CN101591967A - A kind of parquets formula bamboo floor block and manufacture method of forming by clout thereof - Google Patents
A kind of parquets formula bamboo floor block and manufacture method of forming by clout thereof Download PDFInfo
- Publication number
- CN101591967A CN101591967A CNA2008101239758A CN200810123975A CN101591967A CN 101591967 A CN101591967 A CN 101591967A CN A2008101239758 A CNA2008101239758 A CN A2008101239758A CN 200810123975 A CN200810123975 A CN 200810123975A CN 101591967 A CN101591967 A CN 101591967A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- parquets
- bamboo floor
- frame
- clout
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of parquets formula bamboo floor block and manufacture method of forming by clout thereof, belong to the fitting-out work technical field of building.This bamboo floor block comprises bamboo floor parquets, frame, the inlay of bamboo floor is in frame, bamboo floor parquets is made of at least two module unit pieces, cell block is made of the pressing of multilayer bamboo chip veneer, the bamboo line direction of adjacent two cell blocks is orthogonal, frame also is made of the pressing of multilayer bamboo chip veneer, and the bamboo chip veneer all adopts bamboo floor clout.Its manufacture method comprise get the raw materials ready, cut, polishing, pressing, splicing be shaped.Can be with the bamboo floor block clout that serves as discarded object in the process of assembling of originally being in processing and utilization again, and entire making process is easy.Simultaneously, newly formed not only anti-skid wearable, more have present bamboo floor block nearly less than the parquets aesthetic.
Description
Technical field
The present invention relates to house ornamentation bamboo floor block in the industry, relate in particular to a kind of parquets formula bamboo floor block and manufacture method of forming by clout thereof, belong to the fitting-out work technical field of building.
Background technology
Along with the deterioration of environmental quality, people are constantly strengthening for the consciousness of environmental protection.Nowadays, grow with each passing day for the protection of the forest reserves, having caused the forest reserves is that the manufacturing of raw-material former wood flooring reduces day by day.Relative log, the speed of growth of bamboo is very fast, it is suitably utilized also can not destroy the forest reserves.Therefore, the employing bamboo is raw material, and its bamboo floor of making has begun to become gradually important wood flooring substitute.
In existing house ornamentation market, the same application popularization that becomes in bamboo floor with wood flooring.But,, therefore in the installation on bamboo floor is laid, all can produce certain floor clout because household is all far from each other in order to the zone of decorating.With regard to present technology, these floor clouts often are equal to waste material, directly do not topple over processing, have directly wasted, and have caused enormous economic loss thus.Moreover such waste can not be satisfied house ornamentation environment protection requirement in the industry conscientiously.
Summary of the invention
Purpose of the present invention is exactly in order to solve the above-mentioned problems in the prior art, and a kind of parquets formula bamboo floor block and manufacture method of being made up of clout thereof is provided.
Purpose of the present invention is achieved through the following technical solutions:
A kind of parquets formula bamboo floor block of forming by clout, wherein: this bamboo floor block comprises bamboo floor parquets, frame, the inlay of bamboo floor is in frame, bamboo floor parquets is made of at least two module unit pieces, cell block is made of the pressing of multilayer bamboo chip veneer, the bamboo line direction of adjacent two cell blocks is orthogonal, and frame also is made of the pressing of multilayer bamboo chip veneer, and the bamboo chip veneer all adopts bamboo floor clout.
Above-mentioned a kind of parquets formula bamboo floor block of being made up of clout, wherein: the bonding surface of the multilayer bamboo chip veneer of described formation frame is 45 ° of angles.
Further, above-mentioned a kind of parquets formula bamboo floor block of forming by clout, wherein: the color difference of described adjacent cells piece, bamboo floor parquets is the checkerboard type layout.
Further, above-mentioned a kind of parquets formula bamboo floor block of forming by clout, wherein: described bamboo chip veneer thickness is 0.3～0.6cm, width is 1.5～2cm.
Further, above-mentioned a kind of parquets formula bamboo floor block of forming by clout, wherein: the bamboo chip veneer length of described formation cell block is 5.5～6.5cm.
Further, above-mentioned a kind of parquets formula bamboo floor block of forming by clout, wherein: the bamboo chip veneer length of described formation frame is 16.5～30cm.
