CN101265098B - Transparent ceramic scintillator material by using lutecium oxide-gadolinium oxide solid solution as substrate and preparation method thereof - Google Patents

Transparent ceramic scintillator material by using lutecium oxide-gadolinium oxide solid solution as substrate and preparation method thereof Download PDF

Info

Publication number
CN101265098B
CN101265098B CN200810011236XA CN200810011236A CN101265098B CN 101265098 B CN101265098 B CN 101265098B CN 200810011236X A CN200810011236X A CN 200810011236XA CN 200810011236 A CN200810011236 A CN 200810011236A CN 101265098 B CN101265098 B CN 101265098B
Authority
CN
China
Prior art keywords
oxide
powder
preparation
transparent ceramic
solid solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN200810011236XA
Other languages
Chinese (zh)
Other versions
CN101265098A (en
Inventor
李晓东
孙旭东
刘妍
修稚萌
李继光
霍地
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Northeastern University China
Original Assignee
Northeastern University China
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Northeastern University China filed Critical Northeastern University China
Priority to CN200810011236XA priority Critical patent/CN101265098B/en
Publication of CN101265098A publication Critical patent/CN101265098A/en
Application granted granted Critical
Publication of CN101265098B publication Critical patent/CN101265098B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to a transparent ceramic scintillator material containing lutecium oxide-gadolinium oxide solid solution as matrix and a production method thereof. The method comprises the steps of powder synthesis, molding, bisque firing, sintering and annealing treatment. The transparent ceramic scintillator material containing lutecium oxide-gadolinium oxide solid solution as matrix has a visible light linear transmittance more than 60% and good mechanical property, and can be used as matrix material for scintillators. The invention can improve the blocking ability of the gadolinium oxide matrix against ionization radiation, improve the scintillation property of Gd2O3 and reduce the production cost of Lu2O3; and has good application prospect in the field of scintillation radiation detection.

Description

It with lutecium oxide-gadolinium oxide solid solution transparent ceramic scintillator material of matrix and preparation method thereof
Technical field
The invention belongs to field of material preparation, being specifically related to a kind of is the transparent ceramic scintillator material and preparation method thereof of matrix with lutecium oxide-gadolinium oxide solid solution.
Background technology
Scintillation material is a kind ofly can absorb high energy particle or ray and send the material of optical photon, is widely used in fields such as high energy physics (as accurate electromagnetic calorimeter), nuclear medicine (as X-CT, PET and γ camera), industry (CT flaw detection), space physics, geological prospectings.Although different application can propose different requirements to scintillator, but scintillator all is used to detect ionizing rays in the overwhelming majority uses, so require scintillator high blocking ability will be arranged, promptly require scintillator to have high-density and contain the big element of ordination number to ionizing rays.In many application, therefore the large usage quantity of scintillator, also needs scintillator that cheap price is arranged, but high quality, produces in large quantity and process.
Lutecium oxide has high density (9.42g/cm 3) and high ordination number (71), this makes it quite high to the stopping power of all kinds of rays (x ray, gamma-rays); Lu 2O 3Band gap very wide (6.5eV) can hold many activator ions such as Eu as the luminescent material matrix between valence band and conduction band, Tb, and Tm, the emission level of Er etc., so lutecium oxide enjoys people to favor as the scintillator substrate material.As the Lu of the 5%Eu that mixes 2O 3The light output of base transparent flickering body is approximately 50%CsI:Tl, is applicable to the X ray digital imagery.But lutecium oxide has limited its widespread use owing to cost an arm and a leg.
