CN101066620A - Extrusion process and apparatus for producing foamed polyolefin product - Google Patents
Extrusion process and apparatus for producing foamed polyolefin product Download PDFInfo
- Publication number
- CN101066620A CN101066620A CNA2007101108884A CN200710110888A CN101066620A CN 101066620 A CN101066620 A CN 101066620A CN A2007101108884 A CNA2007101108884 A CN A2007101108884A CN 200710110888 A CN200710110888 A CN 200710110888A CN 101066620 A CN101066620 A CN 101066620A
- Authority
- CN
- China
- Prior art keywords
- extruder
- extrusion molding
- olefinic polymerization
- foaming
- seam shape
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to extrusion process and apparatus for producing foamed polyethylene and polypropylene with physical foaming agent. The apparatus includes a high speed mixer, an extruder, a metering pump for feeding the extruder and a towing and cutting device connected to the extruder. The process includes mixing the polymer and the nucleator in the high speed mixer, heating and shearing the mixture in the plastic foaming extruder to form molten material, adding foaming agent and shrinkage resisting agent with the metering pump and mixing with the molten material, extruding the mixture, cooling and cutting.
Description
Technical field
The present invention relates to a kind of device and method of making foaming olefinic polymerization Tetramune, especially a kind of device and method that utilizes extrusion molding and physical blowing agent to make polyethylene foamed or polypropylene articles.
Background technology
(height) polyethylene foamed is to be main raw material(s) with polyethylene (PE), adds the product that blowing agent and other processing aids make through extruding manufacturing process.Foaming product is to be uniformly distributed in foamed plastics in the material with gas, thereby has specific strength height, light weight, sound-absorbing, characteristics such as shockproof, is widely used in the packing of household electrical appliance, furniture, mechanical part, electronic instrument, precision instrument.Because highly foaming polyethylene has high foaming, obturator-type foamed plastics, make it have excellent water proofing property, thermal insulation and good floatability.Highly foaming polyethylene is compared with traditional packaging material moulded from foam EPS, have can directly reclaim, advantage that the quality softness can not damaged the packed article surface, cracky and repeatedly using not, so in the electrical package field, day by day replace the PS expanded material, and become the main material of packaging industry.Produce polyethylene foamed at present both at home and abroad, adopt low-boiling point liquid to make blowing agent, produce the method that polyethylene foam is extruded coiled material with the mode of separate unit extruder or two extruders production.The extrusion foaming die head be circular be main, mainly by changing the setting drum external diameter, adjust the annular die gap, changing means such as hauling speed and make thickness, foam sheet goods that width is very little.It extrudes the product that the thickness of producing foamed products has only 2.0～7.0mm.Because the foamed products thickness of producing is little, can not satisfy the demand of present packaging field.
Summary of the invention
The objective of the invention is to produce the deficiency of the less foaming olefinic polymerization Tetramune of thickness, a kind of novel process units and production method thereof are provided at existing foaming olefin polymer process units.
Technical scheme of the present invention is: a kind of device of extrusion molding preparation foaming olefinic polymerization Tetramune, comprise high-speed mixer, the extruder that links to each other with high-speed mixer, the constant displacement pump that in extruder, in extruder, adds materials, and the traction cutter sweep of extruder front portion, the head of described extruder is provided with a flat seam shape and extrudes head.
Preferably, described flat seam shape is extruded head and is comprised upper and lower two templates that have runner, and is used for side plate that template is sealed.
The gap of the seam shape opening that preferably, constitutes between the described bolster is 0-20mm.
Preferably, described extruding is provided with a typing cover between head and the traction cutter sweep, and described typing cover is made of two stereotype plates, has bosh on the stereotype plate, and is provided with heater.
Preferably, the both sides of two stereotype plate inside of described typing cover are provided with two transportable interior plates.
A kind of said apparatus that utilizes, the method for preparing foaming olefinic polymerization Tetramune by extrusion molding, earlier that olefin polymer plastics and nucleator blend in high-speed mixer are even, again mixture is dropped in the foamed plastic extruder, become the melting material under the shearing of heating of material process and screw rod, the acting in conjunction of extruding; After the whole meltings of material, utilize constant displacement pump to add antishrinking agent and blowing agent or only add blowing agent and mix with the melting material, the melting material that is mixed with antishrinking agent, blowing agent is subsequently lowered the temperature, is reduced pressure and extrude the formation foamed plastic from the flat seam shape molding die of extruder; The foamed plastic of extruding cools off after the traction cutter sweep cuts.
