CN101074292B - 具有色彩补偿和近红外线(nir)阻滞功能的粘性膜及使用该粘性膜的等离子显示面板滤光器 - Google Patents
具有色彩补偿和近红外线(nir)阻滞功能的粘性膜及使用该粘性膜的等离子显示面板滤光器 Download PDFInfo
- Publication number
- CN101074292B CN101074292B CN2007101108742A CN200710110874A CN101074292B CN 101074292 B CN101074292 B CN 101074292B CN 2007101108742 A CN2007101108742 A CN 2007101108742A CN 200710110874 A CN200710110874 A CN 200710110874A CN 101074292 B CN101074292 B CN 101074292B
- Authority
- CN
- China
- Prior art keywords
- film
- replacement
- near infrared
- infrared ray
- unsubstituted
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种具有色彩补偿和近红外线阻滞功能的粘性膜及使用该粘性膜的等离子显示面板滤光器。本发明提供一种用于等离子显示面板的包括基于丙烯酰的粘合剂和氖削减染料的多功能粘性膜。该粘性膜可以进一步包括近红外线阻滞染料。本发明的多功能粘性膜具有在高温高湿下微小的透射比变化的极佳的耐久性和优良的热稳定性。当进一步包括近红外线阻滞染料时,该粘性膜同时发挥色彩补偿和近红外线阻滞性能。由于该膜本身具有极佳的粘合性,所以不需要额外的粘合剂层,从而简化了等离子显示面板滤光器和等离子显示面板的制造工艺。
Description
参照相关专利
本申请要求2004年2月23日向韩国知识产权局提交的韩国专利申请第10-2004-0011798号和2005年2月23日提交的韩国专利申请第10-2005-0014754为优先权,并在此将其作为参考。
技术领域
本发明涉及一种具有象氖削减(neon-cut)这样的色彩补偿及近红外线阻滞功能的粘性膜和包括该粘性膜的等离子显示器滤光器,更具体地涉及由于在高温和高湿下很小的透射比变化而具有较佳的耐久性、热稳定性、和粘合性的粘性膜及使用该膜的等离子显示器滤光器。
背景技术
最近,液晶显示面板(PDP)已被公认作为提供宽屏幕的主要的平面显示面板。
迄今,已开发出能提供约70英寸宽的屏幕的液晶显示面板。用于参考,图1为显示液晶显示面板一般结构的示意图。在图1中,数字11表示壳、数字12表示驱动电路板(driving circuit board)、数字13表示面板装置、数字14表示PDP滤光器、及数字15表示盖子。
PDP滤光器补偿由面板发射的单一桔色光谱引起的红色光谱的纯度降低,并且阻滞引起遥控器故障的近红外线和对人体有害的电磁辐射。为了实现该任务,PDP滤光器包括如抗反射层、补偿色纯度的色彩补偿层、近红外吸收层、电磁辐射屏蔽层等功能层。一般而言,这些功能层由普通膜制成且使用粘合剂彼此间层叠。