Gadolinium sesquioxide has higher density (7.6g/cm equally 3) and effective atomic number (64), X ray is had very high receptivity, and cheap, have actual application value as the scintillator substrate material.But Gd 2O 3Have very high fusing point (2673K), be difficult to have practical value and get monocrystalline by the melting method preparation.In addition, because Gd 2O 3Take place to make it be difficult at high temperature be prepared into crystalline ceramics cube to the monocline phase transformation at～1200 ℃ by the pressureless sintering technology.Limited its application in the flash detection field.Up to the present, also it is not prepared into patent, the bibliographical information of crystalline ceramics by the pressureless sintering technology.In gadolinium sesquioxide matrix, be doped into a certain amount of lutecium oxide, can be expected to obtain crystalline ceramics by sintering with the gadolinium sesquioxide cube temperature increase that arrives the monocline phase transformation to more than the sintering temperature.Lutecium oxide mixed make the solid solution matrix material in the gadolinium sesquioxide, not only can further improve the blocking ability of gadolinium sesquioxide matrix, improve Gd ionizing rays 2O 3Scintillation properties, can also reduce Lu 2O 3Production cost, obtain a kind of scintillator substrate material of high comprehensive performance.
Summary of the invention
The objective of the invention is to adopt that pressureless sintering prepares a kind of highdensity transparent ceramic glaring material that has in vacuum or the hydrogen, relate in particular to lutecium oxide-gadolinium oxide solid solution transparent ceramic and preparation method thereof.
Lutecium oxide-the gadolinium oxide solid solution transparent ceramic glaring material of the present invention's preparation, its general formula is Gd 2-2x-2yLu 2xRE 2yO 3, wherein, 0.15＜x＜1,0＜y＜0.3, x, y are atomic mole fraction, RE is dopant ion Eu, Tb, one or both among Nd, Yb, the Pr.
Of the present invention is the high-density transparent ceramic scintillator material and preparation method thereof of matrix with lutecium oxide-gadolinium oxide solid solution, comprises following processing step:
1, synthetic: synthetic high sintering activity Gd 2-2x-2yLu 2xRE 2yO 3Nano-powder comprises following processing step:
(a) press composition formula Gd 2-2x-2yLu 2xRE 2yO 3Form preparation mother liquor with nitrate;
(b) adopting concentration is 0.5molL -1～2molL -1Ammonium bicarbonate aqueous solution as precipitation agent;
(c) employing prepares the precursor powder with the forward volumetry that precipitation agent splashes into mother liquor, and the pH value after the control precipitin reaction is between 5～7, and titration finishes the back and continues stirring 4h;
(d) the precursor powder obtains oxide powder after washing, drying, calcining;
The washing process parameter is: throw out is washed, to remove the foreign ion that precipitation surface is adhered to; After washing 3～4 times, throw out is soaked 24h with dehydrated alcohol or acetone,, obtain finely disseminated precursor powder to remove the Surface Physical planar water;
The drying process parameter is: will wash good precursor powder and put into drying baker, temperature is 50～120 ℃, and the time is 24h;
The calcining process parameter is: the precursor powder after will drying is put into corundum crucible after grinding in mortar, calcines 1～6 hour down for 800～1100 ℃ in temperature, makes oxide powder;
2, moulding: adopt punching block bidirectional pressed moulding or cold isostatic compaction, with oxide powder compression moulding, pressing pressure is 100～300MPa, makes biscuit;
3, biscuiting: biscuit is put into the biscuiting of van-type stove, 1200～1400 ℃ of biscuiting temperature, biscuiting is 4～24 hours under air or oxygen atmosphere;
4, sintering: the biscuit that biscuiting is good is put into the vacuum oven sintering, 1600～1800 ℃ of sintering temperatures, and sintering time 5～24 hours, vacuum tightness is not less than 1 * 10 -2MPa makes the crystalline ceramics work in-process;
5, anneal: the crystalline ceramics work in-process are put into cabinet-type electric furnace anneal, 1000～1400 ℃ of annealing temperatures, under air or oxygen atmosphere, annealing time 4～24 hours, the high-density transparent ceramic scintillator material density that makes is at 8.0-9.0g/cm 3Between, become with chemical constitution;
Can prepare lutecium oxide-gadolinium oxide solid solution transparent ceramic according to technology of the present invention, can be used as the scintillator substrate material at visible-range straight line transmitance height (＞60%), satisfactory mechanical property.
