CN101293005B

CN101293005B - Negative ion smokeless moxa roll and preparation method thereof

Info

Publication number: CN101293005B
Application number: CN200710040088XA
Authority: CN
Inventors: 许浒
Original assignee: SHANGHAI CAIYI BIOTECHNOLOGY CO Ltd
Current assignee: SHANGHAI CAIYI BIOTECHNOLOGY CO Ltd
Priority date: 2007-04-27
Filing date: 2007-04-27
Publication date: 2011-04-06
Anticipated expiration: 2027-04-27
Also published as: CN101293005A

Abstract

The invention discloses an anion smoke-free moxa stick. The product of the invention is prepared by taking artemesia carbon, tourmaline, good jade wine, zeolite and iron oxide as raw materials. The product of the invention has the effects of efficient emission of infrared rays and release of anions, which can lead the moxa stick to be burnt fully, achieve the smoke eliminating effect, reduce the environmental pollution, enhance the efficacy of the moxa stick and have greater application value.

Description

Negative ion smokeless moxa roll and preparation method thereof

Technical field:

The present invention relates to Chinese medicine, be specifically related to negative ion smokeless moxa roll and preparation method thereof.

Background technology:

Pay attention in health care and the disease treatment people, many tcm therapies have entered health care and treatment field.Traditional Chinese medical science moxibustion has become the generally health care therapeutic method of approval.

Folium Artemisiae Argyi is the primary raw material of traditional Chinese medical science moxibustion therapy, usually, when moxibustion Folium Artemisiae Argyi is made moxa roll and uses.Use the effect that Folium Artemisiae Argyi is brought into play in the moxibustion process to mainly contain two aspects, the one, thermogenetic effect; The 2nd, the chemical constituent effect of the Ai Yanzhong of the contained volatile oil of Folium Artemisiae Argyi in combustion process, and Chinese mugwort cigarette volatile ingredient is mainly ammonia, kinds more than 20 such as ethanol, ethylene glycol acetic acid, acetamide, propanoic acid, first furan.The existing composition that keeps healthy, treat of being used in the Folium Artemisiae Argyi volatile ingredient, still, also there are some defectives in they.For example:

Though 1, the Chinese mugwort cigarette has disinfecting air, anophelifuge etc. that human body is had certain beneficial effect, but the abnormal smells from the patient that is not suitable for of the cigarette that ends is its shortcoming;

2, the Chinese mugwort cigarette has stimulation to asthma patient, may bring out asthma or increase the weight of the state of an illness.

Based on above problem, some relevant methods that reduce smoke of having reported have been studied.

At present, mainly contain following several for the method that reduces the Chinese mugwort cigarette:

1) because the generation of Chinese mugwort cigarette is main relevant with the Folium Isatidis in the Folium Artemisiae Argyi, and Folium Isatidis is few more, and Folium Artemisiae Argyi is white more, and the Chinese mugwort cigarette is also few more, therefore, the Chinese mugwort cigarette is relevant with the quality of Folium Artemisiae Argyi, can manage to solve the problem of removing Folium Isatidis, but select Folium Artemisiae Argyi to become the big problem of raw material sources.

2) in Folium Artemisiae Argyi, increase some aromatic substances as Lignum Santali Albi, Moschus biomass, the Chinese mugwort cigarette tarted up, but this fragrance not necessarily is fit to, and curative effect is had certain influence.

Thereby said method is not the basic way of dealing with problems.

Summary of the invention:

Technical problem to be solved by this invention is to overcome above-mentioned weak point, and research design can solve the moxa roll smoke, can improve the moxa roll of curative effect again.

The invention provides a kind of negative ion smokeless moxa roll.

