CN101125444A - Hards mixing mortar and its processing method - Google Patents
Hards mixing mortar and its processing method Download PDFInfo
- Publication number
- CN101125444A CN101125444A CNA2006100104078A CN200610010407A CN101125444A CN 101125444 A CN101125444 A CN 101125444A CN A2006100104078 A CNA2006100104078 A CN A2006100104078A CN 200610010407 A CN200610010407 A CN 200610010407A CN 101125444 A CN101125444 A CN 101125444A
- Authority
- CN
- China
- Prior art keywords
- hards
- cement
- mortar
- lime
- sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a hards composite mortar and the method thereof, belonging to the field of building material. The original cement mortar for building raw material has large weight after solidification without tensile resistance, is easy to chap, and has low strength; moreover, such index of the traditional cement mortar as the coursing degree, the plunging degree, the strength and the cycle of freeze-thaw resistance is lower, and the traditional cement mortar wastes the cement and the sand, and has high manufacturing cost. The hards composite mortar comprises: hards, cement, lime and yellow sand, wherein, the cement mortar is mixed with hards, and the weight ratio is that: cement: lime: sand: hards equal to that firstly, the waste of flax is made into the hards with the length of 20 to 30 mm, and the diameter of 0.5 to 1.5 mm, and then all the ingredients are mixed according to the mixture ratio: cement: lime: sand: hards equals to 1: 1: 1-2 to 3-4 so as to produce the hards composite mortar, wherein, the hards accounts for 40-50 percent of the natural volume. The product is used for building raw material.
Description
Technical field:
This product relates to a kind of intensity height, and cost is low, the New Building Materials that warmth retention property is good.
Background technology:
Flax is one of China's main farm produce, and the Heilongjiang Province accounts for 85% of national cultivated area.The fiber crops skin is as the textile industry raw material, and peel off waste of flax light weight, corrosion resistant behind the numb skin, easily be processed into fine fibre, cost is low.
Raw material cement mortar for building in the past, weight after solidification is big, and tension is not easily chapped, and intensity is low.
And traditional cement mortar delamination degree, degree of sinking to, intensity, indexs such as freeze thawing resistance circulation are all lower, and water wasting mud takes sand, the cost height.
Above-mentioned purpose realizes by following technical scheme:
Hards mixing mortar, its composition comprises: hards, cement, lime, yellow ground, be mixed with hards in the described cement mortar, ratio of weight and number wherein is a cement: lime: sand: hards=1: 1: 1-2: 3-4 mixes.
Described hards mixing mortar and processing method thereof, described hards be for after peeling off numb skin with flax, the chip that is processed into waste of flax.
The processing method of described hards mixing mortar, it is long earlier waste of flax to be made 20-30mm, the hards of 0.5-1.5mm diameter, and by cement: lime: sand: the proportioning of hards=1: 1: 1-2: 3-4 mixes, make hards mixing mortar, it is 40-50% that hards accounts for natural volume content.
This technical scheme has following beneficial effect:
1. through experiment, indexs such as the delamination degree of hards mixing mortar, degree of sinking to, intensity, freeze thawing resistance circulation all satisfy the requirement of motar, and are slightly higher than traditional cement mortar.
2. this product bulk density is 64.7% of a common mixed mortar, has reduced the coat of plaster deadweight;
3. the thermal conductivity factor of hards mixing mortar is much smaller than common mixed mortar, and the thermal and insulating performance of the coat of plaster behind the 50mm is equivalent to the brick wall behind the 90mm, becomes a kind of light-weight thermal-insulation wall raw material.
4. hards mixing mortar can be used cement 32.1% for every cubic metre less, uses sand 54.4% less, can reduce coat of plaster cost 29.53%, and only the Heilongjiang Province in architectural engineering is plastered, can save 80,000,000 yuan of building costs to annual flax waste bar development and use every year.
5. the hards cement mortar can also be improved the insulation in house, sound absorption qualities, and the crack resistance of raising coat of plaster improves wall quality, reduces construction costs.
6. undergraduate course is ground into fruit and can widelys popularize in the township enterprise in flax place of production, has broad application prospects and obtains remarkable economic efficiency.Raw material flax waste of flax is agricultural byproducts, and output is big, and it is wide to distribute, and can gather materials on the spot, and turns waste into wealth.Its resource is inexhaustible.
