CN101122042A - Method for preparing hydroxyapatite nano composite coat with gradient function - Google Patents
Method for preparing hydroxyapatite nano composite coat with gradient function Download PDFInfo
- Publication number
- CN101122042A CN101122042A CNA2007100093059A CN200710009305A CN101122042A CN 101122042 A CN101122042 A CN 101122042A CN A2007100093059 A CNA2007100093059 A CN A2007100093059A CN 200710009305 A CN200710009305 A CN 200710009305A CN 101122042 A CN101122042 A CN 101122042A
- Authority
- CN
- China
- Prior art keywords
- hydroxyapatite nano
- composite coating
- powder
- preparation
- suspension
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A method of preparing a hydroxyapatite nano composite coating with gredient function relates to a method of preparing the hydroxyapatite nano composite coating on the surface of titanium or titanium alloy. The invention provides a method of preparing the hydroxyapatite nano composite coating with gredient function on the surface of titanium or titanium alloy by multi-layer electrophoretic codeposition of the hydroxyapatite nano powder and the metal A1 micro powder, reaction, sintering and heat treatment, so as to improve the bonding strength between the hydroxyapatite nano composite coating and the basal. The titanium or titanium alloy after mechanical finishing, alkaline washing and degreasing as well as acid etch treatment receive at least three times of electrophoretic deposition subsequently in the suspension with different Hap powder and A1 powder content in the order of gradually reduced content of A1; DC current is adopted to deposit the voltage 30 to 40V for 15 to 30 minutes; and then the sample reacts and receives sintering and heat treatment in a tube type resistance furnace to obtain the hydroxyapatite nano composite coating with gredient function, and the coating is not easy to crack during the preparation process.
Description
Technical field
The present invention relates to a kind of method for preparing hydroxyapatite nano-composite coating at titanium or titanium alloy surface.
Technical background
Pure titanium (Ti) and titanium alloy are because its biocompatibility and good mechanical properties be widely used in clinical embedded material, but its biological activity deficiency combine with the chemical of surrounding tissue relatively poor.Hydroxyapatite (hydroxyapatite, be called for short HAp) be the main inorganic composition of sclerous tissues such as human body bone, have quite high biological activity and biocompatibility, it can promote new bone in its surface growth after implanting, and participates in the metabolism of osseous tissue, can form Chemical bond with osseous tissue, the early stage bonding strength of implanting that has increased interface between planting body and bone, but the HAp mechanical property is more crisp, and fatigue performance is poor, has limited its application at human body heavy burden position.Preparation HAp coating on the metal titanium surface makes implant have both the high biological activity and the biocompatibility of Ti metal excellent mechanical property and HAp pottery, and the bone that becomes excellent property substitutes embedded material, is one of focus of present biomedical material research.
Method in titanium surface preparation HAp coating has a lot, and as plasma spraying method, sol-gel method, electrophoretic deposition etc., these methods have bigger difference on preparation technology, relative merits are respectively arranged.Electrophoretic deposition (Electrophoretic deposition, be called for short EPD) be a kind of new ceramic coatings preparation method, be widely used in the preparation of magnetic, superconduction and bioactive ceramic coating, EPD has shown significant advantage in the preparation process of ceramic coating, the mode of deposition gentleness generally can be carried out at normal temperatures; Required equipment is simple, and cost is low; By regulating voltage or electric current, be easy to the microtexture of sedimentation rate and coating is controlled; Deposition process is a non-rectilinear process, be suitable for complex-shaped, the multiple base material of porous surface.Yet, the ceramic coating green compact of electrophoretic deposition gained, density is relatively low, and only about 40%, mechanical property generally can not satisfy application requiring, so coating also needs through follow-up thermal treatment, mutually combines with densification itself that reach and with matrix.
