CN101509207B - Printing method for polyester fibre/acetate blended high-grade resist printing face fabric - Google Patents
Printing method for polyester fibre/acetate blended high-grade resist printing face fabric Download PDFInfo
- Publication number
- CN101509207B CN101509207B CN2009100105271A CN200910010527A CN101509207B CN 101509207 B CN101509207 B CN 101509207B CN 2009100105271 A CN2009100105271 A CN 2009100105271A CN 200910010527 A CN200910010527 A CN 200910010527A CN 101509207 B CN101509207 B CN 101509207B
- Authority
- CN
- China
- Prior art keywords
- printing
- dye
- dyeing
- paste
- resisting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to the textile printing and dyeing industry. A method for printing a terylene/acetic acid blended high-grade dye-resisting printed fabric, which comprises the following steps: a first step of preparing printing paste: adding dye-resisting agent C into pearlescent pigment printing paste, and adding dye-resisting agent 550 into disperse dye printing paste; a second step of overprinting: carrying out multi-chromatic printing by a flat screen printing machine, drying and cropping; a third step of dyeing a ground color: pad-dyeing the ground color by using the dye-resisting disperse dye prepared in the first step; and a fourth step of post treatment: ageing the fabric dyed with the ground color at a high temperature of between 170 and 190 DEG C, then water washing, and cropping to obtain a product. The method uses differential fiber P/TA blended fabric to develop a new double-component dye resisting printing process, prevents the disperse dye dyed with the ground color from locally dyeing on a printed part, and removing the disperse dye to achieve the aim of fresh color; and proper water washing assistant and water washing temperature overcome the defect of staining of the printed fabric caused by the loose color of the disperse dye. The printed fabric has good printing durability.
Description
One, technical field:
The present invention relates to the textile printing and dyeing production method, particularly the printing technology of terylene/fibre in differentiation blended yarn woven fabric.
Two, background technology:
As everyone knows, Japan, Korea S, and some countries of Europe, using that terylene/novel fibre in differentiation develops aspect the high-grade textile garment lining is advanced in the world, particularly at the high-end technology of printing and dyeing deep processing and special dyeing and printing process technical elements, has very successful empirical value to use for reference.Although China's chemical fibre industry is started late, in recent ten years, China closes fine industry and develops rapidly, brings the high speed impetus for follow-up industry chain (supply chain), and the level of domestic research and development printing technology is greatly enhanced.Fibre in differentiation new raw material (P/TA printed fabric) is that long filament is washed in the warp-wise employing, and broadwise adopts 35% terylene short fiber and 65% triacetate staple blended yarn, forms through tatting; Contrast with terylene filament fabric, have the splendid sense of dangling, soft hand feeling, nice and cool comfort, thereby extensively liked by the consumer, but on printing technology, also exist many not enough problems at present, mainly be folded to dye that the DISPERSE DYES at stamp position is difficult to remove, influence colour brightness; Loose colour causes the staining of printed fabric etc. during washing, influences pattern, and the designs and varieties major part is dull.
Three, Fa Ming content:
The objective of the invention is to overcome above-mentioned not enough problem, a kind of printing method of polyester fibre/acetate blended high-grade resisting printing lining is provided, technology is simple, prevents colour contamination, increases the product designs and varieties, and the washing loose colour does not stain printed fabric.
The technical scheme that the present invention is adopted for achieving the above object is: the printing method of polyester fibre/acetate blended high-grade resisting printing lining, and concrete technology is:
First step preparation printing paste: it is standby with anti-dyeing paste to make stamp; Wherein add resist agent C in the pearlescent pigment printing paste; Add resist agent 550 in the DISPERSE DYES printing paste;
The second step chromatography: flat screen printing machine carries out the stamp of many chromatographys (5-12 cover) of terylene/triacetate blended yarn woven fabric, and at drying room of printing machine (100 ℃) oven dry, cropping;
The 3rd step was dyed ground colour: with the resist printing DISPERSE DYES pad dyeing ground colour of first step preparation;
The 4th step post processing: the fabric behind the pad dyeing ground colour evaporates at 170 ℃ of-190 ℃ of high temperature, washes then, and cropping makes product.
