CN101094822B - 发泡石膏 - Google Patents
发泡石膏 Download PDFInfo
- Publication number
- CN101094822B CN101094822B CN2005800432428A CN200580043242A CN101094822B CN 101094822 B CN101094822 B CN 101094822B CN 2005800432428 A CN2005800432428 A CN 2005800432428A CN 200580043242 A CN200580043242 A CN 200580043242A CN 101094822 B CN101094822 B CN 101094822B
- Authority
- CN
- China
- Prior art keywords
- plaster
- phosphoric acid
- paris
- lime carbonate
- foaming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及制造发泡石膏的方法,该方法包括如下步骤:(a)将熟石膏与碳酸钙混合;(b)提供水以及(c)加入磷酸。所述磷酸与所述碳酸钙反应,释放出气体二氧化碳。它还可与存在的任何钢材反应,形成不可溶的磷酸铁涂层。
Description
技术领域
本发明涉及发泡石膏及其制造方法。
发明内容
根据本发明的一个方面,提供一种制造发泡石膏的方法,该方法的特征在于,其包括步骤:
(a)将熟石膏与碳酸钙混合,碳酸钙为熟石膏的2wt%~12wt%;
(b)提供水;以及
(c)加入磷酸,
所述磷酸与所述碳酸钙反应,释放出气体二氧化碳,所述水给所述熟石膏提供用于水合的水,以形成石膏。
具体实施方式
在本发明的优选实施方式中,用如下方法形成建筑板材。
将含有合适的碳酸钙的材料研磨至尺寸为50微米以下。含有合适的碳酸钙的材料包括石灰石、大理石、石灰砂和珊瑚砂。优选地,该材料主要是含有低水平的可溶钠盐和镁盐的碳酸钙。将研磨的碳酸钙以如下量加入粉末状的熟石膏中,使得所得到的熟石膏与碳酸钙的混合物中含有大约6wt%的碳酸钙。
将表面板材如钢、铝或玻璃纤维板设置为框架,使得它们之间产生空腔。该空腔的末端用已知方法密封。
板材的内表面优选用粘合剂处理,该粘合剂如含有玻璃或其他纤维的环氧底漆,以增加板材与石膏之间的粘结力。
然后,以大约两体积份的熟石膏与碳酸钙的混合物对大约一体积份的磷酸溶液的比例,将所述混合的熟石膏和碳酸钙的混合物与4%w/v的磷酸溶液混合。还可以加入发泡剂。然后将所得到的悬浮液喷入或者倾到入所述空腔中。
在可选择的实施方式中,以大约两体积份的熟石膏和碳酸钙的混合物对大约1体积份的水的比例,将水加入该混合物中。然后,使用合理设计的喷头,将所得到的悬浮液与浓磷酸一起喷入所述空腔中。优选该酸具有大约81~85%w/v的浓度。
在两种实施方式中,所述的水向所述熟石膏加入用于水合的水,由此形成石膏。同时,磷酸与石灰石中的碳酸钙发生如下式所示的反应:
3CaCO3+2H3PO4→Ca3(PO4)2+3H2O+3CO2↑
以释放二氧化碳气体。石膏凝固在气泡周围,形成发泡石膏。
可以认识到,以上比例考虑了碳酸钙的过量,使得当以上反应完成时,没有剩余的游离酸。所生产的硬发泡石膏主要包括石膏,与少量的磷酸钙和剩余的碳酸钙组成。可以认识到,磷酸钙与碳酸钙是相对不可溶的,由此使发泡石膏使用寿命延长。
本发明的一个优点是,形成发泡石膏期间所使用的磷酸,在与发泡石膏一起使用的任何钢板或钢制增强物上形成不溶的磷酸铁涂层。可以认识到,使用其它的酸可能导致与发泡石膏接触的钢的劣化。
该方法的进一步优点是,可以预料到随着时间的推移,磷酸钙将与所得到的发泡石膏中的氟化物和/或者氯化物进行反应,形成磷灰石,使其结构更坚固,使潜在的可溶氟化物和氯化物转化成相对不溶的磷灰石。
