CN101338164A - Computer color-mixed base paint - Google Patents
Computer color-mixed base paint Download PDFInfo
- Publication number
- CN101338164A CN101338164A CNA2008102132936A CN200810213293A CN101338164A CN 101338164 A CN101338164 A CN 101338164A CN A2008102132936 A CNA2008102132936 A CN A2008102132936A CN 200810213293 A CN200810213293 A CN 200810213293A CN 101338164 A CN101338164 A CN 101338164A
- Authority
- CN
- China
- Prior art keywords
- base paint
- portions
- mixed base
- computer color
- rev
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a computer tinting basic paint, the formulation of which is as follows: 20-30 portions of ionic water, 0.15-1.5 portions of dispersant, 0.1-1 portions of wetting agent, 0.03-0.3 portions of defoaming agent, 0-25 portions of titanium dioxide, 10-45 portions of filling, 0.1-2 portions of nano-material, 0.3-3 portions of propylene glycol, 0.2-2 portions of Eastman Teaxnol, 0.06-0.7 portions of mildewproof and anticorrosion agent, 20-40 portions of latex and 0.01-1 portions of thickener. Compared with other products, the computer tinting basic paint has the advantages that firstly, the generality is good, the paint can be applied to internal and external walls, and the production and sale costs can be lowered; secondly the tinting is accurate and the color reproducibility is good; thirdly, organic pollutants can be degraded, and the paint is provided with self-cleaning function and super-strong adhesion, rigidity, rinsing resistance and durability.
Description
Technical field
The present invention relates to a kind of water-borne coatings for building, is that building coating is covered with paint, lacquer, colour wash, etc. general computer color-mixed base paint.
Background technology
Along with improving constantly of standard of living, people are more and more personalized, diversified to the requirement of home decoration color.Just adopted computer color-mixed since the fifties in the building coating field abroad.On China market, be applied at present computer color-mixed base paint and often will be used for inner wall of building and external wall kind separately.So exist manufacturer to produce production cost because of production formula and kind increase and increase, problem such as the production unit utilization ratio is low causes distributing customer's product inventory to increase shortcomings such as maintenance cost height simultaneously.And the computer color-mixed base paint quality that each enterprise produces is uneven, performances such as paint film adhesion, hardness, abrasion resistance and weather resistance all a little less than, the color that accesses is not accurate enough, poor reproducibility, and, can't meet customer need with shortcomings such as popular mill base consistency differences on the market.
Entered since the new millennium, as the nanotechnology of hot topic, enjoy people's attention and attention, people wish that it has greater functionality.Have fundamental characteristics such as small-size effect, quantum size effect, surface effects and macro quanta tunnel effect because of nano material.Make coating have superpower sticking power, hardness, abrasion resistance and weather resistance after adding corresponding nano material, and have degradable organic pollutant and self-cleaning function.
Summary of the invention
The universal computer color-mixed base paint of exterior wall in the object of the present invention is to provide, it is made up of the base paint of different content titanium dioxide, select the different base paint of titanium dioxide content can access up to ten thousand kinds of colors according to the depth of color only during toning, as the darker color selection free white powder or the base paint of low-titanium white powder content, more shallow color is selected the base paint of high titanium dioxide content.It has, and the toning cost is low, and color reproducibility is good, interior exterior wall general and with market on most mill bases good consistency is all arranged, and adopt nano material, degrading organic pollutant has advantages such as self-cleaning function.
The present invention is achieved by following technical solution, and its prescription is by weight as follows:
Deionized water 20-30 part
Dispersion agent 0.15-1.5 part
Wetting agent 0.1-1 part
Defoamer 0.03-0.3 part
Titanium dioxide 0-25 part
Filler 10-45 part
Nano material 0.1-2 part
Propylene glycol 0.3-3 part
Yi Shiman Teaxnol 0.2-2 part
Antisepticize and mildew preventive 0.06-0.7 part
Emulsion 20-40 part
Thickening material 0.01-1 part
Described dispersion agent is at least a among Sheng Nuopuke Dispersant 5040 or the Dispersant 5027;
Described wetting agent be among DOW Chemical X-405 and the peaceful PE100 of section any one;
Described defoamer be among Sheng Nuopuke SN345 and the Ou Feiya EROL AMP108 any one;
Described filler is talcum powder by weight ratio: kaolin: water-ground limestone=1: 0.1-0.5: 0.3-3;
Described nano material is nano silicon: nano titanium oxide=0.1-1: 1-0.1 by weight ratio;
Described Antisepticize and mildew preventive is at least a among bright Sheng Preventol D7, ROHM AND HAAS LXE, ROHM AND HAAS ROZONE2000, the bright Sheng PreventolA6;
Described emulsion be among ROHM AND HAAS AC-261P or the national starch NaPoly2900 any one;
Described thickening material is at least a among sea this RHEOLATE212 of name and the Lockwood OPTIFLO H400.
