CN101116558A - Shoe material and the production technology thereof - Google Patents
Shoe material and the production technology thereof Download PDFInfo
- Publication number
- CN101116558A CN101116558A CNA2007100094600A CN200710009460A CN101116558A CN 101116558 A CN101116558 A CN 101116558A CN A2007100094600 A CNA2007100094600 A CN A2007100094600A CN 200710009460 A CN200710009460 A CN 200710009460A CN 101116558 A CN101116558 A CN 101116558A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- weight
- parts
- pour
- shoe material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the shoe material field, in particular to a shoe material, comprising 75-90 parts by weight of plastic grain, 6-15 parts weight of calcium carbonate, 0.6-1.5 parts by weight of zinc oxide, 0.1-0.3 parts by weight of nanometer silver antibiosis power, 0.2-0.6 part by weight of zinc stearate, 0.2-0.6 part by weight of stearic acid, 0.4-0.8 part by weight of flow aid, 1-1.6 parts by weight of titanium pigment, 0.1-0.4 part by weight of colouring material, 0.4-0.8 part by weight of cross linker, 1-3 parts by weight of vesicant. The shoe material has low specific gravity and high rigidity, corresponding with the relative national standards. The shoe material has low cost, elasticity, better scratchability and good flexibility and is anti-yellowing, fold-resistant and not easy to crumple; furthermore, the shoe material has the function of antibiosis. The rigidity is 50-55 DEG C and the specific gravity is 0.18-0.22 g/cc. The anti-yellowing level is above middle and the folding number is more than 80 thousand.
Description
Technical field
The present invention relates to footwear material field, be specifically related to a kind of footwear material and production technology thereof.
Background technology
The footwear material at the end is because of meeting light weight in shoe-pad and the footwear, and so characteristics such as high buffering are all can be through the forming process of foaming technique, and at present, be mainly the EVA expanded material at the bottom of being used for making footwear, defectives such as intensity is low, poor dimensional stability, elasticity, toughness and hardness are relatively poor, and easy xanthochromia, yielding fractureing, the long-term wearing, the smelly breed bacteria of meeting is dressed uncomfortable, and can make foot produce multiple disease, be unfavorable for health.
Summary of the invention
The purpose of this invention is to provide a kind of footwear material and production technology thereof, this footwear material hardness height, light specific gravity, anti-xanthochromia, folding and have antibacterial functions.
A kind of footwear material, comprise particles 75-90 weight portion, calcium carbonate 6-15 weight portion, zinc oxide 0.6-1.5 weight portion, nano-silver antimicrobial powder 0.1-0.3 weight portion, zinc stearate 0.2-0.6 weight portion, stearic acid 0.2-0.6 weight portion, flow promortor 0.4-0.8 weight portion, titanium dioxide 1-1.6 weight portion, colorant 0.1-0.4 weight portion, crosslinking agent 0.4-0.8 weight portion, blowing agent 1-3 weight portion.
Described partial cross-linking agent is this formyl of peroxidating.
Its production technology is: in proportion with particles 75-90 weight portion; calcium carbonate 5-15 weight portion; zinc oxide 0.6-1.5 weight portion; stearic acid 0.2-0.6 weight portion; zinc stearate 0.2-0.6 weight portion; flow promortor 0.4-0.8 weight portion; titanium dioxide 0.8-1.6 weight portion and colorant 0.1-0.4 weight portion; pour the banbury the inside into; 105-115 ℃ temperature banburying 9-11 minute; treat after the banburying evenly; pour nano-silver antimicrobial powder 0.1-0.3 weight portion into; crosslinking agent 0.4-0.8 weight portion and blowing agent 1-3 weight portion; 115-120 ℃ temperature banburying after 1.5-2.5 minute; pour the double roller plastic-making device the inside again into; temperature at 75-85 ℃ is mixing; pour comminutor the inside granulation after mixing the finishing again into; and then the inside of falling ejaculator ejaculation, get finished product.
This footwear material light specific gravity, the hardness height meets relevant national standard, and cost is low, anti-xanthochromia, flexible, folding, pliability better, good bandability, be difficult for fold, and have antibacterial functions, hardness is the 50-55 degree, proportion is 0.18-0.22g/cc, and more than the middle rank of anti-the xanthochromia, folding is more than 80,000 times.
