CN101463290A - Bubble candle and preparation thereof - Google Patents
Bubble candle and preparation thereof Download PDFInfo
- Publication number
- CN101463290A CN101463290A CNA2008102498586A CN200810249858A CN101463290A CN 101463290 A CN101463290 A CN 101463290A CN A2008102498586 A CNA2008102498586 A CN A2008102498586A CN 200810249858 A CN200810249858 A CN 200810249858A CN 101463290 A CN101463290 A CN 101463290A
- Authority
- CN
- China
- Prior art keywords
- candle
- bubble
- whipping agent
- paraffin
- auxiliary material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a bubble candle, comprising the following components by weight percentage: 90-95 percent of normal paraffin and excipient, 1-5 percent of a PP oiliness thickening agent, and 1-5 percent of a foaming agent, wherein the foaming agent is supercarbonate. The invention also provides a method for preparing the bubble candle, and bubble takes up partial space inside the candle which is prepared by the method of the invention, so that the candle has a loose structure and optimized performance, can be burnt cleanly and stably, and the residual amount of the candle after burning out can be reduced.
Description
Technical field
The present invention relates to a kind of bubble candle, the candle of bubble is contained in specifically a kind of inside, especially also relates to its preparation method, belongs to field of fine chemical.
Background technology
In ancient times, the illuminating effect of candle is very important.But in today, candle then more has been endowed emotion, for example lovers make an appointment, the birthday dinner, to the mourning for of ghost, to praying of future or the like, particularly in commemoration day and celebrating date, people just can light candle.
The kind of candle production has a lot, generally can be divided into daily illuminating bright candle and artwork candle two big classes according to application target.Illuminating bright candle is fairly simple, generally is exactly pole shape candle.Artistic taper and candle generally melts novelty, ornamental, ornamental, functional in one, can segment a variety ofly, at first can be divided into jelly artistic taper and candle and perfume artistic taper and candle two classes.Secondly also have, show versicolor candle (as birthday candle) because of adding batching, the candle (as spirrillum, digital shape etc.) of the different shape of making because of needs, numerous.The main raw material of candle is a paraffin now, and the auxiliary material of interpolation has white oil, stearic acid, and polyethylene, essence etc., concrete interpolation will be decided on the candle of producing what kind.The manufacture craft of above-mentioned various candles is generally taked the mode of high temperature cast molding, prepared candle structure is tight, be solid homogeneous mass, make that the candle wick that goes out often appears flooding in candle in combustion processes, the gutterings of a candle flows over and the candle afterburnt remains problems such as a large amount of waxes.
Summary of the invention
At the deficiencies in the prior art, technical problem to be solved by this invention is, a kind of bubble candle and preparation method thereof is provided, make candle structure loose, optimize performance, can clean stable burning and reduce the residual wax amount in candle afterburnt.
For solving the problems of the technologies described above, the technical solution used in the present invention is, a kind of bubble candle comprises whipping agent, PP oiliness thickening material and paraffin and auxiliary material commonly used, and the shared weight part of its each component is: 90-95% paraffin and auxiliary material; 1-5%PP oiliness thickening material; The 1-5% whipping agent; Whipping agent is a supercarbonate.
Above-mentioned bubble candle, its whipping agent is a bicarbonate of ammonia.
A kind of preparation method of above-mentioned bubble candle, carry out as follows:
A, by conventional method with the fusing of paraffin and auxiliary material;
B, liquation is warmed up to 90-95 ℃, adds PP oiliness thickening material, mix by prescription;
C, mixed solution is cooled to 60-65 ℃, stir fast and disperse down to add whipping agent, pour in the fetal membrane cooling forming after mixing.
The preparation method of above-mentioned bubble candle, carry out as follows:
A, by conventional method with the fusing of paraffin and auxiliary material;
B, liquation is warmed up to 90 ℃, adds PP oiliness thickening material, mix by prescription;
C, mixed solution is cooled to 60 ℃, stir fast and disperse down to add whipping agent, pour in the fetal membrane cooling forming after mixing.
The contriver is according to foam theory, adjust the viscosity and the density of wax liquation by using additive, in high temperature wax liquid, add a kind of material of meeting thermogenesis gas, and pass through to adjust the viscosity of wax liquid system with the free speed of control bubble, the part bubble is enclosed in the wax liquid, introduce a kind of novel process for candlemaking, made the extensively alveolate candle of distribution of a kind of inside.Because bubble accounts for the segment space of tool candle inside, make candle structure loose, thereby reach the purpose of optimizing the candle combustion performance, reducing the residual wax amount in candle afterburnt.The present invention meets the theory of economical environment-protective.
