CN101575477A - High-solid terrace coating, preparation method and application thereof - Google Patents
High-solid terrace coating, preparation method and application thereof Download PDFInfo
- Publication number
- CN101575477A CN101575477A CNA2009100328674A CN200910032867A CN101575477A CN 101575477 A CN101575477 A CN 101575477A CN A2009100328674 A CNA2009100328674 A CN A2009100328674A CN 200910032867 A CN200910032867 A CN 200910032867A CN 101575477 A CN101575477 A CN 101575477A
- Authority
- CN
- China
- Prior art keywords
- agent
- terrace paint
- solid
- solid level
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-solid terrace coating, a preparation method and application thereof. The coating is prepared from the following raw materials in percentage by weight: 50 to 55 percent of organosilicone modified epoxy resin; 15 to 30 percent of aliphatic amino resin, 4 to 10 percent of plasticizer, 5 to 10 percent of TiO2, 5 to 15 percent of pigment and filler, 4 to 5 percent of reactive diluent, 0.5 to 1.0 percent of defoaming agent, 0.5 to 1.0 percent of dispersant, and 0.2 to 0.5 percent of flatting agent 354. Experimental research shows that the high-solid terrace coating has good corrosion-resistant properties such as acid resistance and alkaline resistance as well as stronger toughness and mechanical property, no volatile solvent exists and the pigment and filler have small consumption in the raw materials of the high-solid terrace coating, and the high-solid terrace coating is an environment-friendly, nontoxic and good terrace coating. The preparation method of the coating has strong maneuverability, high production efficiency and low energy consumption, ensures that finished products obtained through the preparation have high qualification rate, and can realize industrialized large scale production.
Description
Technical field
The present invention relates to a kind of coating, be specifically related to a kind of terrace paint and preparation method thereof and its application in the corrosion protection coating of preparation ground of high-solid level.
Background technology
Terrace paint of the prior art has the hardness height, the characteristics of contamination resistance, generally choose reactive resin as membrane substance, use the most general for SOLVENT BASED EPOXY FLOOR COATINGS but since the difference of filmogen, the coating property that obtains also each is variant, effective as epoxy resin coating to the polarity substrate adhesion, the toughness height, its shortcoming is that weathering resistance is poor, and the low-temperature curing performance is poor; Polyurethanes coating has good mechanical property and toughness, solidification value wide ranges, but can contain deleterious free isocyanate when reacting incomplete, and serious environment pollution also has bigger harm to people's life and health; Acrylic coating photostabilization and outdoor ageing-resistant performance are good, anti-UV irradiation, chemicals-resistant and water-tolerant, but wear resistance, the too late epoxy of impact resistance and polyurethane coating.
Solvent in the SOLVENT BASED EPOXY FLOOR COATINGS of using always in the prior art mostly is aromatic hydrocarbons ester or ketone, and its shortcoming is:
1. SOLVENT BASED EPOXY FLOOR COATINGS has certain toxicity, and volatilization back environmental pollution is bigger, and people's life and health is also had bigger harm;
2. solvent based coating is because volatile organic and thing (VOC) content are bigger, and the volatilization of solvent can make and be coated with rete and the capillary hole occurs in the film-forming process, greatly reduces antiseptic property, toughness and the mechanical property of filming.
Summary of the invention
Goal of the invention: the objective of the invention is in order to solve the deficiencies in the prior art, provide a kind of preservative property, toughness and mechanical property good, and the terrace paint of environmental protection, nontoxic high-solid level, another object of the present invention provide the preparation method of terrace paint of this high-solid level and it is used for preparing the application of ground corrosion protection coating.
Technical scheme: in order to realize purpose of the present invention, the terrace paint of high-solid level provided by the invention is made by following raw materials by weight percent: modifying epoxy resin by organosilicon 50～55%, aliphatics aminoresin 15～30%, softening agent 4～10%, TiO
25～10%, color stuffing 5～15%, reactive thinner 4～5%, defoamer 0.5～1.0%, dispersion agent 0.5～1.0%, flow agent 354 0.2～0.5%.
As preferred version, the terrace paint of high-solid level provided by the invention is made by following raw materials by weight percent: modifying epoxy resin by organosilicon 50%, aliphatics aminoresin 20%, softening agent 5%, TiO
28%, color stuffing 10%, reactive thinner 5%, defoamer 0.5%, dispersion agent 1%, flow agent 0.5%.
