CN101172831A - 节能保温砖 - Google Patents

节能保温砖 Download PDF

Info

Publication number
CN101172831A
CN101172831A CNA2007101335905A CN200710133590A CN101172831A CN 101172831 A CN101172831 A CN 101172831A CN A2007101335905 A CNA2007101335905 A CN A2007101335905A CN 200710133590 A CN200710133590 A CN 200710133590A CN 101172831 A CN101172831 A CN 101172831A
Authority
CN
China
Prior art keywords
parts
energy
insulating brick
brick
heat preserving
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2007101335905A
Other languages
English (en)
Other versions
CN100542991C (zh
Inventor
陶祖歧
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Kang Shunding energy-saving insulation Polytron Technologies Inc
Original Assignee
WUXI HUISHAN ENGINEERING INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUXI HUISHAN ENGINEERING INDUSTRY Co Ltd filed Critical WUXI HUISHAN ENGINEERING INDUSTRY Co Ltd
Priority to CNB2007101335905A priority Critical patent/CN100542991C/zh
Publication of CN101172831A publication Critical patent/CN101172831A/zh
Application granted granted Critical
Publication of CN100542991C publication Critical patent/CN100542991C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及节能保温砖，解决现有建筑墙体节能保温措施施工繁琐、施工周期长、成本高的技术问题。本发明将原材料混合搅拌、挤压成型、养护，所述原材料的重量份比为：硅酸盐水泥230～320份，膨胀珍珠岩35～20份，普砂430～610份，煤渣70～15份，秸秆6～3份，草木灰4～2份，羊毛毡纤维1.6～2份，水97～135份。本发明具有良好的节能保温性能及抗压强度。

