CN101549297B - 一种固定床雷镍催化剂的制备方法 - Google Patents
一种固定床雷镍催化剂的制备方法 Download PDFInfo
- Publication number
- CN101549297B CN101549297B CN200810300788A CN200810300788A CN101549297B CN 101549297 B CN101549297 B CN 101549297B CN 200810300788 A CN200810300788 A CN 200810300788A CN 200810300788 A CN200810300788 A CN 200810300788A CN 101549297 B CN101549297 B CN 101549297B
- Authority
- CN
- China
- Prior art keywords
- nickel
- catalyst
- preparation
- fixed bed
- raney
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种固定床雷镍催化剂的制备方法,其具体步骤为将泡沫镍放入有机溶剂中浸泡10~120min后,用稀酸溶液清洗,然后水洗,干燥;将金属铝在惰性气氛下加热至660~800℃,使其全部熔融,然后将得到的泡沫镍浸入其中,保持温度在660~800℃,浸渍0.5~6h后取出,自然冷却至室温,即得镀铝泡沫镍;将得到的镀铝泡沫镍在氢氧化钠或氢氧化钾溶液中浸取,即得。本发明制备得到的固定床雷尼催化剂具有强度高、催化活性好、催化剂的活性均匀而且重复性好的优点。属于催化剂制备领域。
Description
技术领域
本发明涉及一种固定床雷尼催化剂的制备方法,具体地讲是涉及一种高活性雷尼催化剂的制备方法。
背景技术
氢能是人类社会为缓解资源和环境问题提出的一种未来能源发展方向,这项发展的核心内容就是以氢气代替现有的化石燃料(煤、石油和天然气)作为清洁、绿色、便于携带输送的燃料。而以氢为燃料的燃料电池则是高效、清洁的一种发电装置,并逐渐成为便携式电子产品和电动汽车的理想配套电源。目前,限制燃料电池发展和应用的主要问题是氢的储存,而现今广泛采用的储氢方式,储氢量都较低,如高压气瓶储氢、贮氢合金储氢等。而硼氢化物是一种高储氢含量的材料,如硼氢化钠的储氢量为21.2%。这些化合物作为一种强还原剂与水发生反应,可以释放高纯度的氢气,不需要净化直接可以供给燃料电池发电。而且制氢原料可以固体运输和储存,大大降低成本。反应方程式如下:
NaBH4+2H2O→4H2+NaBO2
目前,硼氢化物水解制氢的催化剂主要有金属卤化物(CoCl2)、负载在离子交换树脂的贵金属(如Pt、Pd、Ru等)、雷尼合金(雷尼Ni)等。但都存在一些问题,如催化剂流失问题、反应不可控和成本等问题等等。
Bin Hong Liu等报道了采用雷尼镍、雷尼钴以及雷尼镍钴等催化硼氢化钠水解发生氢气的方法(Journal of Alloys and Conpounds,415,2006,288-293)。在该报道中,利用粉末雷尼镍、粉末雷尼钴等催化硼氢化钠分解制氢。粉末状雷尼催化剂在实际应用中容易流失,增加了生成氢气与催化剂分离的难度,从而使得其应用受到了限制。在中国公开号为CN1774390A的专利公开了一种利用雷尼镍催化分解硼氢化钠制氢的方法,专利中采用两种方法解决粉末雷尼镍的流失问题。第一种方法是,将雷尼镍附着到有催化剂固定单元的磁体上,浸泡在水中。第二种方法是用聚氨酯泡沫将雷尼镍固定在镍网上,然后储存在蒸馏水中。这两种方法都使得反应装置更为复杂,而且制备得到的催化剂强度较低、活性成分容易脱落。
