CN101049591A - Baking finish of water-soluble silicon sheet varnish - Google Patents
Baking finish of water-soluble silicon sheet varnish Download PDFInfo
- Publication number
- CN101049591A CN101049591A CN 200710015528 CN200710015528A CN101049591A CN 101049591 A CN101049591 A CN 101049591A CN 200710015528 CN200710015528 CN 200710015528 CN 200710015528 A CN200710015528 A CN 200710015528A CN 101049591 A CN101049591 A CN 101049591A
- Authority
- CN
- China
- Prior art keywords
- punching
- water
- lacquer
- viscosity
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A varnish baking technology for the water-soluble varnish of silicon steel sheet includes such steps as cleaning the punched silicon steel sheets, regulating the viscosity of said varnish, turning a varnish coating machine on, coating varnish on the silicon steel sheets, inspecting by testing its insulating resistance, and delivering the qualified silicon steel sheets to next step while returning the unqualified ones for coating vanish again.
Description
Technical field
The present invention relates to a kind of air-cooled steam turbine generator stator fanning strip baking vanish technology, relate in particular to the water-soluble lamination coating of a kind of employing import, carry out the baking vanish technology of the water-soluble lamination coating of stator sector piece baking vanish.
Background technology
Domestic baking vanish for the generator unit stator fanning strip adopts the lamination coatings that contain organic solvent more at present, carries out baking vanish on two roller coating machines.The solvent of lamination coating mostly is toluene, dimethylbenzene etc., and the volatilization meeting serious harm operator's of organic solvent is healthy, contaminated environment.While baking vanish temperature drift, the levelability of lacquer is poor, has the paint film edge to thicken phenomenon.Therefore for many years, the domestic same industry is devoted to develop water-soluble lamination coating production application always, but applies with failing so far.By the water-soluble lamination coating of external import,, cause its result of use also good, thereby influenced product quality in default of comparatively perfect baking vanish technology.
Summary of the invention
Purpose of the present invention be exactly for the baking vanish technology that solves present water-soluble lamination coating not good, influence problems such as product quality, provide a kind of scientific and reasonable, simple and easy to do, adopt rational technological process and technological parameter, make that the slice, thin piece surface paint film that bakes is smooth, thickness evenly, non-flanged thickens phenomenon, it is effective to have a baking vanish, can realize the water-soluble lamination coating of environmental protection, advantage such as energy-conservation simultaneously
For achieving the above object, the present invention has adopted following technical scheme:
A kind of baking vanish technology of water-soluble lamination coating, its technical process is,
A. prepare before the japanning, punching is cleared up, adjust the viscosity of lamination coating;
B. the startup of coating machine; Earlier distance between coating machine two rubber rolls is made as 0.25-0.35mm, makes at the uniform velocity transmission of conveyer, guarantee that roasting sheet drying time is 50-70S; Start conveyer then, connect electric heater power, and stove Nei San district temperature is set at: the proparea: district in 260～300 ℃: 320～380 ℃ of back zones: 240～300 ℃; Start all ventilation blowers again, it is stable to make three district's temperature reach design temperature and furnace temperature;
C. punching japanning; With the punching that branch ties, overlap individual by platform and send into, burr is downward without exception; Take off punching coated with paint at the coating machine end, and stack, divide platform to tie by the burr direction; Being 5～7 μ m after the single face film thickness is once painted, is 10～15 μ m behind the second painting;
D. the smear paint film is checked, and carried out megger test;
E. qualified products are sent into down operation, and substandard product need be deburred, and japanning is handled again.
Among the described step a, when punching is cleared up, remove oil stain, dirt rust staining, oxide skin, keep it smooth, and deburr by drawing; When adjusting the viscosity of lacquer with 4
#The viscosity of Ford cup inspection lacquer, whether be 100 ± 10S, can add running water or former lacquer is adjusted if any deviation if being converted under 23 ℃, in the use, should stir viscosity of periodic measurement at any time by lacquer in the paint bucket.
In the described steps d, megger test is, randomly draw some smears, closed assembly becomes the 28-32mm height, put the insulation board of δ=50mm up and down, effective area by punching in hydraulic press applies the size that 120～150N determines pressure with every square centimeter, and under the 1000V DC voltage, the insulating resistance value of measurement is answered＞800M Ω then.
The invention has the beneficial effects as follows: adopt the water-soluble lamination coating of import, on novel four roller coating machines, finish the baking vanish of stator sector piece.By optimizing the baking vanish technological parameter, make the smear painting quality stable, coating surface is smooth, thickness is even, non-flanged thickens phenomenon.Simple operation of process can realize environmental protection, energy-conservation social benefit simultaneously.
The specific embodiment
The invention will be further described below in conjunction with the specific embodiment.
A kind of baking vanish technology of water-soluble lamination coating, its technical process is:
A. prepare before the japanning;
A.1. punching inspection: can not there be oil stain, dirt etc. in the punching surface; Use brush and remove if any rust staining, oxide skin; Punching should be smooth, and tooth portion should reject if any serious deflection, fracture etc.; The burr height of punching should meet the drawing requirement, otherwise should deburr again on the burr machine.
