CN101348298A - 一种废水快速除铬方法 - Google Patents
一种废水快速除铬方法 Download PDFInfo
- Publication number
- CN101348298A CN101348298A CNA2008101465335A CN200810146533A CN101348298A CN 101348298 A CN101348298 A CN 101348298A CN A2008101465335 A CNA2008101465335 A CN A2008101465335A CN 200810146533 A CN200810146533 A CN 200810146533A CN 101348298 A CN101348298 A CN 101348298A
- Authority
- CN
- China
- Prior art keywords
- chromium
- waste water
- solid
- iron
- sulfide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种废水快速除铬方法,涉及一种处理废水或污水,特别是含铬废水的快速除铬剂方法。采用铁的硫化物为除铬剂,其特征在于除铬过程包括:(1)将铁的硫化物粉碎,过300目筛,取筛下细粉;(2)将步骤(1)所得到的细粉加水,调浆至固液重量比1∶3~1∶4,调节pH值4~6,搅拌,煮沸;(3)在步骤(2)溶液中加入四羟甲基硫酸磷THPS,加入量为铁的硫化物固体重量的0.1~0.4,搅拌,在80-95℃加热;(4)加热至固液重量比1∶1~1∶2时,停止加热,过滤,得到固体和滤液;(5)将步骤(4)得到滤液作除铬剂加入废水中进行除铬。本发明所述的除铬剂制备方法简便、原料廉价,此除铬剂处理含铬废水能力极强,效果极佳。
Description
技术领域
一种废水快速除铬方法,涉及一种处理废水或污水,特别是含铬废水的快速除铬方法。
背景技术
目前,对于铬污染的废水,主要采用的主要有以下几种方法:(1)化学沉淀法,又分为中和沉淀法和硫化物沉淀法;(2)氧化还原处理,分为化学还原法、铁氧体法和电解法;(3)溶剂萃取分离法;(4)吸附法;(5)膜分离技术;(6)离子交换法;(7)生物处理方法。上述方法都存在设备繁琐、成本高的弊端,处理效果不理想。
近年来美国、日本、中国等纷纷研究用环境矿物治理含铬废水,如CN 200510035580.9、CN 99109634.7、CN 03147583.3用黄铁矿/硫铁矿处理含铬废水,虽然所用材料廉价易得,但也存在用量过大,吸附量小,处理时间长等缺点,有的虽然可以再次使用,但终因表面沉积堵塞而失效。
发明内容
本发明的目的就是针对上述已有技术存在的不足,提供一种材料廉价易得、除铬剂用量小、吸附量大,处理时间短,除铬剂能再次使用、表面不易失效的废水快速除铬方法。
本发明的目的是通过以下技术方案实现的。
一种废水快速除铬方法,采用铁的硫化物为除铬剂,其特征在于除铬过程包括:
(1)将铁的硫化物粉碎,过筛,取筛下细粉;
(2)将步骤(1)所得到的细粉加水,调浆至固液重量比为1∶3~1∶4,调节pH值4~6,搅拌,煮沸;
(3)在步骤(2)溶液中加入四羟甲基硫酸磷THPS,加入量为铁的硫化物固体重量的0.1~0.4,搅拌,在80-95℃加热;
(4)加热至固液重量比1∶1~1∶2时,停止加热,过滤,得到固体和滤液;
(5)将步骤(4)得到滤液作除铬剂加入废水中进行除铬。
本发明的一种废水快速除铬方法,所述的铁的硫化物为硫化亚铁、黄铁矿、磁黄铁矿、硫铁矿、硫精砂的天然矿物或人工合成剂中的一种或几种混合物。优选为硫化亚铁、也优选为黄铁矿、磁黄铁矿,更优选为单斜磁黄铁矿。THPS为是一种新型绿色水处理剂,易降解、没有生物聚集的危险,具有还原性,可大幅增加铁的硫化物溶解度。
本发明的一种废水快速除铬方法,其特征在于所述的步骤(4)过滤得到的固体,返回步骤(2)。
本发明的一种废水快速除铬方法,所述的步骤(4)过滤得到的滤液中加入铁的硫化物,在密闭,避光,pH=4-5条件下保存待用。
