CN101469512A - High water absorbent quick-drying terylene fabric and manufacturing method thereof - Google Patents
High water absorbent quick-drying terylene fabric and manufacturing method thereof Download PDFInfo
- Publication number
- CN101469512A CN101469512A CNA2007101734727A CN200710173472A CN101469512A CN 101469512 A CN101469512 A CN 101469512A CN A2007101734727 A CNA2007101734727 A CN A2007101734727A CN 200710173472 A CN200710173472 A CN 200710173472A CN 101469512 A CN101469512 A CN 101469512A
- Authority
- CN
- China
- Prior art keywords
- drying
- high water
- water absorbent
- terylene fabric
- absorbent quick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a fabric for dyeing industry, especially relates to a water absorbtable fast-drying terylene fabric, which is prepared from hydrophilic polyester and polyether block copolymer surface modifying a hydrophobic terylene fiber. Molecular formula of the block polymer is CnHmOx, wherein n is from 100 to 500, m is from 200 to 1000, x is from 50 to 200. A preparation uses a disperse dye, a leveling dispenser, acetic acid, and a hydrophilic polymer, includes a fed dyeing step, a temperature reaction step, a cooling reduction cleaning step, a drying and forming step. Another preparation uses a padding liquid, a hydrophilic polyester, a polyether block copolymer, includes a step for adding the hydrophilic polyester and the polyether block copolymer into the padding liquid and dispersing, a step for padding the fabric in the padding liquid, a step for taking the treated fabric and drying, and a forming step. The fabric has great water absorbing performance and is capable of automatically dried in short time, making the wearer feel comfortable.
Description
Technical field
The present invention relates to the lining of dyeing, relate in particular to a kind of polyester fabric.
Background technology
As everyone knows, the hydrophobic material manufacturing of the general employing of quick-dry type lining, hydrophobic terylene is widely used, however this lining water absorbing properties is relatively poor relatively, and very poor with the clothes that this lining is made owing to moisture permeability, allow the people can feel very vexed.Especially, for moving clothes, it promptly requires energy rapid draing, keeps the comfort of sportsman's skin, simultaneously a large amount of sweat that also require the energy fast Absorption to move and cause.The clothes that adopt hydrophobic terylene to make are difficult to meet this requirement.
Summary of the invention
The objective of the invention is to overcome the above-mentioned defective of existing hydrophobic polyester fabric, hydrophobic polyester fabric of a kind of high water absorbent quick-drying and preparation method thereof is provided.Lining of the present invention has good water absorbing properties and automatic drying in a short period of time, makes the wearer feel more comfortable.
The present invention is achieved in that
A kind of high water absorbent quick-drying terylene fabric, it is made up of hydrophobicity polyster fibre and hydrophily inlay and break copolymer, described lining is that the hydrophobicity polyster fibre carries out surface modification by hydrophilic polyester and polyether block copolymer and forms, the molecular formula of this block polymer is CnHmOx, wherein, n=100-500, m=200-1000, x=50-200.
The hydrophobic polyester fabric of described a kind of high water absorbent quick-drying, described polyester is a polyethylene terephthalate, described polyethers is a polyglycol ether.
The preparation method of described a kind of high water absorbent quick-drying terylene fabric, it comprises that DISPERSE DYES, aliphatic alcohol polyethenoxy ester are as disperseing levelling agent, acetic acid and hydrophilic polymer and comprising the following step:
Reinforced staining procedure,
Under the normal temperature, with described dyestuff, dispersion levelling agent, acetic acid, hydrophilic polyester and polyether block copolymer are mixed into treatment fluid with bath raio 1:10-20 and cloth are dyeed;
The temperature reaction step;
The cooling reduction clearing step; With
Oven dry and setting step.
The preparation method of the hydrophobic polyester fabric of described a kind of high water absorbent quick-drying, described temperature reaction step is for being warmed up to 130 ℃ and kept 60 minutes.
