CN101608399A - One dyeing pretreatment process that grows flax cotton blended fabric - Google Patents
One dyeing pretreatment process that grows flax cotton blended fabric Download PDFInfo
- Publication number
- CN101608399A CN101608399A CN 200810039290 CN200810039290A CN101608399A CN 101608399 A CN101608399 A CN 101608399A CN 200810039290 CN200810039290 CN 200810039290 CN 200810039290 A CN200810039290 A CN 200810039290A CN 101608399 A CN101608399 A CN 101608399A
- Authority
- CN
- China
- Prior art keywords
- grams per
- blended fabric
- immersed
- temperature
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
One dyeing pretreatment process that grows flax cotton blended fabric is characterized in that, comprising the steps: 1., flax cotton blended fabric is immersed in temperature is in 80~95 ℃ the extraction solution 20~25 minutes.2. will be immersed in temperature through the BLENDED FABRIC that step 1 is handled and be in 90~100 ℃ the soda bath 60 minutes.3. will be immersed in temperature through the BLENDED FABRIC that step 2 is handled and be in 50~55 ℃ the acetum 10~15 minutes.4. will be immersed in temperature through the BLENDED FABRIC that step 3 is handled and be in 80~85 ℃ the soda ash solution 30 minutes.Advantage of the present invention is the close metachromia through flax cotton blended fabric of above-mentioned pre-treatment, and COLOR FASTNESS and bright-colored degree all increase significantly, and can be widely used in the every field of weaving face fabric.
Description
Technical scope
The present invention relates to the grow flax dyeing pretreatment process of cotton blended fabric of field of textiles one.
Background technology
Linen fibre has obtained the good reputation of " fiber queen " owing to have moisture absorption, well-pressed, nice and cool, advantage such as fibre strength is high, anti-strong chemical action and natural fabric are harmless.And flax clothes can reduce the perspiration of human body than other lining, and fast several times than cotton of absorption speeds, normal temperature can make the chamber temperature-sensitive degree of human body reduce by 4 to 8 ℃ down, are described as " natural air conditioner ".Therefore, sodolin is looked at by people's parent deeply.But flax is that bundle fiber and impurity are more, so spinnability of flax and wrinkle resistance are poor, and since flax impurity (particularly numb skin) more, cause mercerising after the fabric background color very dark.And its shortcoming of traditional linen fibre is that fibre separation index is not enough, the big poor flexibility of fiber stiffness, and spinning property is poor, spun yarn and to be woven into lining impure more, dyeability is poor, and the dyeing aspect has significant limitation.
Summary of the invention
The objective of the invention is to remove in the fiber intrinsic plurality of impurities, change the dyeability of flax cotton blended fabric, guarantee close metachromia, COLOR FASTNESS and the bright-colored degree of flax cotton blended fabric.
In order to achieve the above object, the technical solution used in the present invention has provided a dyeing pretreatment process that grows flax cotton blended fabric.This dyeing pretreatment process is made up of the following step:
One dyeing pretreatment process that grows flax cotton blended fabric, it is characterized in that, comprising the steps: step 1, flax cotton blended fabric is immersed in temperature is in 80-95 ℃ the extraction solution 20-25 minute, and described extraction solution is respectively the acetic acid (CH of 1-3 grams per liter by concentration
3COOH, PH=5), dispersant of 2 grams per liters (SN-S) and ionized water are formed.
Step 2, described BLENDED FABRIC is immersed in temperature is in 90-100 ℃ the soda bath 60 minutes, and described soda bath is respectively the refining agent (TF-125C) of 1-3 grams per liter, the caustic soda of 1-3 grams per liter (NaOH), the hydrogen peroxide (H of 1-3 grams per liter by concentration
2O
2) and the ionized water composition.
Step 3, described BLENDED FABRIC is immersed in temperature is in 50-55 ℃ the acetum 10-15 minute, and described acetum is respectively the acetic acid (CH of 1-3 grams per liter by concentration
3COOH), the deoxidation enzyme (MD) of 1-2 grams per liter and ionized water are formed.
Step 4, described BLENDED FABRIC is immersed in temperature is in 80-85 ℃ the soda ash solution 30 minutes, and described soda ash solution is respectively the sodium hydrosulfite (Na of 6-12 grams per liter by concentration
2S
2O
4), the soda ash (Na of 6-12 grams per liter
2CO
3) and the ionized water composition.
Advantage of the present invention is the close metachromia through flax cotton blended fabric of above-mentioned pre-treatment, and COLOR FASTNESS and bright-colored degree all increase significantly, and can be widely used in the every field of weaving face fabric.
The specific embodiment
Below in conjunction with embodiment, further specify the present invention, wherein the yarn in the cotton woven of the said flax of the present invention is that linen fibre and Xinjiang Long staple cotton blending by 20-80% forms.
