CN101318313A - Method for manufacturing water resistant flexible complete-resin abrasive cloth - Google Patents
Method for manufacturing water resistant flexible complete-resin abrasive cloth Download PDFInfo
- Publication number
- CN101318313A CN101318313A CNA2007101106198A CN200710110619A CN101318313A CN 101318313 A CN101318313 A CN 101318313A CN A2007101106198 A CNA2007101106198 A CN A2007101106198A CN 200710110619 A CN200710110619 A CN 200710110619A CN 101318313 A CN101318313 A CN 101318313A
- Authority
- CN
- China
- Prior art keywords
- resistant soft
- water
- cloth
- adopted
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing method of water resistant soft whole resin abrasive cloth and includes the following steps of grey cloth winding, singeing, water washing neutralizing, drawing, drying and setting, back pulp cutting, trimming cut and winding, unwinding and identification marking, under glue coating, high pressure electrostatic abrasive planting, pre-drying, complex adhesive coating, main drying, rolling, solidifying, curving, unrolling and warehousing; wherein, the water washing neutralizing adopts an environment-friendly water washing process, a base cloth treatment agent and novel water resistant soft pulp applying materials and the modified phenol resin under adhesive and complex adhesive are adopted as caking agents; the singeing process adopts the air fuel mixture for sintering with the temperature reaching more than 1000 DEG C; the drawing, drying and setting process is carried out on a drawing and setting machine and requires the temperature of 180 to 200 DEG C; the back pulp cuttng process adopts two materials of novel 517H64 and 205PCA (8%) 18 with the thickness of the coating being 0.05 to 0.08mm. The manufacturing method of the water resistant soft whole resin abrasive cloth has the advantages of good heat-resistance property, excellent toughness, good softening property and two performances of dry winding and wet grinding.
Description
Technical field:
The present invention relates to a kind of preparation method of emery cloth, specifically a kind of preparation method of water-resistant soft resin sand cloth.
Background technology:
At present, in the domestic coated abrasive tool product, water-fast product requirement amount is very big, but because the durable water treatment agent of present domestic use and adhesive technology performance fall behind, therefore, the problem that home products exists is as follows:
1. water resistance is poor, and after soaking in water, matrix feels like jelly, and grinding efficiency is low, particularly in southern rainy season, directly can not use.
2. the alkyd resins adhesion strength of Cai Yonging is low, causes abrasive material to come off easily, influences anti-wear performance.
3. adhesive fragility is big, and is easily aging, deposits to occur the phenomenon of being chapped from the cold later in 2 months, has a strong impact on and use performance.
Owing to above reason, domestic main dependence import is at present met the need of market, and is domesticly still belonging to blank aspect the water-resistant soft emery cloth product.
Summary of the invention
Technical problem to be solved of the present invention is at the prior art weak point, the invention provides a kind of preparation method of water-resistant soft resin sand cloth, it is good that this new method makes the product heat resistance of producing, good-toughness, softness is good, possesses dry grinding and two kinds of performances of wet-milling.
The technical solution adopted for the present invention to solve the technical problems is: a kind of preparation method of water-resistant soft resin sand cloth, and its making step is:
Grey cloth reels-singes-wash neutralization-stretching dryness finalization-back side cut to pieces slurry-side cut coiling-uncoiling identification marking-be coated with primer-high-pressure electrostatic plant sand-predrying-coated glue-trunk dry-rolling-curing-gentle song-bundling-warehouse-in;
Environment-friendly type washing technology has been adopted in described washing neutralization, and base cloth inorganic agent and novel water-resistant soft are cut slurry to pieces, and binding agent has adopted new modified phenolic resin primer and multiple glue;
Described singeing adopts the oil gas mixing to carry out sintering, and temperature can reach more than 1000 ℃;
Draw stretch dryness finalization technology be draw stretch and forming machine on carry out temperature requirement: 180 ℃-200 ℃;
The described back side is scraped sizing process and is adopted 18 two kinds of materials of novel 517H64 and 205PCA (8%), and coating layer thickness is the 0.05-0.08 millimeter.
The preparation method of a kind of water-resistant soft resin sand cloth of the present invention is compared with original technology, has following beneficial effect:
Product bond strength height of the present invention, its hot strength and domestic traditional product project improve 46%;
1, heat resistance is good, can be long-term used in 285 ℃ of hot environments, and short-term is used can reach 400 ℃;
3, good-toughness, impact strength are 1.5 times of traditional product;
4, softness is good, can be crooked arbitrarily, and energy grinding big bottle face and shaped face;
5, grinding intensity is 4 times of dry abrasive cloth, is 13 times of water mill emery cloth, possesses dry grinding and two kinds of performances of wet-milling;
6, product is widely used in manufacturings such as machinery, chemical industry, metallurgy, building, five metals, automobile and furniture, is applicable to the processing of big plane and shaped face.