As another preferred version, the terrace paint of high-solid level provided by the invention is made by following raw materials by weight percent: modifying epoxy resin by organosilicon 55%, aliphatics aminoresin 15%, softening agent 8%, TiO
25%, color stuffing 10%, reactive thinner 5%, defoamer 1%, dispersion agent 0.5%, flow agent 0.5%.
As another preferred version, the terrace paint of high-solid level provided by the invention is made by following raw materials by weight percent: modifying epoxy resin by organosilicon 50%, aliphatics aminoresin 30%, softening agent 4%, TiO
25%, color stuffing 5%, reactive thinner 4%, defoamer 0.5%, dispersion agent 0.5%, flow agent 1%.
The terrace paint of high-solid level provided by the invention, wherein softening agent is that concentration is 70%～80% paraffin, thinner is a Polyethylene Glycol Bisglycidyl Ether, TiO
2Be rutile TiO
2, color stuffing is a mica powder, and defoamer is a defoamer 306 (052), and dispersion agent is a dispersion agent 163, and flow agent is a flow agent 354.
The preparation method of the terrace paint of high-solid level of the present invention may further comprise the steps:
1. choose modifying epoxy resin by organosilicon, aliphatics aminoresin, reactive thinner Polyethylene Glycol Bisglycidyl Ether in proportion, dispersion agent 163 mixes, high speed dispersion 1 to 3 hour, and it is standby to get intermediate raw material;
2. get the intermediate raw material that 1. step obtains, adding plasticizer concentration in proportion is paraffin, color stuffing mica powder, mix, and high speed dispersion 1 to 3 hour, it is standby to get intermediate raw material;
3. get the intermediate raw material that 2. step obtains, add rutile TiO in proportion
2, defoamer 306 (052) and flow agent 354, mix, high speed dispersion 1 to 3 hour grinds to form fine powder, intermediate product is standby;
4. get the intermediate product that 3. step obtains, toning, regrinding detects particle diameter, filtration, packing promptly.
Among the preparation method of the terrace paint of high-solid level provided by the invention, the weight percent of each raw material is: modifying epoxy resin by organosilicon 50～55%, aliphatics aminoresin 15～30%, softening agent 4～10%, TiO
25～10%, color stuffing 5～15%, reactive thinner 4～5%, defoamer 0.5～1.0%, dispersion agent 0.5～1.0%, flow agent 354 0.2～0.5%.
Wherein softening agent is that concentration is 70%～80% paraffin, and thinner is a Polyethylene Glycol Bisglycidyl Ether, TiO
2Be rutile TiO
2, color stuffing is a mica powder, and defoamer is a defoamer 306 (052), and dispersion agent is a dispersion agent 163, and flow agent is a flow agent 354.
The terrace paint of preparation high-solid level of the present invention, as preferably, step 1. the high speed dispersive time be 1 hour, step 2. with step 3. the high speed dispersive time be 2 hours, and 4. the sieve particle diameter of the high-solid level terrace paint that obtains of step is 1 to 35 μ m.
The application of the terrace paint of high-solid level of the present invention in preparation ground corrosion protection coating specifically can be used to prepare the anticorrosion terrace layer that the ground such as production plant, warehouse and large-scale sewage lagoon of industry such as are knitted in chemical plant, fertilizer plant, electric power, metallurgy and the mill of printing and dyeing.
Beneficial effect: the terrace paint of high-solid level provided by the invention is compared with prior art and is had the following advantages:
1, the starting material of the terrace paint of high-solid level provided by the invention are easy to get, and each proportioning raw materials of the terrace paint of high-solid level is scientific and reasonable, adopt modifying epoxy resin by organosilicon as filmogen, it has higher cross-linking density to solidify the back, adopt reactive thinner (for non-volatile thinner) in the starting material of the terrace paint of high-solid level, therefore, the terrace layer for preparing with the terrace paint of high-solid level provided by the present invention does not have hole, the space, crackle, through experimental study show have good acidproof, preservative property and stronger toughness and mechanical property such as alkaline-resisting, and the color stuffing addition is wanted much less than traditional terrace paint in the terrace paint of high-solid level provided by the invention, alleviated in the production process dust to worker's harm, it is a kind of environmental protection, nontoxic, the terrace paint of good high-solid level.