Embodiment 1
Step 1, it is in 85 ℃ the extraction solution 25 minutes that 12*12/48*46 (55%L/45%C) flax cotton blended fabric is immersed in temperature, described extraction solution is respectively the acetic acid (CH of 1 grams per liter by concentration
3COOH, PH=5), dispersant of 2 grams per liters (SN-S) and ionized water are formed.
Step 2, it is in 100 ℃ the soda bath 60 minutes that described BLENDED FABRIC is immersed in temperature, described soda bath is respectively the refining agent (TF-125C) of 2 grams per liters, the caustic soda of 2 grams per liters (NaOH), the hydrogen peroxide (H of 3 grams per liters by concentration
2O
2) and the ionized water composition.
Step 3, described BLENDED FABRIC is immersed in temperature is in 50 ℃ the acetum 15 minutes, and described acetum is respectively the acetic acid (CH of 1 grams per liter by concentration
3COOH), the deoxidation enzyme (MD) of 2 grams per liters and ionized water are formed.
Step 4, described BLENDED FABRIC is immersed in temperature is in 85 ℃ the soda ash solution 30 minutes, and described soda ash solution is respectively the sodium hydrosulfite (Na of 8 grams per liters by concentration
2S
2O
4), the soda ash (Na of 8 grams per liters
2CO
3) and the ionized water composition.
Embodiment 2
Step 1,8*8/42*38 (55%L/45%C) flax cotton blended fabric is immersed in temperature is in 95 ℃ the extraction solution 20 minutes, and described extraction solution is respectively the acetic acid (CH of 3 grams per liters by concentration
3COOH, PH=5), dispersant of 2 grams per liters (SN-S) and ionized water are formed.
Step 2, described BLENDED FABRIC is immersed in temperature is in 90 ℃ the soda bath 60 minutes, and described soda bath is respectively the refining agent (TF-125C) of 1 grams per liter, the caustic soda of 3 grams per liters (NaOH), the hydrogen peroxide (H of 1 grams per liter by concentration
2O
2) and the ionized water composition.
Step 3, described BLENDED FABRIC is immersed in temperature is in 55 ℃ the acetum 10 minutes, and described acetum is respectively the acetic acid (CH of 3 grams per liters by concentration
3COOH), the deoxidation enzyme (MD) of 1 grams per liter and ionized water are formed.
Step 4, described BLENDED FABRIC is immersed in temperature is in 80 ℃ the soda ash solution 30 minutes, and described soda ash solution is respectively the sodium hydrosulfite (Na of 12 grams per liters by concentration
2S
2O
4), the soda ash (Na of 12 grams per liters
2CO
3) and the ionized water composition.
Embodiment 3
Step 1,20*20/60*58 (55%L/45%C) flax cotton blended fabric is immersed in temperature is in 80 ℃ the extraction solution 20 minutes, and described extraction solution is respectively the acetic acid (CH of 2 grams per liters by concentration
3COOH, PH=5), dispersant of 2 grams per liters (SN-S) and ionized water are formed.
Step 2, described BLENDED FABRIC is immersed in temperature is in 100 ℃ the soda bath 60 minutes, and described soda bath is respectively the refining agent (TF-125C) of 3 grams per liters, the caustic soda of 1 grams per liter (NaOH), the hydrogen peroxide (H of 3 grams per liters by concentration
2O
2) and the ionized water composition.
Step 3, described BLENDED FABRIC is immersed in temperature is in 55 ℃ the acetum 15 minutes, and described acetum is respectively the acetic acid (CH of 3 grams per liters by concentration
3COOH), the deoxidation enzyme (MD) of 1 grams per liter and ionized water are formed.
Step 4, described BLENDED FABRIC is immersed in temperature is in 80 ℃ the soda ash solution 30 minutes, and described soda ash solution is respectively the sodium hydrosulfite (Na of 6 grams per liters by concentration
2S
2O
4), the soda ash (Na of 6 grams per liters
2CO
3) and the ionized water composition.
Embodiment 4
Step 1,20*13/54*52 (55%L/45%C) flax cotton blended fabric is immersed in temperature is in 80 ℃ the extraction solution 20 minutes, and described extraction solution is respectively the acetic acid (CH of 3 grams per liters by concentration
3COOH, PH=5), dispersant of 2 grams per liters (SN-S) and ionized water are formed.
Step 2, described BLENDED FABRIC is immersed in temperature is in 90 ℃ the soda bath 60 minutes, and described soda bath is respectively the refining agent (TF-125C) of 3 grams per liters, the caustic soda of 3 grams per liters (NaOH), the hydrogen peroxide (H of 1 grams per liter by concentration
2O
2) and the ionized water composition.
Step 3, described BLENDED FABRIC is immersed in temperature is in 55 ℃ the acetum 15 minutes, and described acetum is respectively the acetic acid (CH of 2 grams per liters by concentration
3COOH), the deoxidation enzyme (MD) of 2 grams per liters and ionized water are formed.
