CN101338430A - Method for blacking case of mobile phone - Google Patents
Method for blacking case of mobile phone Download PDFInfo
- Publication number
- CN101338430A CN101338430A CNA2008100636986A CN200810063698A CN101338430A CN 101338430 A CN101338430 A CN 101338430A CN A2008100636986 A CNA2008100636986 A CN A2008100636986A CN 200810063698 A CN200810063698 A CN 200810063698A CN 101338430 A CN101338430 A CN 101338430A
- Authority
- CN
- China
- Prior art keywords
- shell
- phone housing
- black
- housing according
- black preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing method for blackening mobile phone shell. The manufacturing method comprises the procedures as follows: a stainless punch forming shell is adopted; the shell is polished or wiredrawn; the shell is placed on an ultrasonic clean line to be cleaned; the shell is placed in a vacuum furnace; high voltage source is used for argon-ion bombardment for the shell; an Ion plating method is used for depositing a pure metal layer on the surface of the shell; a magnetron sputtering method is used for depositing a middle transition layer on the bottom layer of the pure metal; the magnetron sputtering method is used for coating a hard black film on the middle transition layer; the shell is passivated and cooled; and a static protective film is stuck on the shell for package. The manufacturing method has the characteristics of green environmental protection and energy saving. The tone range of a black nano film is that L is equal to 35 to 39, a is equal to -0.3 or 0.5 and b is equal to 0 to 3. The manufacturing method also has strong bonding capacity which can be over 8H under the loading below 1000g, so the wear-resisting property and the service life of the stainless cell phone casing are greatly improved.
Description
Technical field
The present invention relates to a kind of the phone housing that uses in the daily life is being carried out black preparation method.
Background technology
Stainless steel is with its excellent antiseptic property and metal-like, and environmental protection is just becoming the first-selection of medium-to-high grade phone housing metallic substance.At present electrochemical treatment or electrophoretic process are adopted in the painted processing of stainless steel phone housing more,, do not meet the standard of the RoSH of European Union because the reaction soln of electrochemical treatment generally all contains harmful sexavalent chrome; The decorating film of electrophoretic process mostly is organism, has both covered the metalluster of stainless steel phone housing, and aesthetics is had a greatly reduced quality, again because its hardness has only 2H, antifraying property is poor, make phone housing with the mutual friction mutually of things such as pocket, coin in fade easily, influence attractive in appearance.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of phone housing black preparation method, can effectively solve existing phone housing adopts electrochemical treatment harmful, with adopt electrophoretic process and covered the metalluster of phone housing, because its hardness and antifraying property difference fade easily, influence problem attractive in appearance again.
In order to solve the problems of the technologies described above, the present invention adopts following technical scheme: a kind of phone housing black preparation method, it is characterized in that adopting following steps:
(a) adopt stainless steel impact briquetting shell;
(b) shell is polished or wire drawing;
(c) shell is placed the ultrasonic cleaning line clean;
(d) shell is loaded in the vacuum furnace body, utilizes high-voltage power supply that shell is carried out argon ion bombardment and handle;
(e) method of employing ion plating is at shell surface deposition one deck pure metal bottom;
(f) adopt magnetically controlled sputter method, on the pure metal bottom, deposit intermediate layer;
(g) adopt magnetically controlled sputter method, on intermediate layer, cross the black dura mater;
(h) shell is carried out the passivation cooling;
(i) adopt the electrostatic protection film to carry out the pad pasting packing to shell.
Further, stainless steel employing condition of surface is 2B or BA among the step a.
Further, the intravital vacuum tightness of vacuum oven is 6 * 10 in the steps d
-3~7 * 10
-3
Further, high-voltage power supply adopts 600~1000V.
Further, the pure metal layer adopts titanium or chromium among the step e.
Further, intermediate layer adopts titanium nitride or chromium nitride among the step f.
Further, the black dura mater adopts titanium carbonitride or carbon chromium nitride in the step g.
Further, the electrostatic protection film adopts PE electrostatic protection film in the step I.