Again further, above-mentioned a kind of parquets formula bamboo floor block of forming by clout, wherein: the adjacent both sides of described frame are provided with public tenon or female tenon.
A kind of manufacture method of the parquets formula bamboo floor block of forming by clout, wherein: the method includes the steps of:
Step 1:, cut into the bamboo chip veneer of cell block, frame Len req respectively with the bamboo floor block clout;
Step 2: above-mentioned bamboo chip veneer is partly eliminated the burr on the external surface with the planing machine, meet the requirements with width, the thickness of seasonal bamboo chip veneer;
Step 3: some bamboo chip veneers that will prepare cell block pile up from top to bottom mutually, are heated to 160～230 ℃, use vertical press-fit equipment, and under the pressure of 14～21MPa, pressing 5～15 minutes is pressed into cell block;
Step 4: mode cell block is vertical according to bamboo line direction, color interval is spliced mutually, and by the pressure of 10～16MPa, pressing 2～5 minutes constitutes bamboo floor parquets;
Step 5: some bamboo chip veneers that will prepare frame pile up from top to bottom mutually, and piece together rectangle, are heated to 120～200 ℃, use vertical press-fit equipment, and by the pressure of 12～24MPa, pressing 5～10 minutes is pressed into frame;
Step 6: the inlay of bamboo floor in frame, is heated to 180～240 ℃, uses press equipment, apply the pressure of 12～24MPa, monolithic molding is carried out in pressing 3～6 minutes.
The manufacture method of above-mentioned a kind of parquets formula bamboo floor block of forming by clout, wherein: adopt three layers of bamboo chip veneer to pile up in the described step 3, arrange at least three groups simultaneously, constitute cell block; Adopt three layers of bamboo chip veneer to pile up the formation frame in rapid five.
Further, the manufacture method of above-mentioned a kind of parquets formula bamboo floor block of forming by clout, wherein: on the contact surface of bamboo chip veneer, scribble epoxy resin or Lauxite in described step 3～step 6 as adhesive.
The outstanding substantive distinguishing features and the obvious improvement of technical solution of the present invention is mainly reflected in: after adopting the present invention, can be with the bamboo floor block clout that serves as discarded object in the process of assembling of originally being in processing and utilization again, further make new bamboo floor block, fully satisfied the environmental protection demand that house ornamentation is advocated in the industry.And, adopt processing technology of the present invention need not to the bamboo raw material remove surf green, remove tabasheer, baking, entire making process is easy, helps promoting.Simultaneously, newly formed bamboo floor block laying all has higher adaptive capacity for different rooms.It is anti-skid wearable not only, more have present bamboo floor block nearly less than the parquets aesthetic.This shows that the present invention has substantive technical characterstic and significant technological progress, its application prospect is boundless.
Description of drawings
Purpose of the present invention, advantage and characteristics will illustrate by the non-limitative illustration of following preferred embodiment and explain.These embodiment only are the prominent examples of using technical solution of the present invention, and all technical schemes of taking to be equal to replacement or equivalent transformation and forming all drop within the scope of protection of present invention.In the middle of these accompanying drawings,
Fig. 1 is a unitary construction schematic diagram of the present invention.
The implication of each Reference numeral is as follows among the figure:
1 cell block, 2 frames, 3 public tenons
The specific embodiment
A kind of parquets formula bamboo floor block of forming by clout, its special feature is: this bamboo floor block comprises bamboo floor parquets, frame 2, the inlay of bamboo floor is in frame, bamboo floor parquets is made of at least two module unit pieces 1, cell block 1 is made of the pressing of multilayer bamboo chip veneer, the bamboo line direction of adjacent two cell blocks 1 is orthogonal, and frame 2 also is made of the pressing of multilayer bamboo chip veneer, and the bamboo chip veneer all adopts bamboo floor clout.
Concrete constitute the multilayer bamboo chip veneer of cell block 1 as shown in Figure 1, the bamboo line direction of its adjacent each layer is parallel to each other, and it is also parallel to each other to constitute the bamboo line direction of bamboo chip veneer of frame 2.Simultaneously, have aesthetic feeling in order to make the frame 2 after the shaping, described frame 2 is provided with the bonding surface that is 45 ° of angles, and the bamboo line direction between the adjacent cells piece 1 is orthogonal, presents certain stereovision.Further combined with Fig. 1, the bamboo chip veneer thickness is 0.3～0.6cm, and width is 1.5～2cm.The bamboo chip veneer length that constitutes cell block 1 is 5.5～6.5cm, and the bamboo chip veneer length that constitutes frame 2 is 16.5～30cm.Like this, the bamboo floor parquets of formation and frame 2 can be in conjunction with tight.
