CN1014362B - Colour holographic recording medium - Google Patents
Colour holographic recording mediumInfo
- Publication number
- CN1014362B CN1014362B CN 88101091 CN88101091A CN1014362B CN 1014362 B CN1014362 B CN 1014362B CN 88101091 CN88101091 CN 88101091 CN 88101091 A CN88101091 A CN 88101091A CN 1014362 B CN1014362 B CN 1014362B
- Authority
- CN
- China
- Prior art keywords
- film forming
- forming agent
- photosensitizer
- dry plate
- recording medium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
The present invention relates to a colored holographic recording medium which is composed of photosensitizer, film former and a film base, wherein the photosensitizer which is a photopolymerization imaging system can be widely used for multi-color holographic display of white light reproduction, colored information storage, etc. The present invention has the advantages of resolution which is larger than 4000 line pair / millimeter, diffraction efficiency which is larger than 75% when respectively recording information with red light, green light and blue light, high sensitivity, wide spectral region of full-color sensitizing, high signal-to-noise ratio, long storage life, low cost, innocuity, no pollution, simple mask-making technology, industrial production, etc.
Description
The present invention is a kind of colour holographic recording medium of photopolymerization imaging system, and the color hologram that can be widely used in white light reconstruction shows aspects such as chromatic information storage.
For many years, one of target of pursuing of holography is to obtain colored picture reproducing.Wherein, the reflection hologram of white light reconstruction is subjected to people's appreciation most.Yet, up to the present, do not develop suitable recording medium, so the color hologram of white light reconstruction is to adopt two kinds of recording medium composite methods to make.Promptly use Agfa 8E75HD silver halide holographic plate and dichromated gelatin holographic plate, make red, green, as to reach blue look image respectively, then they are superimposed together, finally form the color image that white light is penetrated again, this technical sophistication, and the diffraction efficiency of image is lower.
By literature search, netrual colour holographic recording medium still in the relevant patent of the U.S. and Japan though the recording medium of photopolymerization system is arranged, is formed part differently with the present invention, does not have both following characteristic:
Title of the present invention is BGH-2(Beijing university of technology holographic recording medium 2 types again).(647,633nm), green glow (514.5nm) and blue streak (488nm) all have light sensitivity preferably to this medium for ruddiness.
BGH-2 type holographic recording medium of the present invention possesses following characteristic:
Resolution>4000 lines right/millimeter
2. diffraction efficiency>75%(is respectively with red, green, blue streak record)
Luminous sensitivity<80 millijoules/centimetre
2(blue, green glow)
4. feel panchromatic spectral range (see Fig. 1, T% is the percentage of transmitance among the figure)
5. signal to noise ratio (S/N ratio) height,
6. storage life>6 month,
7. cost is low,
8. nontoxic, pollution-free.
The object of the present invention is to provide a kind of cost low, make simple, and the high colour holographic recording medium of diffraction efficiency.
The present invention can use the white laser of argon-Kr laser emission to write down the bright color hologram image of a width of cloth on a BGH-2; Also can use monochromatic laser (red, green, orchid) to carry out record.
The present invention adds film forming agent (1) by photosensitizer and sheet base (2) is formed, and sees shown in Figure 2.1 is photosensitizer and film forming agent among the figure, the 2nd, and the sheet base.
Photosensitizer is a vinyl monomer, spectral sensitizer, light trigger and auxiliary material are formed, film forming agent is a gelatin, polyvinyl alcohol (PVA), gum arabic, methylcellulose and various can be on the sheet base hydrophilic substance of film forming.The sheet base is substrate glass or flexible material.
Sensitizing dye visual sense light wavelength used in the present invention and deciding sees following table for details
The absorbing wavelength nm of dyestuff title dyestuff
Serge blue 668,609
Eosin 519
Uranin 494
Easin 224
The tetrachlorotetraiodofluorescein sodium 550
Acridine orange 496,467
When making photosensitizer, the ratio of red, green, blue three kinds of light intensity of launching according to laser instrument adds the sensitizing dye of two kinds or three kinds proper proportions.
The main manufacture craft of BGH-2 is, after being made into the aqueous solution of photosensitizer, with the gelatin dry plate of making by oneself or buying, in photosensitive liquid, soak sensitization 3-10 minute (15-25 ℃), by taking out the good dry plate of sensitization in the solution, 15-25 ℃ of airing 2 hours, the holographic version that performs, if do not use immediately, under the condition of relative humidity<40%, 8-12 ℃ of lucifuge stores.Need when using relative humidity as the condition of 80-90% under humidification handled 10 minutes.
The colour reflection hologram that utilizes BGH-2 to make white light reconstruction is seen following embodiment.
Example 1.