The specific embodiment
Embodiment 1:
Grey cloth reels-singes-wash neutralization-stretching dryness finalization-back side cut to pieces slurry-side cut coiling-uncoiling identification marking-be coated with primer-high-pressure electrostatic plant sand-predrying-coated glue-trunk dry-rolling-curing-gentle song-bundling-warehouse-in;
Environment-friendly type washing technology has been adopted in described washing neutralization, and base cloth inorganic agent and novel water-resistant soft are cut slurry to pieces, and binding agent has adopted new modified phenolic resin primer and multiple glue;
Described singeing adopts the oil gas mixing to carry out sintering, and temperature is 1000 ℃;
Draw stretch dryness finalization technology be draw stretch and forming machine on carry out temperature requirement: 180 ℃;
The described back side is scraped sizing process and is adopted 18 two kinds of materials of novel 517H64 and 205PCA (8%), and coating layer thickness is 0.05 millimeter.
Other technologies needn't be given unnecessary details, and are prior art.
Embodiment 2:
Grey cloth reels-singes-wash neutralization-stretching dryness finalization-back side cut to pieces slurry-side cut coiling-uncoiling identification marking-be coated with primer-high-pressure electrostatic plant sand-predrying-coated glue-trunk dry-rolling-curing-gentle song-bundling-warehouse-in;
Environment-friendly type washing technology has been adopted in described washing neutralization, and base cloth inorganic agent and novel water-resistant soft are cut slurry to pieces, and binding agent has adopted new modified phenolic resin primer and multiple glue;
Described singeing adopts the oil gas mixing to carry out sintering, and temperature is 1000 ℃;
Draw stretch dryness finalization technology be draw stretch and forming machine on carry out temperature requirement: 200 ℃;
The described back side is scraped sizing process and is adopted 18 two kinds of materials of novel 517H64 and 205PCA (8%), and coating layer thickness is 0.08 millimeter.
Other technologies needn't be given unnecessary details, and are prior art.
Embodiment 3:
Grey cloth reels-singes-wash neutralization-stretching dryness finalization-back side cut to pieces slurry-side cut coiling-uncoiling identification marking-be coated with primer-high-pressure electrostatic plant sand-predrying-coated glue-trunk dry-rolling-curing-gentle song-bundling-warehouse-in;
Environment-friendly type washing technology has been adopted in described washing neutralization, and base cloth inorganic agent and novel water-resistant soft are cut slurry to pieces, and binding agent has adopted new modified phenolic resin primer and multiple glue;
Described singeing adopts the oil gas mixing to carry out sintering, and temperature is 1000 ℃;
Draw stretch dryness finalization technology be draw stretch and forming machine on carry out temperature requirement: 190 ℃;
The described back side is scraped sizing process and is adopted 18 two kinds of materials of novel 517H64 and 205PCA (8%), and coating layer thickness is 0.065 millimeter.
Other technologies needn't be given unnecessary details, and are prior art.
Wherein embodiment 3 is a most preferred embodiment, and its product of producing is a best product.
Claims (3)
1, a kind of preparation method of water-resistant soft resin sand cloth, its making step is:
Grey cloth reels-singes-wash neutralization-stretching dryness finalization-back side cut to pieces slurry-side cut coiling-uncoiling identification marking-be coated with primer-high-pressure electrostatic plant sand-predrying-coated glue-trunk dry-rolling-curing-gentle song-bundling-warehouse-in;
Environment-friendly type washing technology has been adopted in described washing neutralization, and base cloth inorganic agent and novel water-resistant soft are cut slurry to pieces, and binding agent has adopted new modified phenolic resin primer and multiple glue;
Described singeing adopts the oil gas mixing to carry out sintering, and temperature can reach more than 1000 ℃;
Draw stretch dryness finalization technology be draw stretch and forming machine on carry out temperature requirement: 180 ℃-200 ℃;
The described back side is scraped sizing process and is adopted 18 two kinds of materials of novel 517H64 and 205PCA (8%), and coating layer thickness is the 0.05-0.08 millimeter.
2, the preparation method of a kind of water-resistant soft resin sand cloth according to claim 1, described drawing stretched the requirement of dryness finalization technological temperature: 190 ℃.
3, the preparation method of a kind of water-resistant soft resin sand cloth according to claim 1, sizing process is scraped at the described back side, and its coating layer thickness is 0.065 millimeter.