如果一张膜同时具有色彩补偿和近红外线阻滞功能或者膜的数目能被减少,则能够减少有关层叠的质量问题和节省材料消耗。例如,如果通过在膜的每一侧上形成两个功能层而赋予膜三个功能,则PDP滤光器的层数可以减少一半。可选择地,可以通过使用能够发挥该种功能的粘合剂来简化结构。典型地,染料被用于近红外线阻滞和色彩补偿。该种染料的例子是在特定的波长区域吸收光的氖削减染料和近红外线阻滞染料。通常,在透明衬底上涂布含有粘合剂聚合物的混合物的层。在这种情况下,应使用粘合剂将其上已涂布有染料层的衬底***PDP滤光器中。
通常用于此目的的粘合剂为橡胶类、聚(乙烯酯)类、丙烯酰基类、硅树脂类等。但是,橡胶粘合剂具有较差的抗老化性、聚(乙烯酯)粘合剂具有较差的耐热性、而硅树脂粘合剂具有粘合性方面的缺点。另一方面,基于丙烯酰基的粘合剂由于优良的熔化特性被广泛用于制备粘合剂组合物,而且由于含有粘合剂的聚合物分子为流动的且对压力敏感,当在室温下对其施加光压时它们通常呈现较好的粘合性。但该流动性往往降低包含在粘合剂中的用于改善色彩补偿或近红外线阻滞性能的染料的耐热性或耐湿性。所以,选择能够经受高温和高湿的耐用性染料是重要的。
使用色彩补偿和近红外线染料的现有技术如下。
日本公开专利第2001-248721号公开了使用在570~605nm区域的氮杂卟吩染料的光学滤光器。尽管该专利提到可以包括透明粘合剂(基于丙烯酰基的粘合剂)以改善粘合性,但没有详细提及所用的粘合剂结构、交联剂、及偶合剂。此外,尽管在584nm处最初的15.9%的透射比是满足要求的,但没有提及关于耐久性试验前和后的透射比维持。
韩国公开专利第2002-0055410号公开了通过在透明衬底上采用花青染料和于550~620nm区域内吸收的近红外线染料制备的近红外线阻滞材料。韩国公开专利第2004-0049280号公开了含有丙烯酰基粘合剂树脂、近红外线染料、UV吸收剂、及受阻胺光稳定剂(hindered aminelight stabilizer)的压敏粘合剂组合物。日本公开专利第2001-207142号公开了含有丙烯酰基粘合剂树脂、花青IR吸收剂、及多功能丙烯酰基聚合物的IR吸收粘合剂组合物,而日本公开专利第2004-107566号公开了包含具有特定酸值的丙烯酰基树脂和聚甲炔氖削减染料的粘合剂。
但是,韩国公开专利第2002-0055410号没有提及粘合剂结构和组成,而韩国公开专利第2004-0049280号没有提出关于近红外线吸收膜的近红外阻滞功效。并且日本公开专利第2001-207142号没有提出基于花青的NIR染料和基于花青的氖削减染料,但当单独使用花青染料时出现差的耐热性和耐光性。
而且,按照常规方法制备的色彩补偿膜和近红外线阻滞膜根据粘合剂种类、涂布条件等而在高温和高湿的耐久性方面显示差异。此外,为了制备PDP滤光器而层叠该等膜是昂贵的和效率低的。因此,已尝试开发多功能粘合层,如包括氖削减层的粘合层及包括近红外线阻滞层的粘合层,但是显示的在高温高湿下的耐久性不令人满意。
发明内容
本发明的一个技术方案是提供一种具有色彩补偿和近红外线阻滞功能的多功能粘性膜,该膜具有在高温高湿下的很小的透射比变化的极佳的耐久性,良好的热稳定性,能够于相当长的时间内维持在可见区的透射比,并且具有好的近红外线阻滞性能。
本发明的另一个技术方案是提供一种等离子显示面板滤光器及包括该滤光器的液晶显示面板,该滤光器包括具有色彩补偿和近红外线阻滞性能的多功能粘性膜而没有额外的粘合层从而能简化该膜。
