CN101045617B - 镁废渣建筑砖及生产方法 - Google Patents

镁废渣建筑砖及生产方法 Download PDF

Info

Publication number
CN101045617B
CN101045617B CN2006100167132A CN200610016713A CN101045617B CN 101045617 B CN101045617 B CN 101045617B CN 2006100167132 A CN2006100167132 A CN 2006100167132A CN 200610016713 A CN200610016713 A CN 200610016713A CN 101045617 B CN101045617 B CN 101045617B
Authority
CN
China
Prior art keywords
weight parts
slag
magnesium
powder
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2006100167132A
Other languages
English (en)
Other versions
CN101045617A (zh
Inventor
肖力光
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Linjiang Dongfeng Non-ferrous Metals Co.,Ltd.
Original Assignee
LINJIANG DONGFENG NON-FERROUS METALS CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LINJIANG DONGFENG NON-FERROUS METALS CO LTD filed Critical LINJIANG DONGFENG NON-FERROUS METALS CO LTD
Priority to CN2006100167132A priority Critical patent/CN101045617B/zh
Publication of CN101045617A publication Critical patent/CN101045617A/zh
Application granted granted Critical
Publication of CN101045617B publication Critical patent/CN101045617B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

镁废渣建筑砖及生产方法，以镁渣、复合激发剂、砂或铸造沙、炉渣或石粉、适量的水为基本原料，还可加入的矿渣粉、经过煅烧处理后的磨细硅藻土、水泥、经过表面处理剂处理的破碎秸秆、纤维、聚合物。其生产过程是：镁渣水中陈伏处理后磨粉，硅藻土煅烧后磨粉，矿渣磨粉，炉渣、秸秆破碎，原料混合加水搅拌均匀，注模，脱模，养生得产成品，本发明的积极效果是：既解除了金属镁生产厂家面临的固体污染物产生与处理的困扰，又为建筑材料行业补充了现成的墙体构件材料，取得了变害为利的双重效果。

