CN101445678B - 一种炼钢转炉氧枪用防粘涂料 - Google Patents

一种炼钢转炉氧枪用防粘涂料 Download PDF

Info

Publication number
CN101445678B
CN101445678B CN2008102469297A CN200810246929A CN101445678B CN 101445678 B CN101445678 B CN 101445678B CN 2008102469297 A CN2008102469297 A CN 2008102469297A CN 200810246929 A CN200810246929 A CN 200810246929A CN 101445678 B CN101445678 B CN 101445678B
Authority
CN
China
Prior art keywords
percent
oxygen lance
steel slag
wedding agent
weight percentage
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2008102469297A
Other languages
English (en)
Other versions
CN101445678A (zh
Inventor
孙中强
陆彩云
芮树森
冯新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Northeastern University Metallurgical Technology Institute Co Ltd
Original Assignee
METALLURGY TECHNOLOGY RESEARCH INSTITUTE Co Ltd NORTHEAST UNIVERSITY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by METALLURGY TECHNOLOGY RESEARCH INSTITUTE Co Ltd NORTHEAST UNIVERSITY filed Critical METALLURGY TECHNOLOGY RESEARCH INSTITUTE Co Ltd NORTHEAST UNIVERSITY
Priority to CN2008102469297A priority Critical patent/CN101445678B/zh
Publication of CN101445678A publication Critical patent/CN101445678A/zh
Application granted granted Critical
Publication of CN101445678B publication Critical patent/CN101445678B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种炼钢转炉氧枪用防粘涂料，由耐火粉料与结合剂组成，按重量百分比耐火粉料30～50％、结合剂50～70％，所述耐火粉料由以下原料构成：按重量百分比为土状石墨40～70％、高铝矾土10～30％、广西泥5～15％、膨润土3～8％、甲基纤维素3～8％；所述结合剂为水基结合剂，由以下原料构成：按重量百分比为黄糊精15～30％、烧碱8～15％、硼酸5～15％。本发明解决了炼钢转炉氧枪表面严重粘钢渣及其刮除困难的问题。氧枪涂料隔绝钢渣与氧枪本体的直接接触，与钢渣润湿性较差的涂料使溅射到氧枪表面上的钢渣的粘结性能变差，经由氧枪刮渣器刮除后，氧枪上已基本不再粘结钢渣，这使得工人的劳动强度大大降低，并消除了用钎子除渣带来的安全隐患。

Description

一种炼钢转炉氧枪用防粘涂料
技术领域
本发明属于冶金技术领域，特别涉及一种炼钢转炉氧枪用防粘涂料。
背景技术
转炉氧枪的工作环境十分恶劣，在每炉20分钟左右的炼钢过程中，它要承受CO、CO2和O2等炉气组成变化所引起的氧化、还原气氛的变化以及钢渣的喷溅和侵蚀、炉内温度、喷溅钢水和炉渣成分等的巨大变化。
由于转炉自身的生产特点，转炉氧枪表面普遍存在粘结钢渣的问题。粘结钢渣严重时会造成氧枪提不出炉口(因粘枪的冷钢卡在氮封口上出不来)，此时就造成炉子不能倾动，影响吹炼操作；其次，严重粘枪时会破坏氧枪传动***的配重平衡，甚至会使氧枪无法提升(当粘结钢渣重量加上氧枪自重大于配重重量时氧枪就无法提升)。
发明内容
针对转炉氧枪表面普遍存在的粘结钢渣问题，本发明提供一种防粘涂料，使氧枪一方面少粘渣，另一方面使粘渣刮除容易。
本发明炼钢转炉氧枪喷涂料，由耐火粉料和结合剂构成。耐火粉料由以下原料组成：按重量百分比为土状石墨40～70％、高铝矾土10～30％、广西泥5～15％、膨润土3～8％、甲基纤维素3～8％；结合剂为水基结合剂，由以下原料组成：以水为基准，按重量百分比为黄糊精15～30％、烧碱8～15％、硼酸5～15％；涂料按重量百分比耐火粉料30～50％、结合剂50～70％。
本发明解决了炼钢转炉氧枪表面严重粘钢渣及其刮除困难的问题。氧枪涂料隔绝钢渣与氧枪本体的直接接触，与钢渣润湿性较差的涂料使溅射到氧枪表面上的钢渣的粘结性能变差，经由氧枪刮渣器刮除后，氧枪上已基本不再粘结钢渣，这使得工人的劳动强度大大降低，并消除了用钎子除渣带来的安全隐患。
具体实施方式
实施例1
氧枪喷涂料由下列组分组成：按重量百分比耐火粉料包括土状石墨60％、高铝矾土20％、广西泥10％、膨润土7％、甲基纤维素3％；结合剂以水为基，由以下原料组成：黄糊精25％、烧碱15％、硼酸5％；涂料包含耐火粉料40％、结合剂60％。
首先进行结合剂的配制，将预混合均匀的结合剂粉料与水在混料机中混合30分钟，待均匀混合后，将预充分混合的耐火粉料按耐火粉料∶结合剂＝2∶3的配比配入混料机中，再混合30 分钟，制成转炉氧枪涂料，密封保存。
实施例2
氧枪喷涂料由下列组分组成：按重量百分比耐火粉料包括土状石墨50％、高铝矾土25％、广西泥15％、膨润土7％、甲基纤维素3％；结合剂以水为基，由以下原料组成：黄糊精30％、烧碱10％、硼酸10％；涂料包含耐火粉料30％、结合剂70％。
首先进行结合剂的配制，将预混合均匀的结合剂粉料与水在混料机中混合30分钟，待均匀混合后，将预充分混合的耐火粉料按耐火粉料∶结合剂＝3∶7的配比配入混料机中，再混合30分钟，制成转炉氧枪涂料，密封保存。
将制备好的两份涂料涂在某钢厂转炉氧枪上，氧枪的粘渣量均大大减少，同时氧枪上的粘渣经过刮渣器处理后，基本不留粘渣。这样不仅减轻了工人的劳动强度，也避免了人工除渣带来的安全隐患，大大提高了氧枪的使用寿命。

Claims (1)

1.一种炼钢转炉氧枪用防粘涂料，其特征在于：该涂料由耐火粉料与结合剂组成，按重量百分比耐火粉料30～50％、结合剂50～70％，所述耐火粉料由以下原料构成：按重量百分比为土状石墨40～70％、高铝矾土10～30％、广西泥5～15％、膨润土3～8％、甲基纤维素3～8％；所述结合剂为水基结合剂，由以下原料构成：以水为基准，按重量百分比为黄糊精15～30％、烧碱8～15％、硼酸5～15％。
CN2008102469297A 2008-12-30 2008-12-30 一种炼钢转炉氧枪用防粘涂料 Expired - Fee Related CN101445678B (zh)