In recent years, electrophoretic deposition biological activity hydroxyapatite coating layer has caused the common concern of Chinese scholars, obtained very big progress, but still there are some problems, the difficult point of research mainly is, how to prevent that coating from ftractureing in preparation process, and finally improve the bonding strength of coating and substrate.Cause the major cause of these problems to be that HAp coating and substrate titanium have than big-difference on physicochemical property, especially show thermal expansivity (α HAP=14 * 10 of HAp
-6K
-1) be significantly higher than thermal expansivity (α Ti=10.3 * 10 of metal titanium
-6K
-1), like this, in heat treated temperature-fall period, the easy deleterious tension stress of accumulation at the interface in coating and substrate, thereby make coating be easy to come off, in addition, bigger volumetric shrinkage takes place in the densification process of coating, the substrate titanium is then almost without any contraction, and this not matching also induced the generation of crackle in the inner a large amount of internal stress of accumulation of coating.Reaction sintering is that metal-powder is added in the ceramic powder, with common moulding of pottery and sintering, in sintering process, the reaction of metal-powder generation in-situ oxidation generates metal oxide, promote the mutual bonding of original ceramic particle, can reduce ceramic sintering temperature, improve the ceramic post sintering performance, improve the stupalith mechanical property.Studies show that design and preparation have the compound coating of gradient function, can improve the character of single coating, alleviate the difference of character between coated material and the base material, improve the bonding strength between coating and substrate.
Summary of the invention
Purpose of the present invention aims to provide a kind of employing with hydroxyapatite nano powder and metal A l micro mist multilayer electrophoresis codeposition, through reaction sintering thermal treatment, can improve the bonding strength of hydroxyapatite coating layer and substrate, have the method for gradient function hydroxyapatite nano-composite coating at titanium or titanium alloy surface preparation.
Described a kind of its step of preparation method with gradient function hydroxyapatite nano-composite coating is as follows:
Step 1): substrate pretreatment
(1) mechanical polishing: through being mechanical grinding to evenly light of surface, described substrate is titanium or titanium alloy with substrate;
(2) ester is taken off in alkali cleaning: after grinded substrate is put into alkaline wash and handled 3~10min, take out to clean and remove remained on surface alkali lye;
(3) acid etch: etching solution is put in the substrate after the alkali cleaning handled 30~45s, take out and clean, dry stand-by;
Step 2): the preparation of suspension
As dispersion solvent, add the suspension that HAp powder and Al powder are mixed with different HAp and Al content with ethanol, wherein Hap content is 10~20gL
-1, Al content is 0~10gL
-1, regulate pH to 4~5, mechanical stirring is disperseed, and forms steady suspension, still aging 1~3 day;
Step 3): electrophoretic deposition
Before the deposition, with the ultrasonic 15~30min of suspension, be negative electrode with the substrate earlier, two relative stainless steel thin slices are as counter electrode, substrate places its middle, adopt direct supply, deposition voltage 30~40V, depositing time 15~30s, the order that reduces gradually by the content of Al is electrophoretic deposition at least 3 times in the suspension of different HAp powder and Al powder content successively, after deposition was finished, sample dried naturally, kept dry;
Step 4): reaction sintering thermal treatment
Thermal treatment is carried out in tube type resistance furnace, and sample places the magnetic boat, pushes the tube furnace center, and places the magnetic boat that carbon dust is housed near the inlet end of tube furnace, at first, in air with 3~5 ℃ of min
-1Heat-up rate is warming up to 600~700 ℃, insulation 1~2h, and under argon shield atmosphere, control argon gas flow velocity is 2300~2500mLh then
-1, with same heat-up rate, continuing to be warming up to 850~900 ℃, insulation 2~3h is at last with 1~2 ℃ of min
-1Cooling rate slowly is cooled to below 200 ℃, stops ventilation, takes out, and promptly obtains to have the hydroxyapatite nano-composite coating of gradient function.
In step 1, the concentration of the HF in the described etching solution is 40%, the HNO in the etching solution
3Concentration be 65%~68%, described etching solution is by 80~100mLL
-1HF and 240~300mLL
-1HNO
3Formulated.
