CN101445891B - 汽车空调用导向瓦及其制备方法 - Google Patents
汽车空调用导向瓦及其制备方法 Download PDFInfo
- Publication number
- CN101445891B CN101445891B CN2008102427063A CN200810242706A CN101445891B CN 101445891 B CN101445891 B CN 101445891B CN 2008102427063 A CN2008102427063 A CN 2008102427063A CN 200810242706 A CN200810242706 A CN 200810242706A CN 101445891 B CN101445891 B CN 101445891B
- Authority
- CN
- China
- Prior art keywords
- powder
- guide tile
- air conditioner
- automotive air
- sintering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种汽车空调用导向瓦,尤其是一种汽车空调用导向瓦及其制备方法。按照本发明提供的技术方案,所述汽车空调用导向瓦,包含如下重量百分含量的各组分:铁为94.2%~96.4%,碳为0.15%~0.25%,镍为1.5%~2.5%,钼为0.45%~0.55%,铜为1.5%~2.5%。上述汽车空调用导向瓦的制备方法包含:混合粉料、模压、烧结、整形与渗碳热处理等步骤。本发明的导向瓦在韧性及耐磨性方面均有较大提高。
Description
技术领域
本发明公开了一种汽车空调用导向瓦,尤其是一种汽车空调用导向瓦及其制备方法。
背景技术
汽车空调中,导向球内孔与导向杆配合,外径与导向瓦配合镶在摇盘导向孔内。压缩机工作时,导向球在导向杆上左右滑动,实现摇盘的摆动,摇盘的摆动带动活塞做往复直线运动,从而实现吸排气功能达到压缩机制冷效果。
导向球故障会使摇盘无法实现摆动,内部件运转失常,在短时间内严重损坏导致压缩机卡死继而无法实现制冷功能,具体表现为:
导向球内孔偏小会导致导向球在导向杆上运动不灵活,致使摇盘摆动受阻,严重时出现卡死现象,压缩机失效。导向球内孔偏大时会造成导向球在导向杆上滑动时定向不好,严重时影响压缩机的噪声甚至容易使导向瓦从摇盘中脱出,造成内部件运动失常而损坏。
导向球外径偏大时会造成与导向瓦配合装入摇盘时运动不灵活,增大压缩机的扭矩,严重时压缩机卡死失效。外径过大还会造成与导向瓦配合时无法装入摇盘。导向球外径过小时与导向瓦配合装入摇盘时配合间隙过大,会造成导向瓦连带导向球容易从摇盘中脱出,导致压缩机失效。
目前,一般的导向瓦在韧性及耐磨性方面均较差。
发明内容
本发明的目的是克服现有技术中存在的不足,提供一种在韧性及耐磨性方面均有较大提高的汽车空调用导向瓦。
本发明的另一目的则是提供一种汽车空调用导向瓦的制备方法。
按照本发明提供的技术方案,所述汽车空调用导向瓦,包含如下重量百分含量的各组分:铁为94.2%~96.4%,碳为0.15%~0.25%,镍为1.5%~2.5%,钼为0.45%~0.55%,铜为1.5%~2.5%。
上述汽车空调用导向瓦的制备方法包含如下步骤:
a、将铁粉、镍粉、钼粉、铜粉与碳粉及硬脂酸锌加入容器内,搅拌均匀,形成混合物;每种粉料占粉料总重量的重量百分比为:铁粉94.2%~96.4%、镍粉1.5%~2.5%、钼粉0.45%~0.55%、铜粉1.5%~2.5%与碳粉0.15%~0.25%;再加入占粉料总重量的0.6~0.8%倍的硬脂酸锌;
b、将步骤a得到的混合物置于粉末冶金成型机的成型模具型腔内模压出坯料,模压时的压力以使坯料的密度达7.3~7.5g/cm3为宜;
c、将步骤b所得坯料在炉膛温度为1120~1150℃的烧结炉内进行烧结,烧结时往炉膛内通入甲烷,甲烷的通入量控制在5.9~6.9cm3/min,坯料的烧结时间控制在12~14小时,得到粗品;
d、将步骤c得到的粗品置于整形模具内模压整形;
e、将整形后的粗品放入热处理炉内进行渗碳热处理,使其HRC硬度达到25~37。
本发明的导向瓦在韧性及耐磨性方面均有较大提高。
具体实施方式
下面结合具体实施例对本发明作进一步说明。
实施例1
a、取94.2kg的铁粉、2.5kg的镍粉、0.55kg的钼粉、2.5kg的铜粉与0.25kg的碳粉五种粉料备用;
b、取步骤a所述的五种粉料总重量0.6kg的硬脂酸锌备用;
c、将步骤b的硬脂酸锌加入步骤a的粉料中并搅拌均匀,形成混合物;
