CN101403153B - 哈特涤纶丝及其生产技术 - Google Patents

哈特涤纶丝及其生产技术 Download PDF

Info

Publication number
CN101403153B
CN101403153B CN2008101216027A CN200810121602A CN101403153B CN 101403153 B CN101403153 B CN 101403153B CN 2008101216027 A CN2008101216027 A CN 2008101216027A CN 200810121602 A CN200810121602 A CN 200810121602A CN 101403153 B CN101403153 B CN 101403153B
Authority
CN
China
Prior art keywords
controlled
spinning
hart
cooling device
screw
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN2008101216027A
Other languages
English (en)
Other versions
CN101403153A (zh
Inventor
冯新卫
吴卫东
李雪昌
陆武良
刘忠华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongxiang Zhongwei Chemical Fiber Co ltd
Original Assignee
Tongxiang Zhongwei Chemical Fiber Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongxiang Zhongwei Chemical Fiber Co ltd filed Critical Tongxiang Zhongwei Chemical Fiber Co ltd
Priority to CN2008101216027A priority Critical patent/CN101403153B/zh
Publication of CN101403153A publication Critical patent/CN101403153A/zh
Application granted granted Critical
Publication of CN101403153B publication Critical patent/CN101403153B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明所设计的哈特涤纶丝，其规格参数是单丝束分特数为308DTEX、合股数为16、单纤度为19.25DTEX、强度为5.3CN/DTEX、伸长率为13％、沸水收缩率为3.5％。本发明所设计的这种哈特涤纶丝的生产技术主要由切片输送、干燥、螺杆纺丝箱纺丝、拉伸、卷绕等步骤组成，纺丝粘度降控制在≦0.01dl/g，螺杆纺丝箱的螺杆压力控制在12±0.5MPA，纺丝速度为4200m/min，且喷丝板的喷丝孔采用U形排列；上油工艺时采用抗高温油剂且油轮转速为15r/min；侧吹风冷却装置采用全封闭的风道，且外加冷却装置冷却；全牵伸卷绕时牵伸倍数控制在3.8倍以上，第一热辊的温度设置在100℃，第二热辊的温度设置在175℃，且卷绕成形中心角控制在4.7°，控制丝饼成型张力控制在35CN以下。本发明所得到的哈特涤纶丝，是介于工业丝与服饰丝之间的涤纶长丝，本发明使用的哈特涤纶丝的生产技术，攻克了以往只有使用工业丝设备或通过二步纺才能生产出如此规格的哈特涤纶丝的技术难点。

