CN101333415B - Low-lead black lacquer with high constructability and high adhesion and method for preparing same - Google Patents
Low-lead black lacquer with high constructability and high adhesion and method for preparing same Download PDFInfo
- Publication number
- CN101333415B CN101333415B CN2008101426881A CN200810142688A CN101333415B CN 101333415 B CN101333415 B CN 101333415B CN 2008101426881 A CN2008101426881 A CN 2008101426881A CN 200810142688 A CN200810142688 A CN 200810142688A CN 101333415 B CN101333415 B CN 101333415B
- Authority
- CN
- China
- Prior art keywords
- lacquer
- resin
- dispersion agent
- adhesive force
- siccative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a black glossy finish with low content of plumbum, high workability and high adhesive force, and a preparation method thereof. The black glossy finish contains(based on weight percentage) 40-50wt% of natural asphaltic resin, 30-40wt% of rosin resin, 1-3wt%of drier, 1-3wt%of dispersant, 10-20wt%of ultra-thin talcum powder and 2-6%of solvent. Through the introduction of refined natural asphaltic resin and rosin resin, the invention improves environment protection performance of the product; the application of rosin resin and ultra-thin talcum powder improves the workability and drying speed of the product and improves the adhesive force between the product and the top finish.
Description
Technical field
The present invention relates to technical field of polymer materials, relate in particular to a kind of antique effect and cover with paint, lacquer, colour wash, etc. low plumbous black light lacquer with high application property high adhesive force.
Background technology
Used black light lacquer normally forms through dissolution with solvents with petroleum pitch on the market, but owing to the not environmental protection that exceeds standard of petroleum pitch heavy metal content, and drying property has influenced the ply adhesion with finishing coat more slowly.
Summary of the invention
The technical problem that the present invention will solve provides low plumbous black light lacquer of a kind of high application property high adhesive force and preparation method thereof.
For solving the problems of the technologies described above, the objective of the invention is to realize through following technical scheme.
A kind of low plumbous black light lacquer of high application property high adhesive force, its composition is (%) by weight ratio:
Rock asphalt resin 40-50%;
Gum Rosin 30-40%;
Siccative 1-3%;
Dispersion agent 1-3%;
Super-fine talc 10-15%;
Solvent 2～6%.
Wherein, said siccative is the mixture of cobalt iso-octoate and calcium iso-octoate.
Wherein, said dispersion agent is a HMW polyurethane-type dispersion agent.
Wherein, said Gum Rosin is to defend the tetrol modified rosin resin season.
A kind of preparation method of low plumbous black light lacquer of high according to claim 1 application property high adhesive force comprises step:
A: take by weighing raw material according to weight percent;
B: add solvent and resin to system lacquer container, add while stirring then and dispersion agent, high speed 1200rpm disperseed 3-5 minute, added super-fine talc then while stirring, and high speed 1200rpm disperses 5-10 minute to fineness≤20um;
C: in system lacquer container, add siccative while stirring, middling speed stirs, and is uniformly dispersed.
Above technical scheme can find out that the present invention has following beneficial effect:
The present invention has improved the environmental-protecting performance of product through introducing through blue or green resin of process of refinement pure natural and Gum Rosin; Through use Gum Rosin and super-fine talc improved product workability, do fast, and with the ply adhesion of finish paint.
Embodiment
A kind of low plumbous black light lacquer of high application property high adhesive force, its composition is (%) by weight ratio: rock asphalt resin 40-50%, Gum Rosin 30-40%, siccative 1-3% disperses 1-3%, super-fine talc: 10-20%, solvent 2-6%; Wherein, said siccative is the mixture of cobalt iso-octoate and calcium iso-octoate; Dispersion agent is a HMW polyurethane-type dispersion agent; Gum Rosin is to defend the tetrol modified rosin resin season.
The present invention provides low plumbous black light lacquer of a kind of high application property high adhesive force and preparation method thereof.A: take by weighing raw material according to weight percent; B: add resin to system lacquer container, add while stirring then and dispersion agent, high speed dispersion (1200rpm) 3-5 minute adds super-fine talc then while stirring, and high speed dispersion (1200rpm) 5-10 minute is to fineness≤20um; C: in system lacquer container, add siccative while stirring, middling speed stirs, and is uniformly dispersed.