Adopt following water washing assistant and water composite during 40 ℃-50 ℃ of described washing temperature:
Rinsing agent Lipotng DGZ 1-2 grams per liter,
Soaping agent TC/conc 1-2 grams per liter.
Water washing assistant and water adopts caustic soda 0.5-1 grams per liter and sodium hydrosulfite 1-2 grams per liter composite during 55 ℃-70 ℃ of described washing temperature.
The present invention has outstanding feature: with fibre in differentiation P/TA (polyester fibre/acetate fiber) blended yarn woven fabric, developed bi-component dyestuff resisting printing new technology.The bi-component dye printing is meant pigment printing (comprising gold, silver powder stamp, pearlescent pigment stamp, COAT PRINTING etc.) and DISPERSE DYES stamp.Promptly destroy folded (but resist printing) DISPERSE DYES of dying, make the stamp position keep former color and luster constant (not having bleeding and secondary colour), to print edge contour clear at the stamp position.Behind the stamp along with the curing fixation of dyestuff, resist printing auxiliary agent in the print paste is had an effect, (having destroyed the azo group molecular structure that dyes the ground colour DISPERSE DYES) stoped the DISPERSE DYES of dying ground colour to be dyed on the part at stamp position, and it is removed, and reaches purpose bright in colour; Proper water washing assistant and water, washing temperature condition overcome DISPERSE DYES when washing, and loose colour causes the staining of printed fabric.Fabric after the dyeing has the splendid sense of dangling, soft hand feeling, nice and cool comfort.And the DISPERSE DYES of being screened has good print durability equally to terylene, triacetate.
Four, description of drawings:
Fig. 1 is a process chart of the present invention.
Five, the specific embodiment:
The present invention is described in further detail below in conjunction with specific embodiment, but the invention is not restricted to specific embodiment.
(1), produce preceding engineer testing:
1, stamp is with DISPERSE DYES with can prevent the selection of (dying ground colour) DISPERSE DYES:
Table one
| The stamp DISPERSE DYES | Can prevent (dying ground colour) DISPERSE DYES |
| The yellow 7GL in the big ENIX of blue S-BG, the big ENIX of the big red AM-BN in ENIX | The blue 2RSF of the yellow BRL-S Ka Yalong of the red TL-SF Ka Yalong of the blue BD-S Ka Yalong of Ka Yalong |
2, the thickener of anti-resist agent is selected in the mill base of DISPERSE DYES: table two
● zero better ◇ is general
Difference
3, the thickener of anti-resist agent is selected in the mill base of pearlescent pigment:
1. # printing thickening agent REDUCER conc 400/ sodium alginate
2. # printing thickening agent REDUCER conc 400/ synthetic gum tragacanth
3. (Japanese ラ Star Network Co., Ltd.) stuck with paste 226 in # printing thickening agent REDUCER conc 400/ resist printing
Printing thickening agent REDUCER conc 400 (Guangdong, DIC auxiliary reagent factory, middle mountain esters of acrylic acid thickener)
Table three
● zero better ◇ is general
Difference
(2) printing method of polyester fibre/acetate blended high-grade resisting printing lining, concrete technology is:
First step preparation printing paste: it is standby with anti-dyeing paste to make stamp; Wherein add resist agent C (Japan produces power Co., Ltd. of Mitsubishi) in the pearlescent pigment printing paste; Add resist agent 550 (Japan produces REMARK Co., Ltd.) in the DISPERSE DYES printing paste;
The concrete prescription of the anti-dyeing paste of pearlescent pigment stamp:
Pearlescent pigment 10-15 gram
Printing adhesive FS-460 (Dandong fixed star company product) 350-400 gram
Crosslinked color-fixing agent DF-810 (Dandong fixed star company product) 15-20 gram
Resist agent C (Mitsubishi power Co., Ltd.) 20-30 gram
3. the former paste of # (seeing Table three) 600-650 gram/1000 restrains;
