CN101121840A - Normal temperature solidifying fluorine-carbon coating for rubber roller - Google Patents
Normal temperature solidifying fluorine-carbon coating for rubber roller Download PDFInfo
- Publication number
- CN101121840A CN101121840A CNA2007100771998A CN200710077199A CN101121840A CN 101121840 A CN101121840 A CN 101121840A CN A2007100771998 A CNA2007100771998 A CN A2007100771998A CN 200710077199 A CN200710077199 A CN 200710077199A CN 101121840 A CN101121840 A CN 101121840A
- Authority
- CN
- China
- Prior art keywords
- component
- rubber roller
- normal temperature
- percent
- carbon coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention pertains to the technical field of surface processing materials, disclosing a normal-temperature solidifying fluorocarbon paint applied to rubber rollers. The normal-temperature solidifying paint, consists of component A and component B. Component A consists of fluorocarbon resin (50 to 80 percent) containing hydroxides in the molecular structure, organic silicone resin (3 to 15 percent) containing hydroxides in the molecular structure, extinct powder (2 to 9 percent), sumatriptan (1 to 6 percent), solidifying agent (0.3 to 2 percent) and solvent (10 to 30 percent). Hydroxy content of the fluorocarbon resin covers 1.5 percent to 2.5 percent and hydroxyl content of the organic silicone resin covers 0.5 to 1 percent; the component B is fatty poly-isocyanatopropane solidifying agent, the isocyanatopropane content is 12 to 19.6 percent; the mass ratio between the component A and the component B is 3 to 8:1. The paint is solidified by heating under normal-temperature or low temperature, and a variety of optional raw materials are available for rubber rollers; the friction coefficient of coating is 0.2 to 0.4, meeting the requirements of the rubber roller of a printer on surface friction coefficient; in terms of release property of coating, the ink ribbon is not bonded under room-temperature; the ink ribbon is not bonded in 3 second under 150 DEG C; the paint is coated on the rubber roller of the printer, and the printed pictures have the advantages of fresh colors, bleeding and color contamination-free property and sound definition. And the rubber rollers has no abnormity after 20,000 aging tests.
Description
Technical field
The present invention relates to coating, relate in particular to a kind of normal temperature solidifying fluorine-carbon coating for rubber roller.
Background technology
The coating that is used for printer rubber roll surface requires the performance that suitable coefficient of friction is arranged and all do not glue colour band under normal temperature, high temperature.At present, be used for the coating on printer rubber roll surface, be single-component hot setting type fluorocarbon coating, its solidification value reaches more than 220 ℃.Because the finish size of printer rubber roll is very accurate, dimensional change can take place because of not tolerating high temperature like this with crude rubber in rubber roll, have only silica gel roller to can be used for the application of single-component hot setting type fluorocarbon coating at present and do not deform, make the selection of rubber roll raw material limited greatly.In addition, because silica gel raw material and the costliness of hot setting type fluorocarbon coating and the consumption of the required energy of high temperature make finished product rubber roll cost high.The rubber roll that single-component hot setting type fluorocarbon coating is made, though have lower coefficient of friction, the performance less stable that it does not at high temperature glue colour band brings very big difficulty to machining control, yield rate is lower.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art, provide a kind of and solidify at normal temperatures, have suitable coefficient of friction and under normal temperature or comparatively high temps equal performances of sticking colour band not, be applicable to the fluorocarbon coating on rubber roll surface.
For achieving the above object, the technical solution used in the present invention is:
A kind of normal temperature solidifying fluorine-carbon coating for rubber roller, comprise first component and second component, it is characterized in that: the first component comprises silicone resin 3~15%, the flatting silica 2~9% of hydroxyl in the fluorocarbon resin 50~80%, molecular structure of hydroxyl in the molecular structure, cured powder 1~6%, auxiliary agent 0.3~2% and solvent 10~30%, hydroxy radical content is 1.5%~2.5% in the fluorocarbon resin, and hydroxy radical content is 0.5~1% in the silicone resin; The second component is the aliphatic polymeric isocyanate solidifying agent, and isocyanato content is 12~19.6%; The mass ratio of first component and second component is 3~8: 1.
In a kind of optimized technical scheme, described first component comprises silicone resin 5~8%, the flatting silica 2~6% of hydroxyl in the fluorocarbon resin 65~70%, molecular structure of hydroxyl in the molecular structure, cured powder 2~5%, auxiliary agent 1~1.5% and solvent 15~18%.