For ease of the present invention is further understood, combine specific embodiment to describe the present invention at present:
Embodiment 1:
With weight percent rock asphalt resin 40%, Gum Rosin 40%, dispersion agent 1%; Super-fine talc 12%, siccative 2%, solvent 5%; Process product by above-mentioned method of manufacture, the ratio of setting in prescription adds diluent, mixes; Be sprayed on the ground spraying NC matte varnish behind the dry 2-3h then with the special-purpose spray gun of coating application.
Embodiment 2:
With weight percent rock asphalt resin 42%, Gum Rosin 38%, dispersion agent 1%; Super-fine talc 15%, siccative 2%, solvent 2%; Process product by above-mentioned method of manufacture, the ratio of setting in prescription adds diluent, mixes; Be sprayed on the ground spraying NC matte varnish behind the dry 2-3h then with the special-purpose spray gun of coating application.
Embodiment 3:
With weight percent rock asphalt resin 45%, Gum Rosin 35%, dispersion agent 2%; Super-fine talc 10%, siccative 3%, solvent 5%; Process product by above-mentioned method of manufacture, the ratio of setting in prescription adds diluent, mixes; Be sprayed on the ground spraying NC matte varnish behind the dry 2-3h then with the special-purpose spray gun of coating application.
Embodiment 4:
With weight percent rock asphalt resin 47%, Gum Rosin 33%, dispersion agent 1%; Super-fine talc 14%, siccative 1%, solvent 4%; Process product by above-mentioned method of manufacture, the ratio of setting in prescription adds diluent, mixes; Be sprayed on the ground spraying NC matte varnish behind the dry 2-3h then with the special-purpose spray gun of coating application.
Embodiment 5:
With weight percent rock asphalt resin 50%, Gum Rosin 30%, dispersion agent 2%; Super-fine talc 10%, siccative 2%, solvent 6%; Process product by above-mentioned method of manufacture, the ratio of setting in prescription adds diluent, mixes; Be sprayed on the ground spraying NC matte varnish behind the dry 2-3h then with the special-purpose spray gun of coating application.
Performance test:
With above-mentioned 5 embodiment accomplish that component is mixed and the product application after test products drying property, sticking power, heavy metal content etc.
Product drying property is pressed GB/T 1728-1989
Product sticking power is pressed GB/T 1720-1989
Heavy metal content is pressed GB/T9754-1988;
Prescription and the material property of embodiment 1～5 are seen table 1:
Table 1
Through to learning after the data analysis in the above table; Along with the increase product sticking power of rock asphalt resin demand improves constantly thereupon, reach 38% when above at its consumption, sticking power is best; The drying property of paint film also improves thereupon simultaneously thus, and Gum Rosin then in contrast.When the amount of Gum Rosin is 38%, product sticking power when the amount of bituminous resins is 42%, workability are best.
More than low plumbous black light lacquer of a kind of high application property high adhesive force provided by the present invention and preparation method thereof has been carried out detailed introduction; Used concrete example among this paper principle of the present invention and embodiment are set forth, the explanation of above embodiment just is used for helping to understand method of the present invention and core concept thereof; Simultaneously, for one of ordinary skill in the art, according to thought of the present invention, the part that on embodiment and range of application, all can change, in sum, this description should not be construed as limitation of the present invention.
Claims (3)
1. the low plumbous black light of a high application property high adhesive force coats with lacquer, and it is characterized in that its composition is (%) by weight ratio:
Rock asphalt resin 40-50%;
Gum Rosin 30-40%;
Siccative 1-3%;
Dispersion agent 1-3%;
Super-fine talc 10-15%;
Solvent 2～6%;
Said dispersion agent is a HMW polyurethane-type dispersion agent; Said Gum Rosin is to defend the tetrol modified rosin resin season.
2. the low plumbous black light lacquer of high application property high adhesive force according to claim 1 is characterized in that said siccative is the mixture of cobalt iso-octoate and calcium iso-octoate.
3. the preparation method of the low plumbous black light lacquer of a high according to claim 1 application property high adhesive force is characterized in that, comprises step:
A: take by weighing raw material according to weight percent;
B: add solvent and resin to system lacquer container, add while stirring then and dispersion agent, high speed 1200rpm disperseed 3-5 minute, added super-fine talc then while stirring, and high speed 1200rpm disperses 5-10 minute to fineness≤20um;
C: in system lacquer container, add siccative while stirring, middling speed stirs, and is uniformly dispersed.