2, the preparation method of the terrace paint of high-solid level provided by the present invention, technology is reasonable, and is workable, the production efficiency height, energy consumption is low, and the product qualified rate height for preparing can be realized industrialized production.
3, the terrace paint of high-solid level provided by the invention, stable in properties, excellent property, the terrace that can be widely used in different places is laid.
Embodiment:
Below in conjunction with specific embodiment, further illustrate the present invention, should understand these embodiment only is used to the present invention is described and is not used in and limit the scope of the invention, after having read the present invention, those skilled in the art all fall within the application's claims institute restricted portion to the modification of the various equivalent form of values of the present invention.
Embodiment 1
1, the terrace paint weight proportion of high-solid level: 50 kilograms of modifying epoxy resin by organosilicon, 15 kilograms in aliphatics aminoresin, concentration are 70% 4 kilograms in paraffin, rutile TiO
25 kilograms, 4 kilograms of Polyethylene Glycol Bisglycidyl Ether, 306 (052) 0.5 kilograms of defoamers, dispersion agent 163 are that 0.5 kilogram, flow agent 354 are 5 kilograms of 0.2 kilograms, mica powder.
2, the preparation of the terrace paint of high-solid level:
1. choose 50 kilograms of above modifying epoxy resin by organosilicon, 15 kilograms in aliphatics aminoresin, 4 kilograms of reactive thinner Polyethylene Glycol Bisglycidyl Ether, 0.5 kilogram dispersion agent 163 mixes, high speed dispersion 1 hour, and it is standby to get intermediate raw material;
2. get the intermediate raw material that 1. step obtains, add plasticizer concentration and be 4 kilograms in 70% paraffin, 5 kilograms of color stuffing mica powders mix, high speed dispersion 2 hours, intermediate raw material is standby;
3. get the intermediate raw material that 2. step obtains, add rutile TiO
2The flow agent 354 that 5 kilograms, 0.5 kilogram defoamer is 306 (052) and 0.2 kilograms mixes, and high speed dispersion 2 hours grinds to form fine powder, and it is standby to get intermediate product;
4. get the intermediate product that 3. step obtains, toning, regrinding, the sieve of 30 μ m detects particle diameter excessively, and packing is promptly.
3, the terrace paint of getting 2 high-solid levels that make carries out the ground finishing coat, and experiment detects its performance then, and experimental result is as shown in table 1:
The performance test results of the terrace paint coating of table 1 high-solid level
| Test item | Technical indicator | Detected result | |
| 1 | Surface drying/h | ≤6 | 4 |
| 2 | Do solid work/h | ≤24 | 20 |
| 3 | Tensile strength Mpa | ≥9 | 12 |
| 4 | Rotproofness (500g.500r)/g | ≤0.02 | 0.012 |
| 5 | Acid resistance (5%H 2SO 4) | 60 days no changes | No change |
| 6 | Alkali resistance (5%NaOH) | 60 days no changes | No change |
| 7 | Anti-gasoline (120# gasoline | 60 days no changes | No change |
| 8 | Salt water resistance (5%NaCL) | 60 days no changes | No change |
Show that by table 1 laboratory test results the terrace paint of high-solid level provided by the invention has good acidproof, alkaline resistance properties, has stronger toughness and mechanical property, and the gel time of coating is suitable.
Embodiment 2
1, the terrace paint weight proportion of high-solid level: 55 kilograms of modifying epoxy resin by organosilicon, 30 kilograms in aliphatics aminoresin, concentration are 80% 10 kilograms in paraffin, rutile TiO
210 kilograms, 5 kilograms of Polyethylene Glycol Bisglycidyl Ether, 306 (052) 1 kilograms of defoamers, dispersion agent 163 are that 1 kilogram, flow agent 354 are 15 kilograms of 0.5 kilograms, mica powder.
