CN101408004A - Once-through method of aluminum-plating film resin transfer printing - Google Patents
Once-through method of aluminum-plating film resin transfer printing Download PDFInfo
- Publication number
- CN101408004A CN101408004A CNA2008102192316A CN200810219231A CN101408004A CN 101408004 A CN101408004 A CN 101408004A CN A2008102192316 A CNA2008102192316 A CN A2008102192316A CN 200810219231 A CN200810219231 A CN 200810219231A CN 101408004 A CN101408004 A CN 101408004A
- Authority
- CN
- China
- Prior art keywords
- transfer printing
- resin
- aluminizer
- once
- aluminum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a once-through method of aluminizer resin transfer printing, which is used in the thermal transfer printing technology and comprises the following steps: A. after hot melting resin is hot-melted into liquid, a photogravure press is used for printing a pattern on the aluminium layer of the aluminizer under the condition of keeping the melting state of the resin, and after being cooled to room temperature, the aluminizer is rolled up for standby; and B. when printing is needed, the surface of the aluminizer with the hot melting resin pattern is adhered on a printing stock, treated with impressing at the temperature of between 85 DEG C to 120 DEG C, and the thin film is stripped away after cooling, thus forming the finished product. The method combines the traditional transfer printing of two times, i.e., the pattern thermal transfer printing and the transfer printing of a metallic film layer plated with a metallic film, into the transfer printing of one time, the transfer printing pattern is distinct and smooth, the luster is strong, the color is abundant, and stereoscopic impression can be given.
Description
Technical field
The present invention relates to the thermal transfer printing technology.
Background technology
Fabric, the dyeing industry of leather is because of serious environment pollution, the strictly industry of restriction becomes international, but restriction in any case, wastewater treatment in what kind of factory, but all can't overcome effluxing of those a large amount of waste water, therefore impel the technical staff of all circles to remove to study the printing technique route of a new pollution-free or of low pollution, the thermal transfer printing technology has appearred thereupon, the staining technique of supercritical carbon dioxide etc., described thermal transfer printing technology also has multiple, basically all be on a kind of transfer film, to stamp resin pattern, after treating resin solidification, there is the one side of resin pattern to be attached on the fabric that will print transfer film, or on the leather, being about to the resin pattern transfer printing after hot pressing goes over, in order to make the pattern that is transferred on the fabric that good brightness be arranged, gloss then is to want the secondary transferring method, is about to be printed on the transfer film of resin pattern after curing, its resin pattern heat is transferred on the orange cold foil, treat its solidify after again heat be transferred on fabric or the leather.This thermal transfer printing does not have the waste water discharge substantially, has overcome the hard nut to crack of the serious environment pollution of traditional dyeing and finishing.But use a large amount of organic solvents in the existing thermal transfer printing, such as butanone, cyclohexanone, toluene just evaporates when the seal resin pattern in a large number, causes the workshop internal contamination serious.In addition, at sliding carrier such as the leather of seal air spots, the resin pattern air spots is sliding after the hot transfer printing, causes patterned surfaces coarse, gloss difference.
Summary of the invention
The purpose of this invention is to provide a kind of once-through method of aluminum-plating film resin transfer printing, it is the once-through method transfer printing that this method is closed And with twice transfer printing of the metallic diaphragm transfer printing of hot transfer printing of traditional pattern and metal-coated membrane, and pattern transferring is clear level and smooth, and gloss is strong, rich color has third dimension.
Technical solution of the present invention is performed such, and carries out by the following method:
A: after the thermoplastic resin hot melt become liquid, pattern is printed on the aluminium lamination of aluminizer under the resin molten condition keeping with intaglio press again, is cooled to behind the normal temperature aluminizer clot is standby;
B: when stamp, will have the thermoplastic resin pattern simultaneously to be attached on the stock on this aluminizer,, take film after the cooling off, be finished product through 85 ℃ to 120 ℃ impressions.
