CN101457485A - 一种筒子纱染色工艺 - Google Patents

一种筒子纱染色工艺 Download PDF

Info

Publication number
CN101457485A
CN101457485A CNA200810236324XA CN200810236324A CN101457485A CN 101457485 A CN101457485 A CN 101457485A CN A200810236324X A CNA200810236324X A CN A200810236324XA CN 200810236324 A CN200810236324 A CN 200810236324A CN 101457485 A CN101457485 A CN 101457485A
Authority
CN
China
Prior art keywords
dyeing
weight concentration
enzyme
bobbin
isomery alcohol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA200810236324XA
Other languages
English (en)
Inventor
何培富
王洪明
牧永权
王亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Fuchun Dye and Weave Co Ltd
Original Assignee
Wuhu Fuchun Dye and Weave Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Fuchun Dye and Weave Co Ltd filed Critical Wuhu Fuchun Dye and Weave Co Ltd
Priority to CNA200810236324XA priority Critical patent/CN101457485A/zh
Publication of CN101457485A publication Critical patent/CN101457485A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种筒子纱染色工艺，所述的染色工艺包括前处理染色工序、后处理工序、烘干工序，在前处理染色工序中加入复合炼染酶，所述的复合炼染酶含有重量浓度为10－12％C13异构醇表面活性剂、重量浓度12－14％异构醇非离子磺化改变成阴离子表面活性渗透剂、重量浓度为7－9％维素酶，其余为水。本发明与现有技术相比，通过采用特定的复合炼染酶，将传统的前处理及染色工序合二为一，每吨筒子纱的用水为30－36吨，具有节水减排，生产效率高的特点。