In step 2, the median size of described Al powder is 100~500nm; The median size of HAp powder is 50~100nm.Described alkaline wash is by 15~20gL
-1Yellow soda ash, 15~20gL
-1Sodium phosphate, 5~10gL
-1Sodium silicate and 2~5mLL
-1Triton X-100 is formulated.
The present invention adopts HAp nano powder and Al sub-micro powder multilayer electrophoresis codeposition, makes the HAp/Al nano-composite coating, compound coating along metal base outward, the content of Al reduces gradually, and the content of HAp increases gradually, outermost layer is pure HAp nanometer layer.Adopt the reaction sintering technology, through Overheating Treatment, Al is oxidized to Al
2O
3, the final HAp/Al that forms with gradient function
2O
3Nano-composite coating is in the hope of improving the mechanical property of HAp coating.In thermal treatment, Al → Al
2O
3The volumetric expansion of reaction has been offset the densification of coating and has been shunk, and can suppress the formation of coating crack; Simultaneously, Al
2O
3Thermal expansivity be about 8.2 * 10
-6K
-1, with HAp compound after, at the thermal expansivity that has to a certain degree reduced coating, make itself and base material more approaching, also play a positive role for suppressing coating cracking.After adopting this method, coating is not easy to crack in preparation process, has higher binding strength.
Description of drawings
Fig. 1 is the surface topography SEM figure (SEM, * 50,000) of compound coating after embodiment 1 thermal treatment.
Fig. 2 is the cross section pattern SEM figure (SEM, * 500) of compound coating after embodiment 1 thermal treatment, and in Fig. 2, a, b, c, d, e represent a place of getting of EDS ultimate analysis.
Fig. 3 is a compound coating cross section EDS results of elemental analyses after embodiment 1 thermal treatment.In Fig. 3, X-coordinate is that ordinate zou is constituent content Element Content (wt%) along metal base coat-thickness Distance/ μ m outward, wherein each corresponding position in a, b, c, d, the e difference corresponding diagram 2.
Embodiment
Embodiment 1
1. substrate pretreatment: (1) mechanical polishing: getting thickness is the sample of the titanium sample cutting of 0.8mm into about 30mm * 10mm size, and successively through 100#, 800#, 1200# silicon carbide paper are mechanical grinding to evenly light of surface.(2) finger is taken off in alkali cleaning: in the 500mL deionized water, add 10g yellow soda ash successively, and the 10g sodium phosphate, 5g sodium silicate after the heating for dissolving, adds the Triton X-100 (OP-10) of 2.5mL again, mixes.Pour out about 50mL, with the polishing the titanium sample all put into alkaline wash, boil 5min after, change ultrasonic 5min in the ultrasonic cleaner over to.Take out the back with the tap water flushing, thoroughly remove remained on surface alkali lye.(3) acid etch: in graduated 500mL Plastic Bottle, add a certain amount of deionized water earlier, add 50mL HF (40wt%) then, and the dense HNO of 150mL
3(68wt%), after shaking up, add deionized water, shake up to the 500mL scale marks.Pour out about 50mL in plastic beaker, the titanium sample after the alkali cleaning is put into processing one by one, about 30s of treatment time, take out to put into immediately in the mobile tap water and wash, remove the remained on surface acid solution rapidly, clean up, place 120 ℃ of baking oven oven dry stand-by with deionization.
2. the preparation of suspension: measure the 50mL dehydrated alcohol respectively in the 100mL beaker, drip 1 dense HNO
3, after the stirring, with the pH test paper test pH between 4~5, add the HAp powder and the Al powder of different proportionings, three parts of suspension of configuration, respectively with S1, S2, S3 represent, behind the magnetic agitation 30min, ultrasonic again 1h, still aging afterwards 1d.Wherein powder content is respectively, S1:0.50g HAp, 0.50g Al; S2:0.75g HAp, 0.25g Al; S3:1.0g HAp, 0gAl.