日本公开号为JP2005205265的专利报道了制备固定床雷尼镍制氢催化剂的方法,具体步骤是将铝粉和粘结剂混合涂敷在泡沫镍上,经高温焙烧,制备表面合金化的泡沫镍,再经碱液活化,得到固定床雷尼镍制氢催化剂,解决了一些目前常见的问题,如催化剂流失问题,有效克服了粉末雷尼催化剂的局限性。但是该专利制备的催化剂活性偏低,各部分的催化活性不均一,也限制了实际应用。
发明内容
本发明要解决的技术问题是提供一种强度高、催化活性好、催化剂的活性均匀而且重复性好的雷尼镍催化剂的制备方法。
为解决上述技术问题,本发明的发明人在现有技术的基础上进行了大量的研究和创造性的劳动,研制出了一种高活性、高强度的雷尼镍催化剂的制备方法,其具体步骤如下:①将泡沫镍放入有机溶剂中浸泡10~120min后,用稀酸溶液清洗,然后水洗,干燥;
②将金属铝在惰性气氛下加热至660~800℃,使其全部熔融,然后将步骤①得到的泡沫镍浸入其中,保持温度在660~800℃,浸渍0.5~6h后取出,自然冷却至室温,即得镀铝泡沫镍;
③将步骤②中得到的镀铝泡沫镍在碱性溶液中浸取,即得。
所述的步骤①中的有机溶剂为丙酮、乙醇、***、苯、甲苯、石油醚和氯仿中的一种。
所述的步骤①中的稀酸溶液为稀盐酸、稀硫酸或稀磷酸。
所述的步骤①中的干燥为温度在60~100℃下真空干燥10~120min。
所述步骤③中的碱性溶液为10~30wt%的氢氧化钠或氢氧化钾溶液,所述的浸取为在温度为60~85℃下浸取1~12h。
所述步骤②中的惰性气体是氮气、氦气、氖气和氩气中的一种。
所述的金属铝可以是铝粉、铝丝、铝锭、铝条、铝板等。
所述的金属铝的用量为金属铝熔融后可以将泡沫镍浸没为宜。
本发明采用熔融浸渍法将金属铝均匀的负载于泡沫镍的孔壁上,碱溶液浸取后得到的雷尼镍催化剂则具有催化活性分布均匀,催化活性好的特点,本发明制备的雷尼镍催化剂催化硼氢化物的转化率最高可达90%以上。采用熔融浸渍法可以通过严格控制浸渍时间、浸渍温度得到预期的负载量的镀铝泡沫镍,从而相同条件下碱溶液浸取后,可以制备得到性能均一催化剂,本发明的制备方法有很好的可重复性,适合于产业化的批量生产。本发明采用的泡沫镍既作为镍铝合金的镍源,同时又是载体,因此本发明制备的催化剂有较高的机械强度。在制备催化剂前,可以根据实际需要,将泡沫镍制成实际需要的形状和大小,然后再进行熔融浸渍制备,可以节省催化剂的后续成型的工序,使得固定床雷尼镍催化剂的制备工艺简化,并能降低生产成本。
具体实施方式
下面结合具体实施方式对本发明作进一步详细的说明。
实施例中制备得到的固定床雷尼镍催化剂经过如下步骤进行活性评价:反应液的组成为5wt%的NaBH4,10wt%的NaOH,85wt%的去离子水。盛有100mL反应液的反应器放置于30℃恒温水浴中,称取雷尼镍催化剂5g,将其放入反应液,反应过程中,用气体质量流量计记录单位时间产氢量,与理论产氢量之比即为硼氢化钠催化水解制氢反应的催化转化率。
实施例1
①将泡沫镍放入丙酮中浸泡10min后,用稀盐酸溶液清洗,然后水洗后,于60℃下真空干燥120min;
②将金属铝粉在氮气气氛下加热至660℃,使其全部熔融,然后将步骤①得到的泡沫镍浸入其中,保持温度在660℃,浸渍0.5h后取出,自然冷却至室温,即得镀铝泡沫镍;
③将步骤②中得到的镀铝泡沫镍在10wt%氢氧化钠中,在温度为60℃的条件下,浸取12h,即得。
制备所得到的固定床雷尼镍催化剂经活性评价可得其催化转化率为:82%。
实施例2