In a kind of optimized technical scheme, the silicone resin of hydroxyl is the hydroxyl polydimethylsiloxaneresins resins in the described molecular structure.
In a kind of optimized technical scheme, described flatting silica is the synthetic gas aerosil particle through organic process.
In a kind of optimized technical scheme, described cured powder is that polyethylene micropowderization is cured.
In a kind of optimized technical scheme, described auxiliary agent is defoamer, flow agent, the wetting dispersing agent mixture by mass ratio 1: 0.8~2: 1~3.
In a kind of preferred technical scheme, described defoamer is an organo-siloxane type defoamer.
In a kind of preferred technical scheme, described flow agent is organopolysiloxane mixture, polyether-modified dimethyl-silicon alkyl copolymer or fluorine-carbon modified dimethyl polysiloxane multipolymer.
In a kind of preferred technical scheme, described wetting dispersing agent is the mixture of unsaturated polycarboxylic acid polymkeric substance of lower molecular weight and organosiloxane copolymer.
In a kind of optimized technical scheme, described solvent is the positive fourth fat of acetic acid, 1-Methoxy-2-propyl acetate, pimelinketone, dimethylbenzene or its mixture.
Beneficial effect of the present invention: at normal temperatures or low-temperature heat solidify, the starting material of rubber roll have multiple choices; The coefficient of friction of coating is 0.2~0.4, satisfies the requirement of printer rubber roll to skin friction coefficient; The release of coating: the not sticking colour band of normal temperature; 150 ℃, 3 seconds not sticking colour bands; Paint spay-coating on the printer rubber roll, the bright nonbleeding of the photo color that prints, colour contamination, sharpness is good, it is no abnormal that rubber roll is gone through 20,000 times senile experiment.
Embodiment
Normal temperature solidifying fluorine-carbon coating for rubber roller of the present invention, the preparation method of its first component is: add the fluorocarbon resin, auxiliary agent of specified amount and 1/3 solvent by the weight ratio of first component prescription in container; After under the rotating speed of 500rpm it being mixed, progressively slowly add flatting silica, cured powder.Flatting silica, cured powder are reinforced finish after, the rotating speed of high speed dispersor is heightened to 1500rpm, high speed dispersion 30 minutes, when fineness during to≤30UM, press formula ratio and add silicone resin, remaining solvent, after disperseing 15 minutes under the rotating speed of 500rpm, filter metering packing with 150~200 mesh filter screens.
During use, first, component B is 3~8: 1 proportioning mixing by weight, and slaking was used after 15 minutes.
Fluorocarbon resin can adopt GK570, GK550 that Daikin company produces, GK500 etc., the K-700 that perhaps Japanese Di Aisheng (DIC) company produces, wherein one or both such as K-704, contain hydroxyl in the molecular structure of these fluorocarbon resins, hydroxy radical content between 1.5~2.5% (wt%), can with the contained isocyanato generation crosslinking curing of second component.
Silicone resin is the hydroxyl polydimethylsiloxaneresins resins, and hydroxy radical content is 0.5~1% (wt%), as the XHC-303 of blue star group spark chemical plant production.
Flatting silica adopts the synthetic gas aerosil particle through organic process, as: the ED30 of W. R. Grace ﹠ Co, the OK500 of Degussa company etc.
Cured powder adopts polyethylene micropowderization cured, as the Polyfluo150 of the bright micro mist of Mike company, and the Shamrock s-232 of the U.S. three leaf companies etc.
Auxiliary agent is the mixture of defoamer, flow agent, wetting dispersing agent, and is formulated with 1: 0.8~2: 1~3 weight ratio.Defoamer adopts and to contain organo-siloxane type defoamer, as BYK051, the BYK052 of German Bi Ke chemical company, the EFKA2022 of Ciba company, EFKA2038.Flow agent adopts a kind of of organopolysiloxane mixture, polyether-modified dimethyl-silicon alkyl copolymer, fluorine-carbon modified dimethyl polysiloxane multipolymer etc., as EFKA333, BYK3600, the BYK358 of German Bi Ke chemical company.EFKA3033, EFKA3288 as Ciba company.Wetting dispersing agent is that the unsaturated polycarboxylic acid polymkeric substance of lower molecular weight adds the organo-siloxane multipolymer, as the BYK-P104S of German Bi Ke chemical company, as the EFKA5065. of Ciba company
The mixture of one or more in the positive fourth fat of solvent employing acetic acid, 1-Methoxy-2-propyl acetate, pimelinketone, the dimethylbenzene.