3. electrophoretic deposition: respectively suspension is stirred and ultrasonic 25min before the deposition, (3.5cm * 4cm * 0.06cm) insert abreast respectively in S1, S2 and the S3 suspension, adjustment its spacing is 2cm with two stainless steel disc counter electrode.Sample (as negative electrode) with the pre-treatment after drying, insert in the S1 suspension, place in the middle of two counter electrode, depth of penetration 1~1.5cm transfers to 30V with direct supply voltage, and electric current transfers to zero place, opening power, strengthen electric current rapidly, make power supply output changing into rapidly constant voltage mode, time length 15s.Take out sample, insert in the S2 suspension, place in the middle of two counter electrode, depth of penetration 1~1.5cm transfers to 35V with direct supply voltage, and electric current transfers to zero place, and opening power strengthens electric current rapidly, makes power supply output changing into rapidly constant voltage mode, time length 20s.Take out sample, insert in the S3 suspension, place in the middle of two counter electrode, depth of penetration 1~1.5cm transfers to 40V with direct supply voltage, and electric current transfers to zero place, and opening power strengthens electric current rapidly, makes power supply output changing into rapidly constant voltage mode, time length 30s.After deposition is finished, take out sample and in air, dry, put into moisture eliminator and preserve, usefulness to be heated.
4. thermal treatment: thermal treatment is carried out in tube type resistance furnace, and sample places the magnetic boat, pushes the tube furnace center, and places the magnetic boat that carbon dust is housed near the inlet end of tube furnace.At first, in air with 3 ℃ of min
-1Speed be warming up to 660 ℃, insulation 2h opens high-purity argon gas (purity 〉=99.999%) then as protective atmosphere, control argon gas flow velocity is 2500mLh
-1, with 3 ℃ of min
-1Speed be warming up to 850 ℃, the insulation 2h, at last with 1 ℃ of min
-1Be cooled to below 200 ℃, stop ventilation, take out.
Fig. 1 shows that for the surface topography of compound coating after the thermal treatment compound coating has nanostructure.Fig. 2 shows that for the cross section pattern of compound coating after the thermal treatment compound coating and titanium matrix bond are tight, does not have crackle.Fig. 3 shows that for compound coating cross section EDS results of elemental analyses after the thermal treatment (among the figure elements corresponding be respectively Ca, P, Al and Ti) from top to bottom the chemical ingredients of compound coating is gradually changed to skin by internal layer, has gradient function, has realized by HAp/Al
2O
3The outer field composition transition of the pure HAp of course in compound.
5. bonding strength test: coating and substrate bonding strength testing method are as follows: according to the ASTM-F1044 standard, utilize bonding-stretching method, measure the shearing bond strength of coating, Bond Strength of Coating is calculated as follows: σ=F/S (σ: the shearing bond strength of coating; F: fracture maximum pull; S: the effective stressed area of coating)., stretch with WDS-5 type electronic universal tester as binding agent with FM1000adhesive film (U.S. Cytec Fiberite company), rate of extension is 1mmmin
-1, under the identical conditions, test three samples, obtain mean value, calculating anchoring strength of coating mean value is 37.85MPa (fracture occurs between coating and the substrate).
Embodiment 2
1. substrate pretreatment: (1) mechanical polishing: with embodiment 1.(2) finger is taken off in alkali cleaning: with embodiment 1.(3) acid etch: in graduated 500mL Plastic Bottle, add a certain amount of deionized water earlier, add 40mL HF (40wt%) then, and the dense HNO of 120mL
3(68wt%), after shaking up, add deionized water, shake up to the 500mL scale marks.Pour out about 50mL in plastic beaker, the titanium sample after the alkali cleaning is put into processing one by one, about 40s of treatment time, after the taking-up, put into immediately in the mobile tap water and wash, remove the remained on surface acid solution rapidly, clean up with deionization, place 120 ℃ of baking oven oven dry stand-by.