The concrete prescription of the anti-dyeing paste of DISPERSE DYES stamp:
DISPERSE DYES 5-30 gram
The Japanese REMARK of resist agent 550 Co., Ltd.) 20-30 gram
E-130 (Japanese northern Wide Co., Ltd.) 600-800 gram/1000 grams are stuck with paste in resist printing;
The concrete prescription of ground colour resist printing DISPERSE DYES:
But the DISPERSE DYES of resist printing (seeing Table) 5-20 gram
Chelated dispersants HSY (the big auspicious chemical industry in Shanghai) 2-4 gram
FK sticks with paste the 600-700 of (10%) (kyoto, Japan paste producing Co., Ltd.) gram
Water X gram
Total amount 1000 grams;
The second step chromatography: the anti-dyeing paste of pearlescent pigment stamp and the anti-dyeing paste of DISPERSE DYES stamp that adopt first step preparation, flat screen printing machine carries out the stamp of many chromatographys (5-12 cover) of terylene/triacetate blended yarn woven fabric, and at drying room of printing machine (100 ℃) oven dry, cropping;
The 3rd step was dyed ground colour: with the ground colour resist printing DISPERSE DYES pad dyeing ground colour of first step preparation; (170 ℃);
The 4th step post processing: the fabric high temperature behind the pad dyeing ground colour evaporates, at 170 ℃ of-190 ℃ of infrared preliminary dryings of gas, and cropping after ten drying cylinders baking (100 ℃) again; Get finished product after washing again;
The present invention is by screening proper water washing assistant and water and washing temperature condition, eccysis fall the stamp part can not on the DISPERSE DYES loose colour that dyes, solve the staining that the washing loose colour can not cause printed fabric simultaneously.
Screen suitable washing temperature condition, auxiliary agent: table four
● zero better ◇ is general
Difference
Through above-mentioned screening, adopt following water washing assistant and water composite during 40 ℃-50 ℃ of washing temperature:
Rinsing agent Lipotng DGZ 1-2 grams per liter,
Soaping agent TC/conc 1-2 grams per liter;
Water washing assistant and water adopts caustic soda 0.5-1 grams per liter and sodium hydrosulfite 1-2 grams per liter composite during 55 ℃-70 ℃ of washing temperature.
The finished product washing fastness that makes and the detection of crock fastness: table five
Claims (3)
1. the printing method of the high-grade resisting printing lining of polyester fibre/acetate fiber blend, it is characterized in that: concrete technology is:
First step preparation printing paste: it is standby with anti-dyeing paste to make stamp; Wherein add resist agent C in the pearlescent pigment printing paste; Add resist agent 550 in the DISPERSE DYES printing paste;
The second step chromatography: flat screen printing machine carries out the stamp of the 5-12 chromatography of terylene/triacetate blended yarn woven fabric, and at 100 ℃ of oven dry of drying room of printing machine, cropping;
The 3rd step was dyed ground colour: with the resist printing DISPERSE DYES pad dyeing ground colour of first step preparation;
The 4th step post processing: the fabric behind the pad dyeing ground colour evaporates at 170 ℃ of-190 ℃ of high temperature, washes then, and cropping makes product.
2. the printing method of the high-grade resisting printing lining of polyester fibre/acetate fiber blend according to claim 1 is characterized in that: adopt following water washing assistant and water composite when washing 40 ℃-50 ℃ of temperature:
Rinsing agent Lipotng DGZ 1-2 grams per liter,
Soaping agent TC/conc 1-2 grams per liter.
3. the printing method of the high-grade resisting printing lining of polyester fibre/acetate fiber blend according to claim 1 is characterized in that: water washing assistant and water adopts caustic soda 0.5-1 grams per liter and sodium hydrosulfite 1-2 grams per liter composite during 55 ℃-70 ℃ of washing temperature.