d、将步骤c得到的混合物置于成型模具型腔内模压出坯料,控制坯料的密度为7.0g/cm3;
e、将步骤d所得坯料在炉膛温度为1120℃的烧结炉内进行烧结,烧结时往炉膛内通入甲烷,甲烷的通入量控制在5.9cm3/min,坯料的烧结时间控制在12小时,得到粗品;
f、将步骤e得到的粗品置于整形模具内模压整形;
g、将整形后的粗品放入热处理炉内进行渗碳热处理,使其HRC硬度达到25~37。
使制得的汽车空调用导向瓦包含如下重量百分含量的各组分:铁为94.2%,碳为0.25%,镍为1.5%,钼为0.45%,铜为1.5%。
将制得的导向瓦在万能实验机上进行压溃强度测试,具体结果如下:
导向瓦硬度为HRC35时,所测得的压溃强度为6KN;
导向瓦硬度为HRC30时,所测得的压溃强度为8KN;
导向瓦硬度为HRC26时,所测得的压溃强度为10KN。
实施例2
a、取96.4kg的铁粉、1.5kg的镍粉、0.45kg的钼粉、1.5kg的铜粉与0.15kg的碳粉五种粉料备用;
b、取步骤a所述的五种粉料总重量0.8kg的硬脂酸锌备用;
c、将步骤b的硬脂酸锌加入步骤a的粉料中并搅拌均匀,形成混合物;
d、将步骤c得到的混合物置于成型模具型腔内模压出坯料,控制模压出的坯料的密度为7.1g/cm3;
e、将步骤d所得坯料在炉膛温度为1150℃的烧结炉内进行烧结,烧结时往炉膛内通入甲烷,甲烷的通入量控制在6.9cm3/min,坯料的烧结时间控制在14小时,得到粗品;
f、将步骤e得到的粗品置于整形模具内模压整形;
g、将整形后的粗品放入热处理炉内进行渗碳热处理,使其HRC硬度达到25~37。
使制得的汽车空调用导向瓦包含如下重量百分含量的各组分:铁为96.4%,碳为0.15%,镍为1.5%,钼为0.45%,铜为1.5%。
将制得的导向瓦在万能实验机上进行压溃强度测试,具体结果如下:
导向瓦硬度为HRC36时,所测得的压溃强度为8KN;
导向瓦硬度为HRC30时,所测得的压溃强度为12KN;
导向瓦硬度为HRC26时,所测得的压溃强度为14KN。
实施例3
a、取95.2kg的铁粉、2kg的镍粉、0.5kg的钼粉、2kg的铜粉与0.2kg的碳粉五种粉料备用;
b、取步骤a所述的五种粉料总重量0.7kg的硬脂酸锌备用;
c、将步骤b的硬脂酸锌加入步骤a的粉料中并搅拌均匀,形成混合物;
d、将步骤c得到的混合物置于成型模具型腔内模压出坯料,控制模压出的坯料的密度为7.3g/cm3;
e、将步骤d所得坯料在炉膛温度为1135℃的烧结炉内进行烧结,烧结时往炉膛内通入甲烷,甲烷的通入量控制在6.4cm3/min,坯料的烧结时间控制在13小时,得到粗品;
f、将步骤e得到的粗品置于整形模具内模压整形;
g、将整形后的粗品放入热处理炉内进行渗碳热处理,使其HRC硬度达到25~37。
使制得的汽车空调用导向瓦包含如下重量百分含量的各组分:铁为95.3%,碳为0.2%,镍为2%,钼为0.5%,铜为2%。
将制得的导向瓦在万能实验机上进行压溃强度测试,具体结果如下:
导向瓦硬度为HRC35时,所测得的压溃强度为8KN;
导向瓦硬度为HRC32时,所测得的压溃强度为12KN;
导向瓦硬度为HRC26时,所测得的压溃强度为14KN。
从以上实施例及压溃强度破坏性实验数据表明,密度达到7.0g/cm3以上,所得到的产品性能就能满足产品使用要求;产品密度越高,所得到的产品性能就越好。即本发明的导向瓦在韧性及耐磨性方面均有较大提高。
Claims (2)
1.一种汽车空调用导向瓦的制备方法,其特征是:所述方法包含如下步骤:
a、将铁粉、镍粉、钼粉、铜粉与碳粉及硬脂酸锌加入容器内,搅拌均匀,形成混合物;每种粉料占粉料总重量的重量百分比为:铁粉94.2%~96.4%、镍粉1.5%~2.5%、钼粉0.45%~0.55%、铜粉1.5%~2.5%与碳粉0.15%~0.25%;再加入占粉料总重量的0.6%~0.8%倍的硬脂酸锌;
b、将步骤a得到的混合物置于粉末冶金成型机的成型模具型腔内模压出坯料,控制坯料的密度为7.3~7.5g/cm3;
c、将步骤b所得坯料在炉膛温度为1120~1150℃的烧结炉内进行烧结,烧结时往炉膛内通入甲烷,甲烷的通入量控制在5.9~6.9cm3/min,坯料的烧结时间控制在12~14小时,得到粗品;
d、将步骤c得到的粗品置于整形模具内模压整形;
e、将整形后的粗品放入热处理炉内进行渗碳热处理,使其HRC硬度达到25~37。
2.利用权利要求1所述方法生产的汽车空调用导向瓦,其特征是,该导向瓦包含如下重量百分含量的各组分:铁为94.2%~96.4%,碳为0.15%~0.25%,镍为1.5%~2.5%,钼为0.45%~0.55%,铜为1.5%~2.5%。