2. the preparation of suspension: press embodiment 1 formulated suspension, still aging 2d.
3. electrophoretic deposition: respectively suspension is stirred and ultrasonic 25min before the deposition, (3.5cm * 4cm * 0.06cm) insert abreast respectively in S1, S2 and the S3 suspension, adjustment its spacing is 2cm with two stainless steel disc counter electrode.Sample (as negative electrode) with the pre-treatment after drying, insert in the S1 suspension, place in the middle of two counter electrode, depth of penetration 1~1.5cm transfers to 32V with direct supply voltage, and electric current transfers to zero place, opening power, strengthen electric current rapidly, make power supply output changing into rapidly constant voltage mode, time length 15s.Take out sample, insert in the S2 suspension, place in the middle of two counter electrode, depth of penetration 1~1.5cm transfers to 38V with direct supply voltage, and electric current transfers to zero place, and opening power strengthens electric current rapidly, makes power supply output changing into rapidly constant voltage mode, time length 15s.Take out sample, insert in the S3 suspension, place in the middle of two counter electrode, depth of penetration 1~1.5cm transfers to 40V with direct supply voltage, and electric current transfers to zero place, and opening power strengthens electric current rapidly, makes power supply output changing into rapidly constant voltage mode, time length 30s.After deposition is finished, take out sample and in air, dry, put into moisture eliminator and preserve, usefulness to be heated.
4. thermal treatment: thermal treatment is carried out in tube type resistance furnace, and sample places the magnetic boat, pushes the tube furnace center, and places the magnetic boat that carbon dust is housed near the inlet end of tube furnace.At first, in air with 5 ℃ of min
-1Speed be warming up to 660 ℃, insulation 1h opens high-purity argon gas (purity 〉=99.999%) then as protective atmosphere, control argon gas flow velocity is 2500mLh
-1, with 5 ℃ of min
-1Speed be warming up to 900 ℃, the insulation 3h, at last with 1 ℃ of min
-1Be cooled to below 200 ℃, stop ventilation, take out.The characterization result of compound coating SEM and EDS is with embodiment 1 after the thermal treatment.
5. bonding strength test: testing method is with embodiment 1, and the mean value that calculates anchoring strength of coating is 39.64MPa (fracture occurs between coating and the substrate).
Embodiment 3
1. substrate pretreatment: (1) mechanical polishing: replace titanium with the TC4 titanium alloy, all the other are with embodiment 1.(2) finger is taken off in alkali cleaning: in the 500mL deionized water, add 7.5g yellow soda ash successively, and the 7.5g sodium phosphate, 2.5g sodium silicate after the heating for dissolving, adds the Triton X-100 (OP-10) of 2mL again, mixes.Pour out about 50mL, the titanium sample of polishing all put into alkaline wash, boil 5min after, change that ultrasonic 5min. takes out the back with the tap water flushing in the ultrasonic cleaner over to, thoroughly remove remained on surface alkali lye.(3) acid etch: with embodiment 1.
3. the preparation of suspension: measure the 50mL dehydrated alcohol in the 100mL beaker, drip 1 dense HNO
3, after the stirring, with the pH test paper test pH between 4~5, add the HAp powder and the Al powder of different proportionings, three parts of suspension of configuration, respectively with S1, S2, S3 represent, behind the magnetic agitation 30min, ultrasonic again 1h, still aging afterwards 2d.Powder content is respectively, S1:0.50g HAp, 0.50g Al; S2:0.80g HAp, 0.20g Al; S3:1.0g HAp, 0g Al.
4. electrophoretic deposition: electrophoretic deposition process is with embodiment 1.