Description

节能保温砖
技术领域
本发明涉及建筑物的砖或砌块，尤其是涉及建筑物的保温砖或保温砌块。
背景技术
现有的节能建筑墙体采取的节能保温措施是在普通砌体的外墙面抹一定厚度的保温砂浆或外挂保温板，普通砌体一般采用实心粘土砖、空心砖、加气混凝土砌块和陶粒砼空心砌块等制作而成，上述节能保温做法施工繁琐、施工周期长、成本高，而且墙面易开裂、渗漏，严重影响建筑物的保温效果。
发明内容
本发明针对上述节能保温措施施工繁琐、施工周期长、成本高的技术问题，提供一种施工简易、施工周期短、成本低的节能保温砖，使用该节能保温砖建造的墙体，不再需要在外墙面抹保温砂浆或外挂保温板，可以取得良好的节能保温效果。
为了解决上述技术问题，本发明采用如下的技术方案：
节能保温砖，将原材料混合搅拌、挤压成型、养护，所述原材料的重量份比为：硅酸盐水泥230～320份，膨胀珍珠岩35～20份，普砂430～610份，煤渣70～15份，秸秆6～3份，草木灰4～2份，羊毛毡纤维1.6～2份，水97～135份。
其进一步的技术方案还可以加入聚苯颗粒2～0.6份。
上述原材料中：硅酸盐水泥作为胶结料；膨胀珍珠岩、普砂以及煤渣作为节能保温砖的骨料，其中膨胀珍珠岩质轻，具有良好的保温性能，又作为保温材料；秸秆、草木灰、聚苯颗粒作为保温材料；羊毛毡纤维作为节能保温砖的抗裂纤维，又具有保温性能；水作为稀释剂。
本发明的技术效果在于：
1、本节能保温砖的原材料中，加入草木灰作为保温辅料。草木灰质轻，而且疏松多孔，具有优良的吸热保温作用。
2、本节能保温砖的原材料中还加入羊毛毡纤维，其保温和抗裂作用优良。
3、本节能保温砖节能保温性能好，用其建造的墙体可免去外墙保温处理，从而大大降低成本，每平方墙面面积节约成本约50元。
4、本节能保温砖质量轻，表面密度为实心粘土砖的1/2-1/3，用它建造的墙体与等功能砖混结构墙体相比，对墙体地基的压力小，地基处理费可降低20％，同时便于抗震。
5、用本节能保温砖建造的墙体平整牢固，无松散颗粒裸露，可直接用于内外墙、干挂石、面砖等，同时比现在采用的砖混结构墙体加外墙抹保温砂浆或外挂保温板的做法，施工周期缩短1/3的时间。
6、采用该节能保温砖的建筑，具有长期有效的保温效果，与砼土砖有同样的使用寿命。
具体实施方式
本发明按照以下步骤实施：在常温下，将各种原材料按重量份数比依次投入JSC500C搅拌机，强力搅拌90秒-120秒；将搅拌物通过物料输送机，微动流入DQT10(A)液压制砖机的成型模具内，进行压制，工作压力为3MPa，通过振动再受压，直至保温砖成型；然后进行蒸汽养护13小时-15小时，蒸汽养护温度为85℃-95℃，使成型保温砖的强度升至设计强度的70％，然后送入成品堆放场。
实施例1至实施例4的原材料重量份数见表1，单位为千克。
表1
实施例     节能保温砖规格   32.5矿渣硅酸盐水泥   膨胀珍珠岩   普砂   煤渣   秸秆   草木灰   聚苯颗粒   羊毛毡纤维    水
    1     Mu2.5     230   35   430   70   6   4   2   1.6     97
    2     Mu5.0     260   30   500   50   5   3   1.8   1.8     103
    3     Mu7.5     290   25   560   30   4   2.5   0.9   1.9     120
    4     Mu10     320   20   610   15   3   2   0.6   2     135
同规格的节能保温砖与市售砌墙体用的陶粒砼空心普通砖的测试结果见下表2，其中抗压强度的检测方法依据GB15229-2002，并采用YE-2000液压压力机来检测，Mu2.5、Mu5.0、Mu7.5、Mu10表示砌块或砖的抗压强度的标准平均值分别为2.5MPa、5.0MPa、7.5MPa、10MPa；热阻的检测依据GB10294-88，用导热系数测定仪以及防护热板法来检测。
从表2中可以看出，同规格的节能保温砖与陶粒砼空心砖相比，其抗压强度、热阻值有较大幅度的提高。
表2
    Mu2.5     Mu5.0     Mu7.5     Mu10
   抗压强度(MPa)   热阻(m2·K/W)   抗压强度(MPa)   热阻(m2·K/W)   抗压强度(MPa)     热阻(m2·K/W)    抗压强度(MPa)    热阻(m2·K/W)
节能保温砖 2.8 1.20 5.1 1.0 7.5 0.894 11 0.86
陶粒砼空心砌块 2.5 0.7 5.0 0.76 7.5 0.78 10 0.67
本发明的原材料还可以加入石膏粉、早强剂等成份。
按照建筑物不同部位的不同功能和强度的要求，可将本发明的抗压强度等级设计为Mu2.5-Mu15，可以满足用于承重或非承重墙体的要求。
节能保温砖或砌块规格齐全，包括190系列、140系列、90系列等标准规格，除此之外，还能根据用户及设计单位要求制作特定尺寸的保温砖。
本发明的砖体为空心砖结构，砖体上的开孔为一端封闭的盲孔，对外防渗功能强，阻燃性强，并可以提高保温砖或砌块抗压抗剪性能。

Claims (2)

1.节能保温砖，将原材料混合搅拌、挤压成型、养护，其特征在于所述原材料的重量份比为：硅酸盐水泥230～320份，膨胀珍珠岩35～20份，普砂430～610份，煤渣70～15份，秸秆6～3份，草木灰4～2份，羊毛毡纤维1.6～2份，水97～135份。
2.按权利要求1所述节能保温砖，其特征在于所述原材料的重量份还包括聚苯颗粒2～0.6份。
CNB2007101335905A 2007-09-24 2007-09-24 节能保温砖 Expired - Fee Related CN100542991C (zh)