为了实现这些技术方案,本发明提供了一种用于等离子显示面板的包括丙烯酰基粘合剂和氖削减染料的多功能粘性膜。优选地,该粘性膜进一步包括近红外线阻滞染料。
本发明进一步提供一种在衬底的至少一侧上包括至少一种上述多功能粘性膜的等离子显示面板滤光器。
本发明进一步提供一种包括该等离子显示面板滤光器的等离子显示面板。
附图说明
图1为显示等离子显示面板结构的示意图。
图2显示根据本发明的实施例4中制备的多功能粘性膜的光谱变化。
图3显示根据本发明的实施例5中制备的多功能粘性膜的光谱变化。
图4显示根据本发明的实施例6中制备的多功能粘性膜的光谱变化。
图5显示高温耐久性试验后对比实施例1中制备的粘性膜的光谱变化。
图6显示高温/高湿试验后对比实施例1中制备的粘性膜的光谱变化。
图7显示对比实施例2中制备的粘性膜的光谱变化。
图8显示包括根据本发明的多功能粘合剂的实施例7的等离子显示器滤光器的结构。
图9显示包括根据本发明的多功能粘合剂的实施例8的等离子显示器滤光器的结构。
图10显示对比实施例3的等离子显示器滤光器的结构。
具体实施方式
下文给出本发明的详细描述。
本发明提供一种用于等离子显示面板的具有较好的耐久性和粘合性的多功能粘性膜,包括作为粘合剂树脂的具有极佳的粘合性和耐久性并且能代替常规粘合剂(PSA)的基于丙烯酰基的压敏粘合剂、色彩补偿染料、以及近红外线染料。
本发明的膜包括能够阻滞590nm周围的氖光的氖削减染料和能够阻滞850nm及950nm周围的近红外线的近红外线染料,从而满足等离子显示器滤光器所需的典型光学特性。
本发明的多功能粘性膜有效地减小了由PDP组件产生的570~600nm周围的氖峰,且阻滞800~1100nm的NIR区的光到10%或以下。当在高温高湿下测试,更具体地在80℃下500小时和在60℃、90%RH下500小时,在可见和NIR区的染料浓度改变10%或更小。由于一张膜可以具有色彩补偿或同时具有色彩补偿和近红外线阻滞性能,所以膜的数目可以被减少,从而简化结构。
下文给出本发明的粘性膜的更具体的描述。
PDP在面板的前面具有发挥多功能的膜(滤光器)以阻滞工作时产生的电磁辐射、氖辐射、近红外线等。粘合剂(PSA)被用于形成膜。该粘合剂应不仅具有极佳的粘合性而且在可见区(380~780nm)具有较好的透射比。
所以,本发明的膜包括基于丙烯酰基的粘合剂和近红外线阻滞染料。而且,本发明的膜可以包括基于丙烯酰基的粘合剂和氖削减染料,以及进一步包括近红外阻滞染料。
优选地,本发明中作为粘合剂树脂的粘合剂为具有0℃或以下的玻璃化转变温度(Tg)的基于丙烯酰基的粘合剂。基于丙烯酰基的粘合剂可以通过75~99.89wt%的具有C1-12烷基的(甲基)丙烯酸酯单体、0.1~20wt%的作为功能单体的α,β-不饱和羧酸酯单体、及0.01~5wt%的具有羟基的聚合物单体共聚合得到。本领域的技术人员可以完成该共聚合。
更优选地,基于丙烯酰基的粘合剂为丙烯酸丁酯(BA)/甲基丙烯酸羟乙基酯(HEMA)共聚物或丙烯酸丁酯/丙烯酸(AA)共聚物,因为这些粘合剂与现有技术中的丙烯酰基粘合剂相比在可见区和近红外线区具有更佳的吸收能力。
近红外线阻滞染料可以是常规使用的染料,例如二亚铵(diimmonium)染料。如果需要,它可以与金属络合物染料或酞菁染料一起使用。二亚铵染料在900~1200nm的宽区域内吸收近红外线。
