CN101386505A - 一种干粉砂浆粘接剂及其配制方法 - Google Patents
一种干粉砂浆粘接剂及其配制方法 Download PDFInfo
- Publication number
- CN101386505A CN101386505A CNA2008102317824A CN200810231782A CN101386505A CN 101386505 A CN101386505 A CN 101386505A CN A2008102317824 A CNA2008102317824 A CN A2008102317824A CN 200810231782 A CN200810231782 A CN 200810231782A CN 101386505 A CN101386505 A CN 101386505A
- Authority
- CN
- China
- Prior art keywords
- cement
- dry powder
- sand
- water
- polyvinyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种干粉砂浆粘接剂及其配制方法。配方中,以水泥为100个重量单位计,各组分含量为:水泥:100;砂子:140~180;纤维素醚:0.5~0.8;聚乙烯醇:0.4~0.7;高性能外加剂:0.4~0.6;水(占干粉重量)18-20。配制时:先将各种添加剂纤维素醚、聚乙烯醇、聚乙烯醇、高性能外加剂和水泥进行预拌合,随后,加入砂子,最后加入上述各组分的总量之18-20%的水,搅拌均匀即可。本发明采用价格较低的聚乙烯醇替代可分散乳胶粉,大大降低了产品的成本30%左右;采用高性能外加剂,可减少用水量20-30%,既可以提高粘接强度,还可消除有机外加剂加入而引起的水泥砂浆的缓凝,改善水泥砂浆粘接剂的施工性能。
Description
技术领域 本发明涉及一种无机非金属粘接剂及其配制方法。
背景技术 建筑工程中用于粘接大理石、瓷砖和外保温材料的粘接剂,需要具有一定的韧性,即好的变形性。建筑工程用的粘接剂常采用水泥砂浆,为了提高砂浆的粘接强度,降低砂浆的弹性模量,提高砂浆的变形性,通常采用加入有机添加剂的方法以改善水泥砂浆的性能,解决墙体与瓷砖因变形性能不同而引起的空鼓脱落问题。
常用的有机添加剂有可再分散乳胶粉、聚乙烯醇、纤维素醚等。可再分散乳胶粉,是乙烯—醋酸乙烯共聚物,它是一种粉状的有机粘接剂,是通过喷雾干燥的特殊水性乳液,其与水混合后,可以回复到它们的水性乳液状态,当有机粘接剂与水泥混合后,待水分蒸发时,聚合物粒子通过聚结,形成一层聚合物薄膜,从而起到胶粘剂的作用,聚合物薄膜作为有机粘接剂,将各种填料的粒子胶结在一起,增强了砂浆材料的粘接强度,降低了弹性模量,增强了材料的弹性和抗弯强度,提高了材料的耐冲击性和耐候性。聚乙烯醇,因其分子结构中含有羟基,耐水性较差,很少被使用。纤维素醚,吸水性好,可极大的增强水泥砂浆的保水性,能为水泥水化提供充足的水分,防止水泥砂浆过快失水干燥和硬化开裂,因而被用作保水剂。
水泥砂浆中加入有机高分子添加剂,其负面作用是:往往会影响水泥砂浆的凝结时间,引起水泥砂浆的缓凝。如果有机材料加入量过大,会出现水泥砂浆的假凝,后期强度增长过慢,甚至不凝结,影响施工质量。为此,常选用早强剂来调整水泥的凝结时间,以满足施工的需要。
Waker公司给出的瓷砖粘接剂建议配方为(重量比):
水泥 乳胶粉 纤维素醚 砂 水
30-40% 2-4% 0.3-0.5% 若干 若干
罗地亚公司给出的瓷砖粘接剂建议配方为(重量比):
水泥 砂 纤维素醚 乳胶粉 水(相对于干粉)
36.2% 58.3% 0.5% 3-5% 24-26%
维纳欧公司给出的瓷砖粘接剂建议配方为(重量比):
水泥 石英砂 纤维素醚 乳胶粉 水
25% 71.75% 0.25% 3% 若干
上述诸多公开的技术资料表明,现有的粘接剂普遍存在成本高的缺点,这些粘接剂在成本构成上,可分散乳胶粉在配方中占1~2%在成本中占30~50%是影响成本高的主要原料成分。
发明内容
为克服现有粘接剂成本高的缺点,本发明的目的在于,在满足技术标准要求的前提下,选择替代材料,优化配方,达到降低成本,提高经济效益的目的。为此,本发明现提供一种既能提高水泥砂浆粘接强度,又能大幅度降低原料成本的新型粘接剂——干粉砂浆粘接剂及其配制方法。