Smokeless moxa roll of the present invention contains the constituent of following weight percent proportion raw material:

Chinese mugwort charcoal 70-90wt%

Mellow liquor jade 1-5wt%

Zeolite 0.5-1.5wt%

Tourmaline 6-24wt%

Ferrum oxide 0.3-0.5wt%

Elm powder 0.5-3wt%

The raw material constituent of selecting in the prescription of the present invention has following characteristics:

1. charcoal ends: select the Chinese mugwort charcoal, can reach the medicinal ingredient of both having brought into play Folium Artemisiae Argyi, reduce the effect of smoke again, and can use with the tourmaline coupling.

2. tourmaline: its unique curative effect effect is arranged:

1, increases the far infrared effect

1. the far infrared wavelength scope of moxa roll is 0.8---and 4.4 microns

2. the far infrared wavelength scope of tourmaline is 4---and 14 microns, emissivity is up to 0.92.

2, piezoelectric effect: promptly tourmaline can make the phenomenon of its surface charging under pressure.

3, pyroelectric effect: because variation of temperature causes the phenomenon of tourmaline heating.

Because tourmaline exists piezoelectric effect and pyroelectric effect simultaneously, thereby tourmaline has following special performances, tourmaline and moxibustion instrument and usefulness, because the heat effect of moxibustion, the pyroelectric effect of having strengthened holding in the palm agate is strengthened the following function of tourmaline and gives full play to.

(1), efficiently emitting far-infrared;

(2), continue to discharge anion;

(3), has similar bioelectric weak current effect;

(4), has the surface activity effect;

(5), has the inhibiting bacteria and diminishing inflammation effect.

3. mellow liquor jade: emission far infrared effect.

4. zeolite: it can absorb gas with foreign flavor.

5. ferrum oxide: discharge anion and eliminate the effect of toxic gas.

Above-mentioned raw materials can obtain by commercially available.

For realizing technical scheme of the present invention, the inventor has also done a large amount of research:

(1) solved consistency problem

1. tourmaline is a gem level ore materials, and whether the physicochemical property of its physicochemical property and other composition such as Chinese mugwort charcoal etc. is compatible is complementary.Experimental result proves, five kinds of materials all are the far good material of emission, have the capacitive of thinking, matching, and the present invention just selects to end charcoal and the reason of not selecting Folium Artemisiae Argyi especially.

2. the coupling of diameter of particle, the particle diameter of tourmaline is the key issue of mating with raw material, particle diameter is excessive, the effect of tourmaline can not be given full play to, because of tourmaline is a polar substances, its piezoelectric effect and pyroelectric effect must match with relevant particle size, its function of competence exertion, and it is the 0.3-5 micron that the present invention selects the particle diameter of tourmaline especially.

(2) adjusted the best proportioning of filling a prescription

Because of tourmaline powder body proportion is 3.0-3.3.And the proportion of Chinese mugwort charcoal has only 0.3-0.9, five kinds of material proportion great disparities quite big, therefore has only repetition test that two ratio is adjusted to selection of the present invention, and the ability mix homogeneously reaches easy to process, the effect of determined curative effect.

(3) during negative ion smokeless moxa roll is made, select which type of binding agent also very important, one will guarantee nontoxicly, and two will guarantee bondingly, and elm glue is natural glue, bonding effect might as well, so the present invention chooses usefulness elm glue as binding agent.

Another object of the present invention has provided the preparation method of negative ion smokeless moxa roll, and this method comprises the following steps:

1) Chinese mugwort powdered carbon preparation: get the Chinese mugwort charcoal, be crushed to 200-500 purpose fine powders;

2) preparation of tourmaline, mellow liquor jade, zeolite, ferric oxide powder:

A. get tourmaline mellow liquor jade, zeolite, the cleaning of ferrum oxide decontamination, sterilization, dry, pulverizing respectively;

B. respectively with tourmaline,, mellow liquor jade, zeolite, ferrum oxide be ground to 200-500 order fine powders;

3). with above-mentioned Chinese mugwort charcoal, tourmaline, mellow liquor jade, zeolite, the full and uniform mixing of ferrum oxide fine powder, adding is ground to 200-500 purpose elm powder again;

4) with the mixed powder of step 3) press forming in the mould of compacting moxa roll, get product.