Description of drawings
Fig. 1: Gd 2-2x-2yLu 2xRE 2yO 3X ray diffracting spectrum after 1000 ℃ of calcinings of precursor powder
Fig. 2: 800 ℃ of calcining Gd 2-2x-2yLu 2xRE 2yO 3The SEM pattern photo of powder
Fig. 3: 1700 ℃ of sintering Gd 2-2x-2yLu 2xRE 2yO 3The outward appearance photo of sample
Fig. 4: 1700 ℃ of sintering Gd 2-2x-2yLu 2xRE 2yO 3Sample XRD figure spectrum
Fig. 5: Gd 2-2x-2yLu 2xRE 2yO 3The emmission spectrum of crystalline ceramics
Embodiment
Embodiment 1
1, high sintering activity Gd 2-2x-2yLu 2xRE 2yO 3Nano-powder is synthetic:
(a) with analytically pure Lu 2O 3, Gd 2O 3And Eu 2O 3Meal is dissolved in respectively in the analytical pure concentrated nitric acid solution, is mixed with 0.5molL after the filtration -1Nitrate solution, measure Gadolinium trinitrate 350ml, lutecium nitrate 125ml, europium nitrate 25ml, compound concentration is 0.5molL -1Nitrate mother liquor 500ml;
(b) preparation 0.5molL -1NH 4HCO 3Solution is as precipitation agent;
(c) 0.5molL -1NH 4HCO 3It is 0.5molL that solution splashes into 500ml concentration -1In the rare earth nitrate mother liquor, rate of addition is 3mlmin -1Between the reaction period, magnetic agitation is carried out on titration limit, limit, control terminal point pH=5, and titration finishes the back and continues to stir 4h;
(d) the precursor powder obtains oxide powder after washing, drying, calcining;
The washing process parameter is: throw out is washed, to remove the foreign ion that precipitation surface is adhered to; After washing 3～4 times, throw out is soaked 24h with dehydrated alcohol or acetone,, obtain finely disseminated precursor powder to remove the Surface Physical planar water;
The drying process parameter is: will wash good precursor powder and put into drying baker, and dry 24h down at 50 ℃;
The calcining process parameter is: the precursor powder after will drying is put into corundum crucible after grinding in mortar, at 800 ℃ of calcining 1h, makes oxide powder;
2, moulding: adopt punching block bidirectional pressed moulding or cold isostatic compaction, oxide powder is pressed into biscuit, pressing pressure is 100MPa, and the base substrate diameter after the compacting is 13mm, and thickness is 3mm;
3, biscuiting: biscuit is gone in the van-type stove to burn base substrate 1200 ℃ of pre-burnings 4 hours in resistance furnace;
4, sintering: biscuit is put into the vacuum oven sintering, and base substrate places 1600 ℃ of insulations of vacuum oven 5h, vacuum tightness 1 * 10 -2MPa makes the crystalline ceramics work in-process;
5, anneal: the crystalline ceramics work in-process are put into cabinet-type electric furnace anneal, under air or oxygen atmosphere, anneal in cabinet-type electric furnace, temperature is 1000 ℃, and 4 hours time, the high-density transparent ceramic scintillator material density that makes is 8.0g/cm 3
Embodiment 2
1, high sintering activity Gd 2-2x-2yLu 2xRE 2yO 3Nano-powder is synthetic:
(a) with analytically pure Lu 2O 3, Gd 2O 3And Tb 2O 3Meal is dissolved in respectively in the analytical pure concentrated nitric acid solution, is mixed with 0.5molL after the filtration -1Nitrate solution, Gadolinium trinitrate 300ml, lutecium nitrate 175ml, Terbium trinitrate 25ml, compound concentration are 0.5molL -1Nitrate mother liquor 500ml;
(b) preparation 1.0molL -1NH 4HCO 3Solution is as precipitation agent;
(c) 1.0molL -1NH 4HCO 3It is 0.5molL that solution splashes into 500ml concentration -1In the rare earth nitrate mother liquor, rate of addition is 3mlmin -1Between the reaction period, magnetic agitation is carried out on titration limit, limit, control terminal point pH=5.7, and titration finishes the back and continues to stir 4h;
(d) the precursor powder obtains oxide powder after washing, drying, calcining;