Computer color-mixed base paint preparation method of the present invention is as follows:
Take by weighing deionized water by weight, under 300-600 rev/min rotating speed, drop into dispersion agent, wetting agent, defoamer successively, under 600-1000 rev/min rotating speed, drop into titanium dioxide, filler, nano material, disperseed 5-45 minute; Under 1200-1500 rev/min rotating speed, disperseed 10-60 minute; Quality inspection fineness≤50 μ m; Under 100-400 rev/min rotating speed, drop into propylene glycol, Yi Shiman Teaxnol, Antisepticize and mildew preventive, emulsion, thickening material successively, get product after the filtration that is uniformly dispersed.
The present invention compares with other products has following advantage:
1. versatility is good, and inner, external wall is all applicable, can reduce the production and sales cost.
2. toning is accurate, and color reproducibility is good.
3. can degradable organic pollutant, have self-cleaning function, have superpower sticking power, hardness, abrasion resistance and weather resistance.
Embodiment
Embodiment 1
Take by weighing 20 parts of deionized waters by weight, under 300 rev/mins rotating speed, drop into 0.7 part of dispersion agent, 0.3 part of wetting agent, 0.1 part of defoamer successively; At 700 rev/mins rotating speed, drop into 40 parts of fillers, 0.3 part of nano material, disperseed 10 minutes; Under 1200 rev/mins rotating speed, disperseed quality inspection fineness≤50 μ m 10-60 minute; Under 400 rev/mins of rotating speeds, drop into 1 part of propylene glycol, 1 part of Yi Shiman Teaxnol, 0.2 part of Antisepticize and mildew preventive, 36 parts of emulsions, 0.4 part of thickening material successively, get product after the filtration that is uniformly dispersed.
Embodiment 2
Take by weighing 22 parts of deionized waters by weight, under 400 rev/mins rotating speed, drop into 1.4 parts of dispersion agents, 0.6 part of wetting agent, 0.2 part of defoamer successively; Under 800 rev/mins rotating speed, drop into 8 parts of titanium dioxides, 30 parts of fillers, 0.6 part of nano material, disperseed 15 minutes; Under 1300 rev/mins rotating speed, disperseed quality inspection fineness≤50 μ m 40 minutes; Under 600 rev/mins rotating speed, drop into 2 parts of propylene glycol, 2 parts of Yi Shiman Teaxnol, 0.4 part of Antisepticize and mildew preventive, 32.2 parts of emulsions, 0.6 part of thickening material successively, get product after the filtration that is uniformly dispersed.
Embodiment 3
Take by weighing 25 parts of deionized waters by weight, under 500 rev/mins rotating speed, drop into 1.5 parts of dispersion agents, 0.8 part of wetting agent, 0.3 part of defoamer successively; Under 900 rev/mins rotating speed, drop into 20 parts of titanium dioxides, 20 parts of fillers, 1 part of nano material, disperseed 20 minutes; Under 1500 rev/mins rotating speed, disperseed quality inspection fineness≤50 μ m 45 minutes; Under 800 rev/mins rotating speed, drop into 2 parts of propylene glycol, 2 parts of Yi Shiman Teaxnol, 0.5 part of Antisepticize and mildew preventive, 26 parts of emulsions, 0.9 part of thickening material successively, get product after the filtration that is uniformly dispersed.
Main raw material(s) title, technical indicator:
1. Sheng Nuopuke Dispersant 5040
Solids component (%): 43
2. Sheng Nuopuke Di spersant 5027
Solids component (%): 20
3. DOW Chemical X-405
Effective constituent (%): 70
4. the peaceful PE100 of section
Effective constituent (%): 99
5. Sheng Nuopuke SN345
Effective constituent (%): 〉=98
6. the inferior EROL AMP108 of Ou Fei
The modified organic silicon type
Effective constituent (%): 〉=99
7. titanium dioxide
Rutile-type
TiO
2Content (%) 〉=95
8. talcum powder
Fineness (order): 800-1500
9. kaolin
Fineness (order): 800-2000
10. water-ground limestone
Fineness (order): 800-1500
11. nano silicon
Fineness (nm)≤50
12. nano titanium oxide
Fineness (nm): 10-30
13.Texanol
Density: 0.95g/cm
3
Rate of volatilization: 0.002
Vapour pressure: 1.33pa
14. bright Sheng Preventol D7
Activeconstituents: the mixture of multiple isothiazolinone
Effective constituent (%): 〉=99
15. ROHM AND HAAS LXE
Gross activity composition (%): 1.5
16. ROHM AND HAAS ROZONE2000
Density d
20/4(25 ℃) 1.10g/ml
17. bright Sheng PreventolA6
Effective constituent (%): 〉=99
18. ROHM AND HAAS AC-261P
Admittedly contain (%): 50
19. national starch NaPo1y2900
Admittedly contain (%): 48
20. sea this RHEOLATE212 of name
Effective constituent (%): 20
21. Lockwood OPTIFLO H400
Admittedly contain (%): 20
22. propylene glycol technical grade.