The present invention has following beneficial effect owing to adopted technique scheme:
(1) under vacuum environment, will cross the film ionization and deposit film forming dry type and cross membrane method at shell, have environmental protection and energy-conservation characteristics;
(2) the steady elegance of black nano rete color and luster, metal-like is strong, and tone range is wide, and its tone range is: L=35~39, a=-0.3~0.5, b=0~3;
(3) bonding force of black nano hard membrane layer is strong, and its hardness is issued to more than the 8H in 1000g load, has greatly strengthened the wear resisting property and the work-ing life of stainless steel phone housing;
(4) but in the painted preparation of the stainless steel casing of the present invention's widespread use and various stainless steel phone housings and other 3C Product and built-in part.
Description of drawings
The invention will be further described below in conjunction with accompanying drawing:
Fig. 1 the structural representation of each coatings of phone housing surface among the black preparation method for a kind of phone housing of the present invention.
Embodiment
A kind of phone housing of the present invention black preparation method, and comprising the steps: to adopt condition of surface is the stainless steel impact briquetting shell 1 of 2B or BA, shell 1 is polished or the wire drawing processing, to strengthen the luminance brightness on shell 1 surface; Shell 1 after polishing or the wire drawing is placed the ultrasonic cleaning line, shell 1 is carried out decontamination, the oil removing clean on surface; In shell 1 loading and vacuum furnace body, reach 6 * 10 in vacuum tightness
-3~7 * 10
-3After, utilize the high-voltage power supply of 600~1000V that shell 1 is carried out the argon ion bombardment processing, remove the zone of oxidation on decapsidate 1 surface; Adopt ion electroplating method, at shell 1 surface deposition one deck pure metal layer 2, as shown in Figure 1, pure metal layer 2 adopts titanium or chromium, to improve the bonding force of subsequent plating layer; Adopt magnetically controlled sputter method, deposition intermediate layer 3 on 2 layers on pure metal layer, intermediate layer 3 adopts titanium nitride or chromium nitrides, to reduce the internal stress between each coating; Adopt magnetically controlled sputter method, plate final black dura mater 4 on intermediate layer 3, black dura mater 4 adopts titanium carbonitride or carbon chromium nitride, and its rete is the TiC of the different atomic ratios of tens layers nano level
1-XN
XOr CrC
1-XN
X, wear resisting property and work-ing life that the plated film that adopts magnetically controlled sputter method to carry out has greatly strengthened stainless steel casing 1; Plated film carries out the passivation cooling process to shell 1 after finishing; At last the 1 usefulness PE electrostatic protection film of the shell after the passivation cooling process being carried out pad pasting packs.
Claims (8)
1, a kind of phone housing black preparation method, it is characterized in that adopting following steps:
(a) adopt stainless steel impact briquetting shell;
(b) described shell is polished or wire drawing;
(c) place the ultrasonic cleaning line to clean on described shell;
(d) described shell is loaded in the vacuum furnace body, utilizes high-voltage power supply that described shell is carried out argon ion bombardment and handle;
(e) method of employing ion plating is at described case surface deposition one deck pure metal bottom;
(f) adopt magnetically controlled sputter method, on described pure metal bottom, deposit intermediate layer;
(g) adopt magnetically controlled sputter method, black coating look dura mater on described intermediate layer;
(h) described shell is carried out the passivation cooling;
(i) adopt the electrostatic protection film to carry out the pad pasting packing to described shell.
2, a kind of phone housing according to claim 1 black preparation method, it is characterized in that: the Stainless Steel Watch surface state is 2B or BA described in the step (a).
3, a kind of phone housing according to claim 1 black preparation method, it is characterized in that: the intravital vacuum tightness of vacuum oven is 6 * 10 described in the step (d)
-3~7 * 10
-3
4, a kind of phone housing according to claim 3 black preparation method, it is characterized in that: described high-voltage power supply adopts 600~1000V.
5, a kind of phone housing according to claim 1 black preparation method, it is characterized in that: pure metal layer described in the step (e) adopts titanium or chromium.
6, a kind of phone housing according to claim 1 black preparation method, it is characterized in that: intermediate layer described in the step (f) adopts titanium nitride or chromium nitride.
7, a kind of phone housing according to claim 1 black preparation method, it is characterized in that: black dura mater described in the step (g) adopts titanium carbonitride or carbon chromium nitride.
8, a kind of phone housing according to claim 1 black preparation method, it is characterized in that: electrostatic protection film described in the step (i) adopts PE electrostatic protection film.