The specific embodiment
Embodiment 1
A kind of footwear material, comprise particles 75-90 weight portion, calcium carbonate 6-15 weight portion, zinc oxide 0.6-1.5 weight portion, nano-silver antimicrobial powder 0.1-0.3 weight portion, zinc stearate 0.2-0.6 weight portion, stearic acid 0.2-0.6 weight portion, flow promortor 0.4-0.8 weight portion, titanium dioxide 1-1.6 weight portion, colorant 0.1-0.4 weight portion, crosslinking agent 0.4-0.8 weight portion, blowing agent 1-3 weight portion.
Its production technology is: in proportion with particles 75-90 weight portion; calcium carbonate 5-15 weight portion; zinc oxide 0.6-1.5 weight portion; stearic acid 0.2-0.6 weight portion; zinc stearate 0.2-0.6 weight portion; flow promortor 0.4-0.8 weight portion; titanium dioxide 0.8-1.6 weight portion and colorant 0.2-0.4 weight portion; pour the banbury the inside into; 105-115 ℃ temperature banburying 9-11 minute; treat after the banburying evenly; pour nano-silver antimicrobial powder 0.1-0.3 weight portion into; crosslinking agent 0.4-0.8 weight portion and blowing agent 1-3 weight portion; 115-120 ℃ temperature banburying after 1.5-2.5 minute; pour the double roller plastic-making device the inside again into; temperature at 75-85 ℃ is mixing; pour comminutor the inside granulation after mixing the finishing again into; and then the inside of falling ejaculator ejaculation, get finished product.
Embodiment 2
A kind of footwear material; its production technology is: in proportion with particles 62000 grams; calcium carbonate 8000 grams; zinc oxide 900 grams; stearic acid 300 grams; zinc stearate 300 grams; flow promortor 500 grams; titanium dioxide 1000 grams and colorant 200 grams; pour the banbury the inside into; 105-115 ℃ temperature banburying 9-11 minute; treat after the banburying evenly; pour nano-silver antimicrobial powder 200 grams into; crosslinking agent 500 grams and blowing agent 1500 grams; 115-120 ℃ temperature banburying after 1.5-2.5 minute; pour the double roller plastic-making device the inside again into; temperature at 75-85 ℃ is mixing; pour comminutor the inside granulation after mixing the finishing again into, and then the inside of falling ejaculator ejaculation, finished product 74500 grams got.
Embodiment 3
A kind of footwear material; its production technology is: in proportion with particles 90000 grams; calcium carbonate 5000 grams; zinc oxide 550 grams; stearic acid 150 grams; zinc stearate 150 grams; flow promortor 450 grams; titanium dioxide 1000 grams and colorant 150 grams; pour the banbury the inside into; 105-115 ℃ temperature banburying 9-11 minute; treat after the banburying evenly; pour nano-silver antimicrobial powder 100 grams into; crosslinking agent 450 grams and blowing agent 2000 grams; 115-120 ℃ temperature banburying after 1.5-2.5 minute; pour the double roller plastic-making device the inside again into; temperature at 75-85 ℃ is mixing; pour comminutor the inside granulation after mixing the finishing again into, and then the inside of falling ejaculator ejaculation, finished product 100000 grams got.
Claims (2)
1. footwear material, it is characterized in that: comprise particles 75-90 weight portion, calcium carbonate 6-15 weight portion, zinc oxide 0.6-1.5 weight portion, nano-silver antimicrobial powder 0.1-0.3 weight portion, zinc stearate 0.2-0.6 weight portion, stearic acid 0.2-0.6 weight portion, flow promortor 0.4-0.8 weight portion, titanium dioxide 1-1.6 weight portion, colorant 0.1-0.4 weight portion, crosslinking agent 0.4-0.8 weight portion, blowing agent 1-3 weight portion.
2. a kind of footwear material according to claim 1; it is characterized in that: its production technology is in proportion with particles 75-90 weight portion; calcium carbonate 5-15 weight portion; zinc oxide 0.6-1.5 weight portion; stearic acid 0.2-0.6 weight portion; zinc stearate 0.2-0.6 weight portion; flow promortor 0.4-0.8 weight portion; titanium dioxide 0.8-1.6 weight portion and colorant 0.1-0.4 weight portion; pour the banbury the inside into; 105-115 ℃ temperature banburying 9-11 minute; treat after the banburying evenly; pour nano-silver antimicrobial powder 0.1-0.3 weight portion into; crosslinking agent 0.4-0.8 weight portion and blowing agent 1-3 weight portion; 115-120 ℃ temperature banburying after 1.5-2.5 minute; pour the double roller plastic-making device the inside again into; temperature at 75-85 ℃ is mixing; pour comminutor the inside granulation after mixing the finishing again into; and then the inside of falling ejaculator ejaculation, get finished product.