CN101602611A - 钢包保温盖的原料配方及钢包保温盖的制备方法 - Google Patents

钢包保温盖的原料配方及钢包保温盖的制备方法 Download PDF

Info

Publication number
CN101602611A
CN101602611A CNA2009100977504A CN200910097750A CN101602611A CN 101602611 A CN101602611 A CN 101602611A CN A2009100977504 A CNA2009100977504 A CN A2009100977504A CN 200910097750 A CN200910097750 A CN 200910097750A CN 101602611 A CN101602611 A CN 101602611A
Authority
CN
China
Prior art keywords
heat insulation
insulation cover
powder
raw material
brown corundum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2009100977504A
Other languages
English (en)
Other versions
CN101602611B (zh
Inventor
陈红良
陈雪飞
蒋志忠
江红芬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2009100977504A priority Critical patent/CN101602611B/zh
Publication of CN101602611A publication Critical patent/CN101602611A/zh
Application granted granted Critical
Publication of CN101602611B publication Critical patent/CN101602611B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种钢包保温盖的原料配方，所述原料(质量百分比)由40－60％棕刚玉空心球、10－20％棕刚玉、15－30％莫来石、1－10％氧化铝微粉、1－10％硅微粉、1－5％ρ－Al2O3粉、0.1－0.2％分散剂组成。采用上述原料配方制作钢包保温盖的步骤：1)将配制好的原料搅拌均匀；2)在搅拌好的原料中加入原料总质量6－8％的水混合搅拌3－5min；3)浇注成型并养护8－12h后脱模；4)在100－120℃的温度下干燥。采用本发明钢包保温盖的原料配方制成的钢包保温盖堆积密度小、热导率低、抗热震稳定性好、抗侵蚀、施工性能好、价格低廉、使用寿命长。

Description

钢包保温盖的原料配方及钢包保温盖的制备方法
技术领域
本发明涉及耐火材料，尤其涉及炼钢用的钢包保温盖的原料配方及钢包保温盖的制备方法。
背景技术
钢包是炼钢***的主要使用设备，炼钢过程中，钢水在钢包中的停留时间长，为保证钢水的温度，除了钢包本体的保温效果外，保温盖的保温效果也必须很好，现有的保温盖材料基本上都是采用粘土质浇注料和高铝质浇注料，保温效果差，并且使用寿命低。
为提高保温效果有很多厂家使用保温棉作为保温盖材料，保温效果有了很大的提高，但由于钢包中的钢渣容易飞溅到保温盖上，造成保温棉侵蚀变质硬化导致剥落掉块严重。
发明内容
本发明所要解决的第一个技术问题就是提供一种钢包保温盖的原料配方，利用此配方制成的钢包保温盖堆积密度小、热导率低、抗热震稳定性好、抗侵蚀、施工性能好、使用寿命长。
为解决上述技术问题，本发明采用如下技术方案：钢包保温盖的原料配方，其特征在于：所述原料由棕刚玉空心球、棕刚玉、莫来石、氧化铝微粉、硅微粉、ρ-Al2O3粉、分散剂组成。
作为优选，所述原料(质量百分比)由40-60％棕刚玉空心球、10-20％棕刚玉、15-30％莫来石、1-10％氧化铝微粉、1-10％硅微粉、1-5％ρ-Al2O3粉、0.1-0.2％分散剂组成。
作为优选，所述原料(质量百分比)由45％棕刚玉空心球、15％棕刚玉、26％莫来石、6％氧化铝微粉、6％硅微粉、1.9％ρ-Al2O3粉、0.1％分散剂组成。
作为优选，所述原料(质量百分比)由50％棕刚玉空心球、18％棕刚玉、15％莫来石、8％氧化铝微粉、5％硅微粉、3.8％ρ-Al2O3粉、0.2％分散剂组成。
作为优选，所述原料(质量百分比)由40％棕刚玉空心球、16.8％棕刚玉、25％莫来石、7％氧化铝微粉、6％硅微粉、5％ρ-Al2O3粉、0.2％分散剂组成。
作为优选，所述分散剂为SM高效减水剂或SN-II高效减水剂。
作为优选，所述原料的颗粒度要求分别为棕刚玉空心球颗粒8-0.1mm，棕刚玉180目细粉，莫来石180目细粉。
本发明所要解决的另一个技术问题就是提供一种采用上述原料配方制造钢包保温盖的方法。
为解决上述技术问题，采用如下技术方案：钢包保温盖的制备方法，其特征在于包括如下步骤：
1)将配制好的原料搅拌均匀，其中原料加入顺序为棕刚玉空心球颗粒-硅微粉和ρ-Al2O3、分散剂微粉-棕刚玉和莫来石细粉-减水剂；
2)在搅拌好的原料中加入原料总质量6-8％的水混合搅拌3-5min；
3)浇注成型并养护8-12h后脱模；
4)在100-120℃的温度下干燥。
采用本发明钢包保温盖的原料配方由于棕刚玉空心球的使用，使制成的钢包保温盖堆积密度小、热导率低、抗热震稳定性好、抗侵蚀、施工性能好、降低了原料成本、增长了使用寿命，使用寿命达到粘土质浇注料和高铝浇注料的寿命的2倍以上，钢水冶炼温度降低5-10℃。
具体实施方式
实施例1，钢包保温盖的原料配方，所述原料(质量百分比)由45％棕刚玉空心球、15％棕刚玉、26％莫来石、6％氧化铝微粉、6％硅微粉、1.9％ρ-Al2O3粉、0.1％分散剂组成。所述原料的颗粒度要求分别为棕刚玉空心球颗粒8-0.1mm，棕刚玉180目细粉，莫来石180目细粉。
采用上述原料配方制作钢包保温盖的制备方法包括如下步骤：
1)将配制好的原料搅拌均匀，其中原料加入顺序为棕刚玉空心球颗粒-硅微粉和ρ-Al2O3、分散剂微粉-棕刚玉和莫来石细粉-减水剂；
2)在搅拌好的原料中加入原料总质量6％的水混合搅拌3-5min；
3)浇注成型并养护8h后脱模；
4)在100℃的温度下干燥。
实施例2，钢包保温盖的原料配方，所述原料(质量百分比)由50％棕刚玉空心球、18％棕刚玉、15％莫来石、8％氧化铝微粉、5％硅微粉、3.8％ρ-Al2O3粉、0.2％分散剂组成。所述原料的颗粒度要求分别为棕刚玉空心球颗粒8-0.1mm，棕刚玉180目细粉，莫来石180目细粉。
采用上述原料配方制作钢包保温盖的制备方法包括如下步骤：
1)将配制好的原料搅拌均匀，其中原料加入顺序为棕刚玉空心球颗粒-硅微粉和ρ-Al2O3、分散剂微粉-棕刚玉和莫来石细粉-减水剂；
2)在搅拌好的原料中加入原料总质量8％的水混合搅拌3-5min；
3)浇注成型并养护12h后脱模；
4)在120℃的温度下干燥。
实施例3，钢包保温盖的原料配方，所述原料(质量百分比)由40％棕刚玉空心球、16.8％棕刚玉、25％莫来石、7％氧化铝微粉、6％硅微粉、5％ρ-Al2O3粉、0.2％分散剂组成。所述原料的颗粒度要求分别为棕刚玉空心球颗粒8-0.1mm，棕刚玉180目细粉，莫来石180目细粉。
采用上述原料配方制作钢包保温盖的制备方法包括如下步骤：
1)将配制好的原料搅拌均匀，其中原料加入顺序为棕刚玉空心球颗粒-硅微粉和ρ-Al2O3、分散剂微粉-棕刚玉和莫来石细粉-减水剂；
2)在搅拌好的原料中加入原料总质量7％的水混合搅拌3-5min；
3)浇注成型并养护10h后脱模；
4)在110℃的温度下干燥。
上述实施例中，所述分散剂为SM或SN-II高效减水剂。