Preferably, the described foamed plastic of being extruded by the flat seam shape molding die of extruder is cooled off or is added thermal finalization through the typing cover and handled.
Preferably, described nucleator is citric acid or talcum powder or calcium carbonate or carbon black or metal powder; Described blowing agent is a physical blowing agent, is the multiple mixture in fluorochlorohydrocarbon or butane or carbon dioxide or nitrogen or the above-mentioned substance group.
Preferably, the temperature of the flat seam shape molding die of described extruder is 50-180 ℃.
Preferably, described olefin polymer plastics are vinyon or polypropylene plastics.
Preferably, described polypropylene plastics is the polypropylene plastics of high fondant-strength or through the polypropylene plastics of modification.
Beneficial effect of the present invention is: utilize the flat seam shape molding die of gap between 0～20mm, with and the typing of front end overlap adjustable clearance opening degree, cooperate temperature to control the thickness and the density of foamed products simultaneously, can extrude continuously and produce polyethylene or high foaming plate of polypropylene plastics and section bar, make the high foamed products of thickness, thereby can satisfy the interior demand of household electrical appliance, furniture and other field for packaging material at 5-200mm.
Description of drawings
Fig. 1 is the process chart of the specific embodiment of the invention;
Fig. 2 is the structural representation of the flat seam shape molding die of the specific embodiment of the invention;
Fig. 3 is the structural representation at another visual angle of flat seam shape molding die of the specific embodiment of the invention;
Fig. 4 is the structural representation of the typing cover of the specific embodiment of the invention;
Fig. 5 is the structural representation at another visual angle of the typing cover of the specific embodiment of the invention;
Fig. 6 is the another workflow diagram of the specific embodiment of the invention.
The specific embodiment
As Fig. 1 to specific embodiments of the invention shown in Figure 5, a kind of extrusion molding prepares the device of polyethylene foamed or polypropylene articles, comprise high-speed mixer 1, the extruder 2 that links to each other with high-speed mixer 1, the constant displacement pump 3 that in extruder 2, adds materials, and the traction cutter sweep 7 of extruder 4 front portions, the head of described extruder 4 is provided with a flat seam shape and extrudes head 5.Described flat seam shape is extruded head 5 and is comprised upper and lower two templates 9,10 that have runner, and is used for side plate 11,12 that template is sealed.The gap of the seam shape opening 4 that constitutes between the described upper and lower template 9,10 is 0-20mm.Describedly extrude head 5 and traction is provided with a typing cover 6 between the cutter sweep 7, described typing cover 6 is made of two stereotype plates 13,14, has bosh on the stereotype plate 6, and is provided with heater.The both sides of two stereotype plate 13,14 inside of described typing cover 6 are provided with two transportable interior plates.The traction cutter sweep is made up of drive unit 15 and two folder rods 16, but drive unit 15 stepless speed regulations, two frame rods 16 are under the driving of drive unit 15, and the foaming plate of clamping and traction moulding cuts as required.
First specific embodiment of production method of the present invention, at first be 1.5% 2000 order talcum powder nucleators with vinyon (melt index is 2) and addition, blend evenly drops in the plastics foam shaping by extrusion machine 2 back in high-speed mixer 1, plastic foamed extruder is two rank extrusion systems, first rank are double screw extruder, and diameter is 60mm, and the second rank screw diameter is 150mm, material is through the first rank double screw extruder heating, and its temperature is controlled at more than the vinyon melt temperature.The machine barrel heating-up temperature is respectively 120 ℃, and 150 ℃, 180 ℃, 180 ℃.Shearing at twin-screw, the acting in conjunction plastifying fusion material of extruding, after the whole fusions of material, add antishrinking agent with constant displacement pump 3, addition is 3.5%, constant displacement pump 4 adds blowing agent, addition is 12%, and make its mixing of materials under the effect of twin-screw even with fusion, the rotating speed of double screw extruder is controlled at 35 rev/mins, the material that mixes enters the second rank extruder by online runner, by regulating the temperature of the second rank plastics foam shaping by extrusion machine, the temperature process condition is that temperature will descend gradually, drop to 90 ℃ gradually from 180 ℃ of melt temperatures, plastics foam shaping by extrusion machine screw speed is controlled at 40 rev/mins, and plastics foam shaping by extrusion machine internal pressure is controlled at 10MPa, the melting mixing material is controlled temperature at 100 ℃ behind flat seam shape molding die 5, regulating the clearance opening degree is 1.2mm, and material is extruded decompression at die head and discharged, and makes the fused materials cooling and shaping by cooling typing cover 6 again, the width of cooling typing cover 6 openings is 600mm.The thickness that obtains foaming is 35mm, and width is that 600mm and density are 35kg/m
3Product.Cut then by traction cutter sweep 7 clampings and traction moulding foaming plate 8, and according to Len req.
