CN101294285A - Carburizing technique for medium carbon steel cold rolled bearing case loop - Google Patents
Carburizing technique for medium carbon steel cold rolled bearing case loop Download PDFInfo
- Publication number
- CN101294285A CN101294285A CNA2007100543050A CN200710054305A CN101294285A CN 101294285 A CN101294285 A CN 101294285A CN A2007100543050 A CNA2007100543050 A CN A2007100543050A CN 200710054305 A CN200710054305 A CN 200710054305A CN 101294285 A CN101294285 A CN 101294285A
- Authority
- CN
- China
- Prior art keywords
- carburizing
- carbon steel
- medium carbon
- bearing ring
- cold rolling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a carburizing process for cold rolling the bearing ring through medium carbon steel, which belongs to the technology field of heat treatment. A circular ring is made of tubes or bar stock through punching or forging into wafer after annealing, and made into a bearing ring through cold rolling; then carburizing heat treatment process is performed; in the carburizing atmosphere of 1.15 percent of carbon potential, direct quenching is performed after carburizing is performed for 10 hours at the temperature of 850 to 870 DEG C; the tempering temperature is 150 to 160 DEG C, and the temper time is 3 to 4 hours. The medium carbon steel bearing ring after being treated through the carburizing process has higher toughness and longer fatigue life; particularly, for the bearing working under the contaminated environment, the service life and the operational reliability can be improved.
Description
Technical field
The invention belongs to the heat treatment technics field, specially refer to the cold rolling bearing ring of a kind of medium carbon steel carburization process.
Background technology
The bearing ring common used material mostly is high-carbon-chromium bearing steel greatly, and its carbon content is higher, both just annealed processing, and the cold deformation drag is still higher, influences the work-ing life of cold rolling performance and mould, and is prone to crackle and becomes waste product by the rolling lasso cold running in the journey.External famous bearing company such as NSK etc. have carried out medium carbon alloy steel manufacturing bearing ring in eighties of last century, and adopted special thermal treatment technology the nineties, can make bearing life, and especially the bearing life under the pollution lubricating condition increases substantially.
Medium carbon steel has good cold rolling performance, by cold rolling, and can material-saving, improve tissue, adopt special thermal treatment technology, can make bearing life, especially the bearing life under the pollution lubricating condition increases substantially, but the carburizing heat treatment process of centering carbon steel bearing lasso is not reported as yet.
Summary of the invention
For solving medium carbon steel bearing ring carburizing heat treatment process, the present invention has designed the cold rolling bearing ring of a kind of medium carbon steel carburization process, use the medium carbon steel bearing ring after this carburization process is handled to have higher toughness and longer fatigue lifetime, especially the bearing of working under contaminate environment can improve work-ing life and operating reliability.
For achieving the above object, the present invention adopts following technical scheme:
The cold rolling bearing ring of described medium carbon steel carburization process, the cold rolling bearing ring of its medium carbon steel are in the carburizing atmosphere of 1.15% carbon potential, in 850～870 ℃ of carburizing direct quenchings after 10 hours, 150～160 ℃ of tempering temperatures, tempering time 3～4 hours.
Because adopt aforesaid technical scheme, the present invention has following superiority:
1), the cold rolling bearing ring of medium carbon steel is carried out carburizing heat treatment process, utilizes cold deformation to improve infiltration rate or reduce the carburizing or carbonitriding temperature.
2), the ring table surface layer after handling is distributed with the carbonitride of a large amount of small and disperseds and up to 25～30% residual austenite, can improves the fatigue crack growth resistance of bearing in contaminate environment, reduces crack growth rate, improves bearing work-ing life.
3), compare with the martensite of the routine tempering high-carbon-chromium bearing steel lasso of quenching, the lasso after the processing has higher toughness and longer fatigue lifetime, and especially the bearing of working under contaminate environment can improve work-ing life and operating reliability.
Embodiment
The cold rolling bearing ring of medium carbon steel of the present invention, adopt pipe truck system or bar to forge cake punching annealing back car and make annulus, and through the cold bearing ring of rolling over into, carry out carburizing heat treatment process then: in the carburizing atmosphere of 1.15% carbon potential, in 850～870 ℃ of carburizing direct quenchings after 10 hours, 150～160 ℃ of tempering temperatures, tempering time 3～4 hours.
Bearing ring is selected medium carbon steel for use and after cold rolling, it organizes the ball track portion of tissue that especially deformation ratio is bigger, compare with the lasso that general high-carbon-chromium bearing steel Vehicle Processing is shaped wide variation have taken place, the maximum characteristics that change are that crystal grain is crushed in cold rolling deformation process, and have a large amount of dislocations and subgrain boundary.This being organized in through behind the carburization process of the present invention, its structural transformation mechanism obviously is different from not Deformation structure, and cementation zone is organized very tiny, near nano level.
The cold rolling bearing ring of medium carbon alloy steel adopts carburizing heat treatment process, the work-ing life that can improve pollution lubricating condition lower bearing greatly.The cold rolling bearing ring of medium carbon steel of the present invention carburization process can be widely used in the bearing that uses under the pollution lubricating conditions such as various vehicle gear boxes, mining equiment, improve the state of the art and the quality product of industry, improve the international competitiveness of homemade bearing, its social benefit and economic benefit are more remarkable.
Claims (1)
1, the cold rolling bearing ring of a kind of medium carbon steel carburization process, it is characterized in that: the cold rolling bearing ring of this medium carbon steel is in the carburizing atmosphere of 1.15% carbon potential, in 850～870 ℃ of carburizing direct quenchings after 10 hours, 150～160 ℃ of tempering temperatures, tempering time 3～4 hours.