7. the tow scutcher tool can adopt general pulverizer, need not special process equipment, and production process is simple, and once less input.Need not special factory building.The process less energy consumption, pollution-free, and pile up the contaminated environment of going rotten for waste of flax and find solution route.
8. hards processing can be located at flax place of production, be processed into fiber after, packed each job site of selling to.To the hards processing space, agricultural byproducts are become commodity can obtain economic benefit.To applying unit, saved cement and yellow ground, reduced the coat of plaster cost, also can obtain considerable economic, can think that this scientific and technological achievement has broad application prospects.
The specific embodiment of the present invention:
Embodiment 1:
Hards mixing mortar, its composition comprises: hards, cement, lime, yellow ground, ratio of weight and number wherein are cement: lime: sand: hards=1: 1: 1: 3, mix.
Described hards mixing mortar and processing method thereof, described hards be for after peeling off numb skin with flax, the chip that is processed into waste of flax.
The processing method of described hards mixing mortar, it is long earlier waste of flax to be made 30mm, the hards of 1mm diameter, with hards by cement: lime: sand: hards=1: 1: 1: 3 proportioning mixes, to becoming hards mixing mortar, it is that 40-50% is used for wall plastering and builds by laying bricks or stones that hards accounts for natural volume content.
Embodiment 2:
Hards mixing mortar, its composition comprises: hards, cement, lime, yellow ground, ratio of weight and number wherein are cement: lime: sand: hards=1: 1: 1: 4, mix.
Described hards mixing mortar and processing method thereof, described hards be for after peeling off numb skin with flax, the chip that is processed into waste of flax.
The processing method of described hards mixing mortar, it is long earlier waste of flax to be made 30mm, the hards of 1mm diameter, with hards by cement: lime: sand: hards=1: 1: 1: 4 proportioning mixes, to becoming hards mixing mortar, it is that 40-50% is used for wall plastering and builds by laying bricks or stones that hards accounts for natural volume content.
Embodiment 3:
Hards mixing mortar, its composition comprises: hards, cement, lime, yellow ground, ratio of weight and number wherein are cement: lime: sand: hards==1: 1: 2: 3, mix.
Described hards mixing mortar and processing method thereof, described hards be for after peeling off numb skin with flax, the chip that is processed into waste of flax.
The processing method of described hards mixing mortar, it is long earlier waste of flax to be made 30mm, the hards of 1mm diameter, with hards by cement: lime: sand: hards=1: 1: 2: 3 proportioning mixes, to becoming hards mixing mortar, it is that 40-50% is used for wall plastering and builds by laying bricks or stones that hards accounts for natural volume content.
Embodiment 4:
Hards mixing mortar, its composition comprises: hards, cement, lime, yellow ground, ratio of weight and number wherein are cement: lime: sand: hards==1: 1: 2: 4, mix.
Described hards mixing mortar and processing method thereof, described hards be for after peeling off numb skin with flax, the chip that is processed into waste of flax.
The processing method of described hards mixing mortar, it is long earlier waste of flax to be made 30mm, the hards of 1mm diameter, with hards by cement: lime: sand: hards=1: 1: 2: 4 proportioning mixes, to becoming hards mixing mortar, it is that 40-50% is used for wall plastering and builds by laying bricks or stones that hards accounts for natural volume content.
Claims (3)
1. hards mixing mortar, its composition comprises: hards, cement, lime, yellow ground is characterized in that: ratio of weight and number wherein is a cement: lime: sand: hards=1: 1: 1-2: 3-4 mixes.
2. hards mixing mortar according to claim 1 and processing method thereof is characterized in that: described hards is for after peeling off numb skin with flax, the chip that is processed into waste of flax.
3. the processing method of claim 1 or 2 described hards mixing mortars, it is characterized in that: it is long earlier waste of flax to be made 20-30mm, 0.5-1.5mm the hards of diameter, press cement: lime: sand: hards=1: 1: 1-2: 3-4, proportioning mix, make hards mixing mortar, it is 40-50% that hards accounts for natural volume content.