Negative ion smokeless moxa roll of the present invention has following remarkable result:

One, the far infrared effect is remarkable

1, the far infrared wavelength scope of Folium Artemisiae Argyi is at 0.8-4.4 microns;

2, the far infrared wavelength scope of tourmaline is at 4-14 microns, and emissivity is up to 0.92;

3, five kinds of material compositions are united utilization, are strengthened for far emissivity, supply with the human body more energy;

4, broad more for wave-length coverage, 0.8 between-14 microns, such result, two absworption peaks of human body skin have been covered for far infrared, i.e. two absworption peaks of 2.5-4 microns and 5.6-10 microns, this has not only strengthened human body to far absorption, and has strengthened the suction of human body to the oil that ends, and has strengthened far infrared and the Chinese mugwort oil dual function to human body.Through spectrum analysis, five kinds of raw materials share, no matter on spectral region, on the radiant intensity, still on penetrating power, all surpass single Chinese mugwort charcoal composition of using, and have embodied five kinds of stack and cooperative effects that raw material share.

Two, moxa roll can fully be burnt

Because tourmaline can well-off electronics, make moxa roll be in weakly alkaline environment, the charcoal itself that ends in addition also belongs to alkalescence, the ph value rises to 7.45 from 7.35, oxygen content then increases by 64.9%, and the moxa roll burning has competent oxygen, so moxa roll can fully burn, and can prolong burning time, reach flame resistant purpose.Because fully burning, the Chinese mugwort cigarette greatly reduces or eliminates, but the active ingredient amount that is dissipated into do not reduce, because sufficient combustion, so moxa-moxibustion power is strengthened.

Three, negative ion effect strengthens, and curative effect is strengthened

1, because tourmaline is supplied with the particularly special energy in acupuncture point of body, all can absorb moxibustion power and the near-infrared and the far energy of negative ion smokeless moxa roll again because of two absworption peaks of human body, so curative effect is strengthened greatly.

2, tourmaline is under the effect of moxibustion instrument moxibustion power, and pyroelectric effect is strengthened greatly, also strengthens greatly so discharge the ability of anion, has therefore strengthened curative effect.

Four, eliminate environmental pollution:

1, eliminates specific peculiar smell: because the contained volatilization of Folium Artemisiae Argyi has pungent abnormal flavour for ammonia, ethanol, propanoic acid etc. very much, can cause asthma, the state of an illness such as bronchitis increase the weight of, and common people also are difficult to tolerance, and anion can be eliminated abnormal flavour effectively, not only guarantee the health of human body, can eliminate environmental pollution again.

2, because the anion effect is arranged, not only make patient in moxa-moxibustion, be drawn onto ozone, and make in the whole therapeutic room with fresh air; In addition, execute the personnel that control and all will stay in therapeutic room the inside 8 hours every days, control personnel's health system and also be guaranteed and make to execute with negative ion smokeless moxa roll.

The specific embodiment:

Example 1

Chinese mugwort charcoal 70 grams

Mellow liquor jade 1 gram

Zeolite 0.5 gram

Tourmaline 5 grams

Ferrum oxide 0.3 gram

Elm powder: 0.5 gram

Method for making:

A. the charcoal that will end is crushed to 200-500 order fine powder;

B. get tourmaline mellow liquor jade, zeolite, the cleaning of ferrum oxide decontamination, sterilization, dry, pulverizing respectively;

C. respectively tourmaline, mellow liquor jade, zeolite, ferrum oxide are ground to 200-500 order fine powders;

D. above-mentioned Chinese mugwort charcoal, tourmaline, mellow liquor jade, zeolite, the full and uniform mixing of ferrum oxide fine powder, adding is ground to 200-500 purpose elm powder again;

E, in the compacting moxa roll mould in press forming, promptly.

Example 2

Chinese mugwort charcoal 89 grams

Mellow liquor jade 8 grams

Zeolite 1.5 grams

Tourmaline 25 grams

Ferrum oxide 0.5 gram

Elm powder 3 grams

Method is with example 1.