Component B is the aliphatic polymeric isocyanate solidifying agent, and isocyanato content is 12~19.6%, can adopt as the DESMODEY N75 of Bayer chemical company, N3390.
The coating method of coating of the present invention can adopt spraying, and coat-thickness is controlled at 15um~30um, can obtain promising result.
Below with embodiment the present invention is described, but embodiment does not constitute any limitation of the invention.
Embodiment 1
Consisting of of first component:
Fluorocarbon resin (GK550) 67.5kg
Silicone resin (XHC-303) 7.7kg
Flatting silica (ED-30) 3.7kg
Cured powder (S-232) 3.2kg
EFKA2038 0.35kg
BYK333 0.35kg
BYK-P104S 0.5kg
N-BUTYL ACETATE 10.7kg
Dimethylbenzene 6kg
Consisting of of component B: DESMODUR N3390
The mass ratio of first, component B is 4: 1
Prepare the first component according to following step: in container, add GK550 resin 67.5kg by first component prescription, defoamer EFKA2038 0.35kg, flow agent BYK333 0.35kg, wetting dispersing agent BYK-P104S0.5kg, dimethylbenzene 6kg, after mixing with the stirring velocity of 500rpm at normal temperatures, progressively slowly add flatting silica ED30 3.7kg, cured powder S-232 3.2kg, the high speed dispersor rotating speed is heightened to 1500rpm, disperseed 30 minutes, and, press formula ratio adding silicone resin XHC-303 7.7kg when fineness during to≤30UM, N-BUTYL ACETATE 10.7kg, after disperseing 15 minutes under the rotating speed of 500rpm, the product viscosity that obtains is 73~77KU, solid content 63.5 ± 2%.Through sampling Detection, metering packing is filtered in qualified back with 200 mesh filter screens.
By weight 4: 1 mixings, slaking was sprayed at after 15 minutes on the printer rubber roll of butyronitrile rubber making with above first, the component B that makes, and control coating thickness is 25 ± 2 μ m, and it is as shown in table 1 to detect performance.
Table 1
Test item | Detected result | Remarks |
Film time of drying | Under the room temperature, 24 hours absolutely dry | Pressing GB1728-79 detects |
80 ℃ ± 5 ℃, 30 minutes absolutely dry | ||
Sticking power (cross-hatching) | 1 grade | Press GB9286-1998 |
Shock resistance | 50kg.cm | Press GB1732-93 |
The coefficient of friction of coating | 0.32 | Pressing GB/T10006-1988 detects |
The release of coating | The not sticking colour band of normal temperature; 150 ℃, 3 seconds not sticking colour bands | Detect with reference to ASTMD3330 |
The rubber roll result of use | The photo that prints nonbleeding bright in luster, colour contamination, sharpness is good | The installation test |
The rubber roll ageing-resistant performance | The senile experiment of going through 20,000 times is no abnormal | Detect with reference to GB/T7762-2003 |
Embodiment 2~3
Each component composition and consumption (kg) are as table 2, and the preparation method is with embodiment 1.
Table 2
Component | Constituent | Embodiment 2 | Embodiment 3 |
The first component | Fluorocarbon resin (GK550) | 64.5 | 70.2 |
Silicone resin (XHC-303) | 6.5 | 7.0 | |
Flatting silica (OK-500) | 6.1 | 2.6 | |
Cured powder (S-232) | 4.7 | 2.2 | |
BYK051 | 0.3 | 0.4 | |
BYK333 | 0.3 | 0.4 | |
BYK-P104S | 0.6 | 0.5 | |
N-BUTYL ACETATE | 11 | 12 | |
Dimethylbenzene | 6 | 4.7 | |
Component B | DESMODUR N3390 | 22.2 | 28.6 |
Proportioning | First component: component B | 4.5∶1 | 3.5∶1 |
By weight 4: 1 mixings, slaking was sprayed at after 15 minutes on the printer rubber roll of butyronitrile rubber making with above first, the component B that makes, and control coating thickness is 25 ± 2 μ M, detected performance respectively shown in table 3 and table 4.