Raw material involved in the present invention is the raw material that the industry is known all available from market.
The present invention does not relate to specific equipment, and related detection method is industry customary way.
Embodiment
The present invention is further described below in conjunction with specific embodiment.
The principle of institute of the present invention foundation:
Bubble is the same with other objects to be subjected to buoyancy function in wax liquid.Its buoyancy can calculate by following formula: F=4 π r
3(ρ
1-ρ
2) g/3 (1)
Wherein: F-buoyancy (dyn); The radius of r-bubble (cm); G-universal gravity constant (cm/s
2);
ρ
1-density of liquid (g/cm
3); ρ
2Density (the g/cm of gas in the-bubble
3).
By Stokes'theorem, the bubble needed power that rises in liquid is:
F＝6π?ηrV (2)
Wherein: the viscosity of η-liquid (pool); The lift velocity of V-bubble (cm/s);
Can draw the lift velocity of bubble by (1), (2) formula:
V＝2r
2g(ρ
1-ρ
2)/9η (3)
According to calculation result, by using additive adjustment prescription, and then adjust the viscosity and the density of wax liquid, just can control the bubble speed of dissociating, make that inside still can keep some bubbles behind the candle molding.
Embodiment 1
With 93 gram paraffin and auxiliary material fusing, liquation is warmed up to 90 ℃ by conventional method, adds 3 gram PP oiliness thickening materials, continue to stir, mix; Mixed solution is cooled to 60 ℃ then, stir fast and disperse to add 4 gram bicarbonate of ammonia down, pour in the fetal membrane after mixing, cooling forming makes the foaming candle.
Embodiment 2
With 90 gram paraffin and auxiliary material fusing, liquation is warmed up to 95 ℃ by conventional method, adds 5 gram PP oiliness thickening materials, continue to stir, mix; Mixed solution is cooled to 65 ℃ then, stir fast and disperse to add 5 gram bicarbonate of ammonia down, pour in the fetal membrane after mixing, cooling forming makes the foaming candle.
Embodiment 3
With 95 gram paraffin and auxiliary material fusing, liquation is warmed up to 90 ℃ by conventional method, adds 1 gram PP oiliness thickening material, continue to stir, mix; Mixed solution is cooled to 60 ℃ then, stir fast and disperse to add 4 gram bicarbonate of ammonia down, pour in the fetal membrane after mixing, cooling forming makes the foaming candle.
Embodiment 4
With 95 gram paraffin and auxiliary material fusing, liquation is warmed up to 92 ℃ by conventional method, adds 4 gram PP oiliness thickening materials, continue to stir, mix; Mixed solution is cooled to 63 ℃ then, stir fast and disperse to add 1 gram bicarbonate of ammonia down, pour in the fetal membrane after mixing, cooling forming makes the foaming candle.
The candle that the various embodiments described above make, bubble the have accounted for tool segment space of candle inside makes that candle structure is loose, performance optimization, can clean stable burning and reduce the residual wax amount in candle afterburnt.
Claims (4)
1, a kind of bubble candle comprises whipping agent, PP oiliness thickening material and paraffin and auxiliary material commonly used, and the shared weight part of its each component is: 90-95% paraffin and auxiliary material; 1-5%PP oiliness thickening material; The 1-5% whipping agent; Described whipping agent is a supercarbonate.
2, bubble candle according to claim 1 is characterized in that: its whipping agent is a bicarbonate of ammonia.
3, a kind of preparation method of bubble candle, carry out as follows:
A, by conventional method with the fusing of paraffin and auxiliary material;
B, liquation is warmed up to 90-95 ℃, adds PP oiliness thickening material, mix by prescription;
C, mixed solution is cooled to 60-65 ℃, stir fast and disperse down to add whipping agent, pour in the fetal membrane cooling forming after mixing.
4, preparation method according to claim 3, carry out as follows:
A, by conventional method with the fusing of paraffin and auxiliary material;
B, liquation is warmed up to 90 ℃, adds PP oiliness thickening material, mix by prescription;
C, mixed solution is cooled to 60 ℃, stir fast and disperse down to add whipping agent, pour in the fetal membrane cooling forming after mixing.