Description

一种筒子纱染色工艺
技术领域
本发明属于染色工艺这一技术领域，特别属于一种筒子纱染色工艺。
背景技术
目前节能型筒子纱染色工艺通常是采用生物酶制剂的前处理工艺，相对传统的碱氧前处理在节能减排上有了较大的改进，但在实际生产应用过程中还是存在以下的问题：
1、前处理与染色仍然是两个独立的工序，依然存在多次升温、排液，势必造成水资源的消耗和能源的浪费。
2、纯生物酶制剂的活性保存条件较为苛刻，对PH值、温度等条件敏感，工艺稳定性较差，造成实际生产过程中的一次成功率降低，进而影响到生产效率和节能减排。
发明内容
本发明所要解决的技术问题是提供一种节水的筒子纱染色工艺。
本发明解决技术问题的技术方案为：一种筒子纱染色工艺，所述的染色工艺包括前处理染色工序、后处理工序、烘干工序，在前处理染色工序中加入复合炼染酶，所述的复合炼染酶含有重量浓度为10-12％C13异构醇表面活性剂、重量浓度12-14％异构醇非离子磺化改变成阴离子表面活性渗透剂、重量浓度为7-9％维素酶，其余为水。
优选的复合炼染酶含有重量浓度为10％C13异构醇表面活性剂、重量浓度12％异构醇非离子磺化改变成阴离子表面活性渗透剂、重量浓度为9％维素酶，其余为水。
所述的异构醇表面活性剂、异构醇非离子磺化改变成阴离子表面活性渗透剂由沙索(中国)化学有限公司生产。
所述的前处理染色工序为：浴液初始PH值6.5-7.5，温度为60-65℃、浴比为1：6-6.5、处理时间为120-160分钟、染料的重量百分浓度为2-8％。
所述的染料为COLVAZOL，由上海科华染料工业有限公司生产；
所述的筒子纱为全棉、竹纤维、莫代尔、粘胶。
本发明与现有技术相比，通过采用特定的复合炼染酶，将传统的前处理及染色工序合二为一，每吨筒子纱的用水为30-36吨，具有节水减排，生产效率高的特点。
具体实施方式
下面结合实施例对本发明作详细的说明。
本发明的水洗色牢度按照GB/T3921.1-1997进行检测；
磨擦牢度按照GB/T3920-1997进行检测；
耐汗渍色牢度按照GB/T3922-1997进行检测；
所述的染料为COLVAZOL，由上海科华染料工业有限公司生产。
所述的异构醇表面活性剂、异构醇非离子磺化改变成阴离子表面活性渗透剂由沙索(中国)化学有限公司生产
实施例1：
全棉纱：规格为C32S/1，产量2400公斤，
所述的染色工艺包括前处理染色工序、后处理工序、烘干工序，
所述的前处理染色工序中的初如浴液PH值为7.3，浴比1：6，先在浴槽中注入浓度为1.5克/升的复合炼染酶，所述的复合炼染酶含有重量浓度为10％C13异构醇表面活性剂、重量浓度12％异构醇非离子磺化改变成阴离子表面活性渗透剂、重量浓度为7％维素酶，其余为水，升温到60℃，泵速为1500r/min，保温30分钟，注入染料COLVAZOL，染料的重量百分浓度为6％，保温16分钟，加入硫酸钠，硫酸钠的浓度为80克/升，保温16分钟，再加入复合固色碱，复合固色碱的浓度为3克/升，保温90分钟，排液，即可。
所述的复合固色碱为常用的碳酸钠、烧碱、缓冲剂的混合物。
所述的后处理工序包括清洗工序、PH调节工序、柔软工序。
后处理工序、烘干工序均为现有技术。
实施例1的产品合格率为99％，其水洗色牢度为：变色4-5级、沾色4级；磨擦色牢度为：干4级，湿2-3级；耐汗渍色牢度为：酸3级、碱4级。
实施例2：
竹纤维：规格为B31S/1，产量1074公斤，
所述的染色工艺包括前处理染色工序、后处理工序、烘干工序，
所述的前处理染色工序中的初如浴液PH值为6.8，浴比1：6，先在浴槽中注入浓度为1.5克/升的复合炼染酶，所述的复合炼染酶含有重量浓度为12％C13异构醇表面活性剂、重量浓度14％异构醇非离子磺化改变成阴离子表面活性渗透剂、重量浓度为9％维素酶，其余为水，升温到60℃，泵速为1500r/min，保温30分钟，注入染料COLVAZOL，染料的重量百分浓度为2.3％，保温16分钟，加入硫酸钠，硫酸钠的浓度为40克/升，保温16分钟，再加入复合固色碱，复合固色碱的浓度为2克/升，固色保温60分钟，排液，即可。
所述的后处理工序包括清洗工序、PH调节工序、柔软工序。
后处理工序、烘干工序均为现有技术。
实施例2的产品合格率为97％，其水洗色牢度为：变色4-5级、沾色4-5级；磨擦色牢度为：干4-5级，湿3级；耐汗渍色牢度为：酸4级、碱4级。

Claims (5)

1、一种筒子纱染色工艺，所述的染色工艺包括前处理染色工序、后处理工序、烘干工序，其特征在于：在前处理染色工序中加入复合炼染酶，所述的复合炼染酶含有重量浓度为10-12％ C13异构醇表面活性剂、重量浓度12-14％异构醇非离子磺化改变成阴离子表面活性渗透剂、重量浓度为7-9％维素酶，其余为水。
2、根据权利要求1所述的一种筒子纱染色工艺，其特征在于：所述的的复合炼染酶含有重量浓度为10％ C13异构醇表面活性剂、重量浓度12％异构醇非离子磺化改变成阴离子表面活性渗透剂、重量浓度为9％维素酶，其余为水。
3、根据权利要求1、2所述的一种筒子纱染色工艺，其特征在于：所述的前处理染色工序为：浴液初始PH值6.5-7.5，温度为60-65℃、浴比为1：6-6.5、处理时间为120-160分钟、染料的重量百分浓度为2-8％。
4、根据权利要求3所述的一种筒子纱染色工艺，其特征在于：所述的染料为COLVAZOL，由上海科华染料工业有限公司生产
5、根据权利要求1或2所述的一种筒子纱染色工艺，其特征在于：所述的筒子纱为全棉、竹纤维、莫代尔、粘胶。
CNA200810236324XA 2008-11-07 2008-11-07 一种筒子纱染色工艺 Pending CN101457485A (zh)