Description

哈特涤纶丝及其生产技术
技术领域
本发明涉及一种化纤涤纶丝，以及这种化纤涤纶丝的生产技术。
背景技术
现在化纤市场的竞争日益剧烈，产品的种类不断更新换代，且品质也不断的提高，但是现有的产品使用范围比较的小，都是分别面向工业用料或者服饰用料，同时涵盖这两种使用范围的产品仍是一片空白，这主要是由于这类产品生产难度高，制成率低导致的。
发明内容
本实用新型的目的是为了解决上述技术的不足而提供一种单丝纤度大、强度高、伸缩小、韧性好，介于工业用料与服饰用料之间的哈特涤纶丝以及其生产技术。
为了达到上述目的，本发明所设计的哈特涤纶丝，其规格参数是单丝束分特数为308DTEX、合股数为16、单纤度为19.25DTEX、强度为5.3CN/DTEX、伸长率为13％、沸水收缩率为3.5％。
为了达到上述目的，本发明所设计的这种哈特涤纶丝的生产技术主要由切片输送、干燥、螺杆纺丝箱纺丝、拉伸、卷绕等步骤组成，纺丝粘度降控制在≦0.01dl/g，螺杆纺丝箱的螺杆压力控制在12±0.5MPA，纺丝速度为4200m/min，且喷丝板的喷丝孔采用U形排列；上油工艺时采用抗高温油剂且油轮转速为15r/min；侧吹风冷却装置采用全封闭的风道，且外加冷却装置冷却；全牵伸卷绕时牵伸倍数控制在3.8倍以上，第一热辊的温度设置在100℃，第二热辊的温度设置在175℃，且卷绕成形中心角控制在4.7°，控制丝饼成型张力控制在35CN以下。为了更好的控制成品率及产品的质量，干切片含水率控制在20ppm以下，纺丝箱温度控制在295℃。侧吹风冷却装置的风温控制在20℃以下，且风速控制在0.4m/s以下。
本发明所得到的哈特涤纶丝，是介于工业丝与服饰丝之间的涤纶长丝，打开了涤纶长丝新领域，具有单丝纤度大、强度高、伸缩小、韧性好、使织物挺括有骨架等特点。本发明使用的哈特涤纶丝的生产技术，攻克了以往只有使用工业丝设备或通过二步纺才能生产出如此规格的哈特涤纶丝的技术难点，仅使用常规的FDY设备生产，且成本与过往的其他涤纶丝生产相比并没有增加，还大大降低了后道客户的生产成本，具有良好的可实施性。
附图说明
图1是本发明实施例2的流程图；
图2是本发明实施例2喷丝板的结构示意图。
具体实施方式
下面通过实施例结合附图对本实用新型作进一步的描述。
实施例1
本实施例描述的哈特涤纶丝，是在单束丝分特数为308DTEX，合股数为16，单纤度为19.25DTEX，强度为5.3CN/DTEX，伸长率为13％，沸水收缩率为3.5％。实施例2
如图1、图2所示本实施例描述的哈特涤纶丝的生产技术主要由切片输送、干燥、螺杆纺丝箱纺丝、拉伸卷绕等步骤组成，切片含水率控制在20ppm以下，纺丝箱温度控制在295℃，使纺丝粘度降控制在≦0.01dl/g，螺杆纺丝箱的螺杆压力为12.0MPA，纺丝速度为4200m/min，采用两块含有8个喷丝孔2的纺丝板1，其喷丝孔U形排列；上油工艺时采用型号为DElionF—7190—S的抗高温油剂，且油轮转速为15r/min；侧吹风冷却装置采用全封闭的风道，且外加冷却装置冷却全拉伸卷绕时拉伸倍数控制在3.8倍以上，第一热辊的温度设置在100℃，第二热辊的温度设置在175℃，且卷绕成形中心角控制在4.7°，控制丝饼成型张力为35CN以下。
实施例3
本实施例描述的哈特涤纶丝的生产技术，其所述的螺杆纺丝箱的压力控制在12.0MPA，控制丝饼成型的张力为28CN。侧吹风冷却装置的风温控制在20℃以下，且风速控制在0.4m/s以下。

Claims (3)

1.一种单束分特数为308DTEX，合股数16，单丝纤度为19.25DTEX，强度为5.3CN/DTEX、伸长率为13％、沸水收缩率为3.5％的哈特涤纶丝生产方法，它主要由输送切片、干燥、螺杆纺丝箱纺丝、牵伸卷绕步骤组成，其特征是纺丝粘度降控制在≤0.01dl/g，螺杆纺丝箱的螺杆压力控制在12±0.5MPA，纺丝速度为4200m/min，且纺丝板的喷丝孔采用U形排列；上油工艺时采用抗高温油剂且油轮转速为15r/min；侧吹风冷却装置采用全封闭的风道，且外加冷却装置冷却；全牵伸卷绕时牵伸倍数控制在3.8倍以上，第一热辊的温度设置在100℃，第二热辊的温度设置在175℃，且卷绕成形中心角控制在4.7°，控制丝饼成型张力控制在35CN以下。
2.根据权利要求1所述的哈特涤纶丝生产方法，其特征是所述的切片含水率控制在20ppm以下，纺丝箱温度控制在295℃。
3.根据权利要求1或2所述的哈特涤纶丝生产方法，其特征是所述的侧吹风冷却装置的风温控制在20℃以下，且风速控制在0.4m/s以下。
CN2008101216027A 2008-10-20 2008-10-20 哈特涤纶丝及其生产技术 Active CN101403153B (zh)