CN101116999A - Method for preparation of light wall material - Google Patents
Method for preparation of light wall material Download PDFInfo
- Publication number
- CN101116999A CN101116999A CNA2006100698644A CN200610069864A CN101116999A CN 101116999 A CN101116999 A CN 101116999A CN A2006100698644 A CNA2006100698644 A CN A2006100698644A CN 200610069864 A CN200610069864 A CN 200610069864A CN 101116999 A CN101116999 A CN 101116999A
- Authority
- CN
- China
- Prior art keywords
- parts
- wall material
- light wall
- manufacture method
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a manufacturing method of light wall material, according to the invention, 30-50 shares of portland cement, 2-5 shares of fibre, 60-100 shares of perlite, 10-20 shares of powder coal ash, 1-4 shares of additive and 50-100 shares of water should be mixed and stirred evenly as material slurry, 4-14 shares of vesicant should be put in, the slurry should be stirred evenly and poured in moulds, then be solidified, ejected and maintained to form the light wall material. The invention is characterized in easy getting of the material from market, especially for the adopting of Portland cement, which is capable of being gotten expediently anywhere, thereby reducing the cost greatly.
Description
Technical field
The present invention relates to a kind of manufacture method of materials for wall, particularly relate to a kind of manufacture method of light wall material.
Background technology
The manufacture method of existing lightweight body of wall is essentially raw material and pours into mould after mixing and stirring, then curing, the demoulding, drying, formation product.Chinese patent CN1167863 discloses a kind of aerated concrete walling material and production method thereof, comprises quick-hardening cement in the raw material, but because quick-hardening cement manufacturer is few, be difficult for buying, and the price height, production cost increased, must solidify through temperature control simultaneously, also increase production cost.Chinese patent CN1263065 discloses a kind of aerated light wall panel material and manufacture method, and the raw material of employing is mainly magnesia, magnesium chloride, but because of being mineral products, the price height is exploited the restriction in place, in order to obtain this product, need long-distance transport, increased production cost.
Summary of the invention
The present invention aims to provide the manufacture method of the light wall material that a kind of raw material easily obtains, cost is low.
The present invention is based on such design principle: raw materials such as ordinary cement, fiber, perlite, flyash, additive and water are prepared burden on request, stir into slip, introduce blowing agent then to slip and be stirred to evenly, pour in the mould at last, through curing, the demoulding, maintenance promptly becomes light wall material again.
The technical solution adopted in the present invention is: a kind of manufacture method of light wall material in turn includes the following steps:
(1) ordinary cement, fiber, perlite, flyash, additive and water are prepared burden by following volume ratio:
30～50 parts of ordinary cements
2～5 parts of fibers
60～100 parts of perlites
10～20 parts in flyash
1～4 part of additive
50～100 parts in water
(2) be stirred to and evenly become slip;
(3) blowing agent is mixed in the slip for 4～14 parts, be stirred to evenly;
(4) be poured in the mould, through curing, the demoulding under natural environmental condition, maintenance moulding again.
Fiber described in the step (1) can be vinylon or polypropylene or alkaline-resisting glass.
Described fiber can be a chopped strand, and its length is 1cm～3cm.
Additive described in the step (1) is made up of water reducer, hydrophober, accelerator.
Blowing agent described in the step (3) can be to stir into foam-like or hydrogen peroxide after the dissolving of protein soap class surfactant water.
The invention has the beneficial effects as follows: (1) is owing to added the additive that contains water reducer, reduced the consumption of water when stirring, moisture content is low in the goods, can under natural environmental condition, solidify, curing environment is not had special requirement, be easy to production process control, reduced cost, increase the flowability of slip simultaneously, also improved the intensity of goods; (2) owing to added the additive that contains hydrophober, body of wall solidifies the back and is difficult for suction, has increased the body of wall water resistance, keeps the body of wall drying; (3) added the additive that contains accelerator, foam and slip rapid solidification that blowing agent is produced have been realized adopting ordinary cement; (4) batching of Cai Yonging has especially realized adopting ordinary cement all obtaining easily on the market, all can obtain easily in the each place, has reduced cost significantly.
The specific embodiment
Embodiment, a kind of manufacture method of light wall material is: 2 parts of the additives of forming with 50 parts in 15 parts in 70 parts of 3 parts of vinylon fibers, crushed crude pearlites, flyash, the water of 40 parts of ordinary cements, length 2cm and by water reducer, hydrophober, accelerator equivalent, in the input mixer; The startup mixer will be prepared burden and be stirred 5min at least, reach to uniform state until it, become slip; With stirring into foam-like after 10 parts of protein soap class surfactant water dissolvings, be mixed with in the mixer of slip, stir 4min at least, it is standby to reach uniform state; Slip is poured in the mould, mould can be selected for use according to producing wallboard or building block, under natural environmental condition, be cured, its hardening time is different and different according to season, generally at spring 3d～5d, summer 1d～3d, autumn 2d～4d, winter 3d～4d, the demoulding then, again with water curing to moulding, be materials for wall.
Fiber in the batching also can be polypropylene or alkaline-resisting glass.
Employed blowing agent also can be a hydrogen peroxide.
Claims (5)
1. the manufacture method of a light wall material is characterized in that in turn including the following steps:
(1) ordinary cement, fiber, perlite, flyash, additive and water are prepared burden by following volume ratio:
30～50 parts of ordinary cements
2～5 parts of fibers
60～100 parts of perlites
10～20 parts in flyash
1～4 part of additive
50～100 parts in water
(2) be stirred to and evenly become slip;
(3) blowing agent is mixed in the slip for 4～14 parts, be stirred to evenly;
(4) be poured in the mould, through curing, the demoulding under natural environmental condition, maintenance moulding again.
2. the manufacture method of a kind of light wall material according to claim 1, it is characterized in that: the fiber described in the step (1) can be vinylon or polypropylene or alkaline-resisting glass.
3. the manufacture method of a kind of light wall material according to claim 1 and 2, it is characterized in that: described fiber can be a chopped strand, its length is 1cm～3cm.
4. the manufacture method of a kind of light wall material according to claim 1, it is characterized in that: the additive described in the step (1) is made up of water reducer, hydrophober, accelerator.
5. the manufacture method of a kind of light wall material according to claim 1 is characterized in that: the blowing agent described in the step (3) can be to stir into foam-like or hydrogen peroxide after the dissolving of protein soap class surfactant water.