Second specific embodiment of production method of the present invention, at first be 1.5% 2000 order talcum powder nucleators with polypropylene plastics (melt index is 2) and addition, blend evenly drops in the plastics foam shaping by extrusion machine 2 back in high-speed mixer 1, plastic foamed extruder is two rank extrusion systems, first rank are double screw extruder, and diameter is 60mm, and the second rank screw diameter is 150mm, material is through the first rank double screw extruder heating, and its temperature is controlled at more than the vinyon melt temperature.The machine barrel heating-up temperature is respectively 120 ℃, and 150 ℃, 180 ℃, 180 ℃.Shearing at twin-screw, the acting in conjunction plastifying fusion material of extruding, after the whole fusions of material, constant displacement pump 4 adds blowing agent, addition is 12%, and make its mixing of materials under the effect of twin-screw even with fusion, the rotating speed of double screw extruder is controlled at 40 rev/mins, the material that mixes enters the second rank extruder by online runner, by regulating the temperature of the second rank plastics foam shaping by extrusion machine, the temperature process condition is that temperature will descend gradually, drop to 90 ℃ gradually from 180 ℃ of melt temperatures, plastics foam shaping by extrusion machine screw speed is controlled at 45 rev/mins, plastics foam shaping by extrusion machine internal pressure is controlled at 12MPa, and the melting mixing material is controlled temperature at 90 ℃ behind flat seam shape molding die 5, and regulating the clearance opening degree is 2.2mm, material is extruded decompression at die head and is discharged, make the fused materials cooling and shaping by cooling typing cover 6 again, the width of cooling typing cover 6 is 600mm, highly is 120 wood.The thickness that obtains foaming is 120mm, and width is that 600mm and density are 35kg/m
3Product.Cut then by traction cutter sweep 7 clampings and traction moulding foaming plate 8, and according to Len req.
The 3rd of production method of the present invention the specifically shows embodiment as shown in Figure 6, the twin-stage extrusion device of extruder for constituting by two extrusion systems, and first order extrusion device is single screw rod or double screw extruder.It at first is 1% talcum powder nucleator with vinyon (melt index is 2) and addition, blend evenly drops in the plastics foam shaping by extrusion machine 2 back in high-speed mixer 1, plastic foamed extruder is two rank extrusion systems, the first rank screw diameter is 135mm, the second rank screw diameter is 150mm, material is through the first rank extruder heating, and its temperature is controlled at more than the vinyon melt temperature.Heating-up temperature is respectively 120 ℃, and 150 ℃, 180 ℃, 180 ℃.Shearing at screw rod, the acting in conjunction plastifying fusion material of extruding, after the whole fusions of material, add antishrinking agent with constant displacement pump 3, addition is 3%, and adding blowing agent, addition is 8%, and make its mixing of materials under the effect of screw rod even with fusion, plastics foam shaping by extrusion machine screw speed is controlled at 40 rev/mins, the material that mixes enters the second rank extruder by online runner, by regulating the temperature of the second rank plastics foam shaping by extrusion machine, the temperature process condition is that temperature will descend gradually, drop to 90 ℃ gradually from 180 ℃ of melt temperatures, plastics foam shaping by extrusion machine screw speed is controlled at 35 rev/mins, plastics foam shaping by extrusion machine internal pressure is controlled at 8MPa, the melting mixing material is controlled temperature at 100 ℃ behind flat seam shape molding die 5, regulating the clearance opening degree is 0.8mm, material is extruded decompression at die head and is discharged, make the fused materials cooling and shaping by cooling typing cover 6 again, the A/F of cooling typing cover 6 is 600mm, highly is 25mm.The thickness that obtains foaming is 25mm, and width is that 600mm and density are 35kg/m
3Product.Cut then by traction cutter sweep 7 clampings and traction moulding foaming plate 8, and according to Len req.
The opening of described typing cover can be regulated, so that produce the foam plastic product of different width dimensions, the mode of regulating has two kinds, and a kind of is by changing the typing cover of different bores, another kind be by with two cleat design up and down of orienting cover for moving up and down the structure of regulating open height.