5. thermal treatment: thermal treatment is carried out in tube type resistance furnace, and sample places the magnetic boat, pushes the tube furnace center, and places the magnetic boat (further deoxygenation) that carbon dust is housed near the inlet end of tube furnace.At first, in air with 5 ℃ of min
-1Speed be warming up to 660 ℃, insulation 1h opens high-purity argon gas (purity 〉=99.999%) then as protective atmosphere, control argon gas flow velocity is 2300mLh
-1, then, with 5 ℃ of min
-1Speed be warming up to 850 ℃, the insulation 3h, at last with 2 ℃ of min
-1Be cooled to below 200 ℃, stop ventilation, take out.The characterization result of compound coating SEM and EDS is with embodiment 1 after the thermal treatment.
6. bonding strength test: testing method is with embodiment 1, and the mean value that calculates anchoring strength of coating is 38.27MPa (fracture occurs between coating and the substrate).
Embodiment 4
1. substrate pretreatment: (1) mechanical polishing: with embodiment 1.(2) finger is taken off in alkali cleaning: with embodiment 1.(3) acid etch: in graduated 500mL Plastic Bottle, add a certain amount of deionized water earlier, add 40mL HF (40wt%) then, and the dense HNO of 120mL
3(65wt%), after shaking up, add deionized water, shake up to the 500mL scale marks.Pour out about 50mL in plastic beaker, the titanium sample after the alkali cleaning is put into processing one by one, about 40s of treatment time, after the taking-up, put into immediately in the mobile tap water and wash, remove the remained on surface acid solution rapidly, clean up with deionization, place 120 ℃ of baking oven oven dry stand-by.
2. the preparation of suspension: measure the 50mL dehydrated alcohol in the 100mL beaker, drip 1 dense HNO
3, after the stirring, with the pH test paper test pH between 4~5, add the HAp powder and the Al powder of different proportionings, four parts of suspension of configuration, respectively with S1, S2, S3, S4 represent, behind the magnetic agitation 30min, ultrasonic again 1h, still aging afterwards 3 days.Powder content is respectively, S1:0.50g HAp, 0.50g Al; S2:0.65g HAp, 0.35g Al; S3:0.85g HAp, 0.15g Al; S4:1.0g HAp, 0g Al.
3. electrophoretic deposition: respectively suspension is stirred and ultrasonic 25min before the deposition, (3.5cm * 4cm * 0.06cm) insert abreast respectively in S1, S2, S3 and the S4 suspension, adjustment its spacing is 2cm with two stainless steel disc counter electrode.Sample (as negative electrode) with the pre-treatment after drying, insert in the S1 suspension, place in the middle of two counter electrode, depth of penetration 1~1.5cm transfers to 30V with direct supply voltage, and electric current transfers to zero place, opening power, strengthen electric current rapidly, make power supply output changing into rapidly constant voltage mode, time length 10s.Take out sample, insert in the S2 suspension, place in the middle of two counter electrode, depth of penetration 1~1.5cm transfers to 30V with direct supply voltage, and electric current transfers to zero place, and opening power strengthens electric current rapidly, makes power supply output changing into rapidly constant voltage mode, time length 15s.Take out sample, insert in the S3 suspension, place in the middle of two counter electrode, depth of penetration 1~1.5cm transfers to 35V with direct supply voltage, and electric current transfers to zero place, and opening power strengthens electric current rapidly, makes power supply output changing into rapidly constant voltage mode, time length 15s.Take out sample, insert in the S4 suspension, place in the middle of two counter electrode, depth of penetration 1~1.5cm transfers to 40V with direct supply voltage, and electric current transfers to zero place, and opening power strengthens electric current rapidly, makes power supply output changing into rapidly constant voltage mode, time length 30s.After deposition is finished, take out sample and in air, dry, put into moisture eliminator and preserve, usefulness to be heated.