Claims (9)

1、钢包保温盖的原料配方，其特征在于：所述原料由棕刚玉空心球、棕刚玉、莫来石、氧化铝微粉、硅微粉、ρ-Al2O3粉和分散剂组成。
2、根据权利要求1所述的钢包保温盖的原料配方，其特征在于：所述原料(质量百分比)由40-60％棕刚玉空心球、10-20％棕刚玉、15-30％莫来石、1-10％氧化铝微粉、1-10％硅微粉、1-5％ρ-Al2O3粉、0.1-0.2％分散剂组成。
3、根据权利要求2所述的钢包保温盖的原料配方，其特征在于：所述原料(质量百分比)由45％棕刚玉空心球、15％棕刚玉、26％莫来石、6％氧化铝微粉、6％硅微粉、1.9％ρ-Al2O3粉、0.1％分散剂组成。
4、根据权利要求2所述的钢包保温盖的原料配方，其特征在于：所述原料(质量百分比)由50％棕刚玉空心球、18％棕刚玉、15％莫来石、8％氧化铝微粉、5％硅微粉、3.8％ρ-Al2O3粉、0.2％分散剂组成。
5、根据权利要求2所述的钢包保温盖的原料配方，其特征在于：所述原料(质量百分比)由40％棕刚玉空心球、16.8％棕刚玉、25％莫来石、7％氧化铝微粉、6％硅微粉、5％ρ-Al2O3粉、0.2％分散剂组成。
6、根据权利要求1至5任一项所述的钢包保温盖的原料配方，其特征在于：所述分散剂为SM高效减水剂或SN-II高效减水剂。
7、根据权利要求1至5任一项所述的钢包保温盖的原料配方，其特征在于：所述原料的颗粒度要求分别为棕刚玉空心球颗粒8-0.1mm，棕刚玉180目细粉，莫来石180目细粉。
8、钢包保温盖的制备方法，其特征在于包括如下步骤：
1)将配制好的原料搅拌均匀；
2)在搅拌好的原料中加入原料总质量6-8％的水混合搅拌3-5min；
3)浇注成型并养护8-12h后脱模；
4)在100-120℃的温度下干燥。
9、根据权利要求8所述的钢包保温盖的制备方法，其特征在于：所述步骤1)中原料加入顺序为棕刚玉空心球颗粒-硅微粉和ρ-Al2O3、分散剂微粉-棕刚玉和莫来石细粉-减水剂。
CN2009100977504A 2009-04-17 2009-04-17 钢包保温盖的原料配方及钢包保温盖的制备方法 Expired - Fee Related CN101602611B (zh)