The preparation method of the hydrophobic polyester fabric of described a kind of high water absorbent quick-drying in the described cooling reduction clearing step, adds successively in treatment fluid and comprises sodium dithionite, sodium carbonate and aliphatic amine polyoxyethylene ether step.
The preparation method of described a kind of high water absorbent quick-drying terylene fabric, described reduction clearing step is to handle 15 minutes down at 80 ℃.
A kind of preparation method of high water absorbent quick-drying terylene fabric, it comprises pads processing method and hydrophilic polyester and polyether block copolymer, and comprises the following steps;
Add in the padding liquid hydrophilic polyester and polyether block copolymer and the step of disperseing;
Cloth is padded treatment step in padding liquid;
The step of taking out the cloth after handling and drying; With the setting step.
The preparation method of described a kind of high water absorbent quick-drying terylene fabric, the described liquid carrying rate that pads processing method is 80%.
The preparation method of described a kind of high water absorbent quick-drying terylene fabric, the temperature of described baking step are 100 ℃, and drying time is 3 minutes.
The preparation method of described a kind of high water absorbent quick-drying terylene fabric, the setting temperature of described setting step is 120 ℃~190 ℃, fixing time is 0.5-3 minute.
The present invention adopts the special-purpose wash fast suction of hydrophilic polymer finishing agent hydrophobic property terylene/absorbing sweat quick-drying, has soft hand feeling, antistatic property is good, also have hydrophilic easy decontamination and anti-effect of staiing, the appearance effect that improves snugness of fit greatly and take performance and clothes.
The specific embodiment
The invention discloses hydrophobic polyester fabric of a kind of high water absorbent quick-drying and preparation method thereof: a kind of high water absorbent quick-drying terylene fabric, it is made up of hydrophobicity polyster fibre and hydrophily inlay and break copolymer, described lining is that the hydrophobicity polyster fibre carries out surface modification by hydrophilic polyester and polyether block copolymer and forms, the molecular formula of this block polymer is CnHmOx, wherein, n=100-500, m=200-1000, x=50-200.
The physical and chemical performance of described hydrophilic polyester and polyether block copolymer is as follows:
Outward appearance: milky white liquid
Ionic: nonionic
Viscosity: 100mPas following (25 ℃)
PH:6.0 ± 0.5 (stoste)
Dissolubility: be soluble in the normal-temperature water
The hydrophobic polyester fabric of described a kind of high water absorbent quick-drying, described polyester is a polyethylene terephthalate, described polyethers is a polyglycol ether.
A kind of method for preparing lining of the present invention is:
It comprises that DISPERSE DYES, aliphatic alcohol polyethenoxy ester are as disperseing levelling agent, acetic acid and hydrophilic polymer and comprising the following step:
Reinforced staining procedure,
Under the normal temperature, with described dyestuff, dispersion levelling agent, acetic acid, hydrophilic polyester and polyether block copolymer are mixed into padding liquid with bath raio 1:10-20 and cloth are dyeed, and present embodiment is 1:16;
Temperature reaction step: be warmed up to 130 ℃ and kept 60 minutes;
Cooling reduction clearing step: in treatment fluid, add successively and comprise sodium dithionite, sodium carbonate and aliphatic amine polyoxyethylene ether; With
Reduction clearing step: handled 15 minutes down at 80 ℃.
The another kind of method for preparing lining of the present invention is:
A kind of preparation method of high water absorbent quick-drying terylene fabric, it comprises pads processing method and hydrophilic polyester and polyether block copolymer, and the described processing method liquid carrying rate that pads is 80%, and comprises the following steps;
Add in the padding liquid hydrophilic polyester and polyether block copolymer and the step of disperseing;
Cloth is padded treatment step in padding liquid;
The step of taking out the cloth after handling and drying; The temperature of described oven dry is 100 ℃, and drying time is 3 minutes;
The setting step: setting temperature is 120 ℃~190 ℃, and fixing time is 0.5-3 minute, preferred 155 ℃ 2.5 minutes.