可以认识到,可以变化上述方法,通过向石膏混合物加入稳定成分或者增强成分,比如水泥或者其它火山灰质材料或者有机聚合物、环氧树脂类等。还可以认识到,通过仔细地选择上述方法中所使用的碳酸钙、磷酸和发泡剂的尺寸和用量,可以控制发泡的量和气泡的尺寸。预料到碳酸钙的量为熟石膏的2wt%~12wt%,将产生有益的结果。
在本发明另一实施方式中,发泡石膏块可以通过将相当于8wt%的碳酸钙的等效物与熟石膏混合得以形成。优选碳酸钙是熟石膏的8wt%。然后,向所得混合物中以大约2∶1体积比的比例将大约5%w/v的磷酸加入,所得到的混合物喷入盒子模具(box mould)中。其反应如上所述进行。当发泡石膏块形成时,然后它们可以被切割成所想要的尺寸。
可以认识到,根据本发明所制造的发泡石膏特别用于阻燃剂以及用于绝缘柱子上的暴露钢梁等方面。
对熟练人员来说明显的修改与变更被认为在本发明的范围内。
Claims (19)
1.用于制造发泡石膏的方法,该方法的特征在于,其包括步骤:
(a)将熟石膏与碳酸钙混合,碳酸钙是熟石膏的2wt%~12wt%;
(b)提供水;以及
(c)加入磷酸,
磷酸与碳酸钙反应,释放出气体二氧化碳,所述水给所述熟石膏提供用于水合的水,以形成石膏。
2.根据权利要求1所述的制造发泡石膏的方法,其特征在于,碳酸钙是熟石膏和碳酸钙的混合物的6wt%。
3.根据权利要求1所述的制造发泡石膏的方法,其特征在于,碳酸钙包含在含有碳酸钙的材料内。
4.根据权利要求3所述的制造发泡石膏的方法,其特征在于,含有碳酸钙的材料是石灰石、大理石、石灰砂或者珊瑚砂。
5.根据权利要求3所述的制造发泡石膏的方法,其特征在于,含有碳酸钙的材料被研磨至尺寸为50微米以下。
6.根据权利要求1~5中任一项所述的制造发泡石膏的方法,其特征在于,水和磷酸作为稀释的磷酸溶液被一起提供。
7.根据权利要求6所述的制造发泡石膏的方法,其特征在于,所述稀释的磷酸溶液具有4%w/v的浓度,并且,以两体积份的熟石膏与碳酸钙的混合物对一体积份的磷酸溶液的比例,将所述混合的熟石膏和碳酸钙的混合物与所述4%w/v的磷酸溶液混合。
8.根据权利要求6所述的制造发泡石膏的方法,其特征在于,以两体积份的熟石膏和碳酸钙混合物对一体积份的稀释的磷酸溶液的比例,提供所述稀释的磷酸溶液。
9.根据权利要求1~5中任一项所述的制造发泡石膏的方法,其特征在于,在磷酸加入之前,所述水与熟石膏和碳酸钙混合。
10.根据权利要求9所述的制造发泡石膏的方法,其特征在于,以两体积份的熟石膏和碳酸钙的混合物对1体积份的水的比例,提供所述水。
11.根据权利要求9所述的制造发泡石膏的方法,其特征在于,所加入的磷酸具有81~85%w/v的浓度。
12.根据权利要求9所述的制造发泡石膏的方法,其特征在于,所述结合的水和熟石膏的混合物与磷酸喷雾一起喷入空腔中。
13.根据权利要求10或11所述的制造发泡石膏的方法,其特征在于,所述结合的水和熟石膏的混合物与磷酸喷雾一起喷入空腔中。
14.一种制造建筑板材的方法,该方法包括以下步骤:使表面板材间隔设置,使得它们之间形成空腔;根据权利要求1~13中任一项所述的方法制造发泡石膏,并将该发泡石膏提供入所述空腔。
15.一种制造发泡石膏块的方法,其特征在于,将根据权利要求1生产的发泡石膏喷入盒模具中。
16.根据权利要求15所述的制造发泡石膏块的方法,其特征在于,所述碳酸钙是所述熟石膏的8wt%。
17.根据权利要求16所述的制造发泡石膏块的方法,其特征在于,所述水和磷酸作为5%w/v的磷酸溶液被一起提供,并且碳酸钙和熟石膏的混合物与所述5%w/v的磷酸溶液以2∶1体积比的比例混合。
18.根据权利要求14的方法所生产的建筑板材。
19.根据权利要求15~17中任一项方法所生产的发泡石膏块。