Parquets formula bamboo floor block edge can adopt tack, is convenient to the middle quick amalgamation of bamboo floor block.Certainly, between the parquets formula bamboo floor block in conjunction with soundness, frame 2 adjacent both sides offer public tenon 3 or female tenon.During installation, public tenon 3 is embedded the at first combination between the bamboo floor block of female tenon.And the amalgamation of public tenon 3 and female tenon can allow bamboo floor block is better must to bear external stress.
Again further, preparation method of the present invention comprises following operation: at first, with the bamboo floor block clout, cut into the bamboo chip veneer of cell block 1, frame 2 Len reqs respectively.Subsequently, above-mentioned bamboo chip veneer is partly eliminated the burr on the external surface with the planing machine, meet the requirements with width, the thickness of seasonal bamboo chip veneer.Then, with three layers of bamboo chip veneer of preparation cell block 1, arrange three groups, pile up mutually from top to bottom, be heated to 160～230 ℃, use vertical press-fit equipment, under the pressure of 14～21MPa, pressing 5～15 minutes is pressed into cell block 1.And then, mode nine cell blocks 1 are vertical according to bamboo line direction, color interval is spliced mutually, and by the pressure of 10～16MPa, pressing 2～5 minutes constitutes bamboo floor parquets, and promptly bamboo floor parquets is the checkerboard type layout.Same, three layers of bamboo chip veneer that prepare frame 2 are piled up from top to bottom mutually, and after constituting at least three groups, be heated to 120～200 ℃, use vertical press-fit equipment, by the pressure of 12～24MPa, pressing 5～10 minutes is pressed into frame 2.And when frame 2 constituted rectangle, the bonding surface that constitutes the multilayer bamboo chip veneer of frame 2 was 45 ° of angles.At last, the inlay of bamboo floor in frame 2, is heated to 180～240 ℃, uses press equipment, apply the pressure of 12～24MPa, monolithic molding is carried out in pressing 3～6 minutes.In order further to guarantee the whole conjugation of bamboo floor block finished product, in the middle of above-mentioned process, scribble epoxy resin or Lauxite on the contact surface of bamboo chip veneer as adhesive.
" embodiment one "
A kind of parquets formula bamboo floor block of being made up of clout, its manufacturing process is as follows: at first, with the bamboo floor block clout, cut into the bamboo chip veneer of cell block 1, frame 2 Len reqs respectively.The bamboo chip veneer length that constitutes cell block 1 specifically is 5.5cm, and the bamboo chip veneer length that constitutes frame 2 is 16.5cm.Subsequently, above-mentioned bamboo chip veneer is partly eliminated the burr on the external surface with the planing machine, meet the requirements with width, the thickness of seasonal bamboo chip veneer, promptly the bamboo chip veneer thickness is 0.3cm, and width is 1.5cm.Then, three layers of bamboo chip veneer with preparation cell block 1 pile up from top to bottom mutually, arrange three groups, are heated to 160 ℃, use vertical press-fit equipment, and under the pressure of 14MPa, pressing 5 minutes is pressed into cell block 1.And then, mode nine cell blocks 1 are vertical according to bamboo line direction, color interval is spliced mutually, and by the pressure of 10MPa, pressing 2 minutes constitutes bamboo floor parquets.Same, three layers of bamboo chip veneer that prepare frame 2 are piled up from top to bottom mutually, and after constituting few three groups, be heated to 120 ℃, use vertical press-fit equipment, by the pressure of 12MPa, pressing 5 minutes is pressed into frame 2.And when frame 2 constituted rectangle, the bonding surface that constitutes the multilayer bamboo chip veneer of frame 2 was 45 ° of angles.At last, the inlay of bamboo floor in frame 2, is heated to 180 ℃, uses press equipment, apply the pressure of 12MPa, monolithic molding is carried out in pressing 3 minutes.In order further to guarantee the whole conjugation of bamboo floor block finished product, in the middle of above-mentioned process, scribble epoxy resin or Lauxite on the contact surface of bamboo chip veneer as adhesive.