本发明的一种废水快速除铬方法,采用廉价、环保型有机溶剂,将铁的硫化物溶解其中,制备出液体除铬剂,将除铬剂加入含铬废水中,立刻产生黄色沉淀,使废水中铬含量达到排放标准。有效降低了含铬废水处理成本,快速除去水中铬离子。原料来源广泛、廉价,而且环境友好。
具体实施方式
一种废水快速除铬方法,采用铁的硫化物为除铬剂,该方法包括以下步骤:(1)将铁的硫化物粉碎,过300目筛;(2)将步骤(1)所得到的细粉加水,固液重量比1∶3~1∶4,调节pH值4-6,搅拌,煮沸1h;(3)在步骤(2)溶液中加入四羟甲基硫酸磷(THPS),加入量为固体量的0.1~0.4,搅拌,在80-95℃加热溶解;(4)当液面下降,固液比1∶1~1∶2时,停止加热,过滤,滤液即为除铬剂进行除铬。除铬剂储存方法为:往其中加入少量(1)的原料,密闭,避光,pH=4-5。
实施例1
将50克硫化亚铁粉碎,过300目筛,放入密闭容器中,加水200ml,调节pH=6,搅拌,煮沸,1h后加入5克THPS,搅拌,在80℃加热溶解;当液面下降,固液重量比1∶1时,停止加热,过滤,滤液即为除铬剂。
取此除铬剂0.3ml,加入200mg/l,100ml,pH=3含铬废水中,立刻产生黄色沉淀,静置,倒出上清液,调节pH=6,测总Cr浓度<0.5mg/l,可达标排放。
实施例2
将50克单斜磁黄铁矿粉碎,过300目筛,放入密闭容器中,加水200ml,调节pH=5,搅拌,煮沸,1h后加入10克THPS,搅拌,在90℃加热溶解;当液面下降,固液重量比1∶2时,停止加热,过滤,滤液即为除铬剂。
取此除铬剂0.2ml,加入150mg/l,100ml,pH=4含铬废水中,立刻产生黄色沉淀,静置,倒出上清液,调节pH=6,测总Cr浓度<0.5mg/l,可达标排放。
实施例3
将50克黄铁矿粉碎,过300目筛,放入密闭容器中,加水250ml,调节pH=4,搅拌,煮沸,1h后加入15克THPS,搅拌,在95℃加热溶解;当液面下降,固液重量比1∶2时,停止加热,过滤,滤液即为除铬剂。
取此除铬剂0.15ml,加入100mg/l,100ml,pH=5含铬废水中,立刻产生黄色沉淀,静置,倒出上清液,调节pH=6,测总Cr浓度<0.5mg/l,可达标排放。
实施例4
将50克硫铁矿粉碎,过300目筛,放入密闭容器中,加水250ml,调节pH=5,搅拌,煮沸,1h后加入20克THPS,搅拌,在95℃加热溶解;当液面下降,固液重量比1∶2时,停止加热,过滤,滤液即为除铬剂。
取此除铬剂0.1ml,加入50mg/l,100ml,pH=6含铬废水中,立刻产生黄色沉淀,静置,倒出上清液,pH=6,测总Cr浓度<0.5mg/l,可达标排放。
实施例5
将50克硫精砂粉碎,过300目筛,放入密闭容器中,加水250ml,调节pH=5,搅拌,煮沸,1h后加入15克THPS,搅拌,在95℃加热溶解;当液面下降,固液重量比1∶2时,停止加热,过滤,滤液即为除铬剂。
取此除铬剂0.1ml,加入50mg/l,100ml,pH=9含铬废水中,立刻产生黄色沉淀,静置,倒出上清液,调节pH=7,测总Cr浓度<0.5mg/l,可达标排放。
Claims (4)
1.一种废水快速除铬方法,采用铁的硫化物为除铬剂,其特征在于除铬过程包括:
(1)将铁的硫化物粉碎,过300目筛,取筛下细粉;
(2)将步骤(1)所得到的细粉加水,调浆至固液重量比1∶3~1∶4,调节pH值4~6,搅拌,煮沸;
(3)在步骤(2)溶液中加入四羟甲基硫酸磷THPS,加入量为铁的硫化物固体重量的0.1~0.4,搅拌,在80-95℃加热;
(4)加热至固液重量比1∶1~1∶2时,停止加热,过滤,得到固体和滤液;
(5)将步骤(4)得到滤液作除铬剂加入废水中进行除铬。
2.根据权利要求1所述的一种废水快速除铬方法,其特征在于所述的铁的硫化物为硫化亚铁、黄铁矿、磁黄铁矿、硫铁矿、硫精砂的天然矿物或人工合成剂中的一种或几种混合物。
3.根据权利要求1所述的一种废水快速除铬方法,其特征在于所述的步骤(4)过滤得到的固体,返回步骤(1)。
4.根据权利要求1所述的一种废水快速除铬方法,所述的步骤(4)过滤得到的滤液中加入铁的硫化物,在密闭,避光,pH=4-5条件下保存待用。