The making of BGH-2 holographic plate
1. the preparation of photosensitive liquid
Acrylamide 10g
NN ' methylene-bisacrylamide 0.5~2g
Organic multicomponent amine 1.5~3g
Serge blue 0.05~0.1g
Tetrachlorotetraiodofluorescein sodium 0.003~0.005g
Acridine orange 0.003~0.01g
Surfactant 0.005g
Ethanol 20~60ml
Water 100~150ml
2. the making of gelatin dry plate
Gelatin solution is in following ratio preparation
Gelatin 6~8g
Antiseptic 0.5g
The EDTA(ethylene dinitrilotetra-acetic acid) 0.06~0.08g
Formaldehyde 0.01~0.02g
Potassium chromium sulfate 0.02~0.05g
Ethanol 10~20ml
Distilled water 100~150ml
Gelatin solution is coated on the sheet base support equably, gets final product after the drying, thicknesses of layers depends on the needs, and is generally 10 ± 2 μ m.
3. artotype is soaked the 3-10 branch in photosensitive liquid, temperature is 15-25 ℃, dry plate is taken out at room temperature to dry up or airing then.
4. exposure.Make the light path of the reflection hologram of white light reconstruction and see Fig. 3,1 is laser instrument among the figure, and 2 is beam expanding lens, and 3 is reference light, and 4 is target, and 5 is thing light, and 6 is BGH-2.
5. aftertreatment technology is
(1) dry plate after the exposure washed 5 minutes in 20~25 ℃ of water
(2) in 50% isopropyl alcohol or ethanol, soaked 30 seconds
(3) in 80% isopropyl alcohol or ethanol, soaked 1 minute
(4) in 100% isopropyl alcohol or ethanol, soaked 2-3 minute
(5) the color hologram image that can obtain becoming clear after drying up.
Example 2.
After photosensitive liquid in the example 1 and gelatin solution mixing, be coated on the sheet base, can make the BGH-2 dry plate.
The manufacture craft of hologram is 4 in the example 1 roughly the same, and 5.
Example 3.
1. the preparation of photosensitive liquid is with example 1
2. the gelatin dry plate that adopts Tianjin sensitive film factory to make is made film forming agent and sheet base support, and the sensitization treatment process is with 3 in the example 1.
3. the making of hologram is with 4 and 5 in the example 1.
Advantage of the present invention is:
Resolution ratio>4000 lines right/millimeter,
2. diffraction efficiency height>75%,
Luminous sensitivity height<80 millijoules/centimetre2,
4. signal to noise ratio height, long>6 months of life-span,
5. cost is low, make simpler,
6. nontoxic, pollution-free.
Claims (4)
1, a kind of colour holographic recording medium is characterized in that being made up of photosensitizer, film forming agent dry plate, contains vinyl monomer, light trigger, spectral sensitizer and auxiliary material in the photosensitizer and forms, and concrete prescription is:
Acrylamide 10g
NN ' methylene-bisacrylamide 0.5~2g
Organic multicomponent amine 1.5~3g
Serge blue 0.05~0.1g
Tetrachlorotetraiodofluorescein sodium 0.003~0.005g
Acridine orange 0.003~0.01g
Surfactant 0.005~0.007g
Ethanol 20~60ml
Water 100~150ml
The film forming agent dry plate is film forming agent [1], is coated on the sheet base [2], and film forming agent [1] is gelatin, polyvinyl alcohol (PVA), gum arabic, methylcellulose and various can be on the sheet base hydrophilic substance of film forming, and be mixed with antiseptic, hardener, concrete prescription is:
Film forming agent 6~8g
Antiseptic 0.5g
EDTA (ethylene dinitrilotetra-acetic acid) 0.06~0.08g
Formaldehyde 0.01~0.02g
Potassium chromium sulfate 0.02~0.05g
Ethanol 10~20ml
Distilled water 100~150ml
Sheet base [2] is a photomechanical production glass, or the flexible sheets base done of polyester, triacetate fiber.
2, colour holographic recording medium according to claim 1 is characterized in that photosensitizer and film forming agent dry plate deposit separately respectively, before the holographic photography film forming agent dry plate is immersed in sensitization in the photosensitizer, and photosensitizer is evenly distributed in the film forming agent layer.
3, colour holographic recording medium according to claim 2 is characterized in that the dry plate that sensitization is good, should leave relative humidity in below 40%, and temperature is 8~12 ℃, needs under relative humidity is 80~90% condition humidification 10 minutes during use.
4, according to claim 3 described colour holographic recording mediums, the thicknesses of layers that it is characterized in that the film forming agent dry plate is 8~12 μ m, the size of film forming agent dry plate, and user oneself makes as required.