①将泡沫镍放入乙醇中浸泡60min后,用稀硫酸溶液清洗,然后水洗后,于80℃下真空干燥10min;
②将金属铝丝在氦气气氛下加热至700℃,使其全部熔融,然后将步骤①得到的泡沫镍浸入其中,保持温度在700℃,浸渍1h后取出,自然冷却至室温,即得镀铝泡沫镍;
③将步骤②中得到的镀铝泡沫镍在20wt%氢氧化钠中,在温度为65℃的条件下,浸取12h,即得。
制备所得到的固定床雷尼镍催化剂经活性评价可得其催化转化率为:85%。
实施例3
①将泡沫镍放入苯中浸泡100min后,用稀磷酸溶液清洗,然后水洗后,于100℃下真空干燥60min;
②将金属铝带在氖气气氛下加热至750℃,使其全部熔融,然后将步骤①得到的泡沫镍浸入其中,保持温度在750℃,浸渍2h后取出,自然冷却至室温,即得镀铝泡沫镍;
③将步骤②中得到的镀铝泡沫镍在30wt%氢氧化钠中,在温度为85℃的条件下,浸取4h,即得。
制备所得到的固定床雷尼镍催化剂经活性评价可得其催化转化率为:90%。
实施例4
①将泡沫镍放入甲苯中浸泡120min后,用稀盐酸溶液清洗,然后水洗后,于70℃下真空干燥20min;
②将金属铝条在氩气气氛下加热至800℃,使其全部熔融,然后将步骤①得到的泡沫镍浸入其中,保持温度在800℃,浸渍3h后取出,自然冷却至室温,即得镀铝泡沫镍;
③将步骤②中得到的镀铝泡沫镍在25wt%氢氧化钾中,在温度为70℃的条件下,浸取6h,即得。
制备所得到的固定床雷尼镍催化剂经活性评价可得其催化转化率为:88%。
实施例5
①将泡沫镍放入石油醚中浸泡80min后,用稀盐酸溶液清洗,然后水洗后,于75℃下真空干燥40min;
②将金属铝板在氮气气氛下加热至720℃,使其全部熔融,然后将步骤①得到的泡沫镍浸入其中,保持温度在720℃,浸渍5h后取出,自然冷却至室温,即得镀铝泡沫镍;
③将步骤②中得到的镀铝泡沫镍在18wt%氢氧化钾中,在温度为75℃的条件下,浸取8h,即得。
制备所得到的固定床雷尼镍催化剂经活性评价可得其催化转化率为:91%。
实施例6
①将泡沫镍放入氯仿中浸泡40min后,用稀硫酸溶液清洗,然后水洗后,于80℃下真空干燥90min;
②将金属铝板在氮气气氛下加热至780℃,使其全部熔融,然后将步骤①得到的泡沫镍浸入其中,保持温度在780℃,浸渍6h后取出,自然冷却至室温,即得镀铝泡沫镍;
③将步骤②中得到的镀铝泡沫镍在20wt%氢氧化钾中,在温度为80℃的条件下,浸取10h,即得。
制备所得到的固定床雷尼镍催化剂经活性评价可得其催化转化率为:92%。
Claims (4)
1.一种固定床雷尼镍催化剂的制备方法,其特征在于所述的制备方法具体步骤如下:
①将泡沫镍放入有机溶剂中浸泡10~120min后,用稀酸溶液清洗,然后水洗,在60~100℃下真空干燥10~120min;
②将金属铝在惰性气氛下加热至660~800℃,使其全部熔融,然后将步骤①得到的泡沫镍浸入其中,保持温度在660~800℃,浸渍0.5~6h后取出,自然冷却至室温,即得镀铝泡沫镍;
③将步骤②中得到的镀铝泡沫镍在60~85℃的碱性溶液中浸取1~12h,其中碱性溶液为10~30wt%的氢氧化钠或氢氧化钾溶液,即得固定床雷尼镍催化剂。
2.根据权利要求1所述的固定床雷尼镍催化剂的制备方法,其特征在于所述的步骤①中的有机溶剂为丙酮、乙醇、***、苯、甲苯、石油醚和氯仿中的一种。
3.根据权利要求1所述的固定床雷尼镍催化剂的制备方法,其特征在于所述步骤①中的稀酸溶液为稀盐酸、稀硫酸或稀磷酸。
4.根据权利要求1所述的固定床雷尼镍催化剂的制备方法,其特征在于所述步骤②中的惰性气氛是氮气、氦气、氖气和氩气中的一种。