本发明是这样实现的:本发明由水泥、砂子、纤维素醚、聚乙烯醇、外加剂混合而成。其间的配比,以水泥为100个重量单位计,各组分为:
水泥 砂子 纤维素醚 聚乙烯醇 高性能外加剂 水(占干粉总重)
100 140~180 0.5~0.8 0.4~0.7 0.4~0.6 18-20
所说的高性能外加剂,由高效减水剂和无机盐复合而成,高效减水剂与无机盐的比例为1:2~3。
本发明配制时,将称量好的水泥与砂子、各种添加剂均匀混合在一起,使用时,加水搅拌均匀即可。水的加入量为水泥、砂子、纤维素醚、聚乙烯醇、高性能外加剂之总量(即干粉重量)的18-20%。
更好的配制方法是:先将各种添加剂:纤维素醚、聚乙烯醇、聚乙烯醇、高性能外加剂和水泥进行预拌合,然后加入砂子,搅拌均匀。这样分散效果会更好——因为所有添加剂的颗粒都非常小,比表面积又非常大,添加量又很小。如果分散不均匀,将会严重影响产品质量,甚至会出现局部不凝结。使用时,加入上述各组分总量之18-20%的水,搅拌均匀即可。
冬季(日平均气温—0℃以下),还必须加入具有防冻早强成分的无机盐,其加入量为高性能外加剂的20~30%,以提高粘接剂的早期强度和抗冻性能。选择防冻剂时应尽量少用含有钾、钠离子的无机盐类早强剂,以避免来年春天出现的“泛碱”现象。
本发明与现有的粘接剂比较,保水剂纤维素醚的用量基本相当,但采用了价格较低的聚乙烯醇替代可分散乳胶粉,降低产品成本30%左右。聚乙烯醇作为有机粘接剂,存在的最大问题是聚乙烯醇含有羟基,能溶于水,干燥后,耐水性差,本发明选择高性能外加剂,既可以提高粘接强度,又能封闭聚乙烯醇的羟基,提高粘接剂的软化系数,且高性能外加剂的加入可减少用水量20-30%,按照水泥强度理论,水泥砂浆的强度随着用水量减少而提高,同时还可以消除有机外加剂加入而引起的水泥砂浆的缓凝,改善水泥砂浆粘接剂的施工性能。
具体实施方式 下面叙述三个本发明的实施例
实施例1.原料配方,以水泥为100个重量单位计,各组分(%)之间的配比为:
水泥 砂子 纤维素醚 聚乙烯醇 高性能外加剂 水(占干粉重量)
100 140 0.8 0.4 0.6 18
其中,高性能外加剂中高效减水剂与无机盐的比例为1:2。
配制时,先将添加剂纤维素醚、聚乙烯醇、高性能外加剂和水泥,放人回旋上料机内进行预拌合,随后加入称量好的砂子和水,搅拌均匀即可。
实施例2原料配方:以水泥为100个重量单位计,各组分(%)之间的配比为:
水泥 砂子 纤维素醚 聚乙烯醇 高性能外加剂 水(相对于干粉)
100 180 0.5 0.7 0.4 20
其中,高性能外加剂中高效减水剂与无机盐的比例为1:3。
配制:使用双螺旋倒锥式搅拌机,先加入添加剂纤维素醚、聚乙烯醇、高性能外加剂和水泥进行预拌合,随后加入称量好的砂子和水,搅拌均匀即可。
实施例3.冬季(日平均气温—3~15℃)的配方及配制方法
原料配方,以水泥为100个重量单位计,各组分(%)之间的配比为:
水泥 砂子 纤维素醚 聚乙烯醇 高性能外加剂 水(占干粉总重)
100 160 0.6 0.6 0.5 19
其中,高性能外加剂中高效减水剂与无机盐的比例为1:2.5。
另需加入具有防冻早强成分的无机盐,其加入量的重量单位为:0.5 X 26%=0.13。
下面表格中的各项性能,系根据JC/T547-2005标准,对本发明之实施例1,进行的试测结果(龄期14天):
Claims (5)
1.一种干粉砂浆粘接剂,含有水泥、砂子、纤维素醚和水,其特征在于:配方组分中含有添加剂聚乙烯醇、高性能外加剂,以水泥为100个重量单位计,各组分含量为:
水泥 砂子 纤维素醚 聚乙烯醇 高性能外加剂 水(占干粉重量)
100 140~180 0.5~0.8 0.4~0.7 0.4~0.6 18-20
所说的高性能外加剂由高效减水剂和无机盐复合而成。
2.按照权利要求1所述的一种干粉砂浆粘接剂的配制方法,其特征是:将称量好的水泥与砂子、各种添加剂混在一起,随后加人水,搅拌均匀即可。
3.按照权利要求2所述的一种干粉砂浆粘接剂的配制方法,其特征是:先将各种添加剂:纤维素醚、聚乙烯醇、聚乙烯醇、高性能外加剂和水泥进行预拌合,随后,加入砂子,搅拌均匀,最后加入上述各组分总量之18-20%的水,搅拌均匀即可。
4.根据权利要求1所述的一种干粉砂浆粘接剂,其特征在于:所说的高性能外加剂之高效减水剂与无机盐的比例为1:2~3。
5.根据权利要求1所述的一种干粉砂浆粘接剂,其特征在于:原料的组分中,含有防冻早强成分的无机盐,其加入量为高性能外加剂的20~30%。