Detect its main performance index such as following table by GB GB18582, GB/T9755 and GB/T9756.
| Test item | Standard-required | Detected result |
| Volatile organic compounds (VOC) g/L | ≤200 | 34 |
| Free formaldehyde g/kg | ≤0.1 | 0.01 |
| Dissoluble lead mg/kg | ≤90 | ＜10.0 |
| Soluble cadmium mg/kg | ≤75 | ＜1.0 |
| Soluble chromium mg/kg | ≤60 | ＜1.0 |
| Soluble mercury mg/kg | ≤60 | ＜0.1 |
| Condition in container | No lump is uniform state after the stirring | Meet |
| Application property | It is accessible to brush two roads | Meet |
| Low-temperature stability | Never degenerate | Meet |
| Time of drying (surface drying) h | ≤2 | ＜2 |
| Appearance of film | Normally | Meet |
| Water tolerance (96h) | No abnormal | Meet |
| Alkali resistance (48h) | No abnormal | Meet |
| Abrasion resistance | ≥2000 | ＞10000 |
| Artificial weathering ageing resistance's (white and light color) | 600h is non-foaming, do not peel off, flawless | Meet |
| Efflorescence, level | ≤1 | ＜1 |
| Variable color, level | ≤2 | ＜1 |
| Contamination resistance (white and light color)/% | 15 | 8 |
| Coating temperature-change resistance (5 circulations) | No abnormal | Meet |
Claims (10)
1. computer color-mixed base paint is characterized in that its formulation ratio:
Deionized water 20-30 part
Dispersion agent 0.15-1.5 part
Wetting agent 0.1-1 part
Defoamer 0.03-0.3 part
Titanium dioxide 0-25 part
Filler 10-45 part
Nano material 0.1-2 part
Propylene glycol 0.3-3 part
Yi Shiman Teaxnol 0.2-2 part
Antisepticize and mildew preventive 0.06-0.7 part
Emulsion 20-40 part
Thickening material 0.01-1 part.
2. computer color-mixed base paint as claimed in claim 1, its feature part is: described dispersion agent is at least a among Sheng Nuopuke Dispersant 5040 or the Dispersant 5027.
3. computer color-mixed base paint as claimed in claim 1, its feature part is: described wetting agent be among DOW Chemical X-405 and the peaceful PE100 of section any one.
4. computer color-mixed base paint as claimed in claim 1, its feature part is: described defoamer be among Sheng Nuopuke SN345 and the Ou Feiya EROL AMP108 any one.
5. computer color-mixed base paint as claimed in claim 1, its feature part is: described filler is talcum powder by weight ratio: kaolin: water-ground limestone=1: 0.1-0.5: 0.3-3.
6. computer color-mixed base paint as claimed in claim 1, its feature part is: described nano material is nano silicon: nano titanium oxide=0.1-1: 1-0.1 by weight ratio.
7. computer color-mixed base paint as claimed in claim 1, its feature part is: described Antisepticize and mildew preventive is at least a among bright Sheng Preventol D7, ROHM AND HAAS LXE, ROHM AND HAAS ROZONE2000, the bright Sheng PreventolA6.
8. computer color-mixed base paint as claimed in claim 1, its feature part is: described emulsion is ROHM AND HAAS AC-261P, among the national starch NaPoly2900 any one.
9. computer color-mixed base paint as claimed in claim 1, its feature part is: described thickening material is at least a among sea this RHEOLATE212 of name or the Lockwood OPTIFLO H400.
10. computer color-mixed base paint as claimed in claim 1, its feature part is: its preparation method is as follows: take by weighing deionized water by weight, under 300-600 rev/min rotating speed, drop into dispersion agent, wetting agent, defoamer successively; Under 600-1000 rev/min rotating speed, drop into titanium dioxide, filler, nano material, disperseed 5-45 minute; Under 1200-1500 rev/min rotating speed, disperseed 10-60 minute; Quality inspection fineness≤50 μ m; Under 100-400 rev/min of rotating speed, drop into propylene glycol, Yi Shiman Teaxnol, Antisepticize and mildew preventive, emulsion, thickening material successively, get product after the filtration that is uniformly dispersed.