、剥落现象,使用寿命长于现有乳胶漆。
具体实施方式
分别称取16kg丙二醇、1.0kg多功能助剂AMP-95、10kg分散剂、2.0kg消泡剂、1.0kg润湿剂、150kg钛白粉、25kg硅酸铝、175kg碳酸钙、75kg高岭土、75kg硅灰石、15kg成膜剂、300kg立邦乳液22-1、100kg立邦乳液860、3.0kg增稠剂、2.5kg防腐剂、1.8kg防霉剂,投入搅拌器内,以加水至总量为1000kg,开启搅拌器,混合均匀,分桶包装。
Claims (3)
1、一种弹性漆,其特征在于包括丙二醇、多功能助剂、分散剂、消泡剂、润湿剂、钛白粉、硅酸铝、碳酸钙、高岭土、硅灰石、成膜剂、立邦乳液22-1、立邦乳液860、增稠剂、防腐剂、防霉剂和水。
2、根据权利要求1所述弹性漆,其特征在于所述每1000kg乳胶漆中含丙二醇、多功能助剂、分散剂、消泡剂、润湿剂、钛白粉、硅酸铝、碳酸钙、高岭土、硅灰石、成膜剂、立邦乳液22-1、立邦乳液860、增稠剂、防腐剂、防霉剂分别为16kg、1.0kg、10kg、2.0kg、1.0kg、150kg、25kg、175kg、75kg、75kg、15kg、300kg、100kg、3.0kg、2.5kg、1.8kg。
3、根据权利要求1或2所述弹性漆,其特征在于所述多功能助剂的型号为AMP-95。