2, the preparation of the terrace paint of high-solid level:
1. choose 55 kilograms of above modifying epoxy resin by organosilicon, 30 kilograms in aliphatics aminoresin, 5 kilograms of reactive thinner Polyethylene Glycol Bisglycidyl Ether, 1 kilogram dispersion agent 163 mixes, high speed dispersion 2 hours, and it is standby to get intermediate raw material;
2. get the intermediate raw material that 1. step obtains, add plasticizer concentration and be 10 kilograms in 80% paraffin, 15 kilograms of color stuffing mica powders mix, high speed dispersion 3 hours, intermediate raw material is standby;
3. get the intermediate raw material that 2. step obtains, add rutile TiO
2The flow agent 354 that 10 kilograms, 1 kilogram defoamer is 306 (052) and 0.5 kilograms mixes, and high speed dispersion 3 hours grinds to form fine powder, and it is standby to get intermediate product;
4. get the intermediate product that 3. step obtains, toning, regrinding, the sieve of 25 μ m detects particle diameter excessively, and packing is promptly.
3, the terrace paint of getting 2 high-solid levels that make carries out the ground finishing coat, and experiment detects its performance then, and experimental result is as shown in table 2:
The performance test results of the terrace paint coating of table 2 high-solid level
| Test item | Technical indicator | Detected result | |
| 1 | Surface drying/h | ≤6 | 3.6 |
| 2 | Do solid work/h | ≤24 | 19 |
| 3 | Tensile strength Mpa | ≥9 | 16 |
| 4 | Rotproofness (500g.500r)/g | ≤0.02 | 0.010 |
| 5 | Acid resistance (5%H 2SO 4) | 60 days no changes | No change |
| 6 | Alkali resistance (5%NaOH) | 60 days no changes | No change |
| 7 | Anti-gasoline (120# gasoline | 60 days no changes | No change |
| 8 | Salt water resistance (5%NaCL) | 60 days no changes | No change |
Embodiment 3
1, the terrace paint weight proportion of high-solid level: 50 kilograms of modifying epoxy resin by organosilicon, 20 kilograms in aliphatics aminoresin, concentration are 80% 5 kilograms in paraffin, rutile TiO
28 kilograms, 5 kilograms of Polyethylene Glycol Bisglycidyl Ether, 306 (052) 0.5 kilograms of defoamers, dispersion agent 163 are that 0.5 kilogram, flow agent 354 are 10 kilograms of 0.5 kilograms, mica powder.
2, the preparation of the terrace paint of high-solid level:
1. choose 50 kilograms of above modifying epoxy resin by organosilicon, 20 kilograms in aliphatics aminoresin, 5 kilograms of reactive thinner Polyethylene Glycol Bisglycidyl Ether, 0.5 kilogram dispersion agent 163 mixes, high speed dispersion 1 hour, and it is standby to get intermediate raw material;
2. get the intermediate raw material that 1. step obtains, add plasticizer concentration and be 5 kilograms in 80% paraffin, 10 kilograms of color stuffing mica powders mix, high speed dispersion 2 hours, intermediate raw material is standby;
3. get the intermediate raw material that 2. step obtains, add rutile TiO
2The flow agent 354 that 8 kilograms, 0.5 kilogram defoamer is 306 (052) and 0.5 kilograms mixes, and high speed dispersion 2 hours grinds to form fine powder, and it is standby to get intermediate product;
4. get the intermediate product that 3. step obtains, toning, regrinding, the sieve of 20 μ m detects particle diameter excessively, and packing is promptly.
3, the terrace paint of getting 2 high-solid levels that make carries out the ground finishing coat, and experiment detects its performance then, and experimental result is as shown in table 3:
The performance test results of the terrace paint coating of table 3 high-solid level
| Test item | Technical indicator | Detected result | |
| 1 | Surface drying/h | ≤6 | 3.1 |
| 2 | Do solid work/h | ≤24 | 17 |
| 3 | Tensile strength Mpa | ≥9 | 17.5 |
| 4 | Rotproofness (500g.500r)/g | ≤0.02 | 0.008 |
| 5 | Acid resistance (5%H 2SO 4) | 60 days no changes | No change |
| 6 | Alkali resistance (5%NaOH) | 60 days no changes | No change |
| 7 | Anti-gasoline (120# gasoline | 60 days no changes | No change |
| 8 | Salt water resistance (5%NaCL) | 60 days no changes | No change |
Embodiment 4
1, the terrace paint weight proportion of high-solid level: 55 kilograms of modifying epoxy resin by organosilicon, 15 kilograms in aliphatics aminoresin, concentration are 80% 8 kilograms in paraffin, rutile TiO
25 kilograms, 5 kilograms of Polyethylene Glycol Bisglycidyl Ether, 306 (052) 1 kilograms of defoamers, dispersion agent 163 are that 0.5 kilogram, flow agent 354 are 10 kilograms of 0.5 kilograms, mica powder.