Water imbibition and drying time such as table 1:
The water imbibition of table 1 cloth of the present invention and drying time are shown
Water imbibition (second) | Drying time (minute) | |
Method of testing | Adidas 6.04 | Adidas 6.07 |
Lining is untreated | Greater than 30 | Greater than 60 |
Handle lining washing 0 time | 1 | 16 |
Handle lining washing 5 times | 1 | 18 |
Handle lining washing 10 times | 1 | 20 |
Annotate: (1) method for washing is according to adidas 4.02
(2) the adidas water imbibition required less than 3 seconds
(3) adidas requires less than 30 minutes drying time
Those of ordinary skill in the art will be appreciated that, above embodiment is used for illustrating claim of the present invention, and be not to be used as limitation of the invention, as long as in connotation scope of the present invention, all will drop in claims scope of the present invention variation, the modification of the above embodiment.
Claims (10)
1. high water absorbent quick-drying terylene fabric, it is made up of hydrophobicity polyster fibre and hydrophily inlay and break copolymer, it is characterized in that, described lining is that the hydrophobicity polyster fibre carries out surface modification by hydrophilic polyester and polyether block copolymer and forms, the molecular formula of this block polymer is CnHmOx, wherein, and n=100-500, m=200-1000, x=50-200.
2. a kind of high water absorbent quick-drying terylene fabric according to claim 1 is characterized in that, described polyester is a polyethylene terephthalate, and described polyethers is a polyglycol ether.
3. the preparation method of a kind of high water absorbent quick-drying terylene fabric according to claim 1 and 2 is characterized in that, it comprises that DISPERSE DYES, aliphatic alcohol polyethenoxy ester are as disperseing levelling agent, acetic acid and hydrophilic polymer and comprising the following step:
Reinforced staining procedure,
Under the normal temperature, with described dyestuff, dispersion levelling agent, acetic acid, hydrophilic polyester and polyether block copolymer are mixed into treatment fluid with bath raio 1:10-20 and cloth are dyeed;
The temperature reaction step;
The cooling reduction clearing step; With
Oven dry and setting step.
4. the preparation method of a kind of high water absorbent quick-drying terylene fabric according to claim 3 is characterized in that, described temperature reaction step is for being warmed up to 130 ℃ and kept 60 minutes.
5. the preparation method of a kind of high water absorbent quick-drying terylene fabric of stating according to claim 3 is characterized in that, in the described cooling reduction clearing step, adds successively in treatment fluid and comprises sodium dithionite, sodium carbonate and aliphatic amine polyoxyethylene ether step.
6. the preparation method of a kind of high water absorbent quick-drying terylene fabric according to claim 3 is characterized in that, described reduction clearing step is to handle 15 minutes down at 80 ℃.
7. the preparation method of a kind of high water absorbent quick-drying terylene fabric according to claim 1 and 2 is characterized in that, it comprises pads processing method and hydrophilic polyester and polyether block copolymer, and comprises the following steps;
Add in the padding liquid hydrophilic polyester and polyether block copolymer and the step of disperseing;
Cloth is padded treatment step in padding liquid;
The step of taking out the cloth after handling and drying; With the setting step.
8. the preparation method of a kind of high water absorbent quick-drying terylene fabric according to claim 7 is characterized in that, the described liquid carrying rate that pads processing method is 80%.
9. the preparation method of a kind of high water absorbent quick-drying terylene fabric according to claim 7 is characterized in that, the temperature of described baking step is 100 ℃, and drying time is 3 minutes.
10. the preparation method of a kind of high water absorbent quick-drying terylene fabric according to claim 7 is characterized in that, the setting temperature of described setting step is 120 ℃~190 ℃, and fixing time is 0.5-3 minute.