CN101571462A - 一种用于预测改性塑料熔接性能的试样模具 - Google Patents
一种用于预测改性塑料熔接性能的试样模具 Download PDFInfo
- Publication number
- CN101571462A CN101571462A CNA2009100270137A CN200910027013A CN101571462A CN 101571462 A CN101571462 A CN 101571462A CN A2009100270137 A CNA2009100270137 A CN A2009100270137A CN 200910027013 A CN200910027013 A CN 200910027013A CN 101571462 A CN101571462 A CN 101571462A
- Authority
- CN
- China
- Prior art keywords
- die cavity
- die
- cast gate
- horizontal direction
- vertical direction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种用于预测改性塑料熔接性能的试样模具，包括静模板、型腔板及动模板，型腔板上设有用于模塑标准拉伸试样的型腔、与型腔相连通的浇口及与浇口相连通的分流道，型腔板上设有3个型腔，3个型腔的外形尺寸完全一致；其中两个型腔沿水平方向呈平行并列排布，水平方向两个型腔的一端设置浇口；另一个型腔沿垂直方向布置，设置在水平方向两个型腔的旁侧，垂直方向型腔的两端均设置浇口；垂直方向型腔的上端浇口与水平方向一型腔的浇口相对，垂直方向型腔的下端浇口与水平方向另一型腔的浇口相对。一次注塑成型即可同时获取有熔接痕与无熔接痕两种类型的拉伸试样，比较两种不同试样的拉伸数据，可表明熔接痕对材料性能的影响。
Description
技术领域
本发明涉及一种模具，尤其涉及一种可以预测改性塑料熔接性能的注塑模具。
背景技术
在注塑成型热塑性塑料制品时，通常在某些情况下，由于与制品设计相关的模具的结构因素，成型制品产生熔接痕的现象几乎是难以完全避免的。产生熔接痕的原因是由于充模过程中来自不同方向的熔体流动前峰，在汇合处未能完全融合所致。熔接痕(熔接线或熔接面)的存在不仅影响制品的外观质量，更为重要的是，熔接痕会成为应力集中点从而影响制品的力学强度，在制品需要二次加工(如涂装、电镀)时，耐化学品性方面的影响也会有所显现。为了避免因熔接痕而产生的诸多产品质量问题，在产品加工成型后，须对试制品进行熔接痕方面的测试，检查制品是否有熔接痕，判别因不同程度的熔接痕所导致的产品质量问题的大小，并根据情况找到解决问题的方法。
制品熔接痕区域的强度、耐化学品性和表观性能受材料选择、制品设计、模具设计和制品加工条件等几个因素影响。
比较材料拉伸试样的熔接强度保留值(即有熔接线的试样与无熔接线的试样其拉伸强度的比值)对于预测改性塑料的熔接性能，优化设计改性材料具有一定的价值。其中有熔接线的拉伸强度试样，可以简单地用两端开设浇口的试样模具制成，而无熔接线的拉伸强度试样可以采用通常使用的标准的单浇口试样模具制成。
发明内容
本发明的目的是克服现有技术存在的不足，提供一种可以预测改性塑料熔接性能的试样模具。
本发明通过以下技术方案来实现：
一种用于预测改性塑料熔接性能的试样模具，包括静模板、型腔板及动模板，型腔板上设有用于模塑标准拉伸试样的型腔、与型腔相连通的浇口及与浇口相连通的分流道，特点是：所述型腔板上设有3个型腔，3个型腔的外形尺寸完全一致；其中两个型腔沿水平方向呈平行并列排布，所述水平方向两个型腔的一端设置浇口；另一个型腔沿垂直方向布置，设置在水平方向两个型腔的旁侧，所述垂直方向型腔的两端均设置浇口；垂直方向型腔的上端浇口与水平方向一型腔的浇口相对，垂直方向型腔的下端浇口与水平方向另一型腔的浇口相对，所述垂直方向型腔两端的浇口和水平方向两个型腔的浇口均与分流道相连通。
进一步地，上述的一种用于预测改性塑料熔接性能的试样模具，其中，所述分流道呈T形。
本发明技术方案突出的实质性特点和显著的进步主要体现在：