近红外线阻滞染料可以为选自包括下面化学式4表示的二亚铵染料、下面化学式5表示的酞菁染料、下面化学式6表示的萘酞菁染料、及下面化学式7和化学式8表示的金属络合染料的组的至少一种。
在化学式4中,各R1~R12独立地为氢原子、卤素原子、取代或未取代的具有C1~C16的烷基、或取代或未取代的具有C1~C16的芳基;且X为单价或二价有机阴离子、单价阴离子、或二价无机阴离子。
在化学式5和6中,各R独立地为氢原子、卤素原子、取代或未取代的具有C1~C16的烷基、取代或未取代的苯基、取代或未取代的具有C1~C5的烷氧基、取代或未取代的烯丙氧基、氟取代的烷氧基、或具有至少一个取代或未取代的氮原子的五元环;且M为选自包括两个氢原子、二价金属原子、三价或四价取代的金属原子、以及氧代-金属原子的组的至少一种,且优选为Ni、Pt、Pd、或Cu。
在化学式7和8中,各R与R1~R4独立地为氢原子、具有C1~C16的烷基、芳基、烷氧基、苯氧基、羟基、具有C1~C16的烷氨基、芳氨基、三氟甲基、具有C1~C16的烷硫基、芳硫基、硝基、氰基、卤素原子、苯基、或萘基。
在化学式4中,单价有机阴离子可以是有机羧酸盐离子、有机磺酸盐离子、有机硼酸盐离子等。有机羧酸盐离子可以是醋酸盐、乳酸盐、三氟乙酸盐、丙酸盐、安息香酸盐、草酸盐、琥珀酸盐、或硬脂酸盐。有机磺酸盐离子可以是金属磺酸盐、甲苯磺酸盐、萘单磺酸盐、氯苯磺酸盐、硝基苯磺酸盐、十二烷基苯磺酸盐、苯磺酸盐、乙炔磺酸盐、或三氟甲烷磺酸盐。优选地,有机硼酸盐离子为四苯硼酸盐或丁基三苯硼酸盐。
在化学式4中,单价无机阴离子优选为卤化阴离子,如氟化物、氯化物、碘化物、硫氰酸盐、六氟锑酸盐、高氯酸盐、高碘酸盐、硝酸盐、四氟硼酸盐、六氟磷酸盐、钼酸盐、钨酸盐、钛酸盐、磷酸盐、及硼酸盐。优选地,二价无机离子为萘-1,5-二磺酸盐、萘-1,6-二磺酸盐、萘二磺酸盐衍生物等。
氖削减染料具有570~600nm的最大吸收波长和50nm或以下的半带宽。优选地,该染料具有分子内或分子间的金属络合的结构。
例如,氖削减染料可以是选自包括如下面化学式1表示的具有分子内金属络合的卟啉染料、及如下面化学式2和3表示的具有分子间金属络合结构的花青染料。优选地,氖剪切染料可以是卟啉染料。
在化学式1中,各R1~R8中独立地为氢原子、卤素原子、取代或未取代的具有C1~C16的烷基或具有C1~C16的烷氧基、取代或未取代的苯基、取代或未取代的烯丙氧基、氟取代的烷氧基、或具有至少一个取代或未取代的氮原子的五元环;且M为氢原子、氧原子、卤素原子、或配位的二价到四价金属原子。
在化学式2和3中,各R独立地为氢原子、取代或未取代的具有1~30个碳原子的脂肪烃、具有1~8个碳原子的烷氧基、或具有6~30个碳原子的芳基;各X和Y独立地为卤素原子、硝基、羧基、具有2~8个碳原子的烷氧基、苯氧基羰基、羧酸酯基、具有1~8个碳原子的烷基、具有1~8个碳原子的烷氧基、或具有6~30个碳原子的芳基。
在化学式1的M中,二价金属原子可以是Cu、Zn、Fe、Co、Ni、Ru、Rd、Pd、Mn、Sn、Mg、Ti等;三价金属原子可以是被卤素原子、羟基、或烷氧基取代,如Al-Cl、Ga-Cl、In-Cl、Fe-Cl、Ru-Cl等;四价原子可以被选自卤素原子、羟基、及烷氧基的两个取代基取代,如SiCl2、GaCl2、TiCl2、SnCl2、Si(OH)2、Ge(OH)2、Mn(OH)2、Sn(OH)2等。而且,M可以是与氧结合的氧金属,如VO、MnO、TiO等。