Step 4, described BLENDED FABRIC is immersed in temperature is in 85 ℃ the soda ash solution 30 minutes, and described soda ash solution is respectively the sodium hydrosulfite (Na of 10 grams per liters by concentration
2S
2O
4), the soda ash (Na of 10 grams per liters
2CO
3) and the ionized water composition.
Embodiment 5
Step 1,15*15/54*52 (55%L/45%C) flax cotton blended fabric is immersed in temperature is in 90 ℃ the extraction solution 25 minutes, and described extraction solution is respectively the acetic acid (CH of 3 grams per liters by concentration
3COOH, PH=5), dispersant of 2 grams per liters (SN-S) and ionized water are formed.
Step 2, described BLENDED FABRIC is immersed in temperature is in 100 ℃ the soda bath 60 minutes, and described soda bath is respectively the refining agent (TF-125C) of 2 grams per liters, the caustic soda of 1 grams per liter (NaOH), the hydrogen peroxide (H of 2 grams per liters by concentration
2O
2) and the ionized water composition.
Step 3, described BLENDED FABRIC is immersed in temperature is in 55 ℃ the acetum 15 minutes, and described acetum is respectively the acetic acid (CH of 2 grams per liters by concentration
3COOH), the deoxidation enzyme (MD) of 1 grams per liter and ionized water are formed.
Step 4, described BLENDED FABRIC is immersed in temperature is in 80 ℃ the soda ash solution 30 minutes, and described soda ash solution is respectively the sodium hydrosulfite (Na of 11 grams per liters by concentration
2S
2O
4), the soda ash (Na of 11 grams per liters
2CO
3) and the ionized water composition.
Embodiment 6
Step 1, (15/2+15/2) * 10/67*40 (55%L/45%C) flax cotton blended fabric is immersed in temperature is in 95 ℃ the extraction solution 25 minutes, and described extraction solution is respectively the acetic acid (CH of 3 grams per liters by concentration
3COOH, PH=5), dispersant of 2 grams per liters (SN-S) and ionized water are formed.
Step 2, described BLENDED FABRIC is immersed in temperature is in 90 ℃ the soda bath 60 minutes, and described soda bath is respectively the refining agent (TF-125C) of 1 grams per liter, the caustic soda of 1 grams per liter (NaOH), the hydrogen peroxide (H of 1 grams per liter by concentration
2O
2) and the ionized water composition.
Step 3, described BLENDED FABRIC is immersed in temperature is in 55 ℃ the acetum 10 minutes, and described acetum is respectively the acetic acid (CH of 3 grams per liters by concentration
3COOH), the deoxidation enzyme (MD) of 1 grams per liter and ionized water are formed.
Step 4, described BLENDED FABRIC is immersed in temperature is in 85 ℃ the soda ash solution 30 minutes, and described soda ash solution is respectively the sodium hydrosulfite (Na of 6 grams per liters by concentration
2S
2O
4), the soda ash (Na of 12 grams per liters
2CO
3) and the ionized water composition.
Claims (5)
1. a dyeing pretreatment process that grows flax cotton blended fabric is characterized in that, comprises the steps:
Step 1, flax cotton blended fabric is immersed in temperature is in 80-95 ℃ the extraction solution 20-25 minute;
Step 2, described BLENDED FABRIC is immersed in temperature is in 90-100 ℃ the soda bath 60 minutes;
Step 3, described BLENDED FABRIC is immersed in temperature is in 50-55 ℃ the acetum 10-15 minute;
Step 4, described BLENDED FABRIC is immersed in temperature is in 80-85 ℃ the soda ash solution 30 minutes.
2. as claimed in claim 1 one dyeing pretreatment process that grows flax cotton blended fabric is characterized in that the extraction solution described in the step 1 is respectively the acetic acid (CH of 1-3 grams per liter by concentration
3COOH, PH=5), dispersant of 2 grams per liters (SN-S) and ionized water are formed.
3. as claimed in claim 1 one dyeing pretreatment process that grows flax cotton blended fabric, it is characterized in that, soda bath described in the step 2 is respectively the refining agent (TF-125C) of 1-3 grams per liter, the caustic soda of 1-3 grams per liter (NaOH), the hydrogen peroxide (H of 1-3 grams per liter by concentration
2O
2) and the ionized water composition.
4. as claimed in claim 1 one dyeing pretreatment process that grows flax cotton blended fabric is characterized in that the acetum described in the step 3 is respectively the acetic acid (CH of 1-3 grams per liter by concentration
3COOH), the deoxidation enzyme (MD) of 1-2 grams per liter and ionized water are formed.
5. as claimed in claim 1 one dyeing pretreatment process that grows flax cotton blended fabric is characterized in that the soda ash solution described in the step 4 is respectively the sodium hydrosulfite (Na of 6-12 grams per liter by concentration
2S
2O
4), the soda ash (Na of 6-12 grams per liter
2CO
3) and the ionized water composition.