CN101165078A - Method for preparing polyaramide resin modified by aromatic heterocycle and chloromonomer - Google Patents
Method for preparing polyaramide resin modified by aromatic heterocycle and chloromonomer Download PDFInfo
- Publication number
- CN101165078A CN101165078A CNA200610022083XA CN200610022083A CN101165078A CN 101165078 A CN101165078 A CN 101165078A CN A200610022083X A CNA200610022083X A CN A200610022083XA CN 200610022083 A CN200610022083 A CN 200610022083A CN 101165078 A CN101165078 A CN 101165078A
- Authority
- CN
- China
- Prior art keywords
- chloro
- phthaloyl chloride
- ursol
- resin
- aminophenyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (7)