The washing process parameter is: throw out is washed, to remove the foreign ion that precipitation surface is adhered to; After washing 3～4 times, throw out is soaked 24h with dehydrated alcohol or acetone, removing the Surface Physical planar water,
Obtain finely disseminated precursor powder;
The drying process parameter is: will wash good precursor powder and put into drying baker, and dry 24h down at 70 ℃;
The calcining process parameter is: the precursor powder after will drying is put into corundum crucible after grinding in mortar, at 900 ℃ of calcining 2.7h, makes oxide powder;
2, moulding: adopt punching block bidirectional pressed moulding or cold isostatic compaction, oxide powder is pressed into biscuit, pressing pressure is 170MPa.Base substrate diameter after the compacting is 13mm, and thickness is 3mm;
3, biscuiting: biscuit is put into the van-type stove burn, base substrate 1270 ℃ of pre-burnings 11 hours in resistance furnace;
4, sintering: biscuit is put into the vacuum oven sintering, and base substrate places 1670 ℃ of insulations of vacuum oven 11h, vacuum tightness 2 * 10 -2MPa makes the crystalline ceramics work in-process;
5, anneal: the crystalline ceramics work in-process are put into cabinet-type electric furnace anneal, under air or oxygen atmosphere, anneal in cabinet-type electric furnace, temperature is 1130 ℃, and 11 hours time, the high-density transparent ceramic scintillator material density that makes is 8.3g/cm 3
Embodiment 3
1, high sintering activity Gd 2-2x-2yLu 2xRE 2yO 3Nano-powder is synthetic:
(a) with analytically pure Lu 2O 3, Gd 2O 3And Yb 2O 3Meal is dissolved in respectively in the analytical pure concentrated nitric acid solution, is mixed with 0.5molL after the filtration -1Nitrate solution, measure Gadolinium trinitrate 250ml, lutecium nitrate 225ml, ytterbium nitrate 25ml, compound concentration is 0.5molL -1Nitrate mother liquor 500ml;
(b) preparation 1.5molL -1NH 4HCO 3Solution is as precipitation agent;
(c) 1.5molL -1NH 4HCO 3It is 0.5molL that solution splashes into 500ml concentration -1In the rare earth nitrate mother liquor, rate of addition is 3mlmin -1Between the reaction period, magnetic agitation is carried out on titration limit, limit, control terminal point pH=6.4, and titration finishes the back and continues to stir 4h;
(d) the precursor powder obtains oxide powder after washing, drying, calcining;
The washing process parameter is: throw out is washed, to remove the foreign ion that precipitation surface is adhered to; After washing 3～4 times, throw out is soaked 24h with dehydrated alcohol or acetone,, obtain finely disseminated precursor powder to remove the Surface Physical planar water;
The drying process parameter is: will wash good precursor powder and put into drying baker, and dry 24h down at 90 ℃;
The calcining process parameter is: the precursor powder after will drying is put into corundum crucible after grinding in mortar, at 1000 ℃ of calcining 4.4h, makes oxide powder;
2, moulding: adopt punching block bidirectional pressed moulding or cold isostatic compaction, oxide powder is pressed into biscuit, pressing pressure is 200MPa.Base substrate diameter after the compacting is 13mm, and thickness is 3mm;
3, biscuiting: biscuit is put into the van-type stove burn, base substrate 1300 ℃ of pre-burnings 14 hours in resistance furnace; 4, sintering: biscuit is put into the vacuum oven sintering, and base substrate places 1700 ℃ of insulations of vacuum oven 15h, vacuum tightness 3 * 10 -2MPa makes the crystalline ceramics work in-process;