Description

镁废渣建筑砖及生产方法
技术领域
本发明属于建筑领域，具体涉及墙体砌筑材料。
背景技术
镁渣是冶炼金属镁时产生的废渣，每生产1吨镁所产生的镁渣达20吨，还有10吨炉渣。由于目前还没有可行的镁渣的无害处理与再利用途径，如此高于产品比例的固体废物的排放，不仅需要占用土地，而且随着风雨，还给空气和水源造成污染。镁渣的数量与危害，是镁生产企业的一大负担。在环境保护呼声越来越高的当今社会，处理和利用镁渣，消除镁渣对环境造成的污染，是每个生产镁的企业必须尽快解决的问题。
发明内容
本发明的目的是提供一种镁废渣建筑砖，将有害的固体工业废物转化为优质建筑材料，克服现有技术中镁生产企业所存在的上述问题。
本发明的另一个目的是提供一种镁废渣建筑砖的生产方法，使本发明的产品得以工业化生产。
本发明的镁废渣建筑砖由以下重量份数比的原料组成：
镁渣100；复合激发剂2-50；砂或铸造砂50-500；炉渣或石粉50-500；水适量。在以上基本原料成分基础上，还可加入一种或一种以上的下述原料，矿渣粉0-100；硅藻土0-100；水泥0-100；破碎秸秆0-40；有机或无机纤维0-20；聚合物0-50。
上述材料中，复合激发剂由石膏1-10重量份、生石灰1-10重量份、熟石灰1-10重量份、氢氧化钠0.1-10重量份、氢氧化钾0.1-10重量份、减水剂0.1-5重量份混合组成。有机或无机纤维可供选用的有：聚丙烯纤维，聚乙烯醇纤维，聚丙烯晴纤维，聚酯纤维，玻璃纤维，石棉，矿棉等。上述的聚合物可以是胶乳或胶粉，供选用的有聚乙烯醇水溶性聚合物，聚乙烯醇缩甲醛水溶性聚合物，苯丙乳液，乙烯-乙酸乙烯酯共聚物，纤维素，乳胶粉等。
本发明基本原料优选用量重量比为：镁渣100；复合激发剂30；砂或铸造沙200；炉渣或石粉200；
本发明的制做工艺是：
1、原料的预处理
镁渣水中陈伏3-10天，干燥后磨粉，粉末粒度2000cm2/g—8000cm2/g；
硅藻土在450-750℃条件下煅烧1-4小时，磨成1500cm2/g-6000cm2/g粒度粉末；
矿渣磨成3000cm2/g-8000cm2/g的粉末；
炉渣或石粉破碎成5-20mm粒径的颗粒；
秸秆破碎成长度5-20mm的碎条。
2、混合、成形
将所需材料按上述用量比例加入搅拌容器中，搅拌均匀，注入砖模，凝固后脱模。
3、养生
按常规混凝土构件养生过程养生，养生后即为成品。
本发明的积极效果是：可以得到理化性能和黏土砖等同的墙体砖，既解除了金属镁生产厂家面临的固体污染物产生与处理的困扰，又为建筑材料行业补充了现成的墙体构件材料，取得了变害为利的双重效果。
具体实施方式
实施例1
取镁渣100重量份；复合激发剂2重量份；铸造砂50重量份；炉渣50重量份；矿渣粉20重量份；硅藻土20重量份；水泥20重量份；破碎秸秆5重量份；聚丙烯晴纤维5重量份；聚乙烯醇缩甲醛水溶性聚合物5重量份。
镁渣水中陈伏3天，干燥后磨粉，粉末粒度2000cm2/g。硅藻土在600℃条件下煅烧2小时，磨成1500cm2/g粒度粉末。矿渣磨成3000cm2/g的粉末。炉渣或破碎成5-20mm粒径的颗粒。秸秆破碎成长度5-20mm的碎条。
将所需材料按上述用量比例加入搅拌容器中，加适量水，搅拌均匀，注入砖模，凝固后脱模。按常规混凝土构件养生过程养生，养生后即为成品。
实施例2
取镁渣100重量份；复合激发剂50重量份；砂500重量份；石粉500重量份；水泥100重量份；秸秆40重量份；聚丙烯纤维20重量份；纤维素50重量份。
镁渣水中陈伏10天，干燥后磨粉，粉末粒度8000cm2/g。石粉粒径5-20mm。秸秆破碎成长度5-20mm的碎条。其他过程同实施例1。
实施例3
取镁渣100；复合激发剂30重量份；铸造砂200重量份；炉渣200重量份；石粉200重量份；矿渣粉50重量份；硅藻土100重量份；水泥30重量份；聚乙烯醇水溶性聚合物20重量份。
硅藻土在750℃条件下煅烧1小时，磨成6000cm2/g粒度粉末。矿渣磨成8000cm2/g的粉末。其他过程同实施例1。

Claims (2)

1.镁废渣建筑转，其特征是：由以下重量份数比例的原料组成：
镁渣100重量份、复合激发剂2重量份、铸造砂50重量份、炉渣50重量份、矿渣粉20重量份、硅藻土20重量份、水泥20重量份、破碎秸秆5重量份、聚丙烯晴纤维5重量份、聚乙烯醇缩甲醛水溶性聚合物5重量份。
2.一种权利要求1所述的镁废渣建筑砖的生产方法，其特征是：
(1)原料提取
镁渣100重量份、复合激发剂2重量份、铸造砂50重量份、炉渣50重量份、矿渣粉20重量份、硅藻土20重量份、水泥20重量份、破碎秸秆5重量份、聚丙烯晴纤维5重量份、聚乙烯醇缩甲醛水溶性聚合物5重量份；
(2)原料预处理
将步骤(1)所取原料中：
镁渣水中陈伏3天，干燥后磨成比表面积为2000cm2/g的粉末，
硅藻土在600℃条件下煅烧2小时，磨成比表面积为1500cm2/g的粉末，
矿渣磨成比表面积为3000cm2/g的粉末，
炉渣破碎成粒径5-20mm的颗粒，
秸秆破碎成长度5-20mm的碎条；
(3)混合、成型
将经步骤(2)处理的原料与步骤(1)所取的其余原料加入搅拌器中，加入适量水，搅拌均匀，注入砖模，凝固后脱模；
按混凝土构件养生方法养生，养生后得镁废渣建筑砖。
CN2006100167132A 2006-03-27 2006-03-27 镁废渣建筑砖及生产方法 Expired - Fee Related CN101045617B (zh)