4. thermal treatment: thermal treatment is carried out in tube type resistance furnace, and sample places the magnetic boat, pushes the tube furnace center, and places the magnetic boat that carbon dust is housed near the inlet end of tube furnace.At first, in air with 5 ℃ of min
-1Speed be warming up to 660 ℃, insulation 1h opens high-purity argon gas (purity 〉=99.999%) then as protective atmosphere, control argon gas flow velocity is 2300mLh
-1, with 5 ℃ of min
-1Speed be warming up to 900 ℃, the insulation 2h, at last with 1 ℃ of min
-1Be cooled to below 200 ℃, stop ventilation, take out.The characterization result of compound coating SEM and EDS is with embodiment 1 after the thermal treatment.
5. bonding strength test: testing method is with embodiment 1, and the mean value that calculates anchoring strength of coating is 39.07MPa (fracture occurs between coating and the substrate).
Claims (7)
1. the preparation method with gradient function hydroxyapatite nano-composite coating is characterized in that the steps include:
Step 1): substrate pretreatment
(1) mechanical polishing: through being mechanical grinding to evenly light of surface, described substrate is titanium or titanium alloy with substrate;
(2) ester is taken off in alkali cleaning: after grinded substrate is put into alkaline wash and handled 3~10min, take out and clean;
(3) acid etch: etching solution is put in the substrate after the alkali cleaning handled 30~45s, take out and clean, dry stand-by;
Step 2): the preparation of suspension
As dispersion solvent, add the suspension that HAp powder and Al powder are mixed with different HAp and Al content with ethanol, wherein Hap content is 10~20gL
-1, Al content is 0~10gL
-1, regulate pH to 4~5, mechanical stirring is disperseed, and forms steady suspension, still aging 1~3 day;
Step 3): electrophoretic deposition
Before the deposition, with the ultrasonic 15~30min of suspension, be negative electrode with the substrate earlier, two relative stainless steel thin slices are as counter electrode, substrate places its middle, adopt direct supply, deposition voltage 30~40V, depositing time 15~30s, the order that reduces gradually by the content of Al is electrophoretic deposition at least 3 times in the suspension of different HAp powder and Al powder content successively, after deposition was finished, sample dried naturally, kept dry;
Step 4): reaction sintering thermal treatment
Thermal treatment is carried out in tube type resistance furnace, and sample places the magnetic boat, pushes the tube furnace center, and places the magnetic boat that carbon dust is housed near the inlet end of tube furnace, at first, in air with 3~5 ℃ of min
-1Heat-up rate is warming up to 600~700 ℃, insulation 1~2h, and under argon shield atmosphere, control argon gas flow velocity is 2300~2500mLh then
-1, with same heat-up rate, continuing to be warming up to 850~900 ℃, insulation 2~3h is at last with 1~2 ℃ of min
-1Cooling rate slowly is cooled to below 200 ℃, stops ventilation, takes out, and promptly obtains to have the hydroxyapatite nano-composite coating of gradient function.
2. a kind of preparation method with gradient function hydroxyapatite nano-composite coating as claimed in claim 1 is characterized in that described alkaline wash is by 15~20gL
-1Yellow soda ash, 15~20gL
-1Sodium phosphate, 5~10gL
-1Sodium silicate and 2~5mLL
-1Triton X-100 is formulated.
3. a kind of preparation method with gradient function hydroxyapatite nano-composite coating as claimed in claim 1 is characterized in that described etching solution is by 80~100mLL
-1HF and 240~300mLL
-1HNO
3Formulated.
4. a kind of preparation method with gradient function hydroxyapatite nano-composite coating as claimed in claim 3, the concentration that it is characterized in that the HF in the etching solution is 40%.
5. a kind of preparation method with gradient function hydroxyapatite nano-composite coating as claimed in claim 3 is characterized in that the HNO in the etching solution
3Concentration be 65%~68%.
6. a kind of preparation method with gradient function hydroxyapatite nano-composite coating as claimed in claim 1 is characterized in that in the step 2 that the median size of described Al powder is 100~500nm.
7. a kind of preparation method with gradient function hydroxyapatite nano-composite coating as claimed in claim 1 is characterized in that in the step 2 that the median size of described HAp powder is 50~100nm.