Table 3
Test item | Detected result | Remarks |
Film time of drying | Under the room temperature, 24 hours absolutely dry | Pressing GB1728-79 detects |
80 ℃ ± 5 ℃, 25 minutes absolutely dry | ||
Sticking power | 1 grade | Press GB9286-1998 (cross-hatching) |
Shock resistance | 50kg.cm | Pressing GB1732-93 detects |
The coefficient of wear of coating | 0.2 | Pressing GB/T10006-1998 detects |
The release of coating | The not sticking colour band of normal temperature; 150 ℃, 5 seconds not sticking colour bands | Detect with reference to ASTMD3330 |
The rubber roll result of use | The photo that prints is bright in luster, nonbleeding, colour contamination, and sharpness is good | The installation test |
The rubber roll ageing-resistant performance | The senile experiment of going through 20,000 times is no abnormal | Detect with reference to GB/T7762-2003 |
Table 4
Test item | Detected result | Remarks |
Film time of drying | Under the room temperature, 24 hours absolutely dry | Pressing GB1728-79 detects |
80 ℃ ± 5 ℃, 30 minutes absolutely dry | ||
Sticking power | 0 grade | Press GB9286-1998 (cross-hatching) |
Shock resistance | 50kg.cm | Press GB1732-93 |
The coefficient of wear of coating | 0.4 | Pressing GB/T1006-1998 detects |
The release of coating | The not sticking colour band of normal temperature, 150 ℃, 3 seconds not sticking colour bands | Detect with reference to ASTMD3330 |
The rubber roll result of use | The photo that prints is bright in luster, nonbleeding, and colour contamination, sharpness is good | Installation detects |
The rubber roll ageing-resistant performance | The senile experiment of going through 20,000 times is no abnormal | Detect with reference to GB/T7762-2003 |
Claims (10)
1. normal temperature solidifying fluorine-carbon coating for rubber roller, comprise first component and second component, it is characterized in that: the first component comprises silicone resin 3~15%, the flatting silica 2~9% of hydroxyl in the fluorocarbon resin 50~80%, molecular structure of hydroxyl in the molecular structure, cured powder 1~6%, auxiliary agent 0.3~2% and solvent 10~30%, hydroxy radical content is 1.5%~2.5% in the fluorocarbon resin, and hydroxy radical content is 0.5~1% in the silicone resin; The second component is the aliphatic polymeric isocyanate solidifying agent, and isocyanato content is 12~19.6%; The mass ratio of first component and second component is 3~8: 1.
2. normal temperature solidifying fluorine-carbon coating for rubber roller according to claim 1, it is characterized in that: described first component comprises silicone resin 5~8%, the flatting silica 2~6% of hydroxyl in the fluorocarbon resin 65~70%, molecular structure of hydroxyl in the molecular structure, cured powder 2~5%, auxiliary agent 1~1.5% and solvent 15~18%.
3. normal temperature solidifying fluorine-carbon coating for rubber roller according to claim 1 and 2 is characterized in that: the silicone resin of hydroxyl is the hydroxyl polydimethylsiloxaneresins resins in the described molecular structure.
4. normal temperature solidifying fluorine-carbon coating for rubber roller according to claim 1 and 2 is characterized in that: described flatting silica is the synthetic gas aerosil particle through organic process.
5. normal temperature solidifying fluorine-carbon coating for rubber roller according to claim 1 and 2 is characterized in that: described cured powder is that polyethylene micropowderization is cured.
6. normal temperature solidifying fluorine-carbon coating for rubber roller according to claim 1 and 2 is characterized in that: described auxiliary agent is defoamer, flow agent, the wetting dispersing agent mixture by mass ratio 1: 0.8~2: 1~3.
7. normal temperature solidifying fluorine-carbon coating for rubber roller according to claim 1 and 2 is characterized in that: described defoamer is an organo-siloxane type defoamer.
8. normal temperature solidifying fluorine-carbon coating for rubber roller according to claim 1 and 2 is characterized in that: described flow agent is organopolysiloxane mixture, polyether-modified dimethyl-silicon alkyl copolymer or fluorine-carbon modified dimethyl polysiloxane multipolymer.
9. normal temperature solidifying fluorine-carbon coating for rubber roller according to claim 1 and 2 is characterized in that: described wetting dispersing agent is the mixture of unsaturated polycarboxylic acid polymkeric substance of lower molecular weight and organosiloxane copolymer.
10. normal temperature solidifying fluorine-carbon coating for rubber roller according to claim 1 and 2 is characterized in that: described solvent is the positive fourth fat of acetic acid, 1-Methoxy-2-propyl acetate, pimelinketone, dimethylbenzene or its mixture.