2, the preparation of the terrace paint of high-solid level:
1. choose 55 kilograms of above modifying epoxy resin by organosilicon, 15 kilograms in aliphatics aminoresin, 5 kilograms of reactive thinner Polyethylene Glycol Bisglycidyl Ether, 0.5 kilogram dispersion agent 163 mixes, high speed dispersion 1 hour, and it is standby to get intermediate raw material;
2. get the intermediate raw material that 1. step obtains, add plasticizer concentration and be 8 kilograms in 80% paraffin, 10 kilograms of color stuffing mica powders mix, high speed dispersion 2 hours, intermediate raw material is standby;
3. get the intermediate raw material that 2. step obtains, add rutile TiO
2The flow agent 354 that 5 kilograms, 1 kilogram defoamer is 306 (052) and 0.5 kilograms mixes, and high speed dispersion 2 hours grinds to form fine powder, and it is standby to get intermediate product;
4. get the intermediate product that 3. step obtains, toning, regrinding, the sieve of 25 μ m detects particle diameter excessively, and packing is promptly.
3, the terrace paint of getting 2 high-solid levels that make carries out the ground finishing coat, and experiment detects its performance then, and experimental result is as shown in table 4:
The performance test results of the terrace paint coating of table 4 high-solid level
| Test item | Technical indicator | Detected result | |
| 1 | Surface drying/h | ≤6 | 3.2 |
| 2 | Do solid work/h | ≤24 | 17.5 |
| 3 | Tensile strength Mpa | ≥9 | 20 |
| 4 | Wear resistance (500g.500r)/g | ≤0.02 | 0.006 |
| 5 | Acid resistance (5%H 2SO 4) | 60 days no changes | No change |
| 6 | Alkali resistance (5%NaOH) | 60 days no changes | No change |
| 7 | Anti-gasoline (120# gasoline | 60 days no changes | No change |
| 8 | Salt water resistance (5%NaCL) | 60 days no changes | No change |
Embodiment 5
1, the terrace paint weight proportion of high-solid level: 50 kilograms of modifying epoxy resin by organosilicon, 30 kilograms in aliphatics aminoresin, concentration are 80% 4 kilograms in paraffin, rutile TiO
25 kilograms, 4 kilograms of Polyethylene Glycol Bisglycidyl Ether, 306 (052) 0.5 kilograms of defoamers, dispersion agent 163 are that 0.5 kilogram, flow agent 354 are 5 kilograms of 1 kilograms, mica powder.
2, the preparation of the terrace paint of high-solid level:
1. choose 50 kilograms of above modifying epoxy resin by organosilicon, 30 kilograms in aliphatics aminoresin, 4 kilograms of reactive thinner Polyethylene Glycol Bisglycidyl Ether, 0.5 kilogram dispersion agent 163 mixes, high speed dispersion 1 hour, and it is standby to get intermediate raw material;
2. get the intermediate raw material that 1. step obtains, add plasticizer concentration and be 4 kilograms in 80% paraffin, 5 kilograms of color stuffing mica powders mix, high speed dispersion 2 hours, intermediate raw material is standby;
3. get the intermediate raw material that 2. step obtains, add rutile TiO
2The flow agent 354 that 5 kilograms, 0.5 kilogram defoamer is 306 (052) and 1 kilograms mixes, and high speed dispersion 2 hours grinds to form fine powder, and it is standby to get intermediate product;
4. get the intermediate product that 3. step obtains, toning, regrinding, the sieve of 35 μ m detects particle diameter excessively, and packing is promptly.