The above thermoplastic resin is PA (polyamide), PE (polyethylene), PVC (polyvinyl chloride) or PET (polyethylene terephthalate).
Aluminizer of the present invention is seven color aluminizers, citicall limited aluminium film or pearly-lustre film.
Operation principle of the present invention is that thermoplastic resin is melt into liquid, on the metal aluminium lamination that keeps under the resin molten condition being printed onto on this aluminizer with intaglio press, resin promptly tightly bonds together with metallic diaphragm after being cooled to normal temperature, can not fall separation in storage and transportation.During stamp, under 85 ℃ to 120 ℃ temperature, make thermoplastic resin fusing, under certain pressure and resin pattern is transferred on the stock, after cooling, the one side of resin is closely linked with stock, and the another side of resin and the metallic diaphragm on the plated film are closely linked.When taking film off, the part of the metallic diaphragm of combining closely with resin has just been stayed on the stock by resin, and therefore gloss is strong, and floral designs are clear, level and smooth.If what adopt is seven color aluminizers, citicall limited aluminium film, the pearly-lustre film is rich color then.Pearly-lustre film of the present invention comprises on the pearly-lustre print film film of pearly-lustre aluminizer and water-based, oiliness because of having resin bed to separate between metal film and the stock, so produced some stereoeffects.The present invention does not relate to organic solvent, so non-environmental-pollution in the hot transfer printing.
Advantage of the present invention is that And is closed in twice transfer printing of the metallic diaphragm transfer printing of the hot transfer printing of traditional pattern and metal-coated membrane is the once-through method transfer printing, and pattern transferring is clear, and level and smooth, gloss is strong, and rich color has third dimension.
The specific embodiment:
Once-through method of aluminum-plating film resin transfer printing of the present invention, be with the polyethylene thermoplastic resin after 120 ℃ of hot melts become liquid, again with the intaglio press that heat tracing hopper and interior warm-up mill are arranged, keep under the resin molten condition, pattern is printed on the aluminium lamination of seven color aluminizers, after cooling to room temperature that the aluminizer clot is standby.When wanting stamp, will there be polyethylene thermoplastic resin pattern simultaneously to be attached on the stock on this aluminizer,, takes film after the cooling off, promptly become finished product through 85 ℃ to 120 ℃ impressions.The above impression is the impression that comprises the roll-in of coiled strip, or to the impression of the concora crush of part material.
The present invention is that thermoplastic resin also can adopt polyvinyl chloride or polyamide and other resin, during thermal transfer printing, should regulate the resin melt temperature according to the melting temperature of different resins, and the physical property of different stock linings is regulated the temperature when impressing.Aluminizer adopts citicall limited aluminium film or pearly-lustre film, and the preparation method during thermal transfer printing is by the above method.
Claims (5)
1, once-through method of aluminum-plating film resin transfer printing is characterized in that carrying out by the following method:
A: after the thermoplastic resin hot melt become liquid, pattern is printed on the aluminium lamination of aluminizer under the resin molten condition keeping with intaglio press again, is cooled to behind the normal temperature aluminizer clot is standby;
B: when stamp, will have the thermoplastic resin pattern simultaneously to be attached on the stock on this aluminizer,, take film after the cooling off, be finished product through 85 ℃ to 120 ℃ impressions.
2, once-through method of aluminum-plating film resin transfer printing according to claim 1 is characterized in that described thermoplastic resin is PA, PE, PVC or PET.
3, once-through method of aluminum-plating film resin transfer printing according to claim 1 is characterized in that described aluminizer is seven color aluminizers, citicall limited aluminium film or pearly-lustre film.
4, once-through method of aluminum-plating film resin transfer printing according to claim 1 is characterized in that intaglio press is the method maintenance resin molten condition by heat tracing hopper and interior warm-up mill.
5, once-through method of aluminum-plating film resin transfer printing according to claim 1 is characterized in that described impression is roll-in or concora crush.