CN101302386A - Anti-pollution pearlescent exterior wall paint - Google Patents
Anti-pollution pearlescent exterior wall paint Download PDFInfo
- Publication number
- CN101302386A CN101302386A CNA2007100278623A CN200710027862A CN101302386A CN 101302386 A CN101302386 A CN 101302386A CN A2007100278623 A CNA2007100278623 A CN A2007100278623A CN 200710027862 A CN200710027862 A CN 200710027862A CN 101302386 A CN101302386 A CN 101302386A
- Authority
- CN
- China
- Prior art keywords
- percent
- pearlescent
- wall paint
- pollution
- exterior wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antifouling pearlescent outer wall paint. The antifouling pearlescent outer wall paint is characterized by mainly consisting of the following materials in percentage by weight: 3 to 28 percent of soft water, 0.1 to 0.23 percent of hydroxyethylcellulose, 0.1 to 0.2 percent of preservative, 0.1 to 0.4 percent of mildewcide, 1 to 3 percent of propanediol, 0.1 to 0.28 percent of organic amine, 0.1 to 0.3 percent of amine salt dispersant, 0.01 to 0.1 percent of low-foam wetting agent, 0.03 to 0.23 percent of defoaming agent, 60 to 90 percent of silicon modified pure acrylic emulsion with a vitrification temperature of over 33 DEG C, 1 to 3 percent of ethylene-polyvinyl acetate emulsion, 3 to 5 percent of dodecanol lipid, 5 to 20 percent of pearlescent powder with good weather resistance and 0.1 to 0.3 percent of thickening agent. The paint is used for an outdoor craftwork, an outer door, etc, has high hardness and good flexility, weather resistance, scrub resistance and antifouling property, also emits fascinated luster like jewelry and is water-based environment-friendly.
Description
Technical field
The present invention relates to a kind of water-borne coatings, particularly a kind ofly be used for outdoor artwork, applications such as exterior wall have the exterior coating of pearly-lustre and pollution resistance.
Background technology
Be used for outdoor artwork at present, what the coating of exterior wall etc. had is oiliness, not environmental protection; Though what have is water-based, hardness is low, abrasion resistance, and pollution resistance is relatively poor, or does not resemble the charming brilliance that jewelry sends.
Summary of the invention
In order to overcome the deficiencies in the prior art, the invention provides a kind of outdoor artwork that is used for, applications such as exterior wall have the exterior wall water-borne environmental protection coating material of pearly-lustre and pollution resistance.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of anti-pollution pearlescent exterior wall paint is characterized in that this coating mainly is made up of following materials in weight percentage: soft water 3-28%, Natvosol 0.1-0.23%, sanitas 0.1-0.2%, mould inhibitor 0.1-0.4%, propylene glycol 1-3%, organic amine 0.1-0.28%, amine salt dispersion agent 0.1-0.3%, low-foam wetting agents 0.01-0.1%, defoamer 0.03-0.23%, the silicon modification pure-acrylic emulsion 60-90% of second-order transition temperature more than 33 ℃, ethene-polyvinyl acetate emulsion 1-3%, lauryl alcohol fat 3-5%, weathering resistance is pearlescence 5-20% preferably, thickening material 0.1-0.3%.
The material that the present invention adopts all can directly be bought from market, and as the emulsion that the silicon modification pure-acrylic emulsion of second-order transition temperature more than 33 ℃ adopts American, Guangdong company to produce, lauryl alcohol fat can be purchased from Hubei company of Xinhua, and sanitas can be purchased from U.S. Rhom and Hass.
The present invention removes pearlescence and adds at last, and outside low speed disperseed, rest materials all put into production successively by the emulsion paint common process.
Beneficial effect of the present invention is: be used for outdoor artwork, and applications such as exterior wall, it is higher to have hardness, abrasion resistance, weathering resistance, pollution resistance is better; Resemble the charming brilliance that jewelry sends in addition; Aqueous, environmental protective.
Because silicon modification pure-acrylic emulsion and the ethene-polyvinyl acetate emulsion compound system, anti-after tackiness of the second-order transition temperature that adds among the present invention more than 33 ℃ is better, hardness, snappiness is better, abrasion resistance, weathering resistance, pollution resistance is better, aqueous, environmental protective; Weathering resistance preferably pearlescence outdoor have for a long time resemble the charming brilliance that jewelry sends; Sanitas, mould inhibitor content is low, than general environmental protection.
The present invention is further described below in conjunction with embodiment.
Embodiment
Embodiment 1 (unit: kilogram; Total amount: 100 kilograms)
Soft water: silicon modification pure-acrylic emulsion 68 more than 33 ℃ of surplus, Natvosol 0.2, sanitas 0.1, mould inhibitor 0.28, propylene glycol 2, organic amine 0.13, amine salt dispersion agent 0.18, low-foam wetting agents 0.05, defoamer 0.08, second-order transition temperature, ethene-polyvinyl acetate emulsion 1, lauryl alcohol fat 3.4, weathering resistance be pearlescence 12, thickening material 0.23 preferably.
Embodiment 2 (unit: kilogram; Total amount: 100 kilograms)
Soft water: silicon modification pure-acrylic emulsion 72 more than 33 ℃ of surplus, Natvosol 0.18, sanitas 0.1, mould inhibitor 0.32, propylene glycol 2, organic amine 0.16, amine salt dispersion agent 0.2, low-foam wetting agents 0.06, defoamer 0.1, second-order transition temperature, ethene-polyvinyl acetate emulsion 2, lauryl alcohol fat 3.6, weathering resistance be pearlescence 10, thickening material 0.17 preferably.
Embodiment 3 (unit: kilogram; Total amount: 100 kilograms)
Soft water: silicon modification pure-acrylic emulsion 75 more than 33 ℃ of surplus, Natvosol 0.13, sanitas 0.12, mould inhibitor 0.38, propylene glycol 2, organic amine 0.1, amine salt dispersion agent 0.18, low-foam wetting agents 0.05, defoamer 0.13, second-order transition temperature, ethene-polyvinyl acetate emulsion 1, lauryl alcohol fat 3.8, weathering resistance be pearlescence 8, thickening material 0.13 preferably.
Claims (3)
1. anti-pollution pearlescent exterior wall paint is characterized in that this coating mainly is made up of following materials in weight percentage: silicon modification pure-acrylic emulsion 60-90% more than 33 ℃ of soft water 3-28%, propylene glycol 1-3%, organic amine 0.1-0.28%, low-foam wetting agents 0.01-0.1%, second-order transition temperature, ethene-polyvinyl acetate emulsion 1-3%, lauryl alcohol fat 3-5%, weathering resistance be pearlescence 5-20%, thickening material 0.1-0.3% preferably.
2. a kind of anti-pollution pearlescent exterior wall paint according to claim 1 is characterized in that it also includes mould inhibitor 0.1-0.4%, amine salt dispersion agent 0.1-0.3%, defoamer 0.03-0.23%.
3. a kind of anti-pollution pearlescent exterior wall paint according to claim 2 is characterized in that it also includes Natvosol 0.1-0.23%, sanitas 0.1-0.2%.