3, the terrace paint of getting 2 high-solid levels that make carries out the ground finishing coat, and experiment detects its performance then, and experimental result is as shown in table 5:
The performance test results of the terrace paint coating of table 5 high-solid level
| Test item | Technical indicator | Detected result | |
| 1 | Surface drying/h | ≤6 | 4.2 |
| 2 | Do solid work/h | ≤24 | 19.5 |
| 3 | Tensile strength Mpa | ≥9 | 16.8 |
| 4 | Rotproofness (500g.500r)/g | ≤0.02 | 0.009 |
| 5 | Acid resistance (5%H 2SO 4) | 60 days no changes | No change |
| 6 | Alkali resistance (5%NaOH) | 60 days no changes | No change |
| 7 | Anti-gasoline (120# gasoline | 60 days no changes | No change |
| 8 | Salt water resistance (5%NaCL) | 60 days no changes | No change |
Draw by above experiment, each proportioning raw materials of the terrace paint of high-solid level provided by the invention is scientific and reasonable, lay the coating that obtains with high-solid level terrace paint provided by the invention and detect performance index requirement all up to specification through multi-performance index, have well acidproof, alkaline resistance properties and have stronger toughness and mechanical property, and the gel time of coating is suitable, environmental protection, nontoxic, being expected to exploitation becomes terrace paint of new generation.
Claims (10)
1, a kind of terrace paint of high-solid level is characterized in that, it is made by following raw materials by weight percent: modifying epoxy resin by organosilicon 50～55%, aliphatics aminoresin 15～30%, softening agent 4～10%, TiO
25～10%, color stuffing 5～15%, reactive thinner 4～5%, defoamer 0.5～1.0%, dispersion agent 0.5～1.0%, flow agent 354 0.2～0.5%.
2, the terrace paint of high-solid level according to claim 1 is characterized in that, it is made by following raw materials by weight percent: modifying epoxy resin by organosilicon 50%, aliphatics aminoresin 20%, softening agent 5%, TiO
28%, color stuffing 10%, reactive thinner 5%, defoamer 0.5%, dispersion agent 1%, flow agent 0.5%.
3, the terrace paint of high-solid level according to claim 1 is characterized in that, it is made by following raw materials by weight percent: modifying epoxy resin by organosilicon 55%, aliphatics aminoresin 15%, softening agent 8%, TiO
25%, color stuffing 10%, reactive thinner 5%, defoamer 1%, dispersion agent 0.5%, flow agent 0.5%.
4, the terrace paint of high-solid level according to claim 1 is characterized in that, it is made by following raw materials by weight percent: modifying epoxy resin by organosilicon 50%, aliphatics aminoresin 30%, softening agent 4%, TiO
25%, color stuffing 5%, reactive thinner 4%, defoamer 0.5%, dispersion agent 0.5%, flow agent 1%.
According to the terrace paint of each described high-solid level of claim 1 to 4, it is characterized in that 5, described softening agent is that concentration is 70%～80% paraffin, thinner is a Polyethylene Glycol Bisglycidyl Ether, TiO
2Be rutile TiO
2, color stuffing is a mica powder, and froth breaking is a defoamer 306 (052), and dispersion agent is a dispersion agent 163, and flow agent is a flow agent 354.
6, a kind of method for preparing the terrace paint of each described high-solid level of claim 1 to 5 is characterized in that may further comprise the steps:
1. in the described ratio of claim 1, choose modifying epoxy resin by organosilicon, aliphatics aminoresin, reactive thinner Polyethylene Glycol Bisglycidyl Ether, dispersion agent 163 mixes, high speed dispersion 1 to 3 hour, and it is standby to get intermediate raw material;
2. get the intermediate raw material that 1. step obtains, adding plasticizer concentration in the described ratio of claim 1 is paraffin, color stuffing mica powder, mix, and high speed dispersion 1 to 3 hour, it is standby to get intermediate raw material;
3. get the intermediate raw material that 2. step obtains, add rutile TiO in the described ratio of claim 1
2, froth breaking 306 (052) and flow agent 354, mix, high speed dispersion 1 to 3 hour grinds to form fine powder, intermediate product is standby;
4. get the intermediate product that 3. step obtains, toning, regrinding detects particle diameter, filtration, packing promptly.
7, the method for the terrace paint of high-solid level according to claim 6 is characterized in that, step 1. the time of high speed dispersion be 1 hour, 2. 3. the time of high speed dispersion is 2 hours to step with step.
According to the method for the terrace paint of claim 6 or 7 described high-solid levels, it is characterized in that 8,4. the sieve particle diameter of the high-solid level terrace paint that obtains of step is 1 to 35 μ m.
9, the application of the terrace paint of each described high-solid level of claim 1 to 4 in the corrosion protection coating of preparation ground.
10, the application of the terrace paint of the described high-solid level of claim 5 in the corrosion protection coating of preparation ground.