In addition, the operation of making as foamed plastic in the past is identical, and the user also can pass through the conventional method of the hauling speed of adjustment hitch structure, further adjusts the thickness of polyethylene foamed or expanded polypropylene.
Every index of the product that obtains such as following table:
| Expansion ratio | Relative density Kg/m 3 | Thickness range mm | Compressive deformation amount % | Load creep compliance % | Unstability load kPa | Pyroconductivity w/mk | Buoyancy Kg/m 3 | Hot strength kPa | Tensile elongation % | Tearing strength N/ |
| 5 | 90～100 | 5～200 | 10 | 1.3 | 212 | 0.063 | 905 | 481 | 25 | 2.9 |
| 15 | 70～80 | 5～200 | 12 | 1.6 | 126 | 0.058 | 925 | 393 | 34 | 2.4 |
| 25 | 40～50 | 5～200 | 13 | 2.5 | 73 | 0.059 | 965 | 345 | 67 | 2.3 |
| 35 | 35～40 | 5～200 | 14 | 2.5 | 56 | 0.063 | 970 | 294 | 62 | 2.0 |
| 45 | 25～30 | 5～200 | 14 | 2.1 | 49 | 0.064 | 975 | 245 | 59 | 1.9 |
Claims (10)
1. the device of extrusion molding preparation foaming olefinic polymerization Tetramune, comprise high-speed mixer, the extruder that links to each other with high-speed mixer, the constant displacement pump that in extruder, in extruder, adds materials, and the traction cutter sweep of extruder front portion, it is characterized in that: the head of described extruder is provided with a flat seam shape and extrudes head, and described extruding is provided with a typing cover between head and the traction cutter sweep.
2. the device of extrusion molding as claimed in claim 1 preparation foaming olefinic polymerization Tetramune, it is characterized in that: described flat seam shape is extruded head and is comprised upper and lower two templates that have runner, and is used for side plate that template is sealed.
3. the device of extrusion molding preparation foaming olefinic polymerization Tetramune as claimed in claim 2, it is characterized in that: the gap of the seam shape opening that constitutes between the described bolster is 0-20mm.
4. the device of extrusion molding preparation foaming olefinic polymerization Tetramune as claimed in claim 1, it is characterized in that: described typing cover is made of two stereotype plates, has bosh on the stereotype plate, and is provided with heater.
5. the device of extrusion molding preparation foaming olefinic polymerization Tetramune as claimed in claim 1, it is characterized in that: the both sides of two stereotype plate inside of described typing cover are provided with two transportable interior plates.
6. an extrusion molding prepares the method for foaming olefinic polymerization Tetramune, earlier that olefin polymer plastics and nucleator blend in high-speed mixer are even, again mixture is dropped in the foamed plastic extruder, become the melting material under the shearing of heating of material process and screw rod, the acting in conjunction of extruding; After the whole meltings of material, utilize constant displacement pump to add antishrinking agent and blowing agent or only add blowing agent and mix with the melting material, it is characterized in that: the melting material that is mixed with antishrinking agent, blowing agent is lowered the temperature, reduce pressure and extrude the continuous polyethylene of formation or polypropylene plastics foaming plate or section bar from the flat seam shape molding die of extruder; Plastic foamed sheet material of extruding or section bar cool off after the traction cutter sweep cuts.
7. extrusion molding as claimed in claim 6 prepares the method for foaming olefinic polymerization Tetramune, it is characterized in that: the described foamed plastic of being extruded by the flat seam shape molding die of extruder cools off or adds thermal finalization through the typing cover to be handled.
8. extrusion molding as claimed in claim 6 prepares the method for foaming olefinic polymerization Tetramune, and it is characterized in that: described nucleator is citric acid or talcum powder or calcium carbonate or carbon black or metal powder; Described blowing agent is a physical blowing agent, is the multiple mixture in fluorochlorohydrocarbon or butane or carbon dioxide or nitrogen or the above-mentioned substance group.
9. extrusion molding as claimed in claim 6 prepares the method for foaming olefinic polymerization Tetramune, and it is characterized in that: the temperature of the flat seam shape molding die of described extruder is 50-180 ℃.
10. the method for preparing foaming olefinic polymerization Tetramune as extrusion molding as described in any of claim 6 to 9, it is characterized in that: described olefin polymer plastics are vinyon or polypropylene plastics, and described polypropylene plastics is the polypropylene plastics of high fondant-strength or the polypropylene plastics of modification.