5, anneal: the crystalline ceramics work in-process are put into cabinet-type electric furnace anneal, under air or oxygen atmosphere, anneal in cabinet-type electric furnace, temperature is 1200 ℃, and 14 hours time, the high-density transparent ceramic scintillator material density that makes is 8.5g/cm 3
Embodiment 4
1, high sintering activity Gd 2-2x-2yLu 2xRE 2yO 3Nano-powder is synthetic:
(a) with analytically pure Lu 2O 3, Gd 2O 3And Nd 2O 3Meal is dissolved in respectively in the analytical pure concentrated nitric acid solution, is mixed with 0.5molL after the filtration -1Nitrate solution, measure Gadolinium trinitrate 200ml, lutecium nitrate 275ml, neodymium nitrate 25ml compound concentration is 0.5molL -1Nitrate mother liquor 500ml;
(b) preparation 1.7molL -1NH 4HCO 3Solution is as precipitation agent;
(c) 1.7molL -1NH 4HCO 3It is 0.5molL that solution splashes into 500ml concentration -1In the rare earth nitrate mother liquor, rate of addition is 3mlmin -1Between the reaction period, magnetic agitation is carried out on titration limit, limit, control terminal point pH=6.5, and titration finishes the back and continues to stir 4h;
(d) the precursor powder obtains oxide powder after washing, drying, calcining;
The washing process parameter is: throw out is washed, to remove the foreign ion that precipitation surface is adhered to; After washing 3～4 times, throw out is soaked 24h with dehydrated alcohol or acetone,, obtain finely disseminated precursor powder to remove the Surface Physical planar water;
The drying process parameter is: will wash good precursor powder and put into drying baker, and dry 24h down at 100 ℃;
The calcining process parameter is: the precursor powder after will drying is put into corundum crucible after grinding in mortar, at 1000 ℃ of calcining 5h, makes oxide powder;
2, moulding: adopt punching block bidirectional pressed moulding or cold isostatic compaction, oxide powder is pressed into biscuit, pressing pressure is 250MPa.Base substrate diameter after the compacting is 13mm, and thickness is 3mm;
3, biscuiting: biscuit is put into the van-type stove burn, base substrate 1350 ℃ of pre-burnings 19 hours in resistance furnace;
4, sintering: biscuit is put into the vacuum oven sintering, and base substrate places 1750 ℃ of insulations of vacuum oven 19h, vacuum tightness 4 * 10 -2MPa makes the crystalline ceramics work in-process;
5, anneal: the crystalline ceramics work in-process are put into cabinet-type electric furnace anneal, under air or oxygen atmosphere, anneal in cabinet-type electric furnace, temperature is 1300 ℃, and 19 hours time, the high-density transparent ceramic scintillator material density that makes is 8.7g/cm 3
Embodiment 5
1, high sintering activity Gd 2-2x-2yLu 2xRE 2yO 3Nano-powder is synthetic:
(a) with analytically pure Lu 2O 3, Gd 2O 3, Pr 2O 3And Eu 2O 3Meal is dissolved in respectively in the analytical pure concentrated nitric acid solution, is mixed with 0.5molL after the filtration -1Nitrate solution, measure Gadolinium trinitrate 200ml, lutecium nitrate 275ml, praseodymium nitrate 5ml, europium nitrate 20ml compound concentration is 0.5molL -1Nitrate mother liquor 500ml;
(b) preparation 2.0molL -1NH 4HCO 3Solution is as precipitation agent;
(c) 2.0molL -1NH 4HCO 3It is 0.5molL that solution splashes into 500ml concentration -1In the rare earth nitrate mother liquor, rate of addition is 3mlmin -1Between the reaction period, magnetic agitation is carried out on titration limit, limit, control terminal point pH=7, and titration finishes the back and continues to stir 4h;
(d) the precursor powder obtains oxide powder after washing, drying, calcining;
The washing process parameter is: throw out is washed, to remove the foreign ion that precipitation surface is adhered to; After washing 3～4 times, throw out is soaked 24h with dehydrated alcohol or acetone,, obtain finely disseminated precursor powder to remove the Surface Physical planar water;