将双浇口进料的拉伸试样模具与单浇口进料的拉伸试样模具整合优化设计后在同一个型腔板模具上实现，一次注塑成型即可同时获取有熔接痕与无熔接痕两种类型的拉伸试样，通过拉伸试验，比较两种不同试样的拉伸数据，可以表明熔接痕对材料性能的影响，并计算出成型材料的熔接强度保留值，从而预测试验用成型材料的熔接性能，为改性材料的最优化设计提供路径。
附图说明
下面结合附图对本发明技术方案作进一步说明：
图1：本发明型腔板的结构示意图。
图中各附图标记的含义：
1-型腔板，2-型腔，3-浇口，4-分流道。
具体实施方式
用于预测改性塑料熔接性能的试样模具，为普通注塑模具，主要包括静模板、型腔板及动模板，如图1所示，在型腔板1上设有用于模塑标准拉伸试样的型腔2、与型腔相连通的浇口3及与浇口3相连通的分流道4；型腔板1上设有3个型腔，3个型腔的外形尺寸完全一致；其中两个型腔沿水平方向呈平行并列排布，水平方向两个型腔的一端设置浇口，水平方向的每个型腔采用单浇口进料。另一个型腔沿垂直方向布置，设置在水平方向两个型腔的旁侧，垂直方向型腔的两端均设置浇口，垂直方向型腔采用双浇口进料。垂直方向型腔的上端浇口与水平方向一型腔的浇口相对，垂直方向型腔的下端浇口与水平方向另一型腔的浇口相对，垂直方向型腔两端的浇口和水平方向两个型腔的浇口均与分流道4相连通，分流道4呈T形。
上述模具结构中，型腔数为3个，外形尺寸完全一致。其中两个型腔呈水平方向排列且互相平行，每个型腔采用单浇口进料，以获取无熔接痕的试样成品。在两个平行型腔的一侧，设计有垂直方向布置的一个型腔，型腔的两端均设置浇口，目的是可以根据熔融的改性材料进浇后在模具型腔的中间部位熔合的情况，观察由此产生的熔接痕。在同一个型腔板上，通过浇口设计方案，可以成型有熔接痕和无熔接痕两种试样，从而得以进行性能比较，为材料设计提供依据。分流道的设计对熔接痕的产生和强弱无直接影响，满足流道平衡原则。
本发明将两端设置进料浇口的拉伸试样模具与单浇口进料的拉伸试样模具整合优化设计后在同一个型腔板模具上实现，一次注塑成型即可同时获取有熔接痕与无熔接痕两种类型的拉伸试样。通过拉伸试验，比较两种不同试样的拉伸性能数据，可以表明熔接痕对材料性能的影响，并计算出成型材料的熔接强度保留值，从而预测试验用成型材料的熔接性能，为改性材料的最优化设计提供路径。
该模具***还包括有浇口套，浇口套可穿过静模板正对型腔板上的分流道的正中央。浇口套上设有主浇口及与主浇口相连通的主流道，主流道与型腔板上的分流道相连通，主流道的直径不小于4mm。模具结构设有顶出装置，包括与型腔2相配合的整体顶出型芯，型芯设在一顶出板上，而一顶柱穿过动模板承抵住顶出板，再由顶出板向前顶出型芯而将试样顶出，顶出用的型芯与型腔尺寸完全一致，能使试样在整个被顶出面受力均匀，易于顶出，且试样被顶出的表面不会有任何顶出痕迹，试样表面的平整度好，试样质量高。
需要说明的是，本发明涉及的模具结构，提供的是可以预测改性塑料熔接性能的一种设计方案，模具***设计中涉及的型腔数量和分布、测试试样的类型以及试样所采用的材料可依据实际使用要求予以设定。
综上所述，本发明设计独特、结构新颖，将传统的单浇口试样模具与两端进料的双浇口试样模具整合优化设计后在同一个型腔板模具上实现，在同等工艺条件下，一次成型两种类型的试验用样条，便于分析材料因素对试样熔接强度的影响程度，从而为合理设计改性塑料的组分和用量提供一条有益的途径。
如前文所述，需要强调和理解到的是：上述说明并非是对本发明的限制，在本发明构思范围内，所进行的添加、变换、替换等，也应属于本发明的保护范围。
Claims (2)
1.一种用于预测改性塑料熔接性能的试样模具，包括静模板、型腔板及动模板，型腔板上设有用于模塑标准拉伸试样的型腔、与型腔相连通的浇口及与浇口相连通的分流道，其特征在于：所述型腔板上设有3个型腔，3个型腔的外形尺寸完全一致；其中两个型腔沿水平方向呈平行并列排布，所述水平方向两个型腔的一端设置浇口；另一个型腔沿垂直方向布置，设置在水平方向两个型腔的旁侧，所述垂直方向型腔的两端均设置浇口；垂直方向型腔的上端浇口与水平方向一型腔的浇口相对，垂直方向型腔的下端浇口与水平方向另一型腔的浇口相对，所述垂直方向型腔两端的浇口和水平方向两个型腔的浇口均与分流道相连通。
2、根据权利要求1所述的一种用于预测改性塑料熔接性能的试样模具，其特征在于：所述分流道呈T形。