Because the bamboo floor block made of this technology derives from the clout of bamboo floor block, it is compact therefore to allow the area of bamboo floor block trend towards in process, can be suitable for use in the less room of area and lay, and can not produce the secondary clout again.
" embodiment two "
A kind of parquets formula bamboo floor block of forming by clout, can come advanced processing and fabricating by the following method: at first, with the bamboo floor block clout, cut into the bamboo chip veneer of cell block 1, frame 2 Len reqs respectively, the bamboo chip veneer length that is about to constitute cell block 1 is cut into 6.5cm, and the bamboo chip veneer length that constitutes frame 2 is cut into 30cm.
Then, the bamboo chip veneer is eliminated burr part on the external surface by the planing machine, during this period, make the width of bamboo chip veneer reach 0.6cm, THICKNESS CONTROL in 2cm.Then, three layers of bamboo chip veneer that will preparation cell block 1 pile up mutually from top to bottom and arrange three groups, are heated to 230 ℃, use vertical press-fit equipment, and under the pressure of 21MPa, pressing 15 minutes is pressed into cell block 1.
And then, mode nine cell blocks 1 are vertical according to bamboo line direction, color interval is spliced mutually, and by the pressure of 16MPa, pressing 5 minutes constitutes bamboo floor parquets.Same, three layers of bamboo chip veneer that prepare frame 2 are piled up from top to bottom mutually, and after constituting at least three groups, be heated to 200 ℃, use vertical press-fit equipment, by the pressure of 24MPa, pressing 10 minutes is pressed into frame 2.And when frame 2 constituted rectangle, the bonding surface that constitutes the multilayer bamboo chip veneer of frame 2 was 45 ° of angles.
At last, the inlay of bamboo floor in frame 2, is heated to 240 ℃, uses press equipment, apply the pressure of 24MPa, monolithic molding is carried out in pressing 6 minutes.In order further to guarantee the whole conjugation of bamboo floor block finished product, in the middle of above-mentioned process, scribble epoxy resin or Lauxite on the contact surface of bamboo chip veneer as adhesive.
Adopt the bamboo floor block after this technology is made that bigger area is arranged, can be applicable to bigger laying work area, such as parlor etc.
" embodiment three "
A kind of parquets formula bamboo floor block of being made up of clout, its processing mode is as follows: at first, with the bamboo floor block clout, cut into the bamboo chip veneer of cell block 1, frame 2 Len reqs respectively.Specifically, the bamboo chip veneer length that constitutes cell block 1 adopts 6cm, and the bamboo chip veneer length that constitutes frame 2 adopts 20cm.Subsequently, above-mentioned bamboo chip veneer is partly eliminated the burr on the external surface with the planing machine, meet the requirements with width, the thickness of seasonal bamboo chip veneer, promptly the bamboo chip veneer thickness is 0.5cm, and width is 1cm.
Then, will pile up mutually from top to bottom, be arranged in three groups simultaneously, be heated to 200 ℃, make multilayer bamboo chip veneer with vertical press-fit equipment in order to three layers of bamboo chip veneer of preparation cell block 1.Subsequently that at least three group multilayer bamboo chip veneers are transversely arranged from left to right, with horizontal press equipment cell block 1 is processed in its pressing.And then, mode nine cell blocks 1 are vertical according to bamboo line direction, color interval is spliced mutually, and the pressure by 12MPa, and pressing 3 minutes constitutes bamboo floor parquets.
Same, will pile up mutually from top to bottom in order to three layers of bamboo chip veneer of preparation frame 2 and be arranged in three groups, be heated to 180 ℃, use vertical press-fit equipment, by the pressure of 12～24MPa, pressing 7 minutes is pressed into frame 2.And when frame 2 constituted rectangle, the bonding surface that constitutes the multilayer bamboo chip veneer of frame 2 was 45 ° of angles.
At last, the inlay of bamboo floor in frame 2, is heated to 200 ℃, uses press equipment, apply the pressure of 18MPa, monolithic molding is carried out in pressing 5 minutes.In order further to guarantee the whole conjugation of bamboo floor block finished product, in the middle of above-mentioned process, scribble epoxy resin or Lauxite on the contact surface of bamboo chip veneer as adhesive.Simultaneously, offer public tenon 3 or female tenon on the adjacent both sides of frame 2.