The drying process parameter is: will wash good precursor powder and put into drying baker, and dry 24h down at 120 ℃;
The calcining process parameter is: the precursor powder after will drying is put into corundum crucible after grinding in mortar, at 1100 ℃ of calcining 6h, makes oxide powder;
2, moulding: adopt punching block bidirectional pressed moulding or cold isostatic compaction, oxide powder is pressed into biscuit, pressing pressure is 300MPa.Base substrate diameter after the compacting is 13mm, and thickness is 3mm;
3, biscuiting: biscuit is put into the van-type stove burn, base substrate 1400 ℃ of pre-burnings 24 hours in resistance furnace;
4, sintering: biscuit is put into the vacuum oven sintering, and base substrate places 1800 ℃ of insulations of vacuum oven 24h, vacuum tightness 4 * 10 -2MPa makes the crystalline ceramics work in-process;
5, anneal: the crystalline ceramics work in-process are put into cabinet-type electric furnace anneal, under air or oxygen atmosphere, anneal in cabinet-type electric furnace, temperature is 1400 ℃, and 24 hours time, the high-density transparent ceramic scintillator material density that makes is 9.0g/cm 3

Claims (4)

1. one kind is the transparent ceramic scintillator material of matrix with lutecium oxide-gadolinium oxide solid solution, it is characterized in that chemical constitution is Gd 2-2x-2yLu 2xRE 2yO 3, wherein, 0.15＜x＜1,0＜y＜0.3, x, y are atomic mole fraction, RE is one or both among dopant ion Eu, Tb, Nd, Yb, the Pr in the formula.
2. described by claim 1 is the transparent ceramic scintillator material of matrix with lutecium oxide-gadolinium oxide solid solution, and its density is at 8.0-9.0g/cm 3Between, become with chemical constitution.
3. by the preparation method of the described lutecium oxide of claim 1-gadolinium sesquioxide solid solution transparent ceramic scintillator material, it is characterized in that may further comprise the steps:
(1) the active Gd of the high sintering of preparation 2-2x-2yLu 2xRE 2yO 3Nano-powder;
(2) adopt punching block bidirectional pressed moulding or cold isostatic compaction, pressing pressure is 100～300MPa, with the nano-powder moulding, obtains biscuit;
(3) biscuit biscuiting 4～24 hours under air or oxygen atmosphere, 1200～1400 ℃ of biscuiting temperature;
(4) after the biscuiting, with biscuit vacuum sintering 5～24 hours, vacuum tightness was more than or equal to 1 * 10 -2MPa obtains the crystalline ceramics sample;
(5) the agglomerating ceramics sample is annealed in air or in the oxygen atmosphere, and annealing temperature is 1000～1400 ℃, 4～24 hours time.
4. by the preparation method of the described lutecium oxide of right 3 requirements-gadolinium sesquioxide solid solution transparent ceramic scintillator material, it is characterized in that described high sintering activity Gd 2-2x-2yLu 2xRE 2yO 3Nano-powder is taked the following steps preparation:
(1) presses composition formula Gd 2-2x-2yLu 2xRE 2yO 3Form preparation mother liquor with nitrate;
(2) adopting concentration is that the ammonium bicarbonate aqueous solution of 0.5M～2M is as precipitation agent;
(3) employing prepares the precursor powder with the forward volumetry that precipitation agent splashes into mother liquor, and the pH value after the control precipitin reaction is between 5～7;
(4) the precursor powder obtains oxide powder after washing, drying, calcining.Calcining temperature is at 800～1100 ℃, and the time was at 1～6 hour.
CN200810011236XA 2008-04-30 2008-04-30 Transparent ceramic scintillator material by using lutecium oxide-gadolinium oxide solid solution as substrate and preparation method thereof Expired - Fee Related CN101265098B (en)