Example 3

Chinese mugwort charcoal 79 grams

Mellow liquor jade 3 grams

Zeolite 1 gram

Tourmaline 14 grams

Ferrum oxide 0.4 gram

Elm powder 1.75 grams

Method is with example 1.

Example 4

Chinese mugwort charcoal 75 grams

Mellow liquor jade 2 grams

Zeolite 0.75 gram

Tourmaline 22 grams

Ferrum oxide 0.4 gram

Elm powder 1.1 grams

Method is with example 1.

Example 5

Chinese mugwort charcoal 83 grams

Mellow liquor jade 4 grams

Zeolite 1.25 grams

Tourmaline 24 grams

Ferrum oxide 0.45 gram

Elm powder 1.1 grams

Method is with example 1.

Example 6

Chinese mugwort charcoal 77 grams

Mellow liquor jade 2.5 grams

Zeolite 0.9 gram

Tourmaline 22 grams

Ferrum oxide 0.35 gram

Elm powder 1.4 grams

Method is with example 1.

Example 7

Chinese mugwort charcoal 81 grams

Mellow liquor jade 3.5 grams

Zeolite 1.1 grams

Tourmaline 16.2 grams

Ferrum oxide 0.38 gram

Elm powder 1.4 grams

Method is with example 1.

Example 8

Chinese mugwort charcoal 76 grams

Mellow liquor jade 2.3 grams

Zeolite 0.8 gram

Tourmaline 15 grams

Ferrum oxide 0.48 gram

Elm powder 1.25 grams

Method is with example 1.

Example 9

Chinese mugwort charcoal 73 grams

Mellow liquor jade 1.7 grams

Zeolite 0.65 gram

Tourmaline 20 grams

Ferrum oxide 0.42 gram

Elm powder 0.9 gram

Method is with example 1.

Example 10

Chinese mugwort charcoal 85.5 grams

Mellow liquor jade 4.5 grams

Zeolite 1.4 grams

Tourmaline 20.7 grams

Ferrum oxide 0.38 gram

Elm powder 2.1 grams

Method is with example 1.

Claims

1. negative ion smokeless moxa roll is characterized in that it is made up of following weight percent proportion raw material:

Chinese mugwort charcoal 75-90wt%

Mellow liquor jade 1-5wt%

Zeolite 0.5-1.5wt%

Tourmaline 5-23wt%

Ferrum oxide 0.3-0.5wt%

Elm powder 0.5-3wt%

Described each constituent content percent sum equals 100%.

2. negative ion smokeless moxa roll according to claim 1, the particle diameter that it is characterized in that described tourmaline is the 0.3-5 micron.

3. the preparation method of a negative ion smokeless moxa roll as claimed in claim 1 is characterized in that this method comprises the following steps:

Raw material:

Chinese mugwort charcoal 75-90wt%

Mellow liquor jade 1-5wt%

Zeolite 0.5-1.5wt%

Tourmaline 5-23wt%

Ferrum oxide 0.3-0.5wt%

Elm powder 0.5-3wt%

Described each constituent content percent sum equals 100%;

Method:

1) gets the Chinese mugwort charcoal, be crushed to 200-500 purpose fine powder;

2) get tourmaline, mellow liquor jade, zeolite, the cleaning of ferrum oxide decontamination, sterilization, dry, pulverizing respectively;

3) respectively with above-mentionedly clean, sterilize, tourmaline, mellow liquor jade, zeolite, croci dry, after pulverizing grind to form 200-500 order fine powder;

4) with above-mentioned Chinese mugwort charcoal, tourmaline, mellow liquor jade, zeolite, the abundant mix homogeneously of ferrum oxide fine powder, adding grinds to form the mixing of 200-500 purpose binding agent elm powder again;

5) with the mixed powder of step 4) press forming in the mould of compacting moxa roll, get product.