The bamboo floor block that adopts above-mentioned technology to make, its area is more moderate, can comparatively be widely used in each place of house ornamentation, and is higher with the matching degree of coverage.
By above-mentioned text description also in conjunction with the accompanying drawings as can be seen, after adopting the present invention, originally the bamboo floor block clout that serves as discarded object in the process of assembling of being in processing and utilization again further can be made new bamboo floor block, fully satisfy the environmental protection demand that house ornamentation is advocated in the industry.And, adopt processing technology of the present invention need not to the bamboo raw material remove surf green, remove tabasheer, baking, entire making process is easy, helps promoting.Simultaneously, newly formed bamboo floor block laying all has higher adaptive capacity for different rooms.It is anti-skid wearable not only, more have present bamboo floor block nearly less than the parquets aesthetic.This shows that the present invention has expanded the space for the technological progress of this area, implementation result is good.
Claims (10)
1, a kind of parquets formula bamboo floor block of forming by clout, it is characterized in that: this bamboo floor block comprises bamboo floor parquets, frame, the inlay of bamboo floor is in frame, bamboo floor parquets is made of at least two module unit pieces, cell block is made of the pressing of multilayer bamboo chip veneer, the bamboo line direction of adjacent two cell blocks is orthogonal, and frame also is made of the pressing of multilayer bamboo chip veneer, and the bamboo chip veneer all adopts bamboo floor clout.
2, a kind of parquets formula bamboo floor block of being made up of clout according to claim 1, it is characterized in that: the bonding surface of the multilayer bamboo chip veneer of described formation frame is 45 ° of angles.
3, a kind of parquets formula bamboo floor block of being made up of clout according to claim 1, it is characterized in that: the color difference of described adjacent cells piece, bamboo floor parquets is the checkerboard type layout.
4, a kind of parquets formula bamboo floor block of forming by clout according to claim 1, it is characterized in that: described bamboo chip veneer thickness is 0.3～0.6cm, width is 1.5～2cm.
5, a kind of parquets formula bamboo floor block of being made up of clout according to claim 1, it is characterized in that: the bamboo chip veneer length of described formation cell block is 5.5～6.5cm.
6, a kind of parquets formula bamboo floor block of being made up of clout according to claim 1, it is characterized in that: the bamboo chip veneer length of described formation frame is 16.5～30cm.
7, a kind of parquets formula bamboo floor block of being made up of clout according to claim 1, it is characterized in that: the adjacent both sides of described frame are provided with public tenon or female tenon.
8, a kind of manufacture method of the parquets formula bamboo floor block of being made up of clout is characterized in that the method includes the steps of:
Step 1:, cut into the bamboo chip veneer of cell block, frame Len req respectively with the bamboo floor block clout;
Step 2: above-mentioned bamboo chip veneer is partly eliminated the burr on the external surface with the planing machine, meet the requirements with width, the thickness of seasonal bamboo chip veneer;
Step 3: some bamboo chip veneers that will prepare cell block pile up from top to bottom mutually, are heated to 160～230 ℃, use vertical press-fit equipment, and under the pressure of 14～21MPa, pressing 5～15 minutes is pressed into cell block;
Step 4: mode cell block is vertical according to bamboo line direction, color interval is spliced mutually, and by the pressure of 10～16MPa, pressing 2～5 minutes constitutes bamboo floor parquets;
Step 5: some bamboo chip veneers that will prepare frame pile up from top to bottom mutually, and piece together rectangle, are heated to 120～200 ℃, use vertical press-fit equipment, and by the pressure of 12～24MPa, pressing 5～10 minutes is pressed into frame;
Step 6: the inlay of bamboo floor in frame, is heated to 180～240 ℃, uses press equipment, apply the pressure of 12～24MPa, monolithic molding is carried out in pressing 3～6 minutes.
9, the manufacture method of a kind of parquets formula bamboo floor block of being made up of clout according to claim 8 is characterized in that: adopt three layers of bamboo chip veneer to pile up in the described step 3, arrange at least three groups simultaneously, constitute cell block; Adopt three layers of bamboo chip veneer to pile up the formation frame in rapid five.
10, the manufacture method of a kind of parquets formula bamboo floor block of being made up of clout according to claim 8 is characterized in that: scribble epoxy resin or Lauxite in described step 3～step 6 as adhesive on the contact surface of bamboo chip veneer.