A.2. the viscosity adjustment of lamination coating: with 4
#The viscosity of Ford cup inspection lacquer, whether be 100 ± 10S, can add running water or former lacquer is adjusted if any deviation if being converted under 23 ℃.In the use, lacquer in the paint bucket should be stirred at any time per tour time viscosity of measurement.
A.3. coating machine inspection and adjustment: check whether unimpeded drip lacquer manages; The cleaning of rubber roll and steel rider; Check whether the running of transmission and ventilation unit is normal.Adjust the distance (about 0.3mm) between two rubber rolls, proofread and correct with clearance gauge.Adjust conveyer speed, make transmission even, and make roasting sheet be about 60S drying time.
B. the startup of coating machine;
B.1. start conveyer earlier, connect electric heater power again, and stove Nei San district temperature is set at:
Proparea: district in 260～300 ℃: 320～380 ℃ of back zones: 240～300 ℃
B.2. start all ventilation blowers.
B.3. open to the lacquer bolt, lacquer is flowed into from the paint bucket drip the lacquer pipe.
B.4. treat three district's temperature reach design temperature and furnace temperature stable after, put into several slice, thin pieces examinations and be coated with.Adjust the distance between rubber roll and the steel rider simultaneously, make roasting sheet section japanning evenly and the edge do not thicken and be as the criterion.
B.5. examination is coated with roasting good slice, thin piece and carries out quality examination.Only run well, after the painting quality of roasting sheet meets the requirements fully, can produce in batches at coating machine.
C. punching japanning process;
C.1. send sheet: with the punching that branch ties, overlap individual by platform and send into, must not be overlapping, burr is downward without exception.Near not putting punching in 120mm place, rubber roll two ends.
C.2. take up: take off punching coated with paint at the coating machine end, and stack, divide platform to tie by the burr direction.Just roasting good slice, thin piece can not rub mutually, in order to avoid the damage paint film.Need the punching of second painting, must treat to handle by the said process second painting after the roasting sheet cooling.
D. the quality examination of smear;
D.1. paint film appearance: phenomenons such as can not there be bubble on the surface, grow dim, under the state of cooling, should be dry tack-free, and firmly do not come off, with the calico wiping smear that dips in industrial alcohol, face coat can not decolour.
D.2. film thickness: with the punching that the paint film thickness gauge measurement coats, focus measurement tooth portion and edge, checking has non-flanged to thicken phenomenon.Being 5～7 μ m after the single face film thickness is once painted, is 10～15 μ m behind the second painting.
D.3. megger test: randomly draw about 60 smears, closed assembly is put the insulation board of δ=50mm up and down into about the 30mm height.Effective area by punching in hydraulic press applies the size that 120～150N determines pressure with every square centimeter.Under the 1000V DC voltage, the insulating resistance value of measurement is answered＞800M Ω then.
Claims (3)
1, a kind of baking vanish technology of water-soluble lamination coating is characterized in that: its technical process is,
A. prepare before the japanning, punching is cleared up, adjust the viscosity of lamination coating;
B. the startup of coating machine; Earlier distance between coating machine two rubber rolls is made as 0.25-0.35mm, makes at the uniform velocity transmission of conveyer, guarantee that roasting sheet drying time is 50-70S; Start conveyer then, connect electric heater power, and stove Nei San district temperature is set at: the proparea: district in 260～300 ℃: 320～380 ℃ of back zones: 240～300 ℃; Start all ventilation blowers again, it is stable to make three district's temperature reach design temperature and furnace temperature;
C. punching japanning; With the punching that branch ties, overlap individual by platform and send into, burr is downward without exception; Take off punching coated with paint at the coating machine end, and stack, divide platform to tie by the burr direction; Being 5～7 μ m after the single face film thickness is once painted, is 10～15 μ m behind the second painting;
D. the smear paint film is checked, and carried out megger test;
E. qualified products are sent into down operation, and substandard product need be deburred, and japanning is handled again.
2, the baking vanish technology of water-soluble lamination coating according to claim 1 is characterized in that: among the described step a, when punching is cleared up, remove oil stain, dirt rust staining, oxide skin, keep it smooth, and deburr by drawing; When adjusting the viscosity of lacquer with 4
#The viscosity of Ford cup inspection lacquer, whether be 100 ± 10S, can add running water or former lacquer is adjusted if any deviation if being converted under 23 ℃, in the use, should stir viscosity of periodic measurement at any time by lacquer in the paint bucket.
3, the baking vanish technology of water-soluble lamination coating according to claim 1, it is characterized in that: in the described steps d, megger test is, randomly draw some smears, closed assembly becomes the 28-32mm height, puts the insulation board of δ=50mm up and down, and the effective area by punching in hydraulic press applies the size that 120～150N determines pressure with every square centimeter, under the 1000V DC voltage, the insulating resistance value of measurement is answered＞800M Ω then.