基于丙烯酰基的粘合剂与近红外线阻滞染料的重量比为10∶1~10000∶1。重量比还随粘合剂溶液中的溶剂重量比、粘合剂溶液的粘度、近红外线阻滞染料的摩尔消光系数、及想得到的透射比值而改变。
对于含有氖削减染料的膜,丙烯酰基粘合剂与氖削减染料的重量比为10∶1~10000∶1。重量比还随粘合剂溶液中溶剂的重量比、粘合剂溶液的粘度、氖削减染料的摩尔消光系数、及想得到的透射比值而改变。
本发明的多功能膜可以进一步包括溶剂。该溶剂可以是通常使用的有机溶剂,优选甲乙酮(MEK)、四氢呋喃(THF)、乙酸乙酯、甲苯等。不特别限制溶剂的含量。
本发明的粘性膜可以进一步包括交联剂和偶合剂。
交联剂可以是如异氰酸酯交联剂、环氧交联剂、氮丙啶交联剂、及金属螯合物交联剂的多功能化合物。更优选地,该交联剂为异氰酸酯交联剂,如甲苯二异氰酸酯、二甲苯二异氰酸酯、二苯甲烷二异氰酸酯、1,6-己二异氰酸酯等,但不限于此。对于每100重量份的丙烯酰基聚合物可以使用0.01~2重量份的交联剂。
优选地,偶合剂为硅烷偶合剂。硅烷偶合剂改善了粘合可靠性,特别当在高温高湿下长时间单独放置。硅烷偶合剂可以是乙烯基硅烷、环氧硅烷、甲基丙烯酰硅烷等。例如,乙烯基三甲氧基硅烷、乙烯基三乙氧基硅烷、γ-环氧丙基三甲氧基硅烷等,可以单独或组合使用。对于每100重量份的丙烯酰基聚合物可以使用0.01~2重量份的偶合剂。
不特别限制制备粘性膜的方法。例如,该膜可以通过混合染料和粘合剂,向其中加入预定量的交联剂和偶合剂,从而得到涂布溶液,将涂布溶液涂布到膜上,然后固化来制备。优选地,得到的涂层具有至少10μm的厚度。涂布可以通过喷涂法、滚筒涂布、棒涂覆(barcoating)、旋转涂布等来完成。
本发明还提供了用于等离子显示面板的包括多功能粘性膜的等离子显示面板滤光器。等离子显示面板滤光器可通过层叠基底膜、抗反射膜(AR膜)、本发明的近红外线膜、具有色彩补偿或同时具有色彩补偿和近红外线阻滞功能的多功能粘性膜、电磁干扰膜(EMI膜)、黑屏处理膜等被制备。
等离子显示面板滤光器可以通过在由玻璃或聚对苯二甲酸乙二酯(PET)制成的透明衬底上充分层叠上述膜来制备。本发明的滤光器可以包括至少一近红外线膜、色彩补偿膜、及同时具有色彩补偿和近红外线阻滞功能的膜。各膜可以位于衬底之上或之下。当至少一张多功能膜在衬底上直接层叠时,没有使用粘合剂。当形成不包括多功能膜的层时,可以使用通常被使用的压敏粘合剂(PSA)。这就是说,电磁干扰膜和黑屏处理膜可以通过使用常规的粘合剂来层叠。
本发明进一步提供了一种包括等离子显示面板滤光器的等离子显示面板。等离子显示面板可以通过本领域熟知的方法来制备,将不作具体描述。
当包含本发明的粘性膜的滤光器被用于面板装置中时,能够得到具有在高温高湿下微小透射比变化的极佳的耐久性、良好的热稳定性、及在可见区较好的透射比的等离子显示面板。
如上所述,用于等离子显示面板的粘性膜,该粘性膜包括作为粘合剂树脂的具有极佳的粘合性和耐久性的基于丙烯酰基的粘合剂、及色彩补偿染料或色彩补偿染料和近红外线阻滞染料,具有在高温高湿下微小透射比变化的极佳的耐久性、良好的热稳定性、在可见区较好的透射比、及很好的近红外线阻滞性能。特别的,该膜本身是有粘性的,所以在制备等离子显示面板时不需要使用额外的粘合剂,从而简化了制备过程并减小了滤光器的厚度。
用优选的实施例进一步详细描述本发明。但是,以下的实施例只是用于理解本发明而并不限制本发明。
[实施例]
按照下面来制备和测试根据本发明的多功能粘性膜。
<膜制备>
1.溶液的制备:用于制备多功能粘性膜的涂布溶液被单独制备或通过与作为粘合剂树脂的丙烯酸丁酯(BA)/甲基丙烯酸羟乙基酯(HEMA)共聚物或丙烯酸丁酯(BA)/丙烯酸(AA)共聚物、氖削减染料、第一近红外线阻滞染料、及第二近红外线阻滞染料混合来制备。
2.涂布:将涂布溶液涂布到膜上达15μm的厚度。在120℃干燥3分钟后,用膜层压涂布表面。
3.固化:在室温下固化3天。
<耐久性试验>
高温条件:在80℃下保存膜500小时对比前后的透射比。
(实施例1)
包括近红外线阻滞染料的膜制备
100重量份(15.5wt%)的丙烯酸丁酯(BA)/甲基丙烯酸羟乙基酯(HEMA)共聚物溶液溶于84.5ml的乙酸乙酯中,将0.05重量份的化学式4表示的作为近红外线阻滞染料的二亚铵染料(CIR1081,JapanCarlit Co.)、0.05重量份的作为异氰酸酯交联剂的T-39M、及0.07重量份的作为硅烷偶合剂的T-789J加入到45重量份的甲乙酮(MEK)中,然后混合,从而得到涂布溶液。将涂布溶液涂布到基底膜上达23μm的厚度,从而获得多功能粘性膜。
按照上述测试耐久性。在下面表1中给出结果。
表1
由表1可见,高温试验后粘性膜在可见区和近红外线(NIR)区显示极佳的透射比维持。
(实施例2)
除了使用化学式5表示的酞菁染料(IP12,Japan catalyst Co.)作为近红外线阻滞染料外,按照与实施例1相同的方式制备粘性膜。
(实施例3)
除了使用丙烯酸丁酯/丙烯酸共聚物溶液代替丙烯酸丁酯(BA)/甲基丙烯酸羟乙基酯(HEMA)共聚物溶液作为基于丙烯酰的粘合剂外,用与实施例1相同的方式制备粘性膜。
(实施例4)
100重量份(15.5wt%)的丙烯酸丁酯(BA)/甲基丙烯酸羟乙基酯(HEMA)共聚物溶液溶于84.5ml的乙酸乙酯中,将0.05重量份的化学式1表示的卟啉染料、0.05重量份的作为异氰酸酯交联剂的T-39M、及0.07重量份的作为硅烷偶合剂的T-789J加入到45重量份的甲乙酮(MEK)中,然后混合,从而得到涂布溶液。将涂布溶液涂布到基底膜上达23μm的厚度,从而获得多功能粘性膜。
按照上述测试耐久性。在下面表2中给出结果。粘性膜的光谱变化显示于图2。
表2
由表1和图2可见,实施例4的包括色彩补偿染料的粘性膜在可见区显示极佳的透射比维持。
(实施例5)
100重量份(14.5wt%)的丙烯酸丁酯/丙烯酸共聚物溶液溶于84.5ml的乙酸乙酯中,将0.05重量份的化学式1表示的卟啉染料、0.23重量份的作为异氰酸酯交联剂的T-39M、及0.03重量份的作为偶合剂的T-789J加入到45重量份的甲乙酮(MEK)中,然后混合,从而得到涂布溶液。将涂布溶液涂布到基底膜,从而以获得多功能粘性膜。
按照上述测试耐久性。在下面表3中给出结果。粘性膜的光谱变化显示于图3。
表3
由表3和图3可见,实施例5的包括色彩补偿染料的粘性膜在可见区显示极佳的透射比维持。
(实施例6)
除了进一步使用0.3重量份的卟啉染料、0.3重量份的二亚铵染料(第一近红外线阻滞染料)(CIR1081,Japan Carlit Co.)、及0.1重量份的酞菁染料(第二近红外线阻滞染料)(IP12,Japan catalyst Co.)以外,按照与实施例4相同的方式制备粘性膜。
将涂布溶液涂布到基底膜上以获得多功能粘性膜。
按照上述测试耐久性。在下面表4中给出结果。粘性膜的光谱变化显示于图4。
表4
由表4和图4可见,实施例6的包括色彩补偿染料的粘性膜不仅在可见区而且在NIR区显示极佳的透射比维持。
(对比实施例1)
通过将涂布溶液的组成变成下面的组成来制备粘性膜。
组成:作为氖削减染料的花青染料(0.0214g,TY102;Asahi denka),14BB(100g,具有-OH基的基于丙烯酰),固化剂(0.03g,T-39M),偶合剂(0.07g,T-789J)。
在衬底上涂布:棒涂法,干燥厚度25μm。
之后,按照上述测试耐久性。在下面表5中给出结果,且粘性膜的光谱变化显示于图5。
表5
另外,在表6中给出高温和高湿的试验结果,且粘性膜的光谱变化显示于图6。
表6
由结果可见,对比实施例1的包括色彩补偿染料的粘性膜与本发明的实施例相比,在可见区显示较差的透射比维持。
(对比实施例2)
通过将涂布溶液的组成变成下面的组成来制备粘性膜。
组成:酞菁NIR吸收染料(0.01g,TY102;Asahi denka),14BB(100g,具有-OH基的基于丙烯酰的),固化剂(0.006g,T-39M),及偶合剂(0.014g,T-789J)。
在衬底上涂布:棒涂法,干燥厚度20μm。
固化条件:在室温下3天。
之后,按照上述测试耐久性。在下面表7中给出结果,且粘性膜的光谱变化显示于图7。
表7
由结果可见,对比实施例2的粘性膜与本发明的实施例相比,也在可见区显示较差的透射比维持。
(实施例7)
液晶显示面板滤光器的制备
如图8(五层膜结构)显示的等离子显示面板滤光器通过在玻璃衬底上层叠抗反射膜(AR膜)30、实施例1中制备的粘性膜28、硬质玻璃26、压敏粘合剂层(PSA)24、及电磁干扰膜(EMI膜)22来制备。
(实施例8)
液晶显示面板滤光器的制备
如图9(七层膜结构)显示的等离子显示面板滤光器通过在玻璃衬底上层叠抗反射膜(AR膜)30、实施例4中制备的粘性膜28、NIR膜29、硬质玻璃26、PSA 24、及电磁干扰膜(EMI膜)22来制备。
(对比实施例3)
等离子显示面板滤光器通过层叠抗反射膜30、粘合层24、对比实施例1的色彩补偿膜25、粘合层24、对比实施例2的常规的近红外线膜29、粘合层24、硬质玻璃26、粘合层24、及电磁干扰膜22来制备。使用橡胶类粘合剂(PSA)来层叠所有的膜。其结构显示于图10。对比实施例3的滤光器具有九层结构。
从以上所述可以明显看出,本发明的多功能粘性膜由于使用基于丙烯酰的粘合剂作为粘合剂树脂从而改善了耐久性、并且使用色彩补偿染料和近红外线阻滞染料从而使色彩补偿和近红外线阻滞性能功能化。此外,该膜具有极佳的近红外线透射比,特别是由于该膜本身具有很好的粘合性而不需要额外的粘合剂。所以,该膜能简化等离子显示面板滤光器的结构、且能用于等离子显示面板滤光器和等离子显示面板的制造。虽然根据优选实施方案已对本发明进行了详细描述,但本领域的技术人员应认识到,可以在不偏离如所附权利要求中所阐明的本发明的精神和范围下作出各种修改和替代。
Claims (9)
1.一种多功能粘性膜,包括基于丙烯酰的粘合剂和氖削减染料,其中,所述氖削减染料为选自下面化学式1表示的具有分子内金属络合结构的卟啉化合物以及下面化学式2和化学式3表示的具有分子间金属络合结构的花青化合物中的至少之一:
其中
在化学式1中,
各R1~R8独立地为氢原子、卤素原子、取代或未取代的具有C1~C16的烷基、或具有C1~C16的烷氧基、取代或未取代的苯基、取代或未取代的烯丙氧基、氟取代的烷氧基、或具有至少一个取代或未取代的氮原子的五元环,且M为氢原子、氧原子、卤素原子、或配位的二价到四价金属原子;以及
在化学式2和3中,
各R独立地为氢原子、取代或未取代的具有1~30个碳原子的脂族烃、具有1~8个碳原子的烷氧基、或具有6~30个碳原子的芳基;且各X和Y独立地为卤素原子、硝基、羧基、具有2~8个碳原子的烷氧基、苯氧基羰基、羧酸酯基、具有1~8个碳原子的烷基、具有1~8个碳原子的烷氧基、或具有6~30个碳原子的芳基;
所述基于丙烯酰的粘合剂具有0℃或以下的玻璃化转变温度;
所述基于丙烯酰的粘合剂通过75~99.89wt%的具有C1-12烷基的(甲基)丙烯酸酯单体、0.1~20wt%的作为功能单体的α,β-不饱和羧酸酯单体和0.01~5wt%的具有羟基的聚合物单体的共聚合而得到;以及
所述基于丙烯酰的粘合剂与氖削减染料的重量比为10∶1~10000∶1。
2.如权利要求1的多功能粘性膜,其中基于丙烯酰的粘合剂为丙烯酸丁酯/甲基丙烯酸羟乙基酯共聚物或丙烯酸丁酯/丙烯酸共聚物。
3.如权利要求1的多功能粘性膜,其中对于每100重量份的基于丙烯酰的粘合剂,含有0.01~10重量份的氖削减染料。
4.如权利要求1的多功能粘性膜,对于每100重量份的基于丙烯酰的粘合剂,进一步包括0.01~10重量份的近红外线阻滞染料。
5.如权利要求4的多功能粘性膜,其中近红外线阻滞染料为选自下面化学式4表示的二亚铵染料、下面化学式5表示的酞菁染料、下面化学式6表示的萘酞菁染料和下面化学式7或化学式8表示的金属络合物染料中的至少一种:
其中
在化学式4中,各R1~R12独立地为氢原子、卤素原子、取代或未取代的具有C1~C16的烷基、或取代或未取代的具有C1~C16的芳基,且X为单价或二价有机阴离子、或单价或二价无机阴离子;
在化学式5和6中,各R独立地为氢原子、卤素原子、取代或未取代的具有C1~C16的烷基、取代或未取代的苯基、取代或未取代的具有C1~C5的烷氧基、取代或未取代的烯丙氧基、氟取代的烷氧基、或具有至少一个取代或未取代的氮原子的五元环,且M为选自两个氢原子、二价金属原子、三价或四价取代的金属原子、及氧代金属原子中的至少之一;以及,
在化学式7和8中,各R与R1~R4独立地为氢原子、具有C1~C16的烷基、芳基、烷氧基、苯氧基、羟基、具有C1~C16的烷氨基、芳氨基、三氟甲基、具有C1~C16的烷硫基、芳硫基、硝基、氰基、卤素原子、苯基、或萘基。
6.如权利要求1的多功能粘性膜,对于每100重量份的基于丙烯酰的粘合剂,进一步含有至少一种选自0.01~2重量份的交联剂和0.01~2重量份的偶合剂中的添加剂。
7.一种等离子显示面板滤光器,至少在基板的一侧包括权利要求1~6的任一项的多功能粘性膜。
8.如权利要求7的等离子显示面板滤光器,其进一步包括抗反射膜、电磁干扰膜以及黑屏处理膜。
9.包括权利要求7的滤光器的等离子显示面板。