CN101402515A - 石灰、粉煤灰类材料的增强抗裂剂 - Google Patents
石灰、粉煤灰类材料的增强抗裂剂 Download PDFInfo
- Publication number
- CN101402515A CN101402515A CNA2008101972950A CN200810197295A CN101402515A CN 101402515 A CN101402515 A CN 101402515A CN A2008101972950 A CNA2008101972950 A CN A2008101972950A CN 200810197295 A CN200810197295 A CN 200810197295A CN 101402515 A CN101402515 A CN 101402515A
- Authority
- CN
- China
- Prior art keywords
- lime
- fly ash
- parts
- crack
- materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种石灰、粉煤灰类材料的增强抗裂剂，它包括硅酸盐矿物粉、石膏或化工废渣磷石膏和含SO3碱金属物质，其中硅酸盐矿物粉内硅酸三钙的含量在55％以上。石灰、粉煤灰类材料或石灰、粉煤灰类粒料的早期强度很低，抗裂性较差，掺入本增强抗裂剂后，石灰、粉煤灰类材料或石灰、粉煤灰类粒料的早期强度增长明显，其它性能也随之改善，尤其是对抗裂性能大为提高，可以有效解决了路面开裂的问题。由于使用工业废渣、电石渣代替石灰，以劣质粉煤灰代替II级以上的粉煤灰，将会使工程建设成本明显下降，取得较好的经济效益。
Description
技术领域
本发明涉及一种石灰、粉煤灰类材料作各等级公路路面的底基层、基层材料的改进，特别是一种石灰、粉煤灰类材料的增强抗裂剂。
背景技术
石灰、粉煤灰类材料作各等级公路路面的底基层、基层，它具有可操作时间长、较高的中后期强度和刚度、板体性高、很高的路面承载能力、耐久性好、造价低、有利于环境保护等优点，但该类材料早期强度低、收缩较大、容易导致路面早期开裂，致使其使用受到一定的影响和限制。
发明内容
本发明的目的就是要提供一种石灰、粉煤灰类材料的增强抗裂剂，它能解决石灰、粉煤灰类材料的早期强度低、收缩开裂的问题。
本实用新型的目的是这样实现的：一种石灰、粉煤灰类材料的增强抗裂剂，其特征在于它包括下列重量比组份：
硅酸盐矿物粉 55份-70份，
石膏或化工废渣磷石膏 15份-35份，
含SO3碱金属物质 10份-20份，
其中硅酸盐矿物粉内硅酸三钙的含量在55％以上。含SO3碱金属物质是指硫酸钾或硫酸钠。
本发明的制备方法：将硅酸盐矿物粉、石膏或化工废渣磷石膏和含SO3的碱金属物质按上述重量比配制，混合均匀即可。
使用本发明后，石灰、粉煤灰类材料的强度增长明显，尤其是对稳定层的开裂有抑制作用，有效解决了路面开裂的问题。并且石灰、粉煤灰的质量将不受限制，可以用电石渣替代石灰，电石渣和劣质粉煤灰的性能可以达到高等级公路底基层、基层对水泥稳定粒料的技术要求。由于使用工业废渣，将会使工程建设成本明显下降，取得较好的经济效益。本发明还可大量应用高强度的场区填筑材料、路基土改性增强材料、软基上路堤和挡墙后及台背的高强轻质低变形填筑材料。
具体实施方式
一种石灰、粉煤灰类材料的增强抗裂剂，其特征在于它包括下列重量比组份：
硅酸盐矿物粉 55份-70份，
石膏或化工废渣磷石膏 15份-35份，
含SO3碱金属物质 10份-20份，
其中硅酸盐矿物粉内硅酸三钙的含量在55％以上。含SO3碱金属物质是指硫酸钾或硫酸钠。
本发明增强抗裂剂为灰白色粉末状，属无机材料，密度3.0g/cm3左右。
本发明的增强机理为：
1、其中的成份与氢氧化钙反应后，提高了体系的PH值，从而加速玻璃体中的SiO2和Al2O3溶蚀；在加入的促进水化的成份的共同作用下，加速了水化硅酸钙和水化铝酸钙的生成，所以早期强度发展快、后期强度持续增加。
2、其中的成份与氢氧化钙反应后的生成物分散性、溶解度更高，在加入的另外成份的共同作用下，快速并后续继续生成大量的水化硫铝酸钙，使体系具有高的早期强度，同时该类水化产物具有膨胀性，可以降低甚至消除收缩危害。
3、含有水化速度快、早期强度高的矿物及水化促进剂，水化产物早期强度高并可以促进火山灰反应的速度。
实施例1：
取硅酸盐矿物粉65份，石膏20份，硫酸钾15份，混合均匀即可。
实施例2：
取硅酸盐矿物粉55份，磷石膏30份，硫酸钠15份，混合均匀即可。
实施例3：
取硅酸盐矿物粉55份，石膏30份，硫酸钠15份，混合均匀即可。
实施例4：
取硅酸盐矿物粉65份，磷石膏20份，硫酸钾15份，混合均匀即可
使用方法：
根据石灰、粉煤灰类材料或石灰、粉煤灰类稳定粒料的设计要求，通过试验确定本发明增强抗裂剂的掺量。增强抗裂剂的掺量一般为石灰类材料和粉煤灰总质量的10％-30％。施工时，将本增强抗裂剂掺入石灰、粉煤灰类材料或石灰、粉煤灰类稳定粒料中，拌和均匀后即可。
例：某公路底基层采用石灰、粉煤灰类材料，设计强度R7为1.0MPa，但因为当地粉煤灰质量较差，通过试验后石灰、粉煤灰类材料强度仅能达到0.7MPa；掺入本增强抗裂剂15％后，石灰、粉煤灰类材料的强度达到1.2MPa，满足设计要求。
掺入本发明增强抗裂剂后的石灰、粉煤灰类材料及石灰、粉煤灰类稳定粒料的性能见表1：
表1
Claims (2)
1、一种石灰、粉煤灰类材料的增强抗裂剂，其特征在于它包括下列重量比组份：
硅酸盐矿物粉 55份-70份，
石膏或化工废渣磷石膏 15份-35份，
含SO3碱金属物质 10份-20份，
其中硅酸盐矿物粉内硅酸三钙的含量在55％以上。
2、根据权利要求1所述的一种石灰、粉煤灰类材料的增强抗裂剂，其特征是：含SO3碱金属物质是指硫酸钾或硫酸钠。