CN101219909A - Method for manufacturing porcelain polished brick with slurry pouring method - Google Patents
Method for manufacturing porcelain polished brick with slurry pouring method Download PDFInfo
- Publication number
- CN101219909A CN101219909A CNA2007100003391A CN200710000339A CN101219909A CN 101219909 A CN101219909 A CN 101219909A CN A2007100003391 A CNA2007100003391 A CN A2007100003391A CN 200710000339 A CN200710000339 A CN 200710000339A CN 101219909 A CN101219909 A CN 101219909A
- Authority
- CN
- China
- Prior art keywords
- slurry
- glaze
- drenching
- drying
- brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a method for producing vitreous polished tiles by applying a slurry drenching method. The method comprises preparing the slurry, producing powder, forming, drying, biscuiting, drenching glaze, roasting and polishing; the invention is characterized in that the glaze drenching process comprises tinting, drenching the slurry and a second drying, wherein, during tinting, surface slurry is put into a tinting tank and then pigments are added to tint; during drenching the slurry, a plurality of slurry buckets are arranged on the two sides of a glaze line and the pigments with different colors are put into each slurry bucket; at the same time diversified colored slurries are mixed and drenched on a brick surface through a bell jar or a duck-mouth slurry drenching instrument; during the second drying, the blank is put into a drying kiln with infrared drying glaze line or infrared ray to be dried. By adopting the process, a glaze layer with natural texture can be formed on the brick surface and the texture is similar to the texture of the stone; the hardness is the same with that of the polish brick. The method can meet diversified requirements of consumers.
Description
Technical field
The present invention relates to a kind of production method of porcelain polished brick with slurry pouring method.
Background technology
The production method of existing ornamental brick comprises selects materials-fill a prescription-slurrying-powder process-moulding-drying--and drench operations such as glaze-burn till-polish, wherein drench glaze and be mill base pouring with deployed solid color on the brick face, form the glaze layer that a layer thickness is even, color is consistent.This ornamental brick dull coloring can not satisfy the demand of the multiple aesthetic judgement of human consumer.
Summary of the invention
The purpose of this invention is to provide a kind of production method that can produce the porcelain polished brick with slurry pouring method of multiple natural texture effect on the surface.
For achieving the above object, the present invention adopts following technical scheme:
The production method of porcelain polished brick with slurry pouring method of the present invention, comprise slurrying, make powder, moulding, drying, biscuiting, pouring glaze, burn till, polishing process, it is characterized in that: comprise toning, sizing, redrying step drenching the glaze operation, wherein toning is to put starch adhesive into ball mill or toning jar to add colorant toning; On glaze line both sides a plurality of slurry buckets are housed during sizing, the colorant of the different colours of packing in each slurry bucket, the multiple mill base in a plurality of slurry buckets mixes pouring on the brick face mutually through bell jar or duck-beak type pouring slurry device; Redrying is to put in infrared drying glaze line or the infrared dryer blank after the sizing dry.
Above-mentioned technology is at the brick face water spray of sizing forward direction blank.
After adopting above-mentioned technology, can form the glazed layer that has natural texture on the brick face, closely similar with stone texture, its hardness is identical with the hardness of polished tile.Can satisfy human consumer's multiple demand.
Embodiment
The production method of porcelain polished brick with slurry pouring method of the present invention, comprise slurrying, make powder, moulding, drying, biscuiting, pouring glaze, burn till, polishing process, the production method of other steps and common ornamental brick is similar, its difference is: comprise toning, sizing, redrying step drenching the glaze operation, wherein toning is to put starch adhesive into ball mill or toning jar to add colorant toning; On glaze line both sides a plurality of slurry buckets are housed during sizing, the colorant of the different colours of packing in each slurry bucket, the multiple mill base in a plurality of slurry buckets mixes pouring on the brick face mutually through bell jar or duck-beak type pouring slurry device; Redrying is to put in infrared drying glaze line or the infrared dryer blank after the sizing dry.In 50-100 degree centigrade dry environment dry 30-60 minute.
Wherein, warm cotton balls mill in adding in starch adhesive, the middle Wen Mianke slurry that makes the 1-3 millimeter is not easy cracking when dry on the brick face.
Sizing is drenched slurry with bell jar or duckbilled, drench sizing process with ceramics production, difference is that a plurality of slurry buckets are equipped with on glaze line both sides, a plurality of mill bases in a plurality of slurry buckets add through the mixing of flowing from bell jar or duckbilled house steward, along with different mill bases mix pouring forms nature on the brick face texture mutually through bell jar or duck-beak type pouring slurry device, closely similar with stone texture.How many how much deciding of slurry bucket by brick complexion coloured silk.
Decide for the adjustment of texture pattern add-on by the mill base of the different colours in the different slurry jars.By the rate of flow meter of installing on the adding pipe that is adjusted at each slurry jar, may command add-on.Adjust pattern by the flow velocity difference of adjusting different mill bases.
Also can be divided into multistage pouring slurry, do a plurality of shower nozzles that wave automatically when can drench slurry and penetrate slurry, but cloth go out the lines line of stone material.
The thickness that drenches slurry in the present embodiment is 1.5-3.0mm.Slurry proportion is 1.60-1.73 ton/cubic meter.The flow velocity of slurry is a per minute 200-300 gram when measuring the pouring slurry with the flow cup.
In addition, for fear of occur to drench the slurry pin hole or absorb water too urgent and ftracture, should spray water at the brick face before drenching slurry.
The redrying process can or be equipped with in the loft drier of organizing infrared(ray)lamps at infrared drying glaze line more carries out also available common polished tile dry kiln drying.
Claims (2)
1. the production method of porcelain polished brick with slurry pouring method, comprise slurrying, make powder, moulding, drying, biscuiting, pouring glaze, burn till, polishing process, it is characterized in that: comprise toning, sizing, redrying step drenching the glaze operation, wherein toning is to put starch adhesive into ball mill or toning jar to add colorant toning; On glaze line both sides a plurality of slurry buckets are housed during sizing, the mill base of the different colours of packing in each slurry bucket, the multiple mill base in a plurality of slurry buckets mixes pouring on the brick face mutually through bell jar or duck-beak type pouring slurry device; Redrying is to put in infrared drying glaze line or the infrared dryer base substrate after the sizing dry.
2. the production method of porcelain polished brick with slurry pouring method according to claim 1 is characterized in that: at the brick face water spray of sizing forward direction blank.