CN101270261B - 一种抗冰雪、抗腐蚀的涂料及其应用 - Google Patents

一种抗冰雪、抗腐蚀的涂料及其应用 Download PDF

Info

Publication number
CN101270261B
CN101270261B CN2008100973477A CN200810097347A CN101270261B CN 101270261 B CN101270261 B CN 101270261B CN 2008100973477 A CN2008100973477 A CN 2008100973477A CN 200810097347 A CN200810097347 A CN 200810097347A CN 101270261 B CN101270261 B CN 101270261B
Authority
CN
China
Prior art keywords
coating
parts
ice
snow
organosilicon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2008100973477A
Other languages
English (en)
Other versions
CN101270261A (zh
Inventor
刘国强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2008100973477A priority Critical patent/CN101270261B/zh
Publication of CN101270261A publication Critical patent/CN101270261A/zh
Application granted granted Critical
Publication of CN101270261B publication Critical patent/CN101270261B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗冰雪、抗腐蚀的涂料，该涂料包括有重量份数如下的原料：硅油1.0～1.5份、有机硅防水剂1.0～1.5份、氯化钙2.0～2.5份、Na2HPO4·12H2O 0.8～1.2份和甲基乙烯基硅橡胶1.0～1.5份。本发明该涂料兼备无机材料和有机材料的性能，既有耐高低温、电器绝缘、耐臭氧、难燃、憎水、耐腐蚀、耐候性、疏水性、无毒无味以及生理惰性和较小的表面张力，此外还具有低粘温系数和较高的抗压缩，能有效的防止高压电铁塔和通讯设备等户外设施上冻；还具有耐辐射的性能。

Description

一种抗冰雪、抗腐蚀的涂料及其应用
技术领域
本发明涉及一种抗冰雪、抗腐蚀的涂料，以及该涂料在户外高压电铁塔和通讯设备上的抗冰雪抗腐蚀应用。
背景技术
架设在户外的高压电铁塔和通讯设备，由于经常受到风吹日晒、酸雨以及经受冷热交错的损害，容易发生损坏的事故。
经过2007年国内的大雪，南方很多高压电铁塔和通讯设备由于不能耐受严寒，导致倒塌，从而造成大面积的地区断电或信息无法联络，给群众生活带来非常严重的后果。
发明内容
本发明所要解决的技术问题是提供一种抗冰雪、抗腐蚀的涂料，该涂料具有较低的粘温系数和较高的抗腐蚀性能，能有效的防止户外设施上冻；以及该涂料在高压电铁塔和通讯设备上的应用。
为解决上述技术问题，本发明所提供的技术方案是：一种抗冰雪、抗腐蚀的涂料，该涂料包括有重量份数如下的原料：硅油1.0～1.5份、有机硅防水剂1.0～1.5份、氯化钙2.0～2.5份、Na2HPO4·12H2O 0.8～1.2份和甲基乙烯基硅橡胶1.0～1.5份；其中：
所述的氯化钙：2CaCl2·2H2O或CaCl2；
所述的硅油为：C2H8O2Si、(CH3)3SiO[(CH3)]2SiO]N-Si(CH3)3或ZBH-255型苯甲基硅油；
所述的有机硅防水剂为：C2H5-O-[Si(OC2H5)(CH3)-O]-Si(CH3)(OC2H5)2；
所述的甲基乙烯基硅橡胶的结构式为：
Figure G2008100973477D00011
m＝10-20，n＝6000～11500。
所述涂料还包括有丙烯酸，其重量份数为0.7～0.8。
本发明还提供了上述的涂料对户外高压电铁塔和通讯设备的抗冰雪、抗腐蚀应用。
本发明具有的优点：该涂料兼备无机材料和有机材料的性能，既有耐高低温、电器绝缘、耐臭氧、难燃、憎水、耐腐蚀、耐候性、疏水性、无毒无味以及生理惰性和较小的表面张力，此外还具有低粘温系数和较高的抗压缩，能有效的防止高压电铁塔和通讯设备等户外设施上冻；还具有耐辐射的性能。
具体实施方式：
一种涂料，包括有重量份数如下的原料：硅油1.0～1.5份、有机硅防水剂1.0～1.5份、氯化钙2.0～2.5份、Na2HPO4·12H2O 0.8～1.2份和甲基乙烯基硅橡胶1.0～1.5份；
其中：
所述的氯化钙：2CaCl2·2H2O或CaCl2；
所述的硅油为：C2H8O2Si、(CH3)3SiO[(CH3)]2SiO]N-Si(CH3)3或ZBH-255型苯甲基硅油；
所述的有机硅防水剂为：C2H5-O-[Si(OC2H5)(CH3)-O]-Si(CH3)(OC2H5)2；
所述的甲基乙烯基硅橡胶的结构式为：
Figure G2008100973477D00021
m＝10-20，n＝6000～11500。
将上述原料按照比例配合混匀，即可制成本涂料。
实施例1：
一种涂料包括有重量份数比分别如下的原料：
2CaCl2·2H2O                                    2.35份
C2H8O2Si                                        1.45份
Na2HPO4·12H2O                                  1.10份
甲基乙烯基硅橡胶                                1.30份
C2H5-O-[Si(OC2H5)(CH3)-O]-Si(CH3)(OC2H5)2        1.48份。
实施例2：
另一种涂料包括有重量份数比分别如下的原料：
CaCl2                                           2.15份
ZBH-255型苯甲基硅油                             1.20份
C2H5-O-[Si(OC2H5)(CH3)-O]-Si(CH3)(OC2H5)2        0.95份
Na2HPO4·12H2O                                  0.82份
甲基乙烯基硅橡胶                                1.15份
CHCHCOOH                                        0.75份。
其中：ZBH-255型苯甲基硅油为市售的，是青岛中宝化工有限公司生产。
实施例3：
第三种涂料包括有重量份数比分别如下的原料：
CaCl2                                       2.25份
C2H5-O-[Si(OC2H5)(CH3)-O]-Si(CH3)(OC2H5)2   1.0份
Na2HPO4·12H2O                              1.0份
甲基乙烯基硅橡胶                            1.25份
(CH3)3SiO[(CH3)]2SiO]N-Si(CH3)3              1.25份。
对比试验：
有上述涂料的涂层和没有涂层的两组样品各三种：
1、电力输电高架塔50厘米段；
2、电力电缆切断长50厘米的一段；
3、屋顶彩钢段长50厘米一段；
(1)抗冰附着力测试
在野外温度-24℃情况下，树立在山顶上每隔2小时进行雪水泼洒，测试3天；涂刷本涂层的样品未见附冰物，略有湿痕；而没有涂层的样品覆盖很厚一层冰。
(2)抗腐蚀测试
将两组样品渗泡在长型槽中7天，长型槽中混合有盐酸、冷冻液、汽车更换的废机油、齿轮油和沙子约10公斤，进行渗泡搅磨7天后捞出风干，涂刷本涂层的样品的附着杂质物不足3％；而没有涂层的样品附着杂质物达到20％。
对抗腐蚀后的样品再次进行抗冰附着力测试：使用砂纸进行打磨后再用冰雪水进行冷冻实验。涂刷本涂层的样品的抗冰值减弱2.74％，依然有较强的抗冰冻能力；如加高单体配比将大大提高抗冰冻和耐腐、耐磨值。

Claims (3)

1.一种抗冰雪、抗腐蚀的涂料，该涂料包括有重量份数如下的原料：硅油1.0～1.5份、有机硅防水剂1.0～1.5份、氯化钙2.0～2.5份、Na2HPO4·12H2O 0.8～1.2份和甲基乙烯基硅橡胶1.0～1.5份；其中：
所述的氯化钙：2CaCl2·2H2O或CaCl2；
所述的硅油为：C2H8O2Si、(CH3)3SiO[(CH3)]2SiO]N-Si(CH3)3或ZBH-255型苯甲基硅油；
所述的有机硅防水剂为：C2H5-O-[Si(OC2H5)(CH3)-O]-Si(CH3)(OC2H5)2；
所述的甲基乙烯基硅橡胶的结构式为：
Figure F2008100973477C00011
2.根据权利要求1所述的抗冰雪抗腐蚀的涂料，其特征在于：所述涂料还包括有丙烯酸，其重量份数为0.7～0.8。
3.如权利要求1或2所述的涂料对户外高压电铁塔和通讯设备的抗冰雪、抗腐蚀应用。
CN2008100973477A 2008-05-13 2008-05-13 一种抗冰雪、抗腐